• 한국초전도학회:학술대회논문집
• /
• v.9
• /
• pp.152-159
• /
• 1999

YBa$_2Cu_3O_{7-{\delta}}$ (YBCO) films grown on CeO$_2$-buffered r-cut sapphire substrates (CbS's) were prepared and their structural and electrical properties were measured. Post-annealed CeO$_2$ films were used as buffer layers for the experiments. It turned out that the YBCO films grown on post-annealed CbS's had the rms roughness of less than 20 ${\AA}$ and peak-to-peak roughness of about 30 ${\AA}$ when the YBCO film thickness was 3000 ${\AA}$. Meanwhile, YBCO films on in-situ grown CeO$_2$ buffer layers on r-cut sapphire substrates appeared to have the peak-to-peak roughness of more than 450 ${\AA}$. X-ray diffraction data revealed that the YBCO flms were epitaxially grown along the c-axis with the typical FWHM of(005) ${\theta}$ -2 ${\theta}$ peak about 0. 16 $^{\circ}$ and ${\Delta}$ ${\omega}$ of the (005) peak about 0.5 $^{\circ}$. T$_c$ > 87 K, ${\Delta}$T < 1 K and R(look)/R(100K) ${\ge}$3 were observed from the YBCO films. Applicability of the YBCO films for high-frequency applications was described.

• Journal of the Korean Vacuum Society
• /
• v.17 no.6
• /
• pp.528-537
• /
• 2008

60 nm and 20 nm thick hydrogenated amorphous silicon(a-Si:H) layers were deposited on 200 nm $SiO_2$/single-Si substrates by inductively coupled plasma chemical vapor deposition(ICP-CVD). Subsequently, 30 nm-Ni layers were deposited by an e-beam evaporator. Finally, 30 nm-Ni/(60 nm and 20 nm) a-Si:H/200 nm-$SiO_2$/single-Si structures were prepared. The prepared samples were annealed by rapid thermal annealing(RTA) from $200^{\circ}C$ to $500^{\circ}C$ in $50^{\circ}C$ increments for 40 sec. A four-point tester, high resolution X-ray diffraction(HRXRD), field emission scanning electron microscopy(FE-SEM), transmission electron microscopy(TEM), and scanning probe microscopy(SPM) were used to examine the sheet resistance, phase transformation, in-plane microstructure, cross-sectional microstructure, and surface roughness, respectively. The nickel silicide from the 60 nm a-Si:H substrate showed low sheet resistance from $400^{\circ}C$ which is compatible for low temperature processing. The nickel silicide from 20 nm a-Si:H substrate showed low resistance from $300^{\circ}C$. Through HRXRD analysis, the phase transformation occurred with silicidation temperature without a-Si:H layer thickness dependence. With the result of FE-SEM and TEM, the nickel silicides from 60 nm a-Si:H substrate showed the microstructure of 60 nm-thick silicide layers with the residual silicon regime, while the ones from 20 nm a-Si:H formed 20 nm-thick uniform silicide layers. In case of SPM, the RMS value of nickel silicide layers increased as the silicidation temperature increased. Especially, the nickel silicide from 20 nm a-Si:H substrate showed the lowest RMS value of 0.75 at $300^{\circ}C$.

• 전자공학회논문지 IE
• /
• v.44 no.2
• /
• pp.8-13
• /
• 2007

This paper aims to analyze the characteristics of ITO which are caused by variation of plasma condition to fabricate the OLED of high efficiency. We treated $N_2$ gas and $O_2$ gas plasma on the surface of the ITO by changing their RF plasma power into 100 W, 200 W, 400 W and by changing their 9as pressure into 12 mTorr, 120 mTorr. The work function of ITO that plasma treatment was done by using $N_2$ gas had value of $4.88{\sim}5.07\;eV$, and that by using $O_2$ gas, $4.85{\sim}4.97 eV$. The characteristics of the ITO were most efficient in the $N_2$ gas plasma with the RF power of 200W and gas pressure of 120 mTorr. The rms roughness of ITO surface is the value from AFM image. In this case, ITO obtained $25.2\;{\AA}$ and $30.5\;{\AA}$ in the $N_2$ and $O_2$ gas plasma respectively when it had the RF power of 200 W. But ITO that didn't have plasma treatment was $44.5{\AA}$. The variation of ITO transmittance was almost not discovered by the change of $N_2$ gas and $O_2$ gas pressure.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.28 no.1
• /
• pp.51-56
• /
• 2018

To evaluate surface characteristics of AlN single crystal grown by physical vapor transport (PVT) method, chemical mechanical polishing (CMP) were performed with diamond slurry and $SiO_2$ slurry after mechanical polishing (MP), then the surface morphology and analysis of polishing characteristics of the slurry types were analyzed. To estimate how pH of slurry effects polishing process, pH of $SiO_2$ slurry was controlled, the results from estimating the effect of zeta potential and MRR (material removal rate) were compared in accordance with each pH via zeta potential analyzer. Eventually, surface roughness RMS (0.2 nm) could be derived with atomic force microscope (AFM).

• Polymer(Korea)
• /
• v.37 no.3
• /
• pp.316-322
• /
• 2013

In this study, poly(ethylene terephthalate) (PET) was treated with fluorination and ultrasonic washing treatment for hydrophilic modification of PET film. We measured the change of surface modified PET film surface characteristics using contact angle, surface free energy, FE-SEM, AFM and XPS. After direct fluorination and ultrasonic washing treatment, the water contact angle was measured to be $10.81^{\circ}$, 85% reduction compared to the untreated PET film. Total surface free energy has been measured to be $42.25mNm^{-1}$, 650% increase compared to the untreated PET film. Also RMS roughness has been measured to be 1.965 nm, 348% increase compared to the untreated PET film. Hydrophilic functional group C-OH bond concentration has increased approximately 3 times. These results are attributed to the hydrophilic functional group and cavitation due to chemical etching. From this result, it was suggested that the fluorination-ultrasonic washing treatment method could be useful to make PET film surface hydrophilic.

• Journal of the Korean Vacuum Society
• /
• v.15 no.3
• /
• pp.259-265
• /
• 2006

We measured sputtering yield of RF $O_2-plasma$ treated MgO protective layer for AC-PDP(plasma display panel) using a Focused ion Beam System(FIB). A 10 kV acceleration voltage was applied. The sputtering yield of the untreated sample and the treated sample were 0.33 atoms/ion and 0.20 atoms/ion, respectively. The influence of the plasma-treatment of MgO thin film was characterized by XPS and AFM analysis. We observed that the binding energy of the O 1s spectra, the FWHM of O 1s spectra and the RMS(root-mean-square) of surface roughness decreased to 2.36 eV, 0.6167 eV and 0.32 nm, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.46-47
• /
• 2005

이번 연구는 $BCl_3/CF_4$ 플라즈마를 사용하여 반도체소자 제조 시 널리 이용되는 GaAs 계열반도체 중 대표적인 재료인 GaAs/AlGaAs 및 GaAs/InGaP 구조를 선택적으로 건식 식각한 후 분석한 것이다. 공정변수로는 ICP 소스파워를 0-500W, RIE 파워를 0-50W 그리고 $BCl_3/CF_4$ 가스 혼합비를 중점적으로 변화시켰다. $BCl_3$ 플라즈마만을 사용한 경우 (20$BCl_3$, 20W RIE power, 300W ICP source power, 7.5mTorr) 는 GaAs:AlGaAs의 선택비가 0.5:1 이었으며 이때 GaAs의 식각률은 ~2200${\AA}/min$ 이었으며 AlGaAs의 식각률은 ~4500${\AA}/min$ 이었다. 식각 후 표면의 RMS roughness은 < 2nm로 깨끗한 결과를 보여주었다. 15% $CF_4$ 가스가 혼합된 $17BCl_3/3CF_4$, 20W RIE power, 300W ICP source power, 7.5mTorr의 조건에서 3분 동안 공정한 결과 순수한 $BCl_3$ 플라즈마만을 사용한 경우보다 표면은 다소 거칠었지만 (RMS roughness: ~8.4) GaAs의 식각률 (~980nm/min)과 AlGaAs와 InGaP에 대한 GaAs의 선택도 (GaAs:AlGaAs=16:1, GaAs:InGaP=38:1)는 크게 증가하였다. 그리고 AlGaAs 및 InGaP의 경우 식각 시 나타난 휘발성이 낮은 식각 부산물 ($AlF_3:1300^{\circ}C$, $InF_3:1200^{\circ}C$)로 인하여 50nm/min 이하의 낮은 식각률을 보였고, 62.5%의 $CF_4$가 혼합된 $7.5BCl_3/12.5CF_4$플라즈마의 조건에서는 AlGaAs 및 InGaP에 대한 GaAs의 선택도가 각각 280:1, 250:1을 나타내었다.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.9 no.1
• /
• pp.16-22
• /
• 2008

We fabricated thermally-evaporated 10 nm-Ni/30 nm and 70 nm Poly-Si/200 nm-$SiO_2/Si$ structures to investigate the thermal stability of nickel silicides formed by rapid thermal annealing(RTA) of the temperature of $300{\sim}1100^{\circ}C$ for 40 seconds. We employed for a four-point tester, field emission scanning electron microscope(FE-SEM), transmission electron microscope(TEM), high resolution X-ray diffraction(HRIXRD), and scanning probe microscope(SPM) in order to examine the sheet resistance, in-plane microstructure, cross-sectional microstructure evolution, phase transformation, and surface roughness, respectively. The silicide on 30 nm polysilicon substrate was stable at temperature up to $900^{\circ}C$, while the one on 70 nm substrate showed the conventional $NiSi_2$ transformation temperature of $700^{\circ}C$. The HRXRD result also supported the existence of NiSi-phase up to $900^{\circ}C$ for the Ni silicide on the 30 nm polysilicon substrate. FE-SEM and TEM confirmed that 40 nm thick uniform silicide layer and island-like agglomerated silicide phase of $1{\mu}m$ pitch without residual polysilicon were formed on 30 nm polysilicon substrate at $700^{\circ}C\;and\;1000^{\circ}C$, respectively. All silicides were nonuniform and formed on top of the residual polysilicon for 70 nm polysilicon substrates. Through SPM analysis, we confirmed the surface roughness was below 17 nm, which implied the advantage on FUSI gate of CMOS process. Our results imply that we may tune the thermal stability of nickel monosilicide by reducing the height of polysilicon gate.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.07b
• /
• pp.851-856
• /
• 2003

We have investigated the material and electrical properties of $Bi_{4-x}La_xTi_3O_{12}$ (BLT) ferroelectric thin film for ferroelectric nonvolatile memory applications of capacitor type and single transistor type. The 120nm thick BLT films were deposited on $Pt/Ti/SiO_2/Si$ and $SiO_2/Nitride/SiO_2$ (ONO) substrates by the sol-gel spin coating method and were annealed at $700^{\circ}C$. It was observed that the crystallographic orientation of BLT thin films were strongly affected by the excess Bi content and the intermediate rapid thermal annealing (RTA) treatment conditions regardeless of two type substrates. However, the surface microstructure and roughness of BLT films showed dependence of two different type substrates with orientation of (111) plane and amorphous phase. As increase excess Bi content, the crystallographic orientation of the BLT films varied drastically in BLT films and exhibited well-crystallized phase. Also, the conversion of crystallographic orientation at intermediate RTA temperature of above $450^{\circ}C$ started to be observed in BLT thin films with above excess 6.5% Bi content and the rms roughness of films is decreased. We found that the electrical properties of BLT films such as the P-V hysteresis loop and leakage current were effectively modulated by the crystallographic orientations change of thin films.

• Korean Chemical Engineering Research
• /
• v.51 no.6
• /
• pp.774-779
• /
• 2013

We synthesized the solution processible monodispersed $TiO_2$ crystalline nano-sol with ~ 5 nm in size by sol-gel method. Through the spin-coating of crystalline $TiO_2$ nano-sol at low processing temperature, we could make even blocking interlayer on the rough FTO transparent electrode substrate. The rough FTO surface could be gradually smoothed by the spin-coating of nano-crystalline $TiO_2$ sol based blocking interlayer. The 1, 2.5, 5, and 10 wt% of nanocrystalline $TiO_2$ sol formed 29, 38, 62, and 226 nm-thick of blocking interlayer in present experimental condition, respectively. The 5 and 10 wt% of $TiO_2$ nano-sol could effectively fill up the valley part of bare FTO with 48.7 nm of rms (root mean square) roughness and consequently enabled the ZnO to be grown to vertically aligned one dimensional nanorods on the flattened blocking interlayer/FTO substrate.