• Polymer(Korea)
• /
• v.31 no.5
• /
• pp.442-446
• /
• 2007

Alkali soluble and photo-curable polyesters were prepared from fluorene epoxy acrylate and various aromatic dianhydrides. To make a black matrix for LCD color-filter application, photo-resist solution was made by mixing synthesized polyester as binder, carbon black as pigment, initiator and multifunctional monomer in solvent. Black matrix pattern was formed on the glass substrate by lithography process. In this study, we synthesized various polyester-based binder polymers for LCD color-filter applications, and compared the analytical properties of those polymers and lithography patterns.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2004.08a
• /
• pp.468-470
• /
• 2004

CNT pastes with different inorganic binder such as glass frit and spin on glass (SOG) were synthesized by using multi-walled nanotube (MWNT) grown by CVD. The uniformity of cathode layer after firing was enhanced and the emission current density at an applied field of 7.95V/${\mu}m$ increased from 133${\mu}A$/$cm^2$ to 265${\mu}A$/$cm^2$ when inorganic binder changed from glass frit to SOG. The emission properties of CNT pastes with SOG were stable and uniform although firing was carried out at relatively high temperature of 450$^{\circ}C$ under air. It is concluded that SOG is more suitable inorganic binder than glass frit for field emission application.

• Proceedings of the Korean Society of Propulsion Engineers Conference
• /
• 2006.05a
• /
• pp.229-232
• /
• 2006

Two novel synthetic route proposed for Hydro-Terminated Poly(EO-ran-THF) and tri-block(PEC-PTHF-PEG) copolymer by cationic ring-opening polymerization of tetrahydrofuran(THF) and ethylene oxide(EO) and just by polymerization of EO on poly-THF, respectively. Polyurethane was synthesized from random and tri-block HTPE using N-100/IPDI mixture as curing agent, and TPB(Triphenylbismuth) as catalyst. The mechanical properties of resultant polyurethane after mixing with various ratio of isocyanate was also investigated. Finally, the post treatment process of HTPE based on amount of catalyst used in the synthesis was studied, to evaluate the optimum curing condition for the polyurethane propellant binder.

• Journal of Powder Materials
• /
• v.13 no.2 s.55
• /
• pp.129-137
• /
• 2006

In this study, high purity fine $BaTiO_3$ powders were prepared by SHS (Self-propagating High-temperature Synthesis). We would examinate the study of sintering properties and characteristics as a function of temperature with various additives (binder, sintering agent). In separately binder addition, the green and sintered density of specimen were increased as binder content increases. The increased porosity resulted in fine grain size due to the inhibition of grain boundary moving. The $Al_{2}O_{3},\;TiO_{2}$ and MgO playa role of increasing dielectric constants at room temperature. These values were decreased at curie temperature. In case of $SiO_2$, the Curie temperature was decreased. In this study, a high dielectric ceramic capacitor material with temperature stability was synthesized by using various additives.

• Advances in materials Research
• /
• v.4 no.1
• /
• pp.45-60
• /
• 2015

This paper aimed to investigate the effect of MWCNTs on properties of slag Geopolymeric mortar. Geopolymeric matrices containing different MWCNTs concentrations (0.0, 0.1, 0.2, 0.3 and 0.4 % by weight of the used binder) were synthesized. The Geopolymer mortar composed of aluminosilicate slag to sand (1:2), while the alumino silicate source binder composed of 50% air cooled slag and 50%water cooled slag both passing a sieve of $90{\mu}m$, while the sand passing a sieve of 1 ml. The materials prepared at water/binder ratios in a range of 0.34-0.39% depending on the added MWCNT, whereas the Gelenium Ace-30 superplasticizer used in the ratio of 1.4-2.2% from the total dry weight for better dispersion of MWCNT under sonication for 15 min. Alkaline activation of the Geopolymer mortar was carried by using of 6% NaOH. Curing was performed under temperature of $40^{\circ}C$ and 100% R.H. Results showed that the addition of MWCNTs enhanced the resulting amorphous geopolymer structure with marked decrease in the drying shrinkage as well as water absorption specially when using 0.1% MWCNT, while further increase in MWCNTs results in agglomeration in MWCNT within the matrix and so hinder the propagation of Geopolymerization reaction and negatively affect the formed geopolymer structure.

• Korean Journal of Metals and Materials
• /
• v.49 no.5
• /
• pp.362-366
• /
• 2011

Aluminosilicate inorganic polymer binder has been studied as an alternative to ordinary Portland cement due to its higher physical properties, chemical resistance and thermal resistance. This study has been carried out in an attempt to understand the hardening characteristics of aluminosilicate binder by varying the content of calcium. Samples with four different ratios of Al, Si, and Ca were synthesized in this study with the Al:Si:Ca mol ratio being 1.00:1.85~1.98:0.29~2.12. Furthermore, an alkali silicate solution was prepared with the sodium hydroxide (NaOH) and sodium silicate (NaSi). The hardening characteristics of the specimens were analyzed using XRD, SEM, and TG/DTA. In addition, compressive strength and sintering time of specimens were measured as a function of calcium content. The results showed that the specimen containing 2.12 mol% calcium offered the highest compressive strength. However, the compressive strength of the specimen containing 0.26 mol% calcium was lower relative to the other specimens. The results displayed a distinct tendency that as more calcium was added to the inorganic polymer, setting time became shorter. When calcium was added to the inorganic polymer structure, a second phase was not formed, indicating that the addition of calcium does not affect the crystalline structure.

• Environmental Engineering Research
• /
• v.10 no.2
• /
• pp.54-61
• /
• 2005

Liquid-phase catalytic degradation of waste high-density polyethylene (HDPE) over ZSM-5 (powder type (PW)) and ZSM-5+binder (granule type (GR)) has been investigated with a stirred semi-batch operation at 400°C. Two ZSM-5 catalysts with a different crystal size were synthesized and also each ZSM-5 (25%) Catalyst was mixed with a same binder (kaolin: silica sol: alumina = 55%:10%:10%). The performance of prepared catalysts that has different physicochemical properties was discussed with the cumulative amount distribution, molecular weight distribution and also paraffin, olefin, naphthene and aromatic (PONA) distribution in liquid product. These liquid product quality and distributions were changed depending on the physicochemical properties of the catalyst. Moreover, the characteristic of ZSM-5 in the catalyst was strongly influenced on the activity and PONA distribution in liquid product.

• Journal of Powder Materials
• /
• v.22 no.6
• /
• pp.396-402
• /
• 2015

The organic binder-free paste for dye-sensitized solar cell (DSSC) has been investigated using peroxo titanium complex. The crystal structure of $TiO_2$ nanoparticles, morphology of $TiO_2$ film and electrical properties are analyzed by X-Ray Diffraction (XRD), Scanning Electron Microscopy (SEM), Electrochemical Impedance Spectra (EIS), and solar simulator. The synthesized $TiO_2$ nanopowders by the peroxo titanium complex at 150, 300, $400^{\circ}C$, and $450^{\circ}C$ have anatase phase and average crystal sizes are calculated to be 4.2, 13.7, 16.9, and 20.9 nm, respectively. The DSSC prepared by the peroxo titanium complex binder have higher $V_{oc}$ and lower $J_{sc}$ values than that of the organic binder. It can be attributed to improvement of sintering properties of $TCO/TiO_2$ and $TiO_2/TiO_2$ interface and to formation of agglomerate by the nanoparticles. As a result, we have investigated the organic binder-free paste and 3.178% conversion efficiency of the DSSC at $450^{\circ}C$.

• Applied Chemistry for Engineering
• /
• v.29 no.2
• /
• pp.201-208
• /
• 2018

The ortho- and iso- type unsaturated polyester resins were synthesized and used as a polymer binder of the polymer mortar composite. Styrene monomer and acrylonitrile were used as a diluent for the unsaturated polyester resin. Methyl ethyl ketone peroxide (MEKPO) and cobalt octoate (CoOc) were used as a curing agent and an accelerator, respectively. Four kinds of unsaturated polyester resins were prepared according to types of the resin and diluent, and used as a polymer binder in the preparation of the specimen. A total of 16 polymer mortar specimens were prepared according to the added amount of the polymer binder and subjected to a hot water resistance test, followed by compressive and flexural strength tests, and pore and SEM analyses. As a result, it was found that the strength of the specimen using the iso-type unsaturated polyester resin as the polymer binder was better than that of using the ortho-type unsaturated polyester resin. The total pore volume and diameter measured after the hot water resistance test were reduced compared to the values before the test. In the micrographs observed before the hot water resistance test, the polymer binder, filler and fine aggregate were firmly combined to the co-matrix, but the polymer binder was mostly decomposed in the micrographs observed after the test.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2007.08a
• /
• pp.564-566
• /
• 2007

Synthesis of two photoactive compounds containing core imide moiety was carried out for an application to interdielectric layer in TFTLCD array. An aqueous alkaline developable polymer matrix was synthesized by free radical copolymerization. A positive photoresist formulation was developed utilizing synthesized UV monomers, photoactive compound, binder polymer, sulfactant and alkali developable polymer matrix. It was found that via-holes with good resolution, high transmittance and thermal resistance could be obtained by photolithographic process utilizing the new positive interdielectric material with high thermal stability.