• Current Photovoltaic Research
• /
• 제6권1호
• /
• pp.17-20
• /
• 2018

The dependency of the photovoltaic performance of p-/n-type silicon solar-cells on the metallic contaminant type (Fe, Cu, and Ni) and concentration was investigated. The minority-carrier recombination lifetime was degraded with increasing metallic contaminant concentration, however, the degradation sensitivity of recombination lifetime was lower at n-type than p-type silicon wafer, which means n-type silicon wafer have an immunity to the effect of metallic contamination. This is because heavy metal ions with positive charge have a much larger capture cross section of electron than hole, so that reaction with electrons occurs much more easily. The power conversion efficiency of n-type solar-cells was degraded by 9.73% when metallic impurities were introduced in the silicon bulk, which is lower degradation compared to p-type solar-cells (15.61% of efficiency degradation). Therefore, n-type silicon solar-cells have a potential to achieve high efficiency of the solar-cell in the future with a merit of immunity against metal contamination.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2012년도 제43회 하계 정기 학술대회 초록집
• /
• pp.429-429
• /
• 2012

To investigate the gettering effect of B-doped n-type monocrystalline silicon wafer, we made the p-n junction by diffusing boron into n-type monocrystalline Si substrate and then oxidized the boron doped n-type monocrystalline silicon wafer by in-situ wet and dry oxidation. After oxidation, the minority carrier lifetime was measured by using microwave photoconductance and the sheet resistance by 4-point probe, respectively. The junction depth was analyzed by Secondary Ion Mass Spectrometry (SIMS). Boron diffusion reduced the metal impurities in the bulk of silicon wafer and increased the minority carrier lifetime. In the case of wet oxidation, the sheet resistance value of ${\sim}46{\Omega}/{\Box}$ was obtained at $900^{\circ}C$, depostion time 50 min, and drive-in time 10 min. Uniformity was ~7% at $925^{\circ}C$, deposition time 30 min, and drive-in time 10 min. Finally, the minority carrier lifetime was shown to be increased from $3.3{\mu}s$ for bare wafer to $21.6{\mu}s$ for $900^{\circ}C$, deposition 40 min, and drive-in 10 min condition. In the case of dry oxidation, for the condition of 50 min deposition, 10 min drive-in, and O2 flow of 2000 SCCM, the minority carrier lifetime of 16.3us, the sheet resistance of ${\sim}48{\Omega}/{\Box}$, and uniformity of 2% were measured.

• 한국생산제조학회지
• /
• 제20권4호
• /
• pp.395-400
• /
• 2011

Scanning Probe Lithography is a method to localized oxidation on single crystal silicon wafer surface. This study demonstrates nanometer scale non contact lithography process on (100) silicon (p-type) wafer surface using AFM(Atomic force microscope) apparatuses and pulse controlling methods. AFM-based experimental apparatuses are connected the DC pulse generator that supplies ultra short pulses between conductive tip and single crystal silicon wafer surface maintaining constant humidity during processes. Then ultra short pulse durations are controlled according to various experimental conditions. Non contact lithography of using ultra short pulse induces electrochemical reaction between micro-scale tip and silicon wafer surface. Various growths of oxides can be created by ultra short pulse non contact lithography modification according to various pulse durations and applied constant humidity environment.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 영호남학술대회 논문집
• /
• pp.7-12
• /
• 2000

This paper presents the electrochemical etch-stop characteristics of single-crystal silicon in a tetramethyl ammonium hydroxide(TMAH):isopropyl alcohol(IPA):pyrazine solution. Addition of pyrazine to a TMAH:IPA etchant increases the etch-rate of (100) silicon, thus the elapsed time for etch-stop was shortened. The current-voltage (I-V) characteristics of n- and p-type silicon in a TMAH:IPA:pyrazine solution were obtained, respectively. Open circuit potential(OCP) and passivation potential(PP) of n- and p-type silicon, respectively, were obtained and applied potential was selected between n- and p-type silicon PP. The electrochemical etch-stop is applied to the fabrication of 801 microdiaphragms having $20{\mu}m$ thickness on a 5-inch silicon wafer. The averge thicknesses of 801 microdiaphragms fabricated on the one wafer were $20.03{\mu}m$ and standard deviation was ${\pm}0.26{\mu}m$. The silicon surface of the etch-stopped microdiaphragm was extremely flat without noticeable taper or other nonuniformities. The benefits of the electrochemical etch-stop in a TMAH:IPA:pyrazine solution become apparent when reproducibility in the microdiaphragm thickness for mass production is considered. These results indicate that the electrochemical etch-stop in a TMAH:IPA:pyrazine solution provides a powerful and versatile alternative process for fabricating high-yield silicon microdiaphragms.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 춘계학술대회 논문집 전자세라믹스 센서 및 박막재료 반도체재료 일렉트렛트 및 응용기술
• /
• pp.147-151
• /
• 2000

This paper presents the electrochemical etch-stop characteristics of single-crystal silicon in a tetramethyl ammonium hyciroxide(TMAH):isopropyl alcohol(IPA):pyrazine solution. Addition of pyrazine to a TMAH:IPA etchant increases the etch-rate of (100) silicon, thus the elapsed time for etch-stop was shortened. The current-voltage(I-V) characteristics of n- and p-type silicon in a TMAH:IPA:pyrazine solution were obtained, respectively. Open circuit potential(OCP) and passivation potential(PP) of n- and p-type silicon, respectively, were obtained and applied potential was selected between n- and p-type silicon PP. The electrochemical etch-stop is applied to the fabrication of 801 microdiaphragms having $20\;{\mu}m$ thickness on a 5-inch silicon wafer. The averge thicknesses of 801 microdiaphragms fabricated on the one wafer were $20.03\;{\mu}m$ and standard deviation was ${\pm}0.26{\mu}m$. The silicon surface of the etch-stopped microdiaphragm was extremely flat without noticeable taper or other nonuniformities. The benefits of the electrochemical etch-stop in a TMAH:IPA:pyrazine solution become apparent when reproducibility in the microdiaphragm thickness for mass production is considered. These results indicate that the electrochemical etch-stop in a TMAH:IPA:pyrazine solution provides a powerful and versatile alternative process for fabricating high-yield silicon microdiaphragms.

• 제어로봇시스템학회논문지
• /
• 제14권4호
• /
• pp.361-364
• /
• 2008

Tips of probe card were fabricated using MEMS technology. P-type silicon wafer with $SiO_2$ layer was used as a substrate for fabricating the probe card. Ni-Cr and Au used as seed layer for electroplating Ni were deposited on the silicon wafer. Line patterns for probing devices were formed on silicon wafer by electroplating Ni through mold which formed by MEMS technology. Bridge structure was formed by wet-etching the silicon substrate. AZ-1512 photoresist was used for protection layer of back side and DNB-H100PL-40 photoresist was used for patterning of the front side. The mold with the thickness of $60{\mu}m$ was also formed using THB-120N photoresist and probe tip with thickness of $50{\mu}m$ was fabricated by electroplating process.

• Mass Spectrometry Letters
• /
• 제12권1호
• /
• pp.26-30
• /
• 2021

The impurity concentration is a crucial parameter for semiconductor thin films. Evaluating the impurity distribution in silicon thin film is another challenge. In this study, we have investigated the doping concentration of boron in silicon thin film using time of flight secondary ion mass spectrometry in dynamic mode of operation. Boron doped silicon film was grown on i) p-type silicon wafer and ii) borosilicate glass using hot wire chemical vapor deposition technique for possible applications in optoelectronic devices. Using well-tuned SIMS measurement recipe, we have detected the boron counts 101~104 along with the silicon matrix element. The secondary ion beam sputtering area, sputtering duration and mass analyser analysing duration were used as key variables for the tuning of the recipe. The quantitative analysis of counts to concentration conversion was done following standard relative sensitivity factor. The concentration of boron in silicon was determined 1017~1021 atoms/㎤. The technique will be useful for evaluating distributions of various dopants (arsenic, phosphorous, bismuth etc.) in silicon thin film efficiently.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2009년도 제38회 동계학술대회 초록집
• /
• pp.322-322
• /
• 2010

For boron doping on n-type silicon wafer, around $1,000^{\circ}C$ doping temperature is required, because of the relatively low solubility of boron in a crystalline silicon comparing to the phosphorus case. Boron doping by fiber laser annealing and lamp furnace heat treatment were carried out for the uniformly deposited p-a-Si:H layer. Since the uniformly deposited p-a-Si:H layer by cluster is highly needed to be doped with high temperature heat treatment. Amorphous silicon layer absorption range for fiber laser did not match well to be directly annealed. To improve the annealing effect, we introduce additional lamp furnace heat treatment. For p-a-Si:H layer with the ratio of $SiH_4:B_2H_6:H_2$=30:30:120, at $200^{\circ}C$, 50 W power, 0.2 Torr for 30 min. $20\;mm\;{\times}\;20\;mm$ size fiber laser cut wafers were activated by Q-switched fiber laser (1,064 nm) with different sets of power levels and periods, and for the lamp furnace annealing, $980^{\circ}C$ for 30 min heat treatment were implemented. To make the sheet resistance expectable and uniform as important processes for the $p^+$ layer on a polished n-type silicon wafer of (100) plane, the Q-switched fiber laser used. In consequence of comparing the results of lifetime measurement and sheet resistance relation, the fiber laser treatment showed the trade-offs between the lifetime and the sheet resistance as $100\;{\omega}/sq.$ and $11.8\;{\mu}s$ vs. $17\;{\omega}/sq.$ and $8.2\;{\mu}s$. Diode level device was made to confirm the electrical properties of these experimental results by measuring C-V(-F), I-V(-T) characteristics. Uniform and expectable boron heavy doped layers by fiber laser and lamp furnace are not only basic and essential conditions for the n-type crystalline silicon solar cell fabrication processes, but also the controllable doping concentration and depth can be established according to the deposition conditions of layers.

• 비파괴검사학회지
• /
• 제37권1호
• /
• pp.1-6
• /
• 2017

본 논문에서는 테라헤르츠파 시간분광영상시스템을 이용하여 도핑된 실리콘 웨이퍼의 물리적 특성을 측정하는 것에 관한 연구를 진행하였다. 투과모드와 $30^{\circ}$의 입사각을 가진 반사모드를 이용하여 측정하였으며 실리콘 웨이퍼의 도핑 정도는 N-type과 P-type 모두에서 $10^{14}$에서 $10^{18}$까지 다양하게 준비하였다. 그 결과, 도핑 정도와 테라헤르츠파와의 상관관계를 찾았으며 이를 이용하면 모든 경우에 대한 도핑된 실리콘 웨이퍼의 도핑 정도를 확인할 수 있다. 또한, 각 도핑된 실리콘 웨이퍼의 도핑된 두께, 굴절률, 유전율을 테라헤르츠 시간영역 파형분석을 통하여 계산할 수 있었다. 따라서, 테라헤르츠 시간분광영상화 기술은 도핑된 실리콘 웨이퍼의 굴절률과 유전율과 같은 물리적 특성뿐만 아니라 도핑 정도를 측정할 수 있는 유용한 기술이 될 것으로 기대된다.

• 통합자연과학논문집
• /
• 제7권4호
• /
• pp.221-226
• /
• 2014

Optically encoded porous silicon smart particles were successfully fabricated from the free-standing porous silicon thin films using ultrasono-method. DBR PSi was prepared by an electrochemical etch of heavily doped $p^{{+}{+}}$-type silicon wafer. DBR PSi was prepared by using a periodic pseudo-square wave current. The surface-modified DBR PSi was prepared by either thermal oxidation or thermal hydrosilylation. Free-standing DBR PSi films were generated by lift-off from the silicon wafer substrate using an electropolishing current. Free-standing DBR PSi films were ultrasonicated to create DBR-structured porous smart particles. Optical characteristics of porous smart particles were measured by FT-IR spectroscopy. The surface morphology of porous smart particles was determined by FE-SEM.