SLM 방식으로 출력된 STS 316L의 기계적 및 마찰·마모 특성에 미치는 UNSM처리 후 영향에 관한 연구

A Study on the Effect of UNSM Treatment on the Mechanical and Tribological Properties of STS 316L Printed by Selective Laser Melting

  • Ro, J.S. (Graduate School, Dept. of Mechanical Engineering, Sun Moon University) ;
  • Sanseong, C.H. (Graduate School, Dept. of Mechanical Engineering, Sun Moon University) ;
  • Umarov, R. (Graduate School, Dept. of Mechanical Engineering, Sun Moon University) ;
  • Pyun, Y.S. (Dept. of Mechanical Engineering, Sun Moon University) ;
  • Amanov, A. (Dept. of Mechanical Engineering, Sun Moon University)
  • 투고 : 2018.07.27
  • 심사 : 2018.11.10
  • 발행 : 2018.12.31

초록

STS 316L prepared by additive manufacturing (AM) exhibits deterioration of mechanical properties and wear resistance due to the presence of defects such as black-of-fusion defects, internal porosity, residual stress, and anisotropy. In addition, high surface roughness (integrity) of AM products remains an issue. This study aimed to apply ultrasonic nanocrystal surface modification (UNSM) technology to STS 316L prepared by AM to increase the surface hardness, to reduce the surface roughness, and to improve the friction and wear behavior to the level achieved by bulk material manufactured using traditional processes. Herein, the as-received and polished specimens were treated by UNSM technology and their resulting properties were compared and discussed. The results showed that UNSM technology increased the surface hardness and reduced the surface roughness of the as-received and polished specimens. These results can be attributed to grain size refinement and pore elimination from the surface. Moreover, the friction of the as-received and polished specimens after UNSM technology was lower compared to those of the as-received and polished specimens, but no significant differences in wear resistance were found.

키워드

OHHHB9_2018_v34n6_270_f0001.png 이미지

Fig. 1. Dimensions of test specimen in mm.

OHHHB9_2018_v34n6_270_f0001.png 이미지

Fig. 1. Dimensions of test specimen in mm.

OHHHB9_2018_v34n6_270_f0002.png 이미지

Fig. 2. Basic principle of SLM.

OHHHB9_2018_v34n6_270_f0002.png 이미지

Fig. 2. Basic principle of SLM.

OHHHB9_2018_v34n6_270_f0003.png 이미지

Fig. 3. Schematic view of a UNSM process.

OHHHB9_2018_v34n6_270_f0003.png 이미지

Fig. 3. Schematic view of a UNSM process.

OHHHB9_2018_v34n6_270_f0004.png 이미지

Fig. 4. Schematic view of a reciprocating wear tester.

OHHHB9_2018_v34n6_270_f0004.png 이미지

Fig. 4. Schematic view of a reciprocating wear tester.

OHHHB9_2018_v34n6_270_f0005.png 이미지

Fig. 5. Comparison in surface roughness and hardness before and after UNSM treatment.

OHHHB9_2018_v34n6_270_f0005.png 이미지

Fig. 5. Comparison in surface roughness and hardness before and after UNSM treatment.

OHHHB9_2018_v34n6_270_f0006.png 이미지

Fig. 6. Cross-sectional SEM morphologies of the untreated (a) and UNSM-treated (b) specimens.

OHHHB9_2018_v34n6_270_f0006.png 이미지

Fig. 6. Cross-sectional SEM morphologies of the untreated (a) and UNSM-treated (b) specimens.

OHHHB9_2018_v34n6_270_f0007.png 이미지

Fig. 7. SEM images of the as-received and polished surfaces of the untreated (a and c) and UNSM-treated (b and d) specimens.

OHHHB9_2018_v34n6_270_f0007.png 이미지

Fig. 7. SEM images of the as-received and polished surfaces of the untreated (a and c) and UNSM-treated (b and d) specimens.

OHHHB9_2018_v34n6_270_f0008.png 이미지

Fig. 8. EDX images of the as-received and polished surfaces of the untreated (a1 and c1) and UNSM-treated (b1 and d1) specimens.

OHHHB9_2018_v34n6_270_f0008.png 이미지

Fig. 8. EDX images of the as-received and polished surfaces of the untreated (a1 and c1) and UNSM-treated (b1 and d1) specimens.

OHHHB9_2018_v34n6_270_f0009.png 이미지

Fig. 9. Comparison in XRD patterns before and after UNSM treatment.

OHHHB9_2018_v34n6_270_f0009.png 이미지

Fig. 9. Comparison in XRD patterns before and after UNSM treatment.

OHHHB9_2018_v34n6_270_f0010.png 이미지

Fig. 10. Friction coefficient and wear track profiles of the as-received and polished surfaces of the untreated and UNSM-treated specimens.

OHHHB9_2018_v34n6_270_f0010.png 이미지

Fig. 10. Friction coefficient and wear track profiles of the as-received and polished surfaces of the untreated and UNSM-treated specimens.

OHHHB9_2018_v34n6_270_f0011.png 이미지

Fig. 11. SEM images showing wear track of the as-received and polished surfaces of the untreated (a and c) and UNSM-treated (b and d) specimens.

OHHHB9_2018_v34n6_270_f0011.png 이미지

Fig. 11. SEM images showing wear track of the as-received and polished surfaces of the untreated (a and c) and UNSM-treated (b and d) specimens.

OHHHB9_2018_v34n6_270_f0012.png 이미지

Fig. 12. EDX images of the wear track of the as-received and polished surfaces of the untreated (a1, a2, c1, c2) and UNSM-treated (b1, b2, d1, d2) specimens.

OHHHB9_2018_v34n6_270_f0012.png 이미지

Fig. 12. EDX images of the wear track of the as-received and polished surfaces of the untreated (a1, a2, c1, c2) and UNSM-treated (b1, b2, d1, d2) specimens.

Table 1. Physical properties of STS 316L powder

OHHHB9_2018_v34n6_270_t0001.png 이미지

Table 1. Physical properties of STS 316L powder

OHHHB9_2018_v34n6_270_t0001.png 이미지

Table 2. Chemical composition of STS 316L in wt. %

OHHHB9_2018_v34n6_270_t0002.png 이미지

Table 2. Chemical composition of STS 316L in wt. %

OHHHB9_2018_v34n6_270_t0002.png 이미지

Table 3. Mechanical properties of STS 316L

OHHHB9_2018_v34n6_270_t0003.png 이미지

Table 3. Mechanical properties of STS 316L

OHHHB9_2018_v34n6_270_t0003.png 이미지

Table 4. SLM process conditions

OHHHB9_2018_v34n6_270_t0004.png 이미지

Table 4. SLM process conditions

OHHHB9_2018_v34n6_270_t0004.png 이미지

Table 5. UNSM treatment parameters

OHHHB9_2018_v34n6_270_t0005.png 이미지

Table 5. UNSM treatment parameters

OHHHB9_2018_v34n6_270_t0005.png 이미지

Table 6. Tribo-test conditions

OHHHB9_2018_v34n6_270_t0006.png 이미지

Table 6. Tribo-test conditions

OHHHB9_2018_v34n6_270_t0006.png 이미지

Table 7. Surface measurement conditions

OHHHB9_2018_v34n6_270_t0007.png 이미지

Table 7. Surface measurement conditions

OHHHB9_2018_v34n6_270_t0007.png 이미지

참고문헌

  1. Miranda, G., Faria, S., Bartolomeu, F., Pinto, E., Mederia, S., Mateus, A., Carreira, P., Alves, N., Silva, F. S., Carvalho, O., "Predictive models for physical and mechanical properties of 316L stainless steel produced by selective laser melting", Mater. Sci. Eng.: A, doi:10.1016/j.msea.2016.01.028, 2016.
  2. Bartolomeu, F., Faria, S., Carvalho, O., Pinto, E., Alves, N., Silva, F. S., Miranda, G., Silva, F. S., Carvalho, O., "Predictive models for physical and mechanical properties of Ti6Al4V produced by Selective Laser Melting", Mater. Sci. Eng.: A, doi:10.1016/j.msea.2016.03.113, 2016.
  3. Ngo, T. D., Kashani, A., Imbalzano, G., Nguyen, K. T. Q., Uui, D., "Additive manufacturing (3D printing): A review of materials, methods, applications and challenges", Composites Part B, doi:10.1016/j.compositesb.2018.02.012, 2008.
  4. Sun, Z., Tan, X., Tor, S. B., Chua, C. K.,"Simultaneously enhanced strength and ductility for 3D-printed stainless steel 316L by selective laser melting", NPG Asia Mater., Vol. 10, pp. 127-136, 2018. https://doi.org/10.1038/s41427-018-0018-5
  5. Frazier, W. E., "Metal additive manufacturing: A review", J. Mater. Eng. Perform., Vol. 23, pp. 1917-1928, 2014. https://doi.org/10.1007/s11665-014-0958-z
  6. Mumtaz, K. A., Erasenthiran, P., Hopkinson, N., "High density selective laser melting of Waspaloy$^{(R)}$", J. Mater. Process. Technol., doi:10.1016/j.jmatprotec.2007.04.117, 2008.
  7. Martin, J. H., Yahata, B. D., Hundley, J. M., Mayer, J. A., Schaedler, T. A., Pollock, T. M., "3D printing of high-strength aluminium alloys", Nature, Vol. 549, pp. 365-369, 2017. https://doi.org/10.1038/nature23894
  8. Haase, C., Bultmann, J., Hof, J., Ziegler, S., Bremen, S., Hinke, C., Schwedt, A., Prahl, U., Bleck, W., "Exploiting process-related advantages of selective laser melting for the production of high-manganese steel", Materials, doi:10.3390/ma100100562, 2017.
  9. Bartolomeu, F., Buciumeanu, M., Pinto, E., Alves, N., Carvalho, O., Silva, F. S., Miranda, G., "316L stainless steel mechanical and tribological behavior - A comparison between selective laser melting, hot pressing and conventional casting", Addit. Manuf., doi:10.1016/j.addma.2017.05.007, 2017.
  10. Pyoun, Y. S., Park, J. Y., Cho, I. H., Kim, C. S., Suh, C. M., "A study on the ultrasonic nano crystal modification (UNSM) technology and it's application", Transactions of KSME A, doi:10.3795/KSME-A.2009.33.3.190, 2009.
  11. Zhu, Y., Zou, J., Chen, X., Yang, H., "Tribology of selective laser melting processed parts: Stainless steel 316L under lubricated conditions", Wear, doi:10.1016/j.wear.2016.01.004, 2016.
  12. Liu, J., Suslov, S., Li, S., Qin, H., Ren, Z. Ma, C. Wang, G. X., Doll, G. L., Cong, H., Dong, Y., Ye, C., "Effects of ultrasonic nanocrystal surface modification on the thermal oxidation behavior of Ti6Al4V", Surf. Coat. Technol., doi:10.1016/j.surfcoat.2017.04.051, 2017.
  13. Amanov, A., Karimbaev, R., Maleki, E., Unal, O., Pyun, Y. S., Amanov, T., "Effect of combined shot peening and ultrasonic nanocrystal surface modification processes on the fatigue performance of AISI 304", Surf. Coat. Technol., doi:10.1016/j.surfcoat.2018.11.100, 2018.
  14. Amanov, A., Lee, S. W., Pyun, Y. S., "Low friction and high strength of 316L stainless steel tubing for biomedical applications", Mater. Sci. Eng.: C, doi:10.1016/j.msec.2016.10.005, 2017.
  15. Amanov, A., Pyun, Y. S., Kim, J. H., Sasaki, S., "The usability and preliminary effectiveness of ultrasonic nanocrystalline surface modification technique on surface properties of silicon carbide", Appl. Surf. Sci., doi:10.1016/j.apsusc.2014.05.089, 2014.
  16. Gwidon, W., Engineering Tribology, 3nd Edition, Chap. 8, pp. 399, Butterworth-Heinemann, Oxford, UK, 2005(ISBN 9780750678360).

피인용 문헌

  1. 에너지 제어 용착을 이용한 스테인리스 316L의 적층 특성 및 기계적 물성 평가 vol.20, pp.6, 2018, https://doi.org/10.14775/ksmpe.2021.20.06.059