A study on properties of 400kN porcelain suspension insulator for transmission line by analyzing of raw materials

400kN 송전용 자기애자의 재질에 따른 특성 연구

In order to analyze the physical and chemical characteristics of the home production porcelain insulators by change of the alumina addition amount, 36000lbs ball socket type suspension insulators which were manufactured in 1989, 1995 and 2001 removed in transmission line and an experiment was performed. By the result, 8 [wt.%] alumina that influences the mechanical properties and arc resistance properties in case of insulators that were manufactured in 1989 was contained, and the relative density and the fracture toughness of insulators appeared by 94.2% and 1.4 [MPa $M^{1/2}$], respectively. However, 12 [wt.%] alumina was contained in case of insulators that were manufactured in 1995, and the relative density and the fracture toughness of insulators appeared preferably lower by 92% and 1.3 [MPa $M^{1/2}$], respectively. Amount of alumina was contained most by 17 [wt.%] in case of insulators that were manufactured in 2001. It was confirmed that the electrical and mechanical characteristics such as the relative density and the fracture toughness appeared excellently by 96% and 1.7 [MPa $m^{1/2}$], respectively.