• Journal of the Korean Ceramic Society
• /
• v.43 no.2 s.285
• /
• pp.74-78
• /
• 2006

A non-integrated type noise filter on a Coplanar Waveguide (CPW) transmission line is demonstrated by using a highly resistive $Co_{41}Fe_{38}Al_{13}O_8$ nanogranular thin film with the dimensions of $4\;mm (\iota)\times4\;mm(\omega)\times0.1\;{\mu}m(t)$. The noise suppression characteristics are evaluated without placing an insulating layer between the CPW line and the magnetic thin film. The insertion loss is very low being less than 0.3 dB and this low value is maintained up to 2 GHz. At a ferromagnetic resonance frequency of 3.3 GHz, the power loss is very large and the degree of noise attenuation is measured to be 3 dB. This level of noise attenuation is still small for real applications; however, considering the small magnetic volume used in this work, further improvement is expected by simply increasing the magnetic volume and by integrating the magnetic thin film into the CPW transmission line.

• 한국신재생에너지학회:학술대회논문집
• /
• 2007.11a
• /
• pp.270-273
• /
• 2007

In this report, Indium-free and Indium-reduced thin film materials for solar absorber were studied in order to search alternative materials for thin film solar cell. The films of $Cu_2ZnSnSe_4$ and $Cu_2ZnSnSe_2$ were deposited using mixed binary chalcogenides powders. From the film bulk analysis result, it is observed that Cu concentration is a function of substrate temperature as well as CuSe mole ratio in the target. Under optimized conditions, $Cu_2ZnSnSe_4$ and $Cu_2ZnSnSe_2$ thin films grow with strong (112), (220/204) and (312/116) reflections. Films are found to exhibit a high absorption coefficient of $10^4$ $cm^{-1}$. $Cu_2ZnSnSe_4$ film shows a 1.5 eV band gap. On the other side, an increasing of optical band gap from 1.0 eV to 1.25 eV ($CuInSnSe_2$) is found to be proportional with an increasing of Zn concentration. All films have a p-type semiconductor characteristic with a carrier concentration in the order of $10^{14}$ $cm^{-3}$, a mobility about $10^1$ $cm^{2{\cdot}-1.}S^{-1}$ and a resistivity at the range of $10^2-10^6$ ${\Omega}{\cdot}m$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.18 no.2
• /
• pp.159-163
• /
• 2005

This paper gives characterization of ZnO thin film deposited by RF magnetron sputtering method, which is concerned in deposition process and device fabrication process, to fabricate solidly mounted resonator(SMR)-type film bulk acoustic resonator(FBAR). A piezoelectric layer of 1.1${\mu}{\textrm}{m}$ thick ZnO thin films were grown on thermally oxidized SiO$_2$(3000 $\AA$)/Si substrate layers by RF magnetron sputtering at the room temperature. The highly c-axis oriented ZnO thin film was obtained at the conditions of 265 W of RF power, 10 mtorr of working pressure, and 50/50 of Ar/O$_2$ gas ratio. The piezoelectric-active area was 50 ${\mu}{\textrm}{m}$${\times}$50${\mu}{\textrm}{m}$, and the thickness of ZnO film and Al-3 % Cu electrode were 1.4 ${\mu}{\textrm}{m}$ and 180${\mu}{\textrm}{m}$, respectively. Its series and parallel frequencies appeared at 2.128 and 2.151 GHz, respectively, and the qualify factor of the resonator was as high as 401.8$\pm$8.5.

• Korean Journal of Materials Research
• /
• v.19 no.1
• /
• pp.24-27
• /
• 2009

Indium Gallium Zinc Oxide (IGZO) thin films were deposited onto 300 nm-thick oxidized Si substrates and glass substrates by direct current (DC) magnetron sputtering of IGZO targets at room temperature. FESEM and XRD analyses indicate that non-annealed and annealed IGZO thin films exhibit an amorphous structure. To investigate the effect of an annealing treatment, the films were thermally treated at $300^{\circ}C$ for 1hr in air. The IGZO TFTs structure was a bottom-gate type in which electrodes were deposited by the DC magnetron sputtering of Ti and Au targets at room temperature. The non-annealed and annealed IGZO TFTs exhibit an $I_{on}/I_{off}$ ratio of more than $10^5$. The saturation mobility and threshold voltage of nonannealed IGZO TFTs was $4.92{\times}10^{-1}cm^2/V{\cdot}s$ and 1.46V, respectively, whereas these values for the annealed TFTs were $1.49{\times}10^{-1}cm^2/V{\cdot}$ and 15.43V, respectively. It is believed that an increase in the surface roughness after an annealing treatment degrades the quality of the device. The transmittances of the IGZO thin films were approximately 80%. These results demonstrate that IGZO thin films are suitable for use as transparent thin film transistors (TTFTs).

• Proceedings of the Korean Ceranic Society Conference
• /
• 1986.12a
• /
• pp.287-304
• /
• 1986

High quality monocrystalline $\beta$-SiC thin films were grown via two-step process of conversion of the Si(100) surface by reaction with $C_2H_4$ and the subsequent chemical vapor deposition (CVD) at $1360^{\circ}C$ and 1 atm total pressure. Four dopants, B and Al and p-type, and N and P for n-type, were also incorporated into monocrystalline $\beta$-SiC thin films during the CVD growth process. IR and Raman spectroscopies were used to evaluate the quality of the undoped $\beta$-SiC thin films and to investigate the effects of dopants on the structure of the doped $\beta$-SiC thin films. The changes in the shape of IR and Raman spectra of the doped thin films due to dopants were observed. But the XTEM micrographs except for the B-doped and annealed films showed the same density and distribution of stacking faults and dislocations as was seen in the undoped samples, The IR and Raman spectra of the B-doped and annealed films showed the broad and weak bands and one extra peak at the 850 $cm^{-1}$ respectively. The SAD pattern and XTEM micrograph of the B-doped and annealed film provided the evidence for twinning.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.430-430
• /
• 2007

In this study, the nematic liquid crystal (NLC) alignment effects treated on the ZnO thin film layers using ion beam irradiation were successfully studied for the first time. The ZnO thin films were deposited on indium-tin-oxide (ITO) coated glass substrates by rf-sputter and The ZnO thin films were deposited at the three kinds of rf power. The used DuoPIGatron type ion beam system, which can be advantageous in a large area with high density plasma generation. The ion beam parameters were as follows: energy of 1800 eV, exposure time of 1 min and ion beam current of $4\;mA/cm^2$ at exposure angles of $15^{\circ}$, $30^{\circ}$, $45^{\circ}$, and $60^{\circ}$. The homogeneous and homeotropic LC aligning capabilities treated on the ZnO thin film surface with ion beam exposure of $45^{\circ}$ for 1 min can be achieved. The low pretilt angle for a NLC treated on the ZnO thin film surface with ion beam irradiation for all incident angles was measured. The good LC alignment treated on the ZnO thin film with ion beam exposure at rf power of 150 W can be measure. For identifying surfaces topography of the ZnO thin films, atomic force microscopy (AFM) was introduced. After ion beam irradiation, test samples were fabricated in an anti-parallel configuration with a cell gap of $60{\mu}m$.

• Transactions on Electrical and Electronic Materials
• /
• v.10 no.3
• /
• pp.89-92
• /
• 2009

High-quality Al-N doped p-type ZnO thin films were deposited on Si and buffer layer/Si by DC magnetron sputtering in a mixture of $N_2$ and $O_2$ gas. The target was ceramic ZnO mixed with $Al_2O_3$ (2 wt%). The p-type ZnO thin films showed a carrier concentration in the range of $1.5{\times}10^{15}{\sim}2.93{\times}10^{17}\;cm^{-3}$, resistivity in the range of 131.2${\sim}$2.864 ${\Omega}cm$, mobility in the range of 3.99${\sim}$31.6 $cm^2V^{-1}s^{-l}$, respectively. It was easier to dope p-type ZnO films on Si substrates than on buffer layer/Si. The film grown on Si showed the highest quality of photoluminescence (PL) characteristics. The Al donor energy level depth $(E_d)$ of Al-N codoped ZnO films was reduced to about 50 meV, and the N acceptor energy level depth $(E_a)$ was reduced to 63 meV.

• Journal of the Microelectronics and Packaging Society
• /
• v.6 no.1
• /
• pp.23-29
• /
• 1999

An yttria-stabilized zirconia(YSZ) thin film on a porous NiO-YSZ substrate for an anode support type solid oxide fuel cell(SOFC) was prepared by an electrophoretic deposition(EPD). Deposition condition and film properties in order to obtain the homogeneous YSZ thin film from the EPD solution with different polarity were studied. In different case of alcohol solution, hydrogen gas was produced in aqueous solution from the electrolyte reaction under constant current above 0.138 mA /$\textrm{cm}^2$.Its reaction generated the bubble-formed defect in the deposited film and decreased weight of the film. The homogeneous YSZ thin film was formed in alcohol solution at a constant current, 0.035 mA /$\textrm{cm}^2$ for 10 s.

• Journal of Information Display
• /
• v.12 no.1
• /
• pp.61-67
• /
• 2011

A single-clock-driven shift register and a two-stage buffer are proposed, using p-type, low-temperature polycrystalline silicon thin-film transistors. To eliminate the clock skew problems and to reduce the burden of the interface, only one clock signal was adopted to the shift register circuit, without additional reference voltages. A two-stage, p-type buffer was proposed to drive the gate line load and shows a full-swing output without threshold voltage loss. The shift register and buffer were designed for the 3.31" WVGA ($800{\times}480$) LCD panel, and the fabricated circuits were verified via simulations and measurements.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.05a
• /
• pp.649-652
• /
• 1999

The (Ba, Sr)TiO$_3$(BST) thin films were fabricated on Pt/Ti/SiO$_2$/Si substrate by RF sputtering technique. The structural properties of the BST thin films were investigated with substrate temperature by XRD, SEM, EDS and AES depth profils. Increasing the substrate temperature, barium multi titanate phases were decreased. The BST thin film had a structure of perovskite type, and had peaks of (100), (200) at the substrate temperature of 50$0^{\circ}C$. When the BST thin films were deposited at the substrate temperature of 50$0^{\circ}C$, the composition ratio of Ba/sr was 52/48.