• Corrosion Science and Technology
• /
• v.18 no.2
• /
• pp.49-54
• /
• 2019

The purpose of this paper is to present failure analysis, of the heat exchanger tube in a district heating system. SS304 stainless steel is used, as material for the heat exchanger tube. The heat exchanger operates in a soft water environment containing a small amount of chloride ions, and regularly repeats operation and standstill period. This causes concentration of chloride ions on the outer surface of the tube, as well as repeat of thermal expansion, and shrinkage of the tube. As a result of microscopic examination, cracks showed transgranular as well as branched propagation, and many pits were present, at the initiation point of each crack. Energy disperstive spectroscopy analysis showed Fe and O peak, as well as Cl peak, meaning that cracks were affected by Cl ion. Failure of the tube was caused by chloride-induced stress corrosion cracking by thermal stress, high temperature, and localized enrichment of chloride ions.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2021.05a
• /
• pp.140-141
• /
• 2021

Arc thermal spray process is widely used to protect the steel from corrosion and abrasion. In the present study, two different coatings i.e. Al and Al-5%Mg were used to compare their corrosion resistance performance and the effect of 5% Mg addition in the properties of deposited coating. The SEM results showed the more compact and less porous morphology of Al-5%Mg coating compared to Al. The corrosion resistance performance of both deposited coatings was studied in artificial ocean water with exposure periods and results are compared. The total impedance values of Al-5%Mg at 0.01 Hz exhibited highest with exposure periods might be attributed to the coating and corrosion products nature and morphology compared to Al coating.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.21 no.9
• /
• pp.1422-1431
• /
• 1997

When the structures are exposed to their own an application for a long period, a number of variables such as strength properties and corrosion resistance, so on are expected to change. In the present investigation the corrosion behavior and resistance for the original and degraded materials of Ni-Cr-Mo-V steel were evaluated under the conditions of pH 3, 6, 9 and 12 in a distilled water environment. The electrochemical polarization technique was employed in this investigation. Based upon the experimental results obtained, the following conclusions were drawn. A severe and uniform corrosion was observed for both original and degraded materials under the condition of pH 3. At pH 6 and pH 9, these materials showed the degradation by a pitting corrosion. The materials under pH 12 environment were degraded by a uniform corrosion. The corrosion rate per year were the highest in the pH 3 environment, followed by pH 12, pH 6 and pH 9 environment in order. The corrosion resistance was decreased from the original material, slow cooled material (10.deg. C/hr) and step cooled material in order.

• Corrosion Science and Technology
• /
• v.18 no.6
• /
• pp.221-227
• /
• 2019

During the operation, maintenance and decommissioning of nuclear power plant radioactive contaminated waste is produced. This waste is stored in an underground repository 60-100 meters below the surface. The metallic portion of this waste comprises mostly carbon and stainless steel. A long-term field exposure showed high corrosion rates, general corrosion up to 29 ㎛ a^-1 and localized corrosion even higher. High corrosion rate is possible if microbes produce corrosive products, or alter the local microenvironment to favor corrosion. The bacterial and archaeal composition of biofilm formed on the surface of carbon steel was studied using 16S rRNA gene targeting sequencing, followed by phylogenetic analyses of the microbial community. The functional potential of the microbial communities in biofilm was studied by functional gene targeting quantitative PCR. The corrosion rate was calculated from weight loss measurements and the deposits on the surfaces were analyzed with SEM/EDS and XRD. Our results demonstrate that microbial diversity on the surface of carbon steel and their functionality is vast. Our results suggest that in these nutrient poor conditions the role of methanogenic archaea in corrosive biofilm, in addition to sulphate reducing bacteria, could be greater than previously suspected.

• Corrosion Science and Technology
• /
• v.17 no.5
• /
• pp.225-230
• /
• 2018

The effects of birch sap, a possible natural corrosion inhibitor, on the corrosion behavior of steel in chloride solution were investigated. The corrosion rate was significantly reduced by the addition of 1~5 mL of birch sap to 500 mL of 3wt% NaCl or 3wt% $CaCl_2$ solution. A remarkable increase in the pitting potential in NaCl solution was observed by the addition of birch sap although it was almost constant in $CaCl_2$ solution. The corrosion rate of steel in both NaCl and $CaCl_2$ birch sap solution without addition of water was higher compared to that of aqueous solution without birch sap as the pH of the birch sap was 4.0. The presence of organic compounds like, fructose, galactose, glucose, and palmitic acid in the birch sap are thought to be adsorbed effectively on the metal surface, which provided corrosion protection. However, the inorganic elements including Na, Ca, K, Mg, Mn, S, etc. present in the birch sap exhibited no role in corrosion inhibition.

• Corrosion Science and Technology
• /
• v.10 no.1
• /
• pp.24-29
• /
• 2011

The greatest purpose of chromate treatment is to improve anti-corrosion by stabilizing a metal surface. Because metal surface forms a compound by absorbing oxygen or water in the air by being generally unstable, it is necessary to improve anti-corrosion of the metal by forming the metal surface with a stable film. When considering the economical efficiency and requirements together because the film of the metal surface treated with chromate has good anti-corrosion and the stability also in the air by being compact and strong, Chromate treatment has been used most up to the electronics industry from the auto industry. However, these days, because hexavalent chromium is both a toxic agent to be able to cause cancers and deadly poisonous environmental pollutant, the strong legal controls on its use is being imposed all over the world. Because of this reason, a new anti-corrosion method is being required. Also, by users' various demands, the passivations that have recently been developed require various characteristics such as conductivity, chemical resistance, alkali cleaning resistance as well as anti-corrosion. We could confirm the results such as excellent anti-corrosion compared to chromate, conductivity, chemical resistance and detergent resistance as the result of analysis of various characteristics of the galvannealed sheet steels coated with Cr-Free solution developed in this research.

• Journal of Energy Engineering
• /
• v.23 no.4
• /
• pp.49-55
• /
• 2014

In this study, boiler tube thickness measurement and numerical analysis were conducted for standard 500MW coal-fired power plant in order to research the mechanism of tangential-fired boiler corrosion empirically. The most dominant corrosion mechanism of tangential-fired boiler waterwall was corrosion by sulfur contained in the unburned carbon. And the secondary mechanism was $H_2S$ gas corrosion at localized reducing atmosphere. It is required to decrease the air-stage combustion operation in order to mitigate the waterwall tube corrosion. Also stringent coal pulverization quality control and reinforcing work for corrosion susceptible area such as anti-corrosion coatings is required

• Corrosion Science and Technology
• /
• v.12 no.4
• /
• pp.191-197
• /
• 2013

This study is the second stage of developing the corrosion control technical manual about unpainted weathering steel bridge with closed box girder structures. This paper contains selection of corrosive sealant to apply into crevice of upper flange, injecting test of sealant at mock-up equipment with various condition, evaluation of experiment result. Through the experiment of injection of sealants into crevice of mock-up equipment, it is proved that the tar sealant injecting corrosion control method is useful to protect corrosion at box girder upper flange corroded by remaning rain water with calcium chloride.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.05b
• /
• pp.245-248
• /
• 2005

It should be noted that the critical chloride threshold level is not considered to be a unique value for all conditions. This value is dependent on concrete mixture proportions, cement type and constituents, presence of admixtures, environmental factors, steel reinforcement surface. conditions, and other factors. In this study, the accelerated corrosion test for reinforcing steel was conducted by electrochemical and cyclic wet and dry seawater method, respectively and during the test, corrosion monitoring by half cell potential method was carried out to estimate the chloride corrosion threshold value when corrosion for reinforcing steel in concrete was perceived. For this purpose, lollypop and right hexahedron test specimens were made for 31.4$\%$, 41.5$\%$ and 49.7$\%$ of w/c, respectively and then the accelerated corrosion test for reinforcing steel was executed. It was observed from the test that the time to initiation of corrosion was found to be different with water-cement ratio and accelerated corrosion test method, respectively and the chloride corrosion threshold value was found to range from 0.91 to 1.43 kg/$m^{3}$.

• Journal of Applied Reliability
• /
• v.17 no.2
• /
• pp.122-128
• /
• 2017

Purpose: To investigate the corrosion inhibition effect of the natural spearmint oil extracted from Mentha Spicata plants on 304 stainless steel in different concentrations of hydrochloric acid. Method: The anti-corrosive effect has been investigated in 0.5m, 1m and 2m HCl using weight loss test and electrochemical polarization method as a function of inhibitor concentration and immersion time in strong chloride environment. The surface morphology was analysed by scanning electron microscopy (SEM). Results: The corrosion rate of steel decreased and inhibition efficiency increased with the increase in inhibitor concentration. Microscopic evaluation revealed significant corrosion in the specimens immersed in uninhibited conditions. Potentiodynamic polarization test results showed an increase in corrosion potential (Ecorr) and decrease in corrosion current (icorr) value with increasing concentration of inhibitor. Conclusions: Immersion of steel in higher concentration of inhibitor resulted in greater surface coverage value and hence lesser number of surface corrosion sites/pores were formed; thus lowering the corrosion rate.