• Journal of Conservation Science
• /
• v.36 no.6
• /
• pp.456-474
• /
• 2020

This study investigated the initial behavior (flowability and setting properties) and shrinkage characteristics of lime mortar, based on the mixing ratio of hydrated lime (lump, powder) and commercial lime, which is primarily used for repairing and restoring cultural assets. The flowability showed that the optimum mixing water contents of the masonry lime mortar were 8-10% for the lump hydrated lime, 10-18% for the powdered hydrated lime, and 17-40% for the commercial hydrated lime. The results of the setting and shrinkage analysis showed that the average final setting time ratio compared to the standard of cultural asset repair was in the increasing order of commercial hydrated lime(0.4) < powder hydrated lime(5.6) < lump hydrated lime(5.7). Moreover, the average shrinkage ratio was ordered as lump hydrated lime(1.1) < powder hydrated lime(1.2) < commercial hydrated lime(3.0). The analysis of the physical and chemical characteristics of hydrated lime showed that the optimum mixing water content was reduced as the particle size of the lime increased, thus delaying the setting time and decreasing the length change rate (shrinkage). These results are expected to contribute to the prediction of the initial behavior and shrinkage characteristics of mortars using handmade and commercial lime during repair and restoration work on cultural, heritage buildings.

• Journal of the Korea Concrete Institute
• /
• v.23 no.4
• /
• pp.441-448
• /
• 2011

In this study, experimental tests of chemical and autogenous shrinkage were performed to evaluate the early age shrinkage behaviors of ultra high performance cementitious composites (UHPCC) with various replacement ratios of silica fume (SF), shrinkage reducing agent (SRA), expansive admixture (EA), and superplasticizer (SP). Starting time of self-desiccation, was analyzed by comparing the setting times and the deviated point of chemical and autogenous shrinkage strains. The test results indicated that both SF and SRA augment the early age chemical shrinkage, whereas SP delays the hydration reaction between cement particles and water, and reduces chemical shrinkage. About 49% of autogenous shrinkage was depleted by synergetic effect of SRA and EA. The hardening of UHPCC was catalyzed by containing EA. Self-desiccation of UHPCC occurred prior to the initial setting due to the high volume fraction of fibers and low water-binder ratio (W/B).

• Journal of the Korean Ceramic Society
• /
• v.50 no.5
• /
• pp.319-325
• /
• 2013

In this study, petroleum cokes ash and $C_{12}A_7$-based slag were used for the shrinkage reduction and strength enhancement of mortar. The hydration properties of shrinkage reduction agents were analysed. The flow, change of length and compressive strength were experimented with mortar-added shrinkage reduction agents. As a result of this study, petroleum cokes ash : $C_{12}A_7$-based slag = 60~80% : 20~40% showed excellent results. In the case of mortar with 20% $C_{12}A_7$-based slag, the setting time and change of length were similar to Ref. mortar. The flow and compressive strength were superior to Ref. mortar. In the case of mortar with a 40% $C_{12}A_7$-based slag, the setting time was longer than Ref. mortar. The compressive strength of 3 days and 7 days were superior to Ref. mortar.

• Journal of the Korea Concrete Institute
• /
• v.18 no.3 s.93
• /
• pp.397-404
• /
• 2006

This paper investigates experimentally the effect of combined addition of expansive additive and shrinkage reducing agent(SRA) on setting time, compressive strength and drying shrinkage of concrete. An increase of EA and SRA content leads to a reduction in flowability, which causes the increase of superplasticizer dosage, while air content increases. For setting time, in spite of increased superplasticizer dosage, with the increase of EA and SRA, setting time shortens. This is due to the presence of alkali ion by SRA and the faster formation of ettringite. At dosage of 5.0% of EA, concrete has the highest compressive strength and above that dosage, compressive strength decreased. On the contrary, the increase of SRA dosage results in a decrease in compressive strength. Combined addition of EA of 5.0% and SRA of 1.0% shows a comparable strength with control concrete. For drying shrinkage, as expected, the increase of EA and SRA dosage leads to reduction of drying shrinkage markedly. Moreover, combined addition of EA and SRA has better drying shrinkage reduction effect than individual use of EA and SRA by as much as $5{\sim}16%$. Optimal combination of EA and SRA is fixed at 5.0% of EA and 0.5% of SRA based on the consideration of the effect of EA and SRA on fresh state, compressive strength and shrinkage of concrete.

• Journal of the Korea Institute of Building Construction
• /
• v.12 no.4
• /
• pp.393-400
• /
• 2012

The effect of ground granulated blast-furnace slag (GGBS) and alkaline activator on the properties of setting, compressive strength, drying shrinkage and resistance of carbonation was assessed to develop high volume slag concrete, the GGBS replacement rate of which was more than 80 percent. The changes in the concrete as the replacement rate of GGBS increases were as follows. Initial and final setting time was delayed by two and a half hours, and the compressive strength development properties of concrete in early and long term age were decreased. Drying shrinkage was satisfactory as below $6{\times}10^{-4}$ in every mixture, and yet showed a tangible trend by replacement rate. Carbonation was materially increased. Setting time and early strength development property, however, were extremely advanced by the addition of the alkaline activator. While drying shrinkage was improved by the alkaline activator, resistance to carbonation was not.

• Journal of the Korea Concrete Institute
• /
• v.14 no.1
• /
• pp.76-82
• /
• 2002

The rapid-set cement concrete causes high hydration temperature and nay result in a high drying shrinkage and shrinkage-induced cracking. This problem may be fixed by incorporating polypropylene fibers in rapid-set cement concrete, because of increased toughness, resistance to impact, corrosion, fatigue, and durability. A series of concrete drving shrinkage tests was peformed in order to investigate the shrinkage properties of polypropylene fiber reinforced concrete with experimental variables such as concrete types, fiber reinforcement, W/C ratio, with and without restraint. Uni-axially restrained bar specimens were used for the restrained shrinkage tests. The results were as follows; The dry shrinkage of rapid-set cement concrete was much lessor than that oi OPC, probably because of smaller weight reduction rate by early hydration and strength development. The constraint and bridging effects caused by polypropylene fibers were great for the rapid-setting cement concrete when compared with that of plain concrete, and this resulted In increased resistance against tensile stress and cracking.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2005.05a
• /
• pp.25-28
• /
• 2005

This study shows the early quality improvement of concrete with calcium sulfa aluminate(CSA). For the properties of slump, plain concrete incorporating BS $35\%$ and UP $15\%$ resulted in high fluidity compared with OPC without any admixture. As displacement ratio of CSA increased. the fluidity decreased. The fluidity also declined with setting time. Increase of incorporation ratio of CSA declined bleeding and accelerated setting time. Importantly, using more CSA helped to improve early compressive strength and decrease drying shrinkage. In term of water curing, drying shrinkage hardly ever occurred.

• Fibers and Polymers
• /
• v.5 no.1
• /
• pp.19-24
• /
• 2004

PET yarns textured at different texturing conditions were treated with superheated steam or dry heat at different temperatures for different times. The effects of the treatment conditions on the thermomechanical and structural changes of the yarn were examined by shrinkage, X-ray diffraction and birefringence measurements. With increase in superheated steam temperature, the crystalline orientation factor and birefringence decreased, whereas crystal size increased. Dry heat treatment had a smaller effect on shrinkage and structural properties in comparison with superheated steam treatment. The additional shrinkage after texturing process was investigated. The effect of heat-setting in both media was more significant at $200^{\circ}C$. The time dependence of the properties was not linear.

• Journal of Energy Engineering
• /
• v.28 no.1
• /
• pp.17-21
• /
• 2019

Calcium sulfaluminate (CSA) was synthesized to improve the shrinkage of OPC. In this study, the setting time, the compressive strength and the length change ratio were confirmed by replacing the synthesized CSA with OPC by 10% and 13% by 16%. In the case of shrinkage-reducing type cement, formation of Ca-Al-$H_2$-based hydrate was activated. Therefore, the setting time was shortened. The compressive strength of the shrinkage - reducing type cement is comparable to that of OPC after 7 days' strength. However, shrinkage reducing type cement showed improved initial strength compared to OPC. The length change ratio was found to be improved by drying shrinkage from -0.075% to -0.047% on the 28th day.

• Journal of the Korean Society of Clothing and Textiles
• /
• v.3 no.2
• /
• pp.15-22
• /
• 1979

The heat setting of sewing thread is known to have some puckering. In this experiment, the P/C fabrec and polyester thread were heat setted at temperatures ranging from $70^{\circ}C$ to $150^{\circ}C$ at the interval of every $^20{\circ}C$ for the period of 1, 5, 10, 20 and 40 minutes resoectivly. The results obtained are as follows: 1) In general, the pre-laundering sewing shrinkage related negatively to time but related positively to temperature. And it showed the lowest rate at $110^{\circ}C$. 2) In case of slack treatment, the post-laundering sewing sewing shrinkage marked the lowest rate at $130^{\circ}C$ while that of stretch treatment showed the lowest rate at $90^{\circ}C$. 3) The rates of post-laundering sewing shrinkage were higher than those of pre-laundering shrinkage, the difference between them reached the bottom when applied the slack treatment at $130^{\circ}C$ and the streched treatment at $110^{\circ}C$.