• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.6
• /
• pp.487-490
• /
• 2007

In this paper, the formation and thermal stability characteristics of Ni silicide using Ni-V alloy on Boron cluster ($B_{18}H_{22}$) implanted bulk and SOI substrate were examined in comparison with pure Ni for nano-scale CMOSFET. The Ni silicide using Ni-V alloy on $B_{18}H_{22}$ implanted SOI substrate after high temperature post-silicidation annealing showed the lower sheet resistance, no agglomeration interface image and lower surface roughness than that using pure Ni. The thermal stability of Ni silicide was improved by using Ni-V alloy on $B_{18}H_{22}$ implanted SOI substrate.

• Journal of the Korean institute of surface engineering
• /
• v.38 no.3
• /
• pp.89-94
• /
• 2005

We investigate the reaction stability of cobalt and nickel with side-wall materials of $SiO_2\;and\;Si_3N_4$. We deposited 15nm-Co and 15nm-Ni on $SiO_2(200nm)/p-type$ Si(100) and $Si_3N_4(70 nm)/p-type$ Si(100). The samples were annealed at the temperatures of $700\~1100^{\circ}C$ for 40 seconds with a rapid thermal annealer. The sheet resistance, shape, and composition of the residual materials were investigated with a 4-points probe, a field emission scanning electron microscopy, and an AES depth profiling, respectively. Samples of annealed above $1000^{\circ}C$ showed the agglomeration of residual metals with maze shape and revealed extremely high sheet resistance. The Auger depth profiling showed that the $SiO_2$ substrates had no residual metallic scums after $H_2SO_4$ cleaning while $Si_3N_4$ substrates showed some metallic residuals. Therefore, the $SiO_2$ spacer may be appropriate than $Si_3N_4$ for newly proposed Co/Ni composite salicide process.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.10-11
• /
• 2006

In this study, the Ni/Co/TiN (6/2/25 nm) structure was deposited for thermal stability estimation. Vacuum (30 mTorrs) annealing was carried out to compare with furnace annealing in nitrogen ambient. The proposed Ni/Co/TiN structure exhibited low temperature silicidation and wide range of rapid thermal process (RTP) windows. The sheet resistance was too high to measure after furnace annealing at $600^{\circ}C$ due to the thin thickness (15 nm) of the nickel silicide. However, the sheet resistance maintained stable characteristics up to $600^{\circ}C$ for 30 min after vacuum annealing. Therefore, the low resistance of thin film nickel silicide was obtained by vacuum annealing at $600^{\circ}C$.

• Korean Journal of Materials Research
• /
• v.18 no.1
• /
• pp.5-11
• /
• 2008

Thermally evaporated 10 nm-Ni/1 nm-Au/(30 nm-poly)Si structures were fabricated in order to investigate the thermal stability of Au-inserted nickel silicide. The silicide samples underwent rapid thermal annealing at $300{\sim}1100^{\circ}C$ for 40 seconds. The sheet resistance was measured using a four-point probe. A scanning electron microscope and a transmission electron microscope were used to determine the cross-sectional structure and surface image. High-resolution X-ray diffraction and a scanning probe microscope were employed for the phase and surface roughness. According to sheet resistance and XRD analyses, nickel silicide with Au had no effect on widening the NiSi stabilization temperature region. Au-inserted nickel silicide on a single crystal silicon substrate showed nano-dots due to the preferred growth and a self-arranged agglomerate nano phase due to agglomeration. It was possible to tune the characteristic size of the agglomerate phase with silicidation temperatures. The nano-thick Au-insertion was shown to lead to self-arranged microstructures of nickel silicide.

• Journal of the Korean institute of surface engineering
• /
• v.32 no.3
• /
• pp.389-392
• /
• 1999

We employed cobalt-disilicide for high-speed logic devices. We prepared stable and low resistant $CoSi_2$ through typical fabrication process including wet cleaning and rapid thermal process (RTP). We sputtered 15nm thick cobalt on the wafer and performed RTP annealing 2 times to obtain 60nm thick $CoSi_2$. We observed spherical shape voids with diameter of 40nm in the surface and inside $CoSi_2$ layers. The voids resulted in taking over abnormal junction leakage current and contact resistance values. We report that the voids in $CoSi_2$ layers are resulted from surface pits during the ion implantation previous to deposit cobalt layer. Silicide reaction rate around pits was enhanced due to Gibbs-Thompson effects and the volume expansion of the silicidation of the flat active regime trapped dimples. We confirmed that keeping the buffer oxide layer during ion implantation and annealing the silicon surface after ion implantation were required to prevent void defects in CoSi$_2$ layers.

• Korean Journal of Materials Research
• /
• v.31 no.2
• /
• pp.97-100
• /
• 2021

We report the effect of Standard Clean-1 (SC-1) cleaning to remove residual Ti layers after silicidation to prevent Al diffusion into Si wafer for Ti Schottky barrier diodes (Ti-SBD). Regardless of SC-1 cleaning, the presence of oxygen atoms is confirmed by Auger electron spectroscopy (AES) depth profile analysis between Al and Ti-silicide layers. Al atoms at the interface of Ti-silicide and Si wafer are detected, when the SC-1 cleaning is not conducted after rapid thermal annealing. On the other hand, Al atoms are not found at the interface of Ti-SBD after executing SC-1 cleaning. Al diffusion into the interface between Ti-silicide and Si wafer may be caused by thermal stress at the Ti-silicide layer. The difference of the thermal expansion coefficients of Ti and Ti-silicide gives rise to thermal stress at the interface during the Al layer deposition and sintering processes. Although a longer sintering time is conducted for Ti-SBD, the Al atoms do not diffuse into the surface of the Si wafer. Therefore, the removal of the Ti layer by the SC-1 cleaning can prevent Al diffusion for Ti-SBD.

• Korean Journal of Materials Research
• /
• v.3 no.6
• /
• pp.638-644
• /
• 1993

The degradation of dielectric breakdown field of 8nm-thick gate oxide ($SiO_2$) for Tipolycide MOS(meta1-oxide-semiconductor) capacitor with different annealing conditions and thickness of the polysilicon film on gate oxide was investigated. The degree of degradation in dielectric breakdown strength of the gate oxide for Ti-polycide gate became more severe with increasing annealing temperature and time, especially, for the case that thickness of the polysilicon film remained on the gate oxide after silicidation was reduced. The gate oxide degradation may be occurred by annealing although there is no direct contact of Ti-silicide with gate oxide. From SIMS analysis, it was confirmed that the degration of gate oxide during annealing was due to the diffusion of titanium atoms into the gate oxide film through polysilicon from the titanium silicide film.

• 한국태양에너지학회:학술대회논문집
• /
• 2009.04a
• /
• pp.230-234
• /
• 2009

It is significant technique to increase competitiveness that solar cells have a high energy conversion efficiency and cost effectiveness. When making high efficiency crystalline Si solar cells, evaporated Ti/Pd/Ag contact system is widely used in order to reduce the electrical resistance of the contact fingers. However, the evaporation process is no applicable to mass production because high vacuum is needed. Furthermore, those metals are too expensive to be applied for terrestrial applications. Ni/Cu/Ag contact system of silicon solar cells offers a relatively inexpensive method of making electrical contact. Ni silicide formation is one of the indispensable techniques for Ni/Cu/Ag contact sytem. Ni was electroless plated on the front grid pattern, After Ni electroless plating, the cells were annealed by RTP(Rapid Thermal Process). Ni silicide(NiSi) has certain advantages over Ti silicide($TiSi_2$), lower temperature anneal, one step anneal, low resistivity, low silicon consumption, low film stress, absence of reaction between the annealing ambient. Ni/Cu/Ag metallization scheme is an important process in the direction of cost reduction for solar cells of high efficiency. In this article we shall report an investigation of rapid thermal silicidation of nickel on silngle crystalline silicon wafers in the annealing range of $350-390^{\circ}C$. The samples annealed at temperatures from 350 to $390^{\circ}C$ have been analyzed by SEM(Scanning Electron Microscopy).

• Journal of the Korean Institute of Telematics and Electronics D
• /
• v.35D no.5
• /
• pp.87-92
• /
• 1998

Ultr shallow p$^{+}$-n junction with Co/Ti bilayer silicidde contact was formed by ion implantation of BF$_{2}$ [energy : (30, 50)keV, dose:($5{\times}10^{14}$, $5{\times}10^{15}$/$\textrm{cm}^2$] onto the n-well Si(100) region and by RTA-silicidation and post annealing of the evaporated Co(120.angs., 170.angs.)/Ti(40~50.angs.) double layer. The sheet resistance of the silicided p$^{+}$ region of the p$^{+}$-n junction formed by BF2 implantation with energy of 30keV and dose of $5{\times}10^{15}$/$\textrm{cm}^2$ and Co/Ti thickness of $120{\AA}$/(40~$50{\AA}$) was about $8{\Omega}$/${\box}$. The junction depth including silicide thickness of about $500{\AA}$ was 0.14${\mu}$. The fabricated p$^{+}$ -n ultra shallow junction depth including silicide thickness of about $500{\AA}$ was 0.14${\mu}$. The fabricated p$^{+}$-n ultra shallow junction with Co/Ti bilayer silicide contact did not show any agglomeration or variation of sheet resistance value after post annealing at $850^{\circ}C$ for 30 minutes. The boron concentration at the epitaxial CoSi$_{2}$/Si interface of the fabricated junction was about 6*10$6{\times}10^{19}$ / $\textrm{cm}^2$./TEX>.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07a
• /
• pp.358-361
• /
• 2002

Self-aligned MOSFETS using a polysilicon gate are widely fabricated in silicon technology. The polysilicon layer acts as a mask for the source and drain implants and does as gate electrode in the final product. However, the usage of polysilicon gate as a self-aligned mask is restricted in fabricating SiC MOSFETS since the following processes such as dopant activation, ohmic contacts are done at the very high temperature to attack the stability of the polysilicon layer. A metal instead of polysilicon can be used as a gate material and even can be used for ohmic contact to source region of SiC MOSFETS, which may reduce the number of the fabrication processes. Co-formation process of metal-source/drain ohmic contact and gate has been examined in the 4H-SiC based vertical power MOSFET At low bias region (<20V), increment of leakage current after RTA was detected. However, the amount of leakage current increment was less than a few tens of ph. The interface trap densities calculated from high-low frequency C-V curves do not show any difference between w/ RTA and w/o RTA. From the C-V characteristic curves, equivalent oxide thickness was calculated. The calculated thickness was 55 and 62nm for w/o RTA and w/ RTA, respectively. During the annealing, oxidation and silicidation of Ni can be occurred. Even though refractory nature of Ni, 950$^{\circ}C$ is high enough to oxidize it. Ni reacts with silicon and oxygen from SiO$_2$ 1ayer and form Ni-silicide and Ni-oxide, respectively. These extra layers result in the change of capacitance of whole oxide layer and the leakage current