• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.05a
• /
• pp.676-679
• /
• 2004

In this study, we considered the characteristic of drying shrinkage from age of high strength concrete with garnet minute powder to be industry by-product. The factors of experiment are unit water content$(160kg/m^3)$, water-binder ratio(30, $35\%$), fine aggregate ratio(40, 42, $44\%$), admixture replacement ratio(0, 10, $20\%$), admixture type(garnet minute powder, fly ash, blast-furnace slag). We make a comparative study of shrinkage about concrete with a passage of age(1, 3, 7, 14, 28, 56, 91 days). As a result of experiment, we reach a conclusion as follow. In the same mix condition, as unit water content and fine aggregate ratio go up, the drying shrinkage ratio increase. In the drying shrinkage ratio according to admixture replacement ratio, it goes up when admixture replacement Ratio increase in case of fly ash and blast-furnace slag. But, drying shrinkage ratio decrease when admixture replacement ratio increase in case of garnet minute powder.

• Journal of the Korean Ceramic Society
• /
• v.52 no.6
• /
• pp.483-488
• /
• 2015

Blast furnace slag(BFS) is well known for its hardening mechanism in ordinary Portland cement with alkali activation due to its latent hydraulic property. The possibility of using calcium compound as activator for BFS has been investigated in this study. The hydration properties of calcium compound activated BFS binders were explored using heat of hydration, powder X-ray diffraction and compressive strength testing. Heat of hydration results indicate that the hydration heat of BFS is lower than OPC paste by about 50%. And ettringite as hydration product was formed continuously as the calcium sulfate was decreased. The maximum compressive strength of hardened BFS mortar at 28 days is confirmed to be 83% as compared with hardened OPC mortar.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2017.05a
• /
• pp.216-217
• /
• 2017

Slag cement or ternary blended cement is mainly used for non-structural lean concrete for the purpose of foundation work or protection of the waterproof layer on the roof of buildings. However, such non-structural lean concrete has a lot of drying shrinkage cracks, which makes it difficult to maintain the quality of the structure. Therefore, in this study, the compressive strength and the drying shrinkage of ternary blended cement(blended of portland cement, blast furnace slag, fly ash from combined heat and power Plant) for non-structural lean concrete were examined. As a result, it was confirmed that this non-structural lean concrete reduced drying shrinkage compared to the conventional ternary blended cement using fly ash from power plant.

• Advances in concrete construction
• /
• v.4 no.4
• /
• pp.283-303
• /
• 2016

Several types of industrial byproducts are generated. With increased environmental awareness and its potential hazardous effects, the utilization of industrial byproducts in concrete has become an attractive alternative to their disposal. One such by-product is ground granulated blast furnace slag (GGBS), which is a byproduct of the smelting process carried out in the iron and steel industry. The GGBS is very effective in the design and development of high-strength and high-performance concrete. This paper reviews the effect of GGBS on the workability, porosity, compressive strength, splitting tensile strength, and flexural strength of concrete.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2021.11a
• /
• pp.120-121
• /
• 2021

This study examines the performance of the pre-treatment process system to use CGS, a by-product generated in IGCC, as a concrete fine aggregate for construction materials, on the quality of CGS fine aggregate. As a result of the analysis, it is judged that the quality of fine aggregates of CGS can be improved at both density, absorption rate, and 0.08mm body passage amount after the hydroelectric screening process using water as a medium during the pretreatment process. It is believed that it can be used as basic data for national standard certification of CGS fine aggregates in the future.

• Journal of the Korea Institute of Building Construction
• /
• v.8 no.1
• /
• pp.57-62
• /
• 2008

Twelve mortars were mixed and tested to explore the effect of gypsum on the compressive strength development and shrinkage strain of alkali-activated mortars. Powder typed sodium silicate and ground granulated blast-furnace slag were employed as alkaline activator and source material, respectively, to produce cementless mortar. The main variables investigated were alkali quality coefficient combining the concentration of activator and main compositions in source material, and the adding amount of gypsum ranged between 1 and 5% with respect to the weight of binder. Initial flow, compressive strength development, modulus of rupture, and shrinkage strain behavior of mortar specimens were measured. In addition, the hydration production of alkali-activated pastes with gypsum was traced using X-ray diffraction and energy-dispersive X-ray analysis combined with scanning electron microscope image. Test results showed that the initial flow of slag-based alkali-activated mortar was little influenced by the adding amount of gypsum. On the other hand, the effect of gypsum on the compressive strength of mortar specimens was dependent on the alkali quality coefficient, indicating that the compressive strength increased with the increase of the adding amount of gypsum until a certain limit, beyond which the strength decreased slowly. Shrinkage strain of mortar tested was little influenced by the adding amount of gypsum because no ettringite as hydration product was generated. However, the adding of gypsum had a beneficial effect on reducing the microcrack in the alkali-activated mortar.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.5 no.1
• /
• pp.37-44
• /
• 2017

Red mud is an inorganic by-product produced from the mineral processing of alumina from Bauxite ores. The development of alkali-activated slag-red mud cement can be a representative study aimed at recycling the strong alkali of the red mud as a construction material. This study is to investigate the optimum water content, compressive strength, water absorption and efflorescence of alkali-activated slag-red mud soil pavement according to binder type. The results showed that the optimum water content, moisture absorption coefficient and efflorescence area of alkali-activated slag-red mud soil pavement increased but the compressive strength of that decreased as the redmud content increased.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.19 no.3
• /
• pp.39-47
• /
• 2015

In this study, the properties of strength and drying shrinkage of alkali-activated slag cement (AASC) with magnesium oxide (MgO) contents between 0 and 16 wt% were investigated. The ground granulated furnace blast slag (GGBFS) was activated by potassium hydroxide (KOH) and dosage of activator was 2M and 4M. The MgO was replaced with 2% to 16% of GGBFS by weight. The water-binder ratio (w/b) was 0.5. In the result, the higher MgO content leads to a slightly higher degree of reaction and thus to a higher compressive strength at all ages. The compressive strength and ultra sonic velocity (UPV) increased with increases MgO contents. The drying shrinkage of AASC was decreased as the contents of MgO increases. The results from SEM confirmed that there were densified reaction product of higher MgO content specimens.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.7 no.2
• /
• pp.70-77
• /
• 2012

The Ladle Furnace Slag, about 20% of the electric arc furnace slag, has high content of free CaO and free MgO, which generates the expansion collapse by hydration reaction. Although many researchers have been endeavoring to recycle the EAF reducing slag in construction fields, there is not found the effective recycling method up to now. However, the LFS(Ladle Furnace Slag) contains mineral composition of the system of calcium aluminate with high-reactivity. Therefore, it is possible to developed the quick setting property and the high strength at the early age by the rapid cooling. This study aimed to check the reactive minerals and predict the reactivity with water on the LFS discharged from different steel product plants. The test results show that many types of LFS has hydration reactivity and can use in construction field as a inorganic binder with the rapid setting property.

• Journal of the Korean GEO-environmental Society
• /
• v.18 no.12
• /
• pp.25-36
• /
• 2017

This research was conducted to investigate the removal characteristics of heavy metals and sulfate ion from acid mine drainage (AMD) by multi-functional zeolite-slag ceramics (ZS ceramics), in which natural zeolite and converter slag were mixed and calcined at high temperature. The batch test showed that the removal efficiency of heavy metals by pellet-type ZS ceramics increased as the mixing weight ratio of converter slag to natural zeolite increased. The optimal mixing ratio of natural zeolite to converter slag for the removal of heavy metals and sulfate ion from AMD was observed to be 1:2~1:3. The adequate calcination temperature and time of ZS ceramics for the treatment of AMD were found to be $600{\sim}800^{\circ}C$ and 2 hours, respectively. The removal test of heavy metals and sulfate ion from AMD by the ZS ceramics prepared in optimal condition exhibited very high removal efficiencies close to 100% for all heavy metals (Al, As, Cd, Cu, Fe, Mn, Pb, Zn) and 77.1% for sulfate ion. The experimental results in this study revealed that the ZS ceramics could function as an effective agent for the treatment of AMD.