• Journal of the Korean Ceramic Society
• /
• v.33 no.9
• /
• pp.1057-1063
• /
• 1996

Y2O3-CeO2-ZrO2 powders were prepared from water-soluble salts using a coprecipitation method. The forming process of oxide and the characteristics of the calcined powders treated in different drying conditions were investigated. The oxidation was occurred at the temperature of around 40$0^{\circ}C$ and the main crystallization of ZrO2 around $600^{\circ}C$. On calcination at $600^{\circ}C$ heating lamp-dried powders consisted of agglomerates of globular morphology with average agglomerate size of 2.27${\mu}{\textrm}{m}$ and specific surface area of 68.3m2/g and spray dried powders contained dense spheric particles with average agglomerate size of 1.35${\mu}{\textrm}{m}$ and specific surface area of 11.0m2/g which exhibited low agglomeration tendency. Removal of the water by a freeze-drying technique produced calcined powders containing flake-like secondary particle structures with wide agglomerate size distri-bution of 0.1-60${\mu}{\textrm}{m}$ and specific surface area of 24.5${\mu}{\textrm}{m}$. The 20 MPa-pressed density (36.8-41.4% T,D) of calcined powders did not nealy depend on drying methods whilst compaction ratio of calcined powders derived from freeze-drying was the highest ( 6.24) among three drying methods. On continuous heating up to 150$0^{\circ}C$ the sinterability of calcined powders derived from heating lamp-drying was superior to those derived from spray-and freeze-drying. The final sintered density of calcined powders was the highest (96% T,D at 150$0^{\circ}C$) in case of heating lamp-drying.

• Journal of the Korean Ceramic Society
• /
• v.50 no.6
• /
• pp.402-409
• /
• 2013

The objective of this study was to develop a synthesis process for ${\beta}$-SiC powders to reduce the synthesis temperature and to control the particle size and to prevent particle agglomeration of the synthesized ${\beta}$-SiC powders. A phenol resin and TEOS were used as the starting materials for the carbon and Si sources, respectively. $SiO_2$-C hybrid precursors with various C/Si mole ratios were fabricated using a conventional sol-gel process. ${\beta}$-SiC powders were synthesized by a carbothermal reduction process using $SiO_2$-C hybrid precursors with various C/Si mole ratios (1.6 ~ 2.5) fabricated using a sol-gel process. In this study, the effects of excess carbon and the addition of Si powders to the $SiO_2$-C hybrid precursor on the synthesis temperature and particle size of ${\beta}$-SiC were examined. It was found that the addition of metallic Si powders to the $SiO_2$/C hybrid precursor with excess carbon reduced the synthesis temperature of the ${\beta}$-SiC powders to as low as $1300^{\circ}C$. The synthesis temperature for ${\beta}$-SiC appeared to be reduced with an increase of the C/Si mole ratio in the $SiO_2$-C hybrid precursor by a direct carburization reaction between Si and excess carbon.

• 한국신재생에너지학회:학술대회논문집
• /
• 2006.06a
• /
• pp.51-54
• /
• 2006

Cathode material, $(Ba_{0.5}Sr_{0.5})_{0.99}Co_{0.8}Fe_{0.2}O_{3-{\delta}}$, for low temperature SOFC was prepared by the glycine-nitrate synthesis process (GNP). The characteristics of the synthesized powders were studied with controlling pH of a precursor. The synthesis BSCF powders with pH were agglomeration state and calcinations temperature has not influence on particles. Highly acidicprecursor solution increased a single phase forming the temperature. Also, synthesis BSCF powder was show result for thermal analysis and alteration of difference crystal with pH. It is considered that Ba and Sr cannot complex by carboxylic acid group of glycine, because under highly acidic condition the caboxylic group mainly combined with $H^+$ insead of alkali and alkaline earth cations. In case of using precursor solution with pH $2{\sim}3$, a single perovskite phase was obtained at $1000^{\circ}C$. Polarization resistance of $(Ba_{0.5}Sr_{0.5})_{0.99}Co_{0.8}Fe_{0.2}O_{3-{\delta}}$ was measured by AC impedance spectroscopy from the two electrode symmetric cell. Area specific resistance of the $(Ba_{0.5}Sr_{0.5})_{0.99}Co_{0.8}Fe_{0.2}O_{3-{\delta}}$ air electrode at $500^{\circ}C\;and\;600^{\circ}C$ were $0.96{\Omega}?cm^2$ and $0.16{\Omega}?cm^2$, respectively.

• Korean Journal of Metals and Materials
• /
• v.49 no.8
• /
• pp.596-600
• /
• 2011

Thermal degradation behavior of a $WO_3-TiO_2$ monolithic catalyst was investigated in terms of structural, morphological, and physico-chemical analyses. The catalyst with 4 wt.% $WO_3$ contents were prepared by a wet-impregnation method, and a durability test of the catalysts were performed in a temperature range between $400^{\circ}C$ and $800^{\circ}C$ for 3 h. An increase of thermal stress decreased the specific surface area, which was caused by grain growth and agglomeration of the catalyst particles. The phase transition from anatase to rutile occurred at around $800^{\circ}C$ and a decrease in the Brønsted acid sites was confirmed by structural analysis and physico-chemical analysis. A change in Brønsted acidity can affect to the catalytic efficiency; therefore, the thermal degradation behavior of the $WO_3-TiO_2$ catalyst could be explained by the transition to a stable rutile phase of $TiO_2$ and the decrease of specific surface area in the SCR catalyst.

• Journal of the Korean Ceramic Society
• /
• v.48 no.6
• /
• pp.559-564
• /
• 2011

In order to investigate the behavior of $SiO_2$ in the molybdenum silicide powders, crystal structure of these powders was measured by XRD, in addition, surface composition and surface phase (or chemical states) and microstructure were analysed by XPS and TEM, respectively. Mo-silicide powders containing $SiO_2$ were synthesized by SHS (Self-Propagating High-Temperature Synthesis) technique. In XRD result, according to increase of $SiO_2$ contents, the crystal structure for synthesized $MoSi_2$ powders was still typical $MoSi_2$ bct without any other phases. By XPS analysis, the surface of Mo and Si source powders was covered with $MoO_3$ and $SiO_2$, respectively, and the surface of synthesized $MoSi_2$ powder was also covered with $MoO_3$ and $SiO_2$, which were stable oxides at room temperature. However, according to increase of $SiO_2$ addition, $MoSi_2$ phase in XPS spectra decreased and $SiO_2$ phase increased relatively in synthesized $MoSi_2$ powders. From the results by XPS and XRD, we found that the existent $SiO_2$ has amorphous structure. In the microstructure, the small particulates of the synthesized products added $SiO_2$ agglomerated together to form larger clusters (from ~10 nm to ~1 ${\mu}m$). From TEM, XPS, and XRD results, we found that the out layer of agglomeration of synthesized $MoSi_2$ powder is surrounded by amorphous $SiO_2$.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.27 no.3
• /
• pp.122-129
• /
• 2017

For the production of a high-density ITO target, $In_2O_3$ powders with a small particle size and low agglomeration should be synthesized. The purpose of this study is to control the size and shape of the Indium hydroxide precursor which affects the properties of the $In_2O_3$ powder. As a starting raw material, Indium metal was dissolved in a Nitric acid ($HNO_3$) solution. The effect of concentration, pH, and temperature on the properties of Indium hydroxide was investigated using ammonium hydroxide as a precipitant. Crystallite size of each sample was analyzed by X-ray diffraction and the shape and the size of the powder was analyzed by transmission electron microscopy. As a result, the particle size of Indium hydroxide was increased with increase in the concentration of $In(NO_3)_3$ and the particle size and shape of the Indium hydroxide remained unchanged with increase in the pH of the solution. The particle size increased with increase in the precipitation temperature during precipitation.

• Applied Chemistry for Engineering
• /
• v.25 no.1
• /
• pp.72-77
• /
• 2014

Microstructure and thermal stability of mechanically ball milled $FeS_2$ were investigated. The average particle size and distribution of $FeS_2$ powder were changed in two steps with the increased ball milling time. The average particle size drastically decreased from $98.4{\mu}m$ to 1.01 and $0.89{\mu}m$ after ball milling of 10 h and 30 h, respectively. However, the distribution was broad and a shoulder appeared at $2{\mu}m$ because the pulverization was still in process at 10 h ball milling. After 60 h ball milling, the distribution became narrower. After ball milling of 120 h, the average particle size increased because of $FeS_2$ particle agglomeration. Therefore, the particle size distribution became broaden again. Finally, after ball milling of 170 h, $FeS_2$ with the narrowest size distribution can be obtained. Thermal stability of $FeS_2$ was unstable as the $FeS_2$ particle was pulverized. Therefore, the activation energy of the fine size particles is 27% lower than that of the as-received $FeS_2$.

• Applied Chemistry for Engineering
• /
• v.31 no.4
• /
• pp.416-422
• /
• 2020

In this study, eco-friendly biodegradable materials were prepared using poly(lactic acid) (PLA), poly(butylene adipate-co-terephthalate) (PBAT), and hydrogenated castor oil power (HCO) as an additive. The prepared PLA/PBAT/HCO blended films were characterized by the scanning electron microscope (SEM) and fourier-transform infrared spectroscopy (FT-IR). The results of SEM analysis indicated that PLA/PBAT (8 : 2) blended films added HCO showed no rough area, crack, or large agglomeration when compared with those adding various additives (12-hydroxy stearic acid (12HSA) and cellulose). The FT-IR results indicated the presence of specific peak of HCO in the PLA/PBAT blended films, and its peak intensity increased with increasing HCO content (0~5.0 wt%). Tensile strength, elongation at break, and water barrier and thermal properties of the prepared PLA/PBAT/HCO blended films were also investigated, indicating that the physical and thermal properties was improved more than three times by the addition of HCO. The biodegradability test in soil revealed that the prepared biodegradable materials were degraded by about 6.0~20% after 90 days.

• Clean Technology
• /
• v.27 no.4
• /
• pp.359-366
• /
• 2021

Halloysite nanotubes (HNTs), the multiwalled clay mineral with the composition of Al₂Si₂O₅(OH)₄·nH₂O, have been highlighted as a low-cost adsorbent for the removal of dyes from wastewater. Although a powder of halloysite presents a high specific surface area, forming media are significantly considered due to sludge-clogging induced by the water-bound agglomeration. However, higher firing temperature to achieve the structural durability of the media and lower utilization rate due to longer penetration depth into the media act as hurdles to increase the dye-adsorption capacity. In this work, the retention of the adsorption capacity of halloysite was evaluated with methylene blue solution after the heat treatment at 750 ℃. In order to improve the utilization rate, tubular media were fabricated by extrusion. The images taken by transmission electron microscopy show that HNTs present excellent structural stability under heat treatment. The HNTs also provide superb capacity retention for MB adsorption (93%, 18.5 mg g^-1), while the diatomite and Magnesol^® XL show 22% (7.65 mg g^-1) and 6% (11.7 mg g^-1), respectively. Additionally, compositing with lignin enhances adsorption capacity, and the heat treatment under the hydrogen atmosphere accelerates the adsorption in the early stage. Compared to the rod-type, the tubular halloysite media rapidly increases methylene blue adsorption capacity.