• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.17 no.8
• /
• pp.1873-1878
• /
• 2013

ITZO ($In_2O_3$ : $SnO_2$ : ZnO = 90wt.% : 5wt.% : 5wt.%) thin films were fabricated on glass substrates (Eagle 2000) at room temperature with various working pressures (1~7 mTorr) by RF magnetron sputtering. The influence of the working pressure on the structural, electrical, and optical properties of the ITZO thin films were investigated. The XRD and FESEM results showed that all ITZO thin films are amorphous structures with very smooth surfaces regardless of the working pressure. Amorphous ITZO thin films deposited at 3 mTorr showed the best properties, such as a low resistivity, high transmittance, and figure of merit of $3.08{\times}10^{-4}{\Omega}{\cdot}cm$, 81 %, and $10.52{\times}10^{-3}{\Omega}^{-1}$, respectively.

• Korean Chemical Engineering Research
• /
• v.49 no.2
• /
• pp.195-199
• /
• 2011

Mo thin films were deposited on soda lime glass at room temperature by using DC magnetron sputtering The electrical and structural properties of the films were investigated by varying DC power and gas pressure as the deposition parameter. As DC power increased, the deposition rate of Mo films was increased and the electrical resistivity was decreased. It was observable that the crystallinity of the films was improved with increasing DC power. As gas pressure decreased, the deposition rate and resistivity of the films were decreased, and long rectangular grains were densely formed. With increasing gas pressure, the grains were transformed to a round shape and the voids on the film surface were increased. It was confirmed that the electrical resistivity of Mo films was increased as the amount of oxygen combined with Mo atoms increased. It was also disclosed that the films have low resistivity as the degree of coupling of oxygen with Mo was reduced due to the enhancement of the crystallinity of the films.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.7
• /
• pp.414-423
• /
• 2016

In the present study, the $CuN_x-Cu-CuN_x$ layer the partial pressure ratio Cu metal of Ar and $N_2$ gas using a DC magnetron sputtering device, was generated by the In-situ method. $CuN_x$ layer was able to obtain a surface reflectance reduction effect from the advantages of the process and the external light. $CuN_x$ layer is gas partial pressure, DC the Power, the deposition time variable transmittance in response to the thickness and partial pressure ratio, the reflectance was measured. $Ar:N_2$ gas ratio 10:10(sccm), DC power 0.35 A, was derived Deposition time 90 sec optimum conditions. Thus, according to the optimal thickness and the composition ratio was derived surface reflectance of 20.75%. In addition, to derive the value of ${\Delta}$ Ra surface roughness of 0.467. It was derived $CuN_x$ band-gap energy of about 2.2 eV. Thus, to ensure a thickness and process conditions can be absorbed to maximize the light in a wavelength band in the visible light region. As a result, the implementation of the $12k{\Omega}$ base line resistance of using the Cu metal. This is, 5 inch Metal mesh TSP(L/S: $4/270{\mu}m$) is in the range of the reference operation.

• Applied Microscopy
• /
• v.29 no.3
• /
• pp.265-274
• /
• 1999

The microstructure of Cu thin films in various deposition conditions was characterized. Cr films (50 nm thick) and Cu films (500 or 1000 nm thick) were deposited on polyimide films by DC magnetron sputtering. The Ar pressure during Cu deposition was controlled to 5, 50 and 100 mtorr. The microstructure was characterized using conventional and high resolution SEM and TEM. As sputtering pressure increases, open boundaries are observed more frequently. The Cu film deposited at 5 mtorr has a dense and uniform structure, while low-density regions or open boundaries between columns exist in the film deposited at higher pressure. As the film grows thicker, open boundaries are wider and the density of open boundaries are higher. The comparison between SEM and TEM show that the small features shown in high resolution SEM are grains. High resolution SEM is very effective to characterize the microstructure of the thin films. One column in the films deposited at 50 and 100 mtorr consists of several grains, which are smaller than those deposited at 5 mtorr.

• Korean Chemical Engineering Research
• /
• v.46 no.4
• /
• pp.676-680
• /
• 2008

TiN thin films were deposited on a $SiO_2(2000{\AA})/Si$ substrate by radio-frequency(rf) magnetron sputtering. TiN films were prepared under varying $N_2$ concentration in $N_2/Ar$ gas mix, rf power and gas pressure, and investigated in terms of deposition rate, resistivity and surface morphology. As $N_2$ concentration increased, the deposition rate and the surface roughness of the films decreased and the resistivity increased. With increasing rf power, the deposition rate increased but the resistivity was decreased. As gas pressure increased, little change in deposition rate was obtained but the resistivity rapidly increased. TiN film with resistivity of $2.46{\times}10^{-4}{\Omega}cm$ at 1 mTorr was formed. It was observed that there existed a correlation between the deposition rate and resistivity. In particular, the gas pressure has a strong influence on the resistivity of thin films.

• Journal of the Korean Ceramic Society
• /
• v.35 no.8
• /
• pp.871-877
• /
• 1998

$CuInSe_2$ thin films have been formed by two-step method in which Cu-In alloy layer was first deposited and then it was selenized. Cu-In alloy layers were deposited by co-sputtering method at ambient tem-perature. XRD analysis showed that both of $Cu_{11}In_{9}$ and CuIn$_2$ phases were formed from these films. $Cu_{11}In_{9}$ peak intensity was increased increased with varying the composition from In-rich to Cu-rich. The metallic layers were selenized either in low pressure of 10 mTorr or in atmospheric pressure(AP) Less compounds of Cu-Se and In-Se were observed during the early stage of selenization and also $CuInSe_2$ thin films selenized in vacuum showed lower roughness larger grain size and better crystallinity than those in AP.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2001.11a
• /
• pp.35-35
• /
• 2001

agnesium Oxide (MgO) with a NaCI structure is well known to exhibit high secondary electron emission, excellent high temperature chemical stability, high thermal conductance and electrical insulating properties. For these reason MgO films have been widely used for a buffer layer of high $T_c$ superconducting and a protective layer for AC-plasma display panels to improve discharge characteristics and panel lifetime. Up to now MgO films have been synthesized by lE-beam evaporation, Molecular Beam Epitaxy (MBE) and Metalorganic Chemical Vapor Deposition (MOCVD), however there have been some limitations such as low film density and micro-cracks in films. Therefore magnetron sputtering process were emerged as predominant method to synthesis high density MgO films. In previous works, we designed and manufactured unbalanced magnetron source with high power density for the deposition of high quality MgO films. The magnetron discharges were sustained at the pressure of O.lmtorr with power density of $110W/\textrm{cm}^2$ and the maximum deposition rate was measured at $2.8\mu\textrm{m}/min$ for Cu films. In this study, the syntheses of MgO films were carried out by unbalanced magnetron sputtering with various $O_2$ partial pressure and specially target power densities, duty cycles and frequency using pulsed DC power supply. And also we investigated the plasma states with various $O_2$ partial pressure and pulsed DC conditions by Optical Emission Spectroscopy (OES). In order to confirm the relationships between plasma states and film properties such as microstructure and secondary electron emission coefficient were analyzed by X-Ray Diffraction(XRD), Transmission Electron Microscopy(TEM) and ${\gamma}-Focused$ Ion Beam (${\gamma}-FIB$).

• Journal of the Korean Solar Energy Society
• /
• v.30 no.3
• /
• pp.90-97
• /
• 2010

$TiO_2$ thin films for solar energy utilization were prepared on ITO coated glass by r.f magnetron sputtering with variations of working pressure, oxygen flow rate and annealing temperature. Ion insertion and extraction reaction, and ion storage properties of films were investigated by using a cyclic voltammetry. Transmittance of thin films in as-prepared, colored and bleached states was measured by UV-VIS spectrophotometer. The samples deposited in our sputtering conditions showed poor electrochromic properties. Improvement in ion storage properties of $TiO_2$ thin film was observed after annealing at temperature of $400^{\circ}C$ in air for 2 hours. It was found that $TiO_2$ thin film in electrochromic device could be used as a passive counter-electrode.

• Electrical & Electronic Materials
• /
• v.9 no.2
• /
• pp.196-203
• /
• 1996

The highly c-axis oriented zinc oxide thin films were deposited on Sapphire(0001) substrates by reactive RF magnetron sputtering. The characteristics of zinc oxide thin films on RF power, substrate-target distance, and substrate temperature were investigated by XRD, SEM and EDX analyses. The physical characteristics of zinc oxide thin films changed with various deposition conditions. The higher substrate temperatures were, The better crystallinity of zinc oxide thin films. The highly c-axis oriented zinc oxide thin films were obtained at sputter pressure 5mTorr, rf power 200W, substrate temperature 350.deg. C, substrate-target distance 5.5cm. In these conditions, the resistivity of zinc oxide thin films deposited on pt/sapphire was 12.196*10$^{9}$ [.ohm.cm].

• Journal of the Korean Society for Heat Treatment
• /
• v.22 no.5
• /
• pp.275-281
• /
• 2009

The microstructure of copper films prepared by a sputtering apparatus, which was fabricated to enhance the shadowing effect, was investigated by scanning electron microscopy. Black copper films were deposited on copper wires at an Ar pressure of 10 Pa. The black films had an extremely porous structure composed of separated columns. This structure is quite similar to that of black titanium films prepared by cylindrical magnetron sputtering. These results suggest that the porous structure composed of separated columns is easily formed for metal films by enhancing the shadowing effect.