• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2004.11a
• /
• pp.50-51
• /
• 2004

• Korean Journal of Materials Research
• /
• v.18 no.12
• /
• pp.635-639
• /
• 2008

In this paper, experimental studies of the regrinding of tungsten carbide (WC-Co) tools for high-speed machining were conducted. Regrinding and a subsequent evaluation test were carried out for a flat endmill tool with diameters of 10 mm and 3 mm using a CNC five-axis tool grinder and a CNC three-axis machining center. Tool wear on the two types of endmill tools increased as the cutting length increased, and the tool wear was not influenced by the regrinding state. In case of the micro endmill with a tool diameter of 3 mm, the effective regrinding time was determined for a flank wear threshold of 0.3 mm considering the tool life according to cutting length. The tool lives of the 10 mm and 3 mm endmill tools were increased by 80% and 72%, respectively. This conclusion proves the Feasibility of the recycling of tungsten carbide materials in the high-speed machining of high-hardened materials for industrial applications.

• Advances in materials Research
• /
• v.6 no.1
• /
• pp.79-91
• /
• 2017

In the present work, a design of experiment (DOE) technique using Taguchi method, has been applied to optimize the properties of ODS tungsten heavy alloys(WHAs). In this work Taguchi method involves nine experiments groups for four processing parameters (compaction pressure, sintering temperature, binding material type, and oxide type) with three levels was implemented. The signal-to-noise (S/N) ratio and analysis of variance (ANOVA) were employed to obtain the optimal process parameter levels and to analyze the effect of these parameters on density, electrical conductivity, hardness and compressive strength values. The results showed that all the chosen factors have significant effects on all properties of ODS tungsten heavy alloys samples. The density, electrical conductivity and hardness increases with the increase in sintering temperature. The analysis of the verification experiments for the physical properties (density and Electrical conductivity) has shown that Taguchi parameter design can successfully verify the optimal parameters, where the difference between the predicted and the verified values of relative density and electrical conductivity is about 1.01% and 1.15% respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.18 no.9
• /
• pp.787-792
• /
• 2005

Chemical mechanical polishing(CMP) has become the process of choice for modem semiconductor devices to achieve both local and global planarization. CMP is a complex process which depends on numerous variables such as macro, micro and nano-geometry of pad, relative velocity between pad and wafer stiffness and dampening characteristics of pad, slurry, pH, chemical components of slurry, abrasive concentration, abrasive size, abrasive shape, etc. Especially, an oxidizer of chemical components is very important remove a target material in metal CMP process. This paper introduces the effect of oxidizer such as $H_2O_2,\;Fe(NO_3)_3\;and\;KIO_3$ in slurry for tungsten which is used in via or/and plug. Finally the duplex reacting mechanism of $oxidizer(H_2O_2)$ through adding the $catalyst(Fe(NO_3)_3)$ could acquire the sufficient removal rate in tungsten CMP.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.29 no.7 s.238
• /
• pp.921-929
• /
• 2005

This paper presents an accelerated life test for burnout of tungsten filament of incandescent lamp. From failure analyses of field samples, it is shown that their root causes are local heating or hot spots in the filament caused by tungsten evaporation and wire sag. Finite element analysis is performed to evaluate the effect of vibration and impact for burnout, but any points of stress concentration or structural weakness are not found in the sample. To estimate the burnout life of lamp, an accelerated life test is planned by using quality function deployment and fractional factorial design, where voltage, vibration, and temperature are selected as accelerating variables. We assumed that Weibull lifetime distribution and a generalized linear model of life-stress relationship hold through goodness of fit test and test for common shape parameter of the distribution. Using accelerated life testing software, we estimated the common shape parameter of Weibull distribution, life-stress relationship, and accelerating factor.

• Journal of the Korean Ceramic Society
• /
• v.33 no.1
• /
• pp.83-91
• /
• 1996

Monolithic AlN and AlN-W composites were fabricated by pressure-less sintering at 190$0^{\circ}C$ under nitrogen atmosphere and the influences of tungsten phase on the microstructure and mechanical properties were investi-gated. In the fabrication of sintered specimen no additive was used. And monolithic AlN showed substantial grain growth and low relative density. AlN-W composites were fully densified and grain growths of matrix were inhibited. The densification behavior of composites were inferred to be achieved through the liquid phase sintering process such as particle-rearrangement and solutino-reprecipitation. Also the oxid phases which is expected to form liquid phases duringsintering process were detected by XRD analysis. As the tungsten volume content increases fracture strength was decreased and fracture toughness was increased. It was suppo-sed that the strength decrease of composites with tungsten content was due to existence of interface phases. The subcritical crack growth behavior was observed from the stress-strain curve of composites. The effect of the secondary phase and interface phases on toughness in crease were studied through observation of crack propagation path and the influence of residual stress on crack propagation was investigated by X-ray residual stress measurement. In the result of residual stress measurement the compressive stress of matrix in composi-test was increased with tungsten volume content and the compressive stress distribution of matrix must have contributed to the inhibition of crack propagation.

• Nuclear Engineering and Technology
• /
• v.52 no.10
• /
• pp.2290-2298
• /
• 2020

The damage of first wall material in fusion reactor due to the bubbles caused by plasma has been studied by introducing a relation between the von Mises equivalent stress and the temperature field. The locations and shapes of the bubbles and the synergetic effect between the different bubbles under steady operational conditions have been studied using the finite elements method. Under transient heat loads, plastic deformations have been found to occur, and are significantly enhanced by the presence of the bubbles. The calculated concentration locations of von Mises equivalent stress are well consistent with the observed crack positions of the tungsten surface in many test experiments. Our simulations show that the damage of the bubbles is not severe enough to lead to catastrophic failure of the tungsten armor; however, it can cause local and gradual detachment of tungsten surface, which provides a reasonable explanation for the observed pits and rough or hairy surface morphology etc. Considering the transient heat loads, the lower bound of the security thickness of the tungsten tile is estimated to be greater than 2 mm.

• Korean Journal of Materials Research
• /
• v.21 no.12
• /
• pp.703-707
• /
• 2011

The electrochromic properties of tungsten oxide films grown by RF sputtering were investigated. Among the sputter parameters, first the $Ar:O_2$ ratios were controlled with division into only an $O_2$ environment, 1:1 and 4:1. The structure of each film prepared by these conditions was studied by X-ray diffraction, X-ray photoelectron spectroscopy and Rutherford backscattering spectroscopy. The sputter-deposited tungsten oxide films had an amorphous structure regardless of the $Ar:O_2$ ratios. The chemical compositions, however, were different from each other. The stoichiometric structure and low-density film was obtained at higher $O_2$ contents. Electrochemical tests were performed by cyclic voltammetry and chronoamperometry at 0.05 M $H_2SO_4$ solutions. The current density and charge ratio was estimated during the continuous potential and pulse potential cycling at -0.5 V and 1.8 V, respectively. The film grown in a higher oxygen environment had a higher current density and a reversible charge reaction during intercalation and deintercalation. The in-situ transmittance tests were performed by He-Ne laser (633 nm). At higher oxygen contents, a big transmittance difference was observed but the response speed was too slow. This was likely caused by higher film resistivity. Furthermore, the effect of sputtering pressure was also investigated. The structure and surface morphology of each film was observed by X-ray diffraction and scanning electron microscopy. A rough surface was observed at higher sputtering pressure, and this affected the higher transmittance difference and coloration efficiency.

• Journal of Powder Materials
• /
• v.19 no.1
• /
• pp.49-54
• /
• 2012

Tungsten nanopowders were produced by the method of wires electrical explosion in the different gases. The study of phase and dispersed composition of the powders was carried out. The influence of electrical parameters such as the value of energy input in wire and the arc stage of the explosion was discussed. The factors that make for decreasing the particles size are the lower pressure of surrounding gas and the use of addition of chemically reactive gas.

• Proceedings of the Materials Research Society of Korea Conference
• /
• 2011.10a
• /
• pp.16.1-16.1
• /
• 2011

Gas sensor properties of $WO_3$ nanowire structures have been studied. The sensing layer was prepared by deposition of tungsten metal on porous single wall carbon nanotubes followed by thermal oxidation. The morphology and crystalline quality of $WO_3$ material was investigated by SEM, TEM, XRD and Raman analysis. A highly porous $WO_3$ nanowire structure with a mean diameter of 82 nm was obtained. Response to CO, $NH_3$ and $H_2$ gases diluted in air were investigated in the temperature range of $100{\sim}340^{\circ}C$ The sensor exhibited low response to CO gas and quite high response to $NH_3$ and $H_2$ gases. The highest sensitivity was observed at $250^{\circ}C$ for $NH_3$ and $300^{\circ}C$ for $H_2$. The effect of the diameters of $WO_3$ nanowires on the sensor performance was also studied. The $WO_3$ nanowires sensor with diameter of 40 nm showed quite high sensitivity, fast response and recovery times to $H_2$ diluted in dry air. The sensitivity as a function of detecting gas concentrations and gas sensing mechanism was discussed. The effect of dilution carrier gases, dry air and nitrogen, was examined.