• Journal of the Korean Society of Hazard Mitigation
• /
• v.10 no.5
• /
• pp.9-15
• /
• 2010

Recently, the high-compressive strength concrete where the use is extending was weak in fire because of spalling that was occurring with rise of internal vapor pressure by high temperature. For preventing spalling of high-strength concrete in fire, Organic fibers have been using in concrete generally. By melting of organic fibers in concrete in fire, the internal moistures of concrete moves quickly to the outside, and so, preventing of spalling of high-strength concrete. But this method will be able to prevent the spalling of high-strength concrete, but makes the decrease of the concrete strength after fire. This study make a comparison between properties of preventing of spalling and remaining compressive strength of concrete using intumescence Alkali-Silicates fire-resistant material and that of concrete with organic fibers. Using organic fibers for preventing of spalling of concrete are P.P and Nylon fibers, and anti-fire intumescence material for protection of concrete surface is alkali-silicate materials. Fire resistance test executed as long as 3 hr under the flame temperature $1,200^{\circ}C$ over. In the case of concrete with P.P fibers, don't occurred the spalling, but the remaining compressive strength will not be able to measure, the concrete using intumescence Alkali-Silicates system fire-resistant material is not only preventing of the spalling but also the remaining compressive strength maintained until the maximum 96%.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.11a
• /
• pp.605-608
• /
• 2008

This study investigated fundamental properties corresponding to mixtures for the high strength, and their properties of spalling prevention after a fire test. The results were summarized as following. For the flowability of using mixtures for the high strength, the target flow was satisfied with a small quantity of high performance reducing water agent to compare with silica fume. For the compressive strength in the case of using mixtures for the high strength, it was higher to compare with silica fume at 7 days, so it was proved that using mixtures for the high strength was profitable to prevent early frost damage. The compressive strength at the 28 days of silica fume and mixtures for the high strength were similar. There was no reduced tendency at the compressive strength according fiber contents, so it found out that the bonding strength between the fiber and concrete was hardly effective. For the spalling properties, the specimens without fibers were destroyed, however using over 0.05% of NY and PP fibers was effective to prevent spalling on the high strength concrete.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2011.11a
• /
• pp.119-120
• /
• 2011

Recently, the effects of high temperature and fiber content on the residual mechnical properties of high-strength concrete were experimentally investigated. In this paper, residual mechanical properties of concrete with water to cement (w/c) ratios of 55%, 42% and 32% exposed to high temperature are compared with those obtained in fiber reinforced concretes of similar characteristics with the ranging of 0,05% to 0,20% polypropylene (PP) fibers by volume of concrete, and considered factors include pre-load levels (20% and 40% of the maximum load at room temperature). Outbreak time and water contents were tested and were determined the compressive strength. In the result, it is showed that to prevent the explosive spalling of 50MPa grade concretes exposed to high temperature need more than 0.05Vol.% PP fibers. Also, the cross-sectional area of PP fiber can influence on the residual mechanical properties and the spalling tendency of fiber reinforced concrete exposed to high temperature. Especially, the external loading increases not only the residual mechanical properties of concrete but also the risk of spalling and the brittle tendency.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2017.05a
• /
• pp.5-6
• /
• 2017

Ultra high-strength concrete can prevent spalling by mixed ratio of PP and NY fiber. However, there is a lack of research on the deterioration of strength due to changes in mechanical properties after spalling prevention. In this study, the effect of high temperature on the mechanical properties of 150MPa concrete mixed with PP and NY fiber was evaluated. As a result, mixing PP and NY fiber is judge to be little effect on the mechanical properties of the 150MPa concrete at high temperature.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2018.11a
• /
• pp.44-45
• /
• 2018

In this study, water vapor pressure of high strength concrete reinforced with amorphous steel fiber(AF) was evaluated. Experimental results show that spalling occurs when the incorporation rate of amorphous steel fiber is 0.5 vol.% or more. This is because the ratio of AF increased per unit area influenced the formation of the water vapor pressure discharge passage by the polypropylene fiber(PPF) melting. Therefore, it is necessary to find the proper mixing ratio of AF and PPF to prevent spalling.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.11a
• /
• pp.481-484
• /
• 2006

This study investigates the engineering and fire endurance properties of ultra high strength concrete. The mixture proportions with water to binder ratios (W/B) of 0.15 and 0.25 consist of various adding ratios, such as 0, 0.05, 0.1, 0.15, 0.2, 0.25 and 0.3 percent respectively, of polypropylene (PP) fiber. As for the parameters of specimens, fluidity, compressive strength and unloading fire test were carried out. Test showed that an increase of fiber contents had the favorable properties in fire endurance performance; specimens in W/B 15% required 0.3vol% of PP fiber and specimens in W/B 25% needed only 0.1vol% to prevent spalling.

• Journal of the Korea Concrete Institute
• /
• v.22 no.2
• /
• pp.229-235
• /
• 2010

In this study, fire resistance performance of high strength concrete specimen with fireproof gypsum board was investigated for possible use in upgrading fire-resistant performance of the existing building and repair of fire damaged structures. Fire test of eight identical high strength concrete columns were carried out for 180 minutes in accordance with ISO-834. The temperature distributions in longitudinal reinforcement and concrete temperature at various depths were recorded. The fireproof performance of gypsum board and explosive spalling of concrete were observed. The specimens with 15 mm thick twoply fireproof gypsum board spalled after gypsum board crumbled regardless of fastening methods. However, when the thickness of fireproof gypsum board was more than 30 mm, it was possible to prevent the explosive spalling and control the rebar temperature. Although the effect of cover thickness could not be compared because the explosive spalling occurred, there seemed to be no difference in insulation efficiency.

• Journal of Korean Tunnelling and Underground Space Association
• /
• v.16 no.3
• /
• pp.311-320
• /
• 2014

High strength concrete is not only vulnerable to the occurrence of spalling which generates the loss of cross-section in concrete structures but produces faster degradation in its mechanical properties than normal strength concrete in the event of fire. This study aims to evaluate fire resistance of high strength segment concrete with PET fibers mixed to prevent spalling under ISO834 (2hr) and RABT fire curve. As results, the samples without PET fibers show the concrete loss up to the depth of about 8 cm and 9.5 cm from the surface exposed to fire under ISO834 and RABT fire curve respectively. The samples mixed with PET fiber of 0.1% show no spalling under ISO834 fire curve and the spalled thickness of 6.5 cm under RABT fire curve after the fire tests. Finally, the sample mixed with PET fiber of 0.2% shows no spalling under RABT fire curve. The results indicate that the suitable amounts of PET fiber for securing fire resistance performance of this high strength segment concrete are 0.1% under ISO834 fire curve and 0.2% under RABT fire curve. However, even though spalling does not occur, it is necessary to repair the deterioration of concrete up to 4 cm from the surface exposed to fire after fire.

• Journal of the Korea Concrete Institute
• /
• v.20 no.1
• /
• pp.89-97
• /
• 2008

By replacing the meta-kaolin with cement and the waste tire chip with fine aggregate separately, the high strength concrete is protected from the spalling in fire and the method to constrain the temperature increase of steel bar within the concrete and the basic properties of the high strength concrete mixed with the material are reviewed. As the result, meta-kaolin increases the self fire proof characteristics of the concrete, the waste tire chip can share the internal expanding pressure so it can be deleted. In detail, using the meta-kaolin about the cement in 4$\sim$8% of weight ratio about the cement and the waste tire chip under the grade scope of 0.6$\sim$3 mm in 5$\sim$10% of weight ratio about the sand is very effective to prevent the spalling.

• Journal of the Korea Concrete Institute
• /
• v.23 no.5
• /
• pp.627-636
• /
• 2011

Recently, to prevent explosive spalling of high-strength concrete (HSC) members, the usage of nylon fiber instead of polypropylene fiber has increased. Past experimental studies have been conducted to examine the spalling and mechanical properties of HSC with nylon fibers when exposed to elevated temperature. However, the previous studies on HSC with nylon fibers subjected to high temperatures were performed only on the properties such as spalling, compressive strength, and elastic modulus rather than investigations on to the behaviors such as thermal strain, total strain, steady state creep, and transient creep. Therefore, in this study thermal strain, total strain, steady state creep, and transient creep of HSC mixed with nylon fibers with water to binder ratio of 0.30 to 0.15 were tested. The experimental results showed that nylon fibers did not affect the performance of HSC with nylon fibers at high temperatures. However, HSC with nylon fibers generated a larger transient creep strain than that of HSC without fibers and normal strength concrete.