• Journal of the Korean Wood Science and Technology
• /
• 제44권6호
• /
• pp.828-841
• /
• 2016

Relatively little information is available regarding the correlation between wood and veneer quality, especially for Samama wood, an endemic wood species in eastern Indonesia. This study addresses the quality of 8 years old Samama wood and its effect on the veneer quality. Samama wood quality was determined by evaluating its specific gravity, moisture content, fiber dimensions, and microfibril angle from pith toward bark. Meanwhile, veneer quality was assessed by examining veneer thickness and lathe check characteristics. Geometry factor model was constructed to elaborate the quantities of lathe check from pith toward bark. Results show that fair variations of veneer thickness, ranging from 1.5 mm to 3.0 mm, could be obtained from Samama wood. The quantity, depth, and length of lathe check were noticeably decreasing toward bark. Further, in the same manufacturing process, geometry factor was determined as the dominant factor over other wood properties in affecting the frequency of lathe checks from pith towards bark. These facts should be put into consideration in producing veneer from Samama wood. Moreover, these results enlighten the potential of Samama wood as plywood and other excellent veneer-based products.

• Journal of the Korean Wood Science and Technology
• /
• 제8권2호
• /
• pp.6-8
• /
• 1980

일본 잎갈나무, 삼나무, 편백의 로타리단판 절삭 적정 노스바압축도를 얻기 위해서 노스바압축도 5%, 10% 15%의 조건으로 절삭된 단판의 이활, 인장 강도를 시험하여 다음과 같은 결론을 얻었다. 1. 일본잎갈나무 2mm단판의 적정 노스바압축도는 15%이었고, 2. 삼나무 2mm 단판의 적정 노스바압축도는 5%이었으며, 3. 편백 2mm 단판의 적정 노스바압축도는 15%이었다.

• Journal of the Korean Wood Science and Technology
• /
• 제38권5호
• /
• pp.385-390
• /
• 2010

This study was carried out to manufacture very thin natural elm veneer overlaid charcoal board for enhancing aesthetic value of charcoal board for the indoor application, and to use the advantageous properties of the charcoal as a building material for solving the sick house problem. The thin elm veneer had 26.9% opening ratio. The experiment results showed that the spreading area and the nonvolatile content of adhesive did not affect the gas adsoprtion of fancy veneer overlaid charcoal board. The natural thin elm veneer overlaid charcoal board enhanced not only the aesthetic beauty but also showed the same gas adsorption by the charcoal board.

• Journal of the Korean Wood Science and Technology
• /
• 제46권3호
• /
• pp.221-230
• /
• 2018

본 연구에서는 자외선 노출에 의한 목재베니어의 광 열화를 방지하기 위하여 변색 요인을 제거하여 그 효과를 평가하고자 하였다. 목재 중 추출물함량이 높고 어두운 색상을 나타내며 고급용재로 사용되고 있는 대표 활엽수종인 walnut을 공시재료로 선택하여 광 열화 분석 및 방지법에 관한 연구에 사용하였다. 베니어 내 발색단을 함유하는 물질을 탈리하기 위해 실시한 알코올-벤젠, 과산화수소 및 차아염소산나트륨 수용액 처리 후 광 안정성 평가를 실시하였다. 광 변색인자로 알려진 추출물 성분의 제거 후에는 색 안정화 효과를 보이지 않았다. 한편, 리그닌 성분을 제거하기 위하여 과산화수소를 20, 30% 농도로 하여 $75^{\circ}C$에서 1시간 처리하였으며, 그 결과 표면색상에 대한 표백효과는 나타내었으나 추출물 용출에 따른 재색 유지가 어려우며 광 노출에 대한 안정화 효과를 나타내지 않았다. 반면, 차아염소산나트륨 수용액을 1, 2 및 3% 농도로 하여 동일 온도 및 시간 조건에서 처리 한 베니어의 광 노출 평가결과, 추출물 용출에 의한 재색변화는 나타났지만, 광 노출에 의한 색상 변화는 관찰되지 않았으므로 우수한 안정화 효과를 나타낼 수 있었다. 하지만, 3% 이상 농도에서는 베니어 표면의 거칠기와 손상이 발생되므로, walnut 베니어의 경우 적정 농도조건에서의 처리가 필요한 것으로 사료된다.

• Journal of the Korean Wood Science and Technology
• /
• 제39권5호
• /
• pp.451-458
• /
• 2011

Adhesives derived from renewable resources allow wood panel producers to make lower cost alternatives to formaldehyde-based adhesive resins. Among them, adhesive components extracted from industrial by-products or wastes are the most important research fields in the efficient utilization of waste and cost reduction. In our study, the rapeseed flour, which is a by product from the production of biodiesel extracted from rapeseed, was introduced to develop alternative adhesives for the production of wood flooring. The rapeseed flour was hydrolyzed with 1% sodium hydroxide solution and PF prepolymers were prepared with 3-molar ratios, 1.8, 2.1 and 2.4. The linear fracture mechanics was introduced to evaluate the glue bond quality in wood flooring composed of fancy-veneered and plywood, and the formaldehyde emission and adhesive penetration were also investigated. The formaldehyde emissions of wood flooring met the requirement of the standard of $SE_0$ specified in the KS standard. The rapeseed flour adhesive penetrated sufficiently into the vessel elements and lumens in fancy veneer and plywood and gave strong bond quality to the wood flooring. The fracture mechanics was introduced to evaluate the adhesive joint between fancy veneer and plywood. The critical stress intensity factor ($K_{IC}$) of boliva overlayed wood flooring was increased with increasing molar ratio and this was the same tendency in oak overlayed wood flooring. From the results, the formulated adhesives were efficiently used to bond fancy veneer onto the plywood to make wood flooring and showed a potential to be used as a component of environmentally friendly adhesive resin systems for production of flooring.

• Journal of the Korean Wood Science and Technology
• /
• 제47권2호
• /
• pp.239-248
• /
• 2019

This research presents an improvement of the physical and mechanical properties of composite board (com-ply) made of Oriented Strand Board (OSB) coated with wood veneer of Pine (Pinus merkusii), Avocado (Persea Americana) and Mahogany (Swietenia mahogany). 1.5 mm thick veneers of those three wood types were adhered to the surface of OSB using two adhesive types: epoxy and isocyanate. The adhesive with the glue spread of $250g\;m^{-2}$ applied using single glue line was spread and then cold pressed with the pressure of $15kg\;cm^{-2}$ for 3 hours. The research result showed an improving dimension stability of com-ply, but not found on all parameters of physical property test. The moisture content seemed to be influenced by the com-ply type, yet not related to its thickness swelling, water absorption and linear expansion. The exception took place in the parallel linear expansion when immersed for 2 hours. The highest to the lowest increases of MOE and MOR were consecutively found on OSB coated with wood veneer of Pine, Mahogany and Avocado. However, the increases were statistically insignificant. The highest increasing screw hold power was found at the com-ply type AE (avocado veneer and epoxy adhesive) that was by 28%.

• Journal of the Korean Wood Science and Technology
• /
• 제42권4호
• /
• pp.407-419
• /
• 2014

잣나무, 리기다소나무, 낙엽송, 백합나무 등 수종과 두께가 다른 평단판 및 단판롤(롤 형태의 단판)을 고정형 마이크로파로 가열하여 가열 전후 형상, 표면 함수율, 함수중량 변화와 표면 열분포를 분석한 결과는 다음과 같다. 평단판의 경우 마이크로파 가열에 따른 품질상태는 비교적 양호한 것으로 나타났지만, 약간의 뒤틀림이 발생하였으며, 이는 비균일 건조응력에 따른 변형과 고정형 마이크로파 장비의 특성상 단판 형태로 가열 시 국부적인 조사가 이루어진 영향이 컸기 때문으로 판단된다. 단판롤 형태의 마이크로파 가열 특성은 가열 후 품질 모두 양호하였으며, 특히 평단판에서 나타난 뒤틀림 등의 결함은 없는 것으로 나타났다. 또한 열분포 및 확산 등이 매우 안정적으로 이루어진 것으로 판단되며, 이러한 열분포는 표면 함수율 분포 및 함수중량 감소에 많은 영향을 미치는 것으로 나타났다. 따라서 단판롤 형태는 수종 및 두께에 따라 출력과 조사시간 등 충분한 시험이 실시된다면, 고정형 장비에서도 충분한 건조효율을 나타낼 수 있을 것으로 판단된다.

• Journal of the Korean Wood Science and Technology
• /
• 제22권3호
• /
• pp.17-25
• /
• 1994

This study was carried out to compare the properties of Com-Ply Boards with those of OSBs. These two kinds of boards were made of same flakes. Com-Ply Boards were covered with three different thickness veneers, such as 4mm, 3mm, and 2.5mm. All manufactured Com-Ply Boards and OSBs were 12mm thick. In MOR, all Com-Ply Boards were higher than OSB, and especially 3mm-veneer and 2.5mm-veneer Com-Ply Board were highest. But OSB showed 420kg/$cm^2$. 3mm-veneer Com-Ply Board showed the highest internal bonding 7.0kg/$cm^2$ and then 2.5mm-veneer showed 6.8kg/$cm^2$, and OSB showed 6.6kg/$cm^2$. Screw holding strength showed the high value 23.9kg/$cm^2$, 25.5kg/$cm^2$, and 29.3kg/$cm^2$ respectively at 3mm-veneer, 2.5mm-veneer Com-Ply Board and OSB. Thickness swelling of Com-Ply Boards was lower than that of OSB, but Water absorption of OSB was lower. Finally it was very encouraging that all properties of OSB without veneer, whose cost is higher than flake and whose properties is better, were not worse than those of Com-Ply Board with veneer. It seems That more researches on OSB will be required.

• Journal of the Korean Wood Science and Technology
• /
• 제32권6호
• /
• pp.23-35
• /
• 2004

The goal of study was to investigate the influence of the acrylated urethane oligomer on mechanical properties, the chemical resistance and thermal resistance of the UV curable urethane acrylate coatings for fancy veneer overlayed plywood flooring. The pencil hardness and abrasion resistance of the coated fancy veneer overlayed plywood floorings increased with increasing the acrylate functionality of the acrylated urethane oligomer. In the case of the UV cured film containing hexa-functional acrylated aliphatic urethane oligomer, high discoloration of the coated fancy veneer overlayed plywood flooring was observed near the cracks at the beginning of the chemical treatment. In this study, it was found that the degradation of the UV cured film caused by an alkaline reagent was higher than that of the UV cured film caused by an acidic treatment.

• Journal of the Korean Wood Science and Technology
• /
• 제32권1호
• /
• pp.45-51
• /
• 2004

본 연구는 두께 24 mm 뉴질랜드산 라디아타 소나무 단판의 마이크로파-열풍 복합 건조특성을 파악하기 위하여 수행되었다. 단판을 100℃ 열풍과 복합한 마이크로파 건조한 결과 함수율 160%에서 0%까지 건조하는데 7.5분이 소요되었다. 이 건조속도는 100℃ 열풍만으로 건조한 경우에 비하여 약 3배 정도 높은 수준이었다. 그러나 과도한 마이크로파 출력이 가해지면 탄흔이 남는 문제가 발생하였다. 그러므로 최적의 건조조건을 결정하기 위해서는 다양한 규격과 수종의 단판에 대한 마이크로파 건조특성의 파악이 요구됨을 알 수 있었다.