• Journal of the Korean Wood Science and Technology
• /
• v.24 no.1
• /
• pp.34-47
• /
• 1996

Veneers of two nominal thicknesses, 1.5 and 2.5mm, were rotary peeled from Japanese larch (Larix leptolepis). Dahurian larch (Larix gmelinei) and Radiata pine (Pinus radiata) bolts unheated and heated in the water vat temperature of $66^{\circ}C$ by rising a final temperature at 10cm core of $60^{\circ}C$ to remain core diameter of 11.4cm. 1.5 and 2.5mm thick veneer cut from the heated Japanese larch were significantly thinner than those of the unheated bolt and 2.5mm thick veneer cut from the heated Dahurian larch were significantly thicker than that of the unheated bolt. 1.5mm thick Dahurian larch veneer and 1.5 and 2.5mm thick Radiata pine veneers showed insignificant difference between the unheated and heated bolts, respectively. Check distance on the loose side of 1.5mm thick veneer cut from the heated Radiata pine was significantly wider than that of the unheated bolt. However check distances on the loose side of 1.5 and 2.5mm thick Japanese larch and Dahurian larch veneers and 2.5mm thick Radiata pine veneers showed insignificant difference between the unheated and heated bolts. Also the depth of check on the loose side of three species showed insignificantly difference between the unheated and heated bolts. Arithmatic mean deviation($R_a$) and maximum height($R_{max}$) of the profile on the loose side of dried veneer by preheating the bolt compared with unheated bolts were different among apecies and between veneer thickness. The preheating treatment slightly affected qualities of these thin veneers such as 1.5 and 2.5mm. The yield of 2.5mm thick veneer from the heated radiata pine was significantly higher than that of the unheated bolt. However the yield of 2.5mm thick veneer for other two species and 1.5mm thick veneer for three species showed insignificant difference between the unheated and heated bolts. The yield of 2.5mm thick veneer for three species were higher than those of 1.5mm thick veneer. The average yields of green veneer of Japanese larch. Dahurian larch and Radiata pine were 57.1, 55.1 and 54.0 percent, respectively. Variables such as initial MC. drying time and veneer thickness had strong effect for Japanese larch veneer, less effect for Radiata pine veneer and nuch less effect on final MC for Dahurian larch veneer in jet drying. Correlation between the current MC and the drying time of Dahurian larch with low variation of initial MC was higher than those of Japanese larch and Radiata pine veneer with high variation of initial MC in high temperature drying. Thickness shrinkages of 2.5mm thick veneer for Japanese larch and Radiata pine were higher than those of 1.5mm thick veneers, but shrinkages of Dahurian larch veneer were similar between two nominal veneer thicknesses.

• Journal of the Korean Wood Science and Technology
• /
• v.41 no.1
• /
• pp.42-50
• /
• 2013

Since 1990's, a plywood for flooring base has gotten customers' demand. Costs of raw material and production increased because of changed environment of industry. Tropical timber such as Red Meranti (Shorea acuminate) used for raw material of the floor has been depleting beside countries in South Eastern Asia changed species of afforestation. As a result, it gets hard to secure good quality of raw material for plywood. Moreover plywood price is increased suddenly after earthquake in Japan. Eucalyptus (Eucalyptus globulus) in china has been using for raw material as a countermeasure of changed environment of industry. In this study, possibility of using flooring consisted of Eucalyptus veneer as crossband layers was checked by deflection experiments. Flooring consisted of Red Meranti was used for comparison. Two factors which impact on deflection are a type of density gradient and density difference between Long-grain veneer and Short-grain veneer. Red Meranti samples are M type of density gradient on the other hand Eucalyptus samples are W type of density gradient. The more samples have high density difference, the more deformation was checked. A sample which has big density difference between core and cross bands layer warp more also deform. Flooring was deformed smaller than plywood and samples which have big density difference was deformed more.

• Journal of the Korean Wood Science and Technology
• /
• v.10 no.3
• /
• pp.152-164
• /
• 1982

1. In order to make the improvement of plywood quality, this study has been made. The pretreatments applied to the veneers are as follows. a) The soaking treatment of the veneer in 30 percent methanol solution for 24 hours was applied to remove some resinous materials which may cause many stain discolouring on the face of finished plywood. b) The preservative treatment of the veneer in 2 percent malenit solution for 2 to 3 minutes was adopted to make resistance against decay and insect damages. c) The fire retardant treatment of the veneer in 40 percent ammonium phosphate solution for 2 hours was applied to give retardation effect against fire burning. 2. The results summarized in this study are as follows. a) One percent resinous materials was extracted, after the soaking of the veneers in 30 percent diluted methanol. b) No marks of the dirty stains of resinous materials on the face of the treated plywood was shown, although many quite dirty stains on the face of untreated plywood have contrary seen. c) However, the strip shear test strength of the treated plywood was not decreased. It means that there is no difference in the strength between the treated plywood and the untreated plywood. The strength values were 25.08 kg/$cm^2$ and 24.98 kg/$cm^2$, respectively. d) The strip shear test strength of plywood made of the treated veneers in 2 percent malenit solution was not decreased. e) The slight decrease of the strip shear test strength of the treated plywood made of the treated veneer in 40 percent ammonuim phosphate solution was shown. However, the remarkable difference of the fire retardation activities between the treated specimens and the untreated specimens has seen as in Table 10, that is, the fire proofed specimens had taken about 28 seconds to start to burn, while the untreated specimens had taken 15 seconds to reach to burning. This means that the fire retardation effect of the fire proofed plywood was greater than that of the unproofed plywood.

• Journal of the Korean Wood Science and Technology
• /
• v.35 no.1
• /
• pp.27-35
• /
• 2007

This experiment was carried out to investigate the appearance and surface gluing characteristics of laminated boards overlaied with teak sliced veneer, printing paper, wall paper, cotton cloth, and wool cloth, The overlaying sheets were glued on the laminated boards with polyvinyl acetate emulsion adhesives and the species for laminated boards was red pine. The obtained results are summarized as follows; in case of the teak sliced veneer overlaied boards, the appearance quality was very good and showed the first grade of KS standard. but the delamination rate was 44.0% and 895% for cold water or warm water dipping treatments, respectively, so the wet gluing properties were very bed. In the case of the paper or cloth overlaied boards, the appearance quality was same good and showed the first grade of KS standard, but their delamination rate was 10~20% and 39.3~49.0 for cold water or warm water dipping treatments, respectively, so the wet gluing properties were bed, relatively better than sliced veneer overlaied boards. The present work showed that appearance of laminated boards overlaid with several sheets appeared quite positive in terms of secondary gluing qualities of laminated boards, suggesting that sliced veneer, paper, and cloth would be appropriate for the overlaying materials of laminated boards.

• Journal of the Korean Wood Science and Technology
• /
• v.42 no.5
• /
• pp.571-578
• /
• 2014

As a way of developing wooden joint development, a glass fiber reinforced wood plate was manufactured to replace a steel plate. Also, the fracture toughness was evaluated. Through application to a cantilever-type specimen made of a column and a beam, the moment resistance performance was evaluated. For the fracture toughness specimen of the wood plate, 12 types were manufactured by varying the combination of a main member (veneer and plywood) and reinforcement (glass fiber sheet and glass fiber cloth). The results of the fracture toughness test indicated that the 5% yield load of the specimen using plywood was 18% higher than that of the specimen using veneer, and that the specimen reinforced by inserting glass fiber sheets between testing materials (Type-3-PS) had the highest average 5% yield load 4841 N. Thus, a moment resistance strength test was performed by applying Type-3-PS to a column-beam joint. The results of the test indicated that compared to the specimen using a steel plate and a drift pin (Type-A), the maximum moment ratio of the specimen using a glass fiber reinforced wood plate (Type-3-PS) and a drift pin (Type-B) was 0.79; and that a rupture occurred in the wood plate due to high stiffness of the drift pin. The maximum moment ratio of the specimen using a glass fiber reinforced wood plate (Type-3-PS) and a glass fiber reinforced wooden laminated pin (Type-C) was 0.67, which showed low performance. However, unlike Type-A, a ductile fracture occurred on Type-C, and the load gradually decreased even after the maximum moment.

• Journal of the Korea Furniture Society
• /
• v.13 no.1
• /
• pp.71-83
• /
• 2002

This study was carried out to develop colored-wood furniture using veneer, small-round log and fiberboard to protect forest resources through the study of minimalism. which advocates the environmental issue inherent to contemporary furniture in the postmodern era. Based on the historical and theoretical context of minimalism closely related to the environmental protection, this study suggested the technical way how to produce the environment-friendly furniture with the least use of valuable and natural log. Finally, the color-wooden furniture was developed based on the asceticism, simplification, and repetition of the minimalism in a trend of contemporary furniture design. By soaking a veneer, Psuedotsuga menziesii and small-round log, Pinus densiflora into a very-diluted organic dye, the environment-friendly and colored-wood furniture could be created in harmony with contemporary interior space, which has showed various colors such as yellow, blue, red, and green with a pastel tone. The spring wood of the colored softwood was deeply stained, while the summer wood was lightly done. By utilizing such valueless used woods which have been little in furniture production, it was possible to decrease the consumption of precious raw log such as zelkova, ebony, rose, maple, cherry, mahogany and so on. Thus, it became obvious to be able for contemporary furniture designers to produce beautiful furniture with dyed fiberboard and small-round logs pregnant with minimalism.

• Journal of the Korean Wood Science and Technology
• /
• v.16 no.1
• /
• pp.3-8
• /
• 1988

This study was carried out to examine the effect of pretreatment of veneer with aluminum sulfate solution for the manufacture of the kapur plywood on the reduction of urea resin spread. The results were as follows: 1. Specific gravities of plywoods made of the kapur veneers ranged from 0.83 to 0.84 and their moisture contents based on air dry weight showed from 10.6% to 11.4%. These met the Korean Industrial Standards. 2. In the case of dry shear strength for the 3rd class plywood, 40% reduction- spread met K S as well as normal urea resin spread. pH of the aluminum sulfate solution gave better result at pH 4.5 and pH 6 than at pH 3. For the manufacture of the 2nd class plywood, hot and cold water-wet shear strength show the best results at the following conditions; such as 20% reduction spread, pH 4.5 of aluminum sulfate solution and all veneer treatment.

• Textile Coloration and Finishing
• /
• v.34 no.4
• /
• pp.234-240
• /
• 2022

Use of processed timber can help reduce environmental damage and the economic burden of resources (important problems with use of raw timber) and can meet the needs of various fields where the sensibility of raw timber is required. Veneer wood is positioned as a high-value-added product due to its luxury and beauty, and it is used in various fields as a building-related material, such as interior decoration, furniture, flooring, building interior materials, and lumber. Dyeing is necessary to enhance the aesthetic appearance of this pattern and to expand its use. Therefore, in this study, we compared and analyzed the dye ability of oak-patterned materials with reactive dyes, and evaluated their performance as interior materials. As a result, the oak pattern was dyed with 9 kinds of reactive dyes and a comparative analysis was performed. The most suitable conditions are 50℃, 2 hours, and 0.5% o.w.f. In addition, evaluating resilience to daylight, resilience to rubbing, fire resistance, and flame retardance, yielded results suitable for use as an interior material. In this study, the dyeability of veneer dyed under various conditions using reactive dyes was compared and analyzed the performance as an interior material was evaluated.

• Journal of the Korean Wood Science and Technology
• /
• v.35 no.6
• /
• pp.108-117
• /
• 2007

This research was performed to investigate the feasibility of bamboo as a raw material for the manufacture of plywood. Wood veneer-bamboo zephyr composite boards (WBCB) were manufactured using keruing (Dipterocarpus sp.) veneers and hachiku bamboo (Phyllostacbys nigra var. henonis Stapf) using various adhesives, and the effect of the method and amount of resin spread on the mechanical properties of the composites were investigated. The WBCB manufactured using polymeric isocyanate (PMDI) showed the best mechanical properties, followed by phenol-formaldehyde resin (PF), phenol-melamine-formaldehyde resin, urea-melamine-formaldehyde resin, and urea-formaldehyde resin. However, considering the operation feasibility as well as mechanical properties, PF resin proved to be the appropriate adhesive for the practical purpose. As the amount of resin spread increased, the mechanical properties of 5-ply WBCB with 12 mm thicknesses manufactured using PF resin tended to increase, and more failure occurred at the interface between veneer and bamboo zephyr than at the interface among bamboo zephyrs. This result suggests that penetration of resin into bamboo zephyr could be the important factor. In this research, the appropriate amount of resin amount was $320g/m^2$. 5-ply WBCBs were manufactured using various methods of resin spread but the effect of the methods on the mechanical properties showed no little difference, which meant that the method of resin spread could be chosen considering the manufacturing conditions and operation feasibility.

• Journal of the Korean Wood Science and Technology
• /
• v.19 no.3
• /
• pp.35-44
• /
• 1991

In this study, thickness 40mm glulams were composed of thickness 5mm, 10mm Quercus laminas and Pinus koraiensis laminas to study on the effect of load variation on transition of neutral axis of laminated veneer lumber(LVL). The transition of neutral axis was examined by strain variation, which was checked by strain gauge. amplifier, recorder, and strain meter. The elasticity of glulam was estimated by E = $\Sigma(E_i\;I_ i)$/I and this estimated elasticity values were compared with the elasticity values of glulam in bending. The result obtained can be summarized as follows: 1. The location of neutral axis of glulam was effected by glulam composition methods 2. The neutral axis did not shift by load variation within proportional limit. 3. The estimated elasticity of glulam by E = $\Sigma(E_i\;I_ i)$/I showed much lower value than the elasticity of glulam in bending.