• 한국표면공학회지
• /
• 제56권1호
• /
• pp.77-83
• /
• 2023

The reliability of leadframe-based semiconductor package depends on the adhesion between metal and epoxy molding compound (EMC). In this study, the Ag surface was electrochemically treated in a solution containing silanes in order to improve the adhesion between Ag and epoxy substrate. After electrochemical treatment, the thin silane layer was deposited on the Ag surface, whereby the peel strength between Ag and epoxy substrate was clearly improved. The improvement of peel strength depended on the functional group of silane, implying the chemical linkage between Ag and epoxy.

• 한국산학기술학회논문지
• /
• 제14권11호
• /
• pp.5745-5751
• /
• 2013

본 논문은 monomer에서 결합증진에 많은 역할을 하는 MMA와 TEGDMA의 농도별 표면 처리와 silane coupling agent로 표면 처리한 것이 의치상 레진과 이장재간의 결합력에 미치는 영향에 대해 알아보고자 하였다. 의치상 레진에 MMA와 TEGDMA의 농도별 표면 처리와 silane coupling agent로 표면처리 후 이장재를 주입하여 전단결합강도를 측정하였다. MMA와 TEGDMA의 농도별 표면 처리에 따른 의치상 레진과 이장재간의 전단결합강도에서는 Vertex self curing resin에서 95%, 90%, 80%, Kooliner에서는 95%, 90%에서 유의적으로 높게 나타났다(P<0.05). 또한, silane coupling agent 5%로 표면 처리한 그룹이 Vertex self curing resin과 Kooliner 모두에서 전단결합강도가 유의적으로 높게 나타났다(P<0.05). 따라서 적절한 화학적 표면 처리는 의치상 레진과 이장재간의 결합력 증가에 영향을 미치리라 사료된다.

• 한국표면공학회지
• /
• 제37권1호
• /
• pp.49-52
• /
• 2004

In this study, we investigated the fatigue characteristics of silane-treated aluminum/CFRP composite material. Three different specimens of cracked aluminum, cracked aluminum repaired with CFRP patch, and silane-treated aluminum repaired with CFRP patch were used in the fatigue tests. Load ratio and the frequency applied in the fatigue tests were 0 and 10 Hz, respectively. The results showed that the specimen repaired by composite patch showed three times more improved fatigue life than aluminum specimen. Furthermore, the silane-treated specimen repaired by composite patch showed four times more improved fatigue life than the non-treated specimen.

• Restorative Dentistry and Endodontics
• /
• 제25권2호
• /
• pp.262-271
• /
• 2000

The purpose of this study was to estimate shear bond strength according to difference in Targis surface treatment and storage condition. 140 non-carious extracted human molars and Targis D210(Ivoclar, Liechtenstein) were used in the present study and were divided into 7 experimental groups respectively according to surface treatment of Targis. Group 1 ; No treatment, Group 2 ; $50{\mu}m$ aluminium oxide blasting, Group 3 ; 4% HF etching for 3 minutes, Group 4 ; 4% HF etching after blasting, Group 5 ; silane treatment after blasting, Group 6 ; silane treatment after 4% HF etching, Group 7 ; silane treatment after blasting and 4% HF etching. In Each group, one half of 20 specimens was stored in distilled water at $37^{\circ}C$ for 24 hours and the other half was stored at atmosphere for 24 hours respectively. Dentin surface was etched with 10% $H_3PO_4$ for 15 seconds and luting cement(Variolink II, Vivadent, Liechtenstein) was applied by manufacturer's recommendation. Shear bond strength for each group was then measured. To examine the failure patterns after shear bond test and to observe the change after surface treatment of Targis. Specimens were fabricated and observed under the SEM. Statistical analysis was performed by One Way ANOVA test and t-test. The results were as follows ; 1. The shear bond strength of the groups stored in water significantly lower than that of groups stored at atmosphere (P<0.05). 2. There was no significant difference in shear bond strength in groups stored in water (P>0.05). 3. The shear bond strength without surface treatment of Targis were lowest among all experimental groups in atmosphere condition(P<0.05). 4. There was no significant difference in bond strength between groups using the silane or not(P>0.05). 5. The groups treated by blasting, hydrofluoric acid and silane sequentially showed highest bond strength than that of other groups in atmosphere condition, but there was no significant difference(P>0.05). 6 The proportions of the specimens showing the mixed fracture failure were 20% in HF etching group and blasting + HF group, 40% in blasting + HF + silane group in atmosphere condition. All the specimens stored in water showed adhesive fracture failure.

• The Journal of Advanced Prosthodontics
• /
• 제12권1호
• /
• pp.22-32
• /
• 2020

PURPOSE. The aim of this study was to evaluate the microshear bond strength (µSBS) of four computer-aided design/computer-aided manufacturing (CAD/CAM) blocks repaired with composite resin using three different surface treatment protocols. MATERIALS AND METHODS. Four different CAD/CAM blocks were used in this study: (1) flexible hybrid ceramic (FHC), (2) resin nanoceramic (RNC), (c) polymer infiltrated ceramic network (PICN) and (4) feldspar ceramic (FC). All groups were further divided into four subgroups according to surface treatment: control, hydrofluoric acid etching (HF), air-borne particle abrasion with aluminum oxide (AlO), and tribochemical silica coating (TSC). After surface treatments, silane was applied to half of the specimens. Then, a silane-containing universal adhesive was applied, and specimens were repaired with a composite, Next, µSBS test was performed. Additional specimens were examined with a contact profilometer and scanning electron microscopy. The data were analyzed with ANOVA and Tukey tests. RESULTS. The findings revealed that silane application yielded higher µSBS values (P<.05). All surface treatments were showed a significant increase in µSBS values compared to the control (P<.05). For FHC and RNC, the most influential treatments were AlO and TSC (P<.05). CONCLUSION. Surface treatment is mandatory when the silane is not preferred, but the best bond strength values were obtained with the combination of surface treatment and silane application. HF provides improved bond strength when the ceramic content of material increases, whereas AlO and TSC gives improved bond strength when the composite content of material increases.

• 한국환경과학회지
• /
• 제12권7호
• /
• pp.801-807
• /
• 2003

This work aims the search of environmentally friendly pre-treatment technologies to develop chromate replacements for metal finishing industries due to its toxicological properties. Since the corrosion resistance of steel was strongly related to water permeation, galvanized steel sheets were treated with various hydrophobic silane compounds and water-suspended polymer solution. Also, plasma gas discharge was applied to modify the surface of a polymer coated-steel sheet to be hydrophobic. The surface hydrophobicity of materials was introduced by CF$_3$H plasma exposure. The corrosion property before and after the plasma treatment was investigated in a slat spray tester with 3.5 wt.% NaCl at 35$^{\circ}C$. The results showed that both silane/polymer double coatings and plasma treatment of the galvanized steel exhibited significant retardation of corrosion.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 추계학술대회 논문집 Vol.16
• /
• pp.591-593
• /
• 2003

Silicone composites for high voltage insulator(HVI SC) were prepared by adding aluminum trihydrate(ATH) treated by surface treatment agent to base silicone compound at the ratio of 100:20, 100:40, 100:60, 100:80, and 100:100, respectively. And also, ATH was treated by various surface treatment agents, such as stearic acid, acryl silane vinyl silane under compounding process. electrical properties were investigated for the various contents of ATH and solace-treatment agents we mlas ured volume resistivity, breakdown and tracking resistance were for HVISC containing ATH treated by viuyl silane.

• Macromolecular Research
• /
• 제13권5호
• /
• pp.409-417
• /
• 2005

The surface of rutile titania nanoparticles was chemically modified by reacting with alkoxy silane. The surface and rheological properties in silicone oil having a wide range of viscosity were investigated. Total surface free energy($\gamma_S$) of the titania particles decreased from 53.12 to 26.94 mJ/$m^2$ as the silane used for surface treatment was increased from 0 to 5.0 wt$\%$. The surface free energy of neat silane was 25.5 mJ/$m^2$, which is quite close to that oftitania particles treated with 5.0 wt$\%$ silane. Due to the hydrophobic nature oftreated-titania, the contact angle was accordingly higher for polar solvent in the order of water>ethylene glycol> formamide>$\alpha$-bromonaphthalene. In sum of rheological behavior, as the applied shear stress or viscosity of the silicone oil increased, the titania particles tend to form layers and agglomerated clusters, showing shear-thinning and shear-thickening behaviors, sequentially. A good dispersion of discrete titania particles obeying a Newtonian flow behavior was achieved at a surface energy or low concentration of silane-treated titania particles in hydrophobic silicone oil.

• 한국막학회:학술대회논문집
• /
• 한국막학회 2004년도 Proceedings of the second conference of aseanian membrane society
• /
• pp.170-174
• /
• 2004

Most of thin film composite reverse osmosis membranes include amide linkages, which are susceptible to chlorine attack resulting in N-chloro derivatives. This study examined a new method based on post-treatment of reverse osmosis membrane with various silane derivatives to improve chlorine resistance. The silane derivatives contain one alkyl group and three alkoxy groups such as trifluoromethyltrimethoxysilane, 3-aminopropylmethoxydiethoxysilane and 3, 3, 3-trifluoropropyltrimethoxysilane. Compared to commercial membranes, silane derivatives coated membranes showed significantly enhanced chlorine durability.

• 폴리머
• /
• 제26권4호
• /
• pp.445-451
• /
• 2002

본 연구에서는 실리카의 표면처리를 위해 실란 커플링제인, ${\gamma}$-methacryloxy propyl trimethoxy silane (MPS), ${\gamma}$-glycidoxy propyl trimethoxy silane (GPS), and ${\gamma}$-mercapto propyl trimethoxy silane (MCPS) 등을 사용하여 실리카 흡착특성과 기계적 계면물성에 대하여 고착하였다. 실란처리에 따른 실리카의 평형 확산압력, 표면 자유에너지, 비표면적을 BET법을 이용한 $N_2$/77 K 기체 흡착을 통하여 알아보았다. 본 실험결과 신란처리에 의해 실리카 표면에 도입된 비극성 관능기로 인해 실리카의 비표면적, 평형 확산압력, 표면 자유에너지의 비극성 요소가 증가하였으며 결과적으로 실리카/고무 복합재료의 기계적 계면 물성인 tearing energy ($G_{mc}$)가 향상되었음을 확인할 수 있었다. 그리고 MPS로 표면처리한 경우가 GPS, MCPS에 비해서 우수한 기계적 계면물성을 나타남을 관찰할 수 있었다.