• Proceedings of the Korean Ceranic Society Conference
• /
• 2003.04a
• /
• pp.143.2-143
• /
• 2003

• Proceedings of the Korean Vacuum Society Conference
• /
• 2001.07a
• /
• pp.48-48
• /
• 2001

• Current Photovoltaic Research
• /
• v.6 no.2
• /
• pp.56-61
• /
• 2018

In this study, CIGS absorber layers were deposited on low-alkali glass and sodalime glass substrates and potasium floride (KF) of various thicknesses was supplied at an elevated temperature after the CIGS growth. The effect of KF post-deposition treatment on the two types of substrates was extremely different. On the low-alkali substrate, the open-circuit voltage (Voc) was improved but the fill-factor (FF) degradation was severe, whereas the sodalime substrate showed Voc deterioration and FF improvement. In the case of supplying 20 nm of KF on both substrates, the efficiency gain of 0.3~1.1%p was obtained. With increasing the KF thickness, a small protrusion-like microstructure developed on the surface of the absorber layer, and the microstructures that were not removed in the subsequent process were found to be the main cause of the FF loss.

• Korean Journal of Materials Research
• /
• v.24 no.3
• /
• pp.123-128
• /
• 2014

To realize high-performance thin film solar cells, we prepared CIGS by the co-evaporation technique on both sodalime and Corning glass substrates. The structural and efficient properties were investigated by varying the thickness of the Mo:Na layer, where the total thickness of the back contact was fixed at 1${\mu}m$. As a result, when the Mo:Na thickness was 300 nm on soda-lime glass, the measured Na content was 0.28 %, the surface morphology was a plate-like compact structure, and the crystallinity by XRD showed a strong peak of (112) preferential orientation together with relatively intense (220) and (204) peaks as the secondary phases influenced crystal formation. In addition, the substrates on soda-lime glass effected the lowest surface roughness of 2.76 nm and the highest carrier density and short circuit current. Through the optimization of the Mo:Na layer, a solar conversion efficiency of 11.34% was achieved. When using the Corning glass, a rather low conversion efficiency of 9.59% was obtained. To determine the effects of the concentration of sodium and in order to develop a highefficiency solar cells, a very small amount of sodium was added to the soda lime glass substrate.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.151-152
• /
• 2007

탄소나노튜브(CNTs)는 우수한 물리적, 화학적, 기계적 특성으로 다양한 분야에서 연구가 진행 되고있다. 특히, field emission displays (FEDs)로의 응용을 위해서는 기본적으로 sodalime glass 위에 직접 CNTs를 성장시켜야 하며, 소자 응용을 위해 기판인 sodalime glass를 왜곡시키는 온도보다 낮은 온도에서 CNT의 수직 성장이 이루어져야 한다. 본 연구에서는 Hot-filament plasma enhanced chemical vapor deposition (HF-PECVD)를 이용하여 합성온도를 400, 450, 500, $550^{\circ}C$로 변화시켰으며 촉매 층인 Ni의 두께를 5~40 nm까지 조절하여 탄소나노튜브를 합성하였다. 저온에서 합성된 탄소나노튜브는 FE-SEM을 이용하여 성장 형태 및 표면 특성을 확인하였으며, 미세구조는 HR-TEM을 이용하여 확인하였다.

• Journal of Sensor Science and Technology
• /
• v.10 no.5
• /
• pp.292-303
• /
• 2001

This work reports the tunneling effects of the lateral field emitters. Tunneling effect is applicable to the VMFS(vacuum magnetic field sensors). VMFS uses the fact that the trajectory of the emitted electrons are curved by the magnetic field due to Lorentz force. Polysilicon was used as field emitters and anode materials. Thickness of the emitter and the anode were $2\;{\mu}m$, respectively. PSG(phospho-silicate-glass) was used as a sacrificial layer and it was etched by HF at a releasing step. Cantilevers were doped with $POCl_3(10^{20}cm^{-3})$. $2{\mu}m$-thick cantilevers were fabricated onto PSG($2{\mu}m$-thick). Sublimation drying method was used at releasing step to avoid stiction. Then, device was vacuum sealed. Device was fixed to a sodalime-glass #1 with silver paste and it was wire bonded. Glass #1 has a predefined hole and a sputtered silicon-film at backside. The front-side of the device was sealed with sodalime-glass #2 using the glass frit. After getter insertion via the hole, backside of the glass #1 was bonded electrostatically with the sodalime-glass #3 at $10^{-6}\;torr$. After sealing, getter was activated. Sealing was successful to operate the tunneling device. The packaged VMFS showed very small reduced emission current compared with the chamber test prior to sealing. The emission currents were changed when the magnetic field was induced. The sensitivity of the device was about 3%/T at about 1 Tesla magnetic field.

• Tribology and Lubricants
• /
• v.5 no.2
• /
• pp.83-86
• /
• 1989

A wear transition mechanism during sliding in glass has been observed. Disk specimens of sodalime-silicate glass were slid against AISI 52100 steel with paraffin oil as lubricant. Observations of the micrrx structural change on the worn surface showed that semi-circular cone cracks (SCCCs) were suddenly produced after a certain critical sliding time. These SCCCs brought about the severe damage in the form of extensive microchipping during further sliding. It was shown that the abrupt appearance of the SCCCs is attributable to the grooves formed during sliding, which act as surface flaws.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.11a
• /
• pp.267-267
• /
• 2009

Solar cells with CIGS absorber layers have proven their suitability for high efficiency and stable low cost solar cells. We prepared and characterized particle based CIGS thin film using a non-vacuum processing. CIGS powder were obtained at $240^{\circ}C$ for 6 hours from the reaction of $CuCl_2$, $InCl_3$, $GaCl_3$, Se powder in solvent. The nanoparticle precursors were mixed with binder material. The CIGS thin film deposited on a sodalime glass. The CIGS thin film were identified to have a typical chalcopyrite tetragonal structure by using UV/Visible-spectroscopy, X-ray diffraction(XRD), Auger Electron Spectroscopy(AES), Scanning Electron Microscopy(SEM).

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.442-443
• /
• 2009

We prepared and characterized particle based CIGS thin film using a thermal evaporator. CIGS powder were obtained at $240^{\circ}C$ for 6 hours from the reaction of $CuCl_2$, $InCl_3$, $GaCl_3$, Se powder in solvent. The CIGS thin film deposited on a sodalime glass. The CIGS thin film were identified to have a typical chalcopyrite tetragonal structure by using UV/Vis-spectroscopy, X-ray diffraction(XRD), Auger Electron Spectroscopy(AES), Scanning Electron Microscopy(SEM).

• 한국신재생에너지학회:학술대회논문집
• /
• 2009.06a
• /
• pp.96-98
• /
• 2009

This report summarizes our recent efforts to produce large-grained CIGS materials from porous nanoparticle thin films. In our approach, a $Cu_xSe$ nanoparticle colloid were first prepared by reacting a mixture of CuI in pyridine with $Na_2Se$ in methanol at reduced temperature. purified colloid was sprayed onto heated molybdenum-coated sodalime glass substrates to form thin film. After thermal processing of the thin film under a selenium ambient. $Cu_xSe$ colloid and thin film were characterized by scanning electron microscopy, x-ray diffraction. The optical(direct) band gap energy of $Cu_xSe$ thin films is 1.5 eV.