The Fundamental Property and Fire Resistance of the High Strength Concrete Corresponding to mixtures for the High Strength

고강도용 혼합재를 사용한 고강도 콘크리트의 기초물성 및 내화특성 검토

This study investigated fundamental properties corresponding to mixtures for the high strength, and their properties of spalling prevention after a fire test. The results were summarized as following. For the flowability of using mixtures for the high strength, the target flow was satisfied with a small quantity of high performance reducing water agent to compare with silica fume. For the compressive strength in the case of using mixtures for the high strength, it was higher to compare with silica fume at 7 days, so it was proved that using mixtures for the high strength was profitable to prevent early frost damage. The compressive strength at the 28 days of silica fume and mixtures for the high strength were similar. There was no reduced tendency at the compressive strength according fiber contents, so it found out that the bonding strength between the fiber and concrete was hardly effective. For the spalling properties, the specimens without fibers were destroyed, however using over 0.05% of NY and PP fibers was effective to prevent spalling on the high strength concrete.

본 연구는 고강도 혼합재 사용에 따른 고강도 콘크리트의 기초물성 및 내화특성을 검토한 것으로, 그 결과를 요약하면 다음과 같다. 유동특성으로 고강도 혼합재를 사용할 경우, 실리카흄을 사용한 경우보다 목표 슬럼프플로우를 만족키 위한 고성능 감수제의 사용량이 감소하는 것으로 나타나, 유동성 확보 차원에서 고강도 혼합재를 사용할 때 실리카흄과 비교할시 우수한 것으로 나타났다. 강도특성으로는 고강도 혼합재 사용 시 재령 7일 초기압축강도가 실리카흄을 사용한 경우보다 증가하는 것으로 나타나, 초기 강도 확보에서 유리함을 확인할 수 있었고, 재령 28일에서는 모두 비슷하게 압축강도를 발현하는 것으로 나타났다. 섬유 혼입율 변화에 따른 압축강도는 미소한 차이만 있을 뿐 큰 차이는 없는 것으로 나타났다. 섬유 무혼입에서 고강도 혼합재 및 실리카흄 모두 폭열이 발생하였지만, 섬유 혼입량 0.05% 이상에서는 폭열이 방지되는 것으로 나타났다.