• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2021년도 봄 학술논문 발표대회
• /
• pp.120-121
• /
• 2021

The organic insulation material has excellent thermal insulation property, but it is difficult to expect fire stability, and semi inorganic insulation only delays combustible hour but it is difficult to expect fire stability. In this study, thermal insulation property of cement-based non-combustible inorganic insulation using cement and non combustible materials and redispersible polymer powder was studied. As a result of the experiment, the thermal insulation property decreased as the use of redispersible polymer powder increased, but the heat insulation property improved when using the appropriate amount.

• 한국초전도ㆍ저온공학회논문지
• /
• 제12권3호
• /
• pp.49-54
• /
• 2010

This paper presents apparent thermal conductivity of various powder at different vacuum levels for cryogenic insulation. Four kinds of powder insulator are examined by using boil-off calorimetry at pressure range from 50 Torr to 3 mTorr. The first material is perlite which is widely used in cryogenic application. Microsphere is the second one that is recently proposed as a replacement powder for liquid hydrogen storage tanks. It is a hollow sphere made of silica with the diameter in the order of 10 to $100{\mu}m$. Popped rice and polystyrene beads are also selected as candidates for powder insulation even though they are polymers. With their porous elliptic and spherical configuration and light density, they demonstrate fairly good thermal insulation performance at pressure range from 50 Torr to 3 mTorr. According to the experimental investigation in this paper, microsphere and polystyrene beads possess promising insulation characteristic as powder insulators and further study is desired.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2021년도 봄 학술논문 발표대회
• /
• pp.213-214
• /
• 2021

External insulation method is used to conserve energy of buildings. However, the current external insulation method uses organic insulating materials to become a diffusion path in case of fire. In this study, the purpose of this study is to provide basic data on the required performance of the plastering material according to the CaCO₃ powder addition of the finishing material of the external insulation method. In Figure 1, when powder was added, the adhesion strength decreased by 30% to 35% at 10% and 0% to 50% at 20% compared to Plain. In Figure 2, the moisture permeability increases approximately twice when powder is added. The results for the water absorption coefficient are shown in Figure 3.

• 한국산업융합학회 논문집
• /
• 제24권6_2호
• /
• pp.787-793
• /
• 2021

The global demand for Liquefied Natural Gas(LNG) continues to increase and is facing a big cycle. To keep pace with the increase in international demand for LNG, the demand for LNG fueled ships is also increasing. Since LNG fuel tanks are operated in a cryogenic environment, insulation technology is very important, and although there are various types of insulation applied to Type C tanks, multi-layer insulation and vacuum insulation are typically applied. Powder insulation materials are widely used for storage and transportation of cryogenic liquids in tanks with such a complex insulation structure. In this study, compression tests at room and cryogenic temperature were performed on closed perlite, glass bubble, and fumed silica, which are representative powder insulation material candidates. Finally, the applicability to the Type C fuel tank was reviewed by analyzing the experimental results of this study.

• 전기학회논문지
• /
• 제60권8호
• /
• pp.1627-1631
• /
• 2011

During a routine inspection of a large pump motor at power plant, white powder was found on the surface of the stator end windings. Visual inspection and high voltage insulation diagnosis was performed to determine whether this motor is available. The purpose of this paper is to understand the insulation properties of white powder found on high voltage stator and to know prevention of insulation weakness.

• Metals and materials international
• /
• 제28권
• /
• pp.1778-1782
• /
• 2021

This study examines the insulation coating technology of Fe-Si-Cr powder via selective oxidation annealing, which oxidizes elements selectively by controlling the oxidation potential. The study calculated the oxidation driving force of Fe, Si, and Cr, and conducted a thermodynamic analysis of oxidation and reduction conditions according to temperature and oxidation potential. Based on the results, a selective oxidation annealing was performed in an atmosphere in which Fe is reduced and only Si and Cr are selectively oxidized. The oxidation potential was controlled through the partial pressure ratio of hydrogen and water vapor. The XPS analysis results confirmed that a Si and Cr complex oxide layer formed on the powder surface after the selective oxidation annealing. Afterward, withstanding voltages were analyzed to evaluate the insulation property. Then, the withstanding voltage of the powder applying the selective oxidation annealing increased significantly compared to that of the initial powder. Further analysis showed that the powder annealed in an air atmosphere had a significantly lower saturation magnetic flux density than the initial powder, while the powder applying the selective oxidation annealing had only a slightly reduced saturation magnetic flux density.

• 한국수소및신에너지학회논문집
• /
• 제28권5호
• /
• pp.512-520
• /
• 2017

This paper is a numerical study of various methods of applying SOFC hot BOP insulation. The application methods are four cases from case 1 to case 4, and the performance difference between the result of applying powdered insulation and the result of zoning using composite multi-layer insulation was examined. Numerical results show that the thermal stability of composite multi-layer insulation is better than that of powder insulation when the thermal conductivity is 0.04 W/mK. In the future, we will increase the thermal conductivity of the composite multi-layer thermal insulation material and find the greatest value of thermal conductivity with a similar result to that of the powder insulation.

• 한국화재소방학회논문지
• /
• 제23권3호
• /
• pp.17-22
• /
• 2009

에폭시 분체도료는 부스닥트, 및 전기기기에 절연재료로 광범위하게 사용되어 진다. 특히 Coating 절연 방식의 경우 전류에 의한 줄 열로 인해 전기화재 및 폭발의 점화 원인이 된다. 본 연구는 에폭시분체도료의 열화특성에 대해 절연파괴, 아크방전, 수명특성(V-t)을 중심으로 비교검토하고 이에 대한 기초데이터 확보 및 전기화재 원인인 절연특성에 대해 연구 하였다. 온도변화에 따른 절연특성은 시편 KS가 유리전이온도(Tg) 이전까지 $8{\sim}10%$ 정도의 감소로 안정적이었다. V-t 및 아크방전특성의 경우, 열화시편에서도 안정적 특성을 유지하였다. 열화에 의한 전기적특성의 경우 시편KS가 우수한 성능을 가지고 있다.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.1167-1168
• /
• 2006

In this study, the pure iron powder was treated with aqueous phosphoric acid to produce phosphate insulating layer on the surface. After drying the powder, it was compacted in a mold with a diameter of 20mm at 800MPa. The powder compacts were then heat treated at $500^{\circ}C$ for 1 hour. The results showed that insulated iron powder was obtained with uniform phosphate layer by chemical reaction. With increased amount of phosphate layer, the core loss and density of compacts were decreased. It was also found that the addition of ethyl alcohol during insulating reaction resulted in improved core loss value.

• 설비공학논문집
• /
• 제8권4호
• /
• pp.497-509
• /
• 1996

Evacuated powder insulations have long been known to have better thermal performance than existing commercially available insulators, such as fiber glass and CFC-blown foam. To make a composite powder panel, a series of individually evacuated panels was encapsulated in a rigid closed cell foam matrix. The panels were encapsulated in a thin glass sheet barrier to preserve the vacuum. The thermal conductivity of the individual panel was found to be $0.0062W/m^{\circ}K$ by experiment and the polyurethane foam above had a thermal conductivity of $0.024W/m^{\circ}K$. In this study, numerical analysis using finite element method was carried out to investigate insulation performance of rigid foam/evacuated powder composite panel with respect to panel geometries such as panel pitch, panel aspect ratio and panel area ratio. Numerical analysis has indicated that more optimal vacuum panel geometries, much lower overall thermal conductivities can be achieved.