• 한국전기전자재료학회논문지
• /
• 제16권5호
• /
• pp.361-364
• /
• 2003

It was investigated that the structural and electrical Properties of Ce-doped Ba(Zr$_{x}$Ti$_{1-x}$ )O$_3$ (BCZT) thin films with a mole fraction of x=0.2 and a thickness about 100 nm. BCZT films were prepared on Pt/Ti/SiO$_2$/Si substrate by a RF magnetron sputtering system. We have measured the thickness profile with Ar/O$_2$ ratio and the surface roughness. It was observed that the oxygen gas, which introduced during the film deposition, have an influence on the roughness of the film and the film roughness was reduced by annealing from 2.33 nm to 2.02 nm (RMS at 500 $^{\circ}C$, Ar:6 sccm, $O_2$:6 sccm). It was found that annealing procedure after top electrode deposit can reduce the dissipation factor.

• 한국표면공학회지
• /
• 제45권3호
• /
• pp.117-122
• /
• 2012

ZTO/GZO double layered films were prepared on unheated non-alkali glass substrates. ZTO films were deposited by RF/DC hybrid magnetron co-sputtering using ZnO (RF) target and $SnO_2$ (DC) targets, and then GZO films were deposited by DC magnetron sputtering using an GZO ($Ga_2O_3$:5.57 wt%) target. These films were post-annealed at temperature of 200, $300^{\circ}C$ in air and vacuum ambient for 30 min. In the case of post-annealing in air, ZTO/GZO double layer showed relatively low resistivity change, compared to GZO single layer. Furthermore, ZTO/GZO double layer revealed low WVTR, compared to GZO single layer. Therefore, it can be confirmed that ZTO film doing a role with barrier for water or oxygen diffusion.

• 한국태양에너지학회 논문집
• /
• 제30권3호
• /
• pp.90-97
• /
• 2010

$TiO_2$ thin films for solar energy utilization were prepared on ITO coated glass by r.f magnetron sputtering with variations of working pressure, oxygen flow rate and annealing temperature. Ion insertion and extraction reaction, and ion storage properties of films were investigated by using a cyclic voltammetry. Transmittance of thin films in as-prepared, colored and bleached states was measured by UV-VIS spectrophotometer. The samples deposited in our sputtering conditions showed poor electrochromic properties. Improvement in ion storage properties of $TiO_2$ thin film was observed after annealing at temperature of $400^{\circ}C$ in air for 2 hours. It was found that $TiO_2$ thin film in electrochromic device could be used as a passive counter-electrode.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 2001년도 추계학술대회 논문집 전기물성,응용부문
• /
• pp.158-160
• /
• 2001

${\beta}-Ga_2O_3$ nanobelts and nanoparticles were synthesized by a thermal annealing of as-milled GaN powders at $930^{\circ}C$ in nitrogen and oxygen atmosphere. respectively. The width of the nanobelts are $20\;nm{\sim}1000\;nm$. the thickness of the nanobelts are 100 nm. A bundle of the nanobelts is several centimeters in length. The lattice structure of these nanobelts and nanoparticles was identified to be a monoclinic ${\beta}-Ga_2O_3$ by X-ray diffraction (XRD), high-resolution transmission electron microscopy (HRTEM), and selected area electron diffraction (SAED).

• 수산해양기술연구
• /
• 제30권4호
• /
• pp.350-356
• /
• 1994

We have prepared superconducting Bi-Pb-Sr-Ca.Cu-O thin films by RF magnetron sputtering technique, on heated MgO(100) substrates. Sputtering was carried out in a mixture of argon and oxygen(10%) and the pressure was maintained at 5 mTorr during deposition. The substrate temperature was maintained $400^{\circ}C$ during deposition. The films sputtered were amorphous and insulating. All the films became superconducting by annealing, The films annealed at $880^{\circ}C$ for 30 minutes in air showed high-Tc phase with zero resistivity of 93K. These results indicate that the growth of the high-Tc phase is promoted by the presence of Pb at annealing temperature.

• 전기학회논문지
• /
• 제60권6호
• /
• pp.1175-1177
• /
• 2011

The SBN thin films were deposited on Pt/Ti/$SiO_2$/Si and p-type Si(100) substrate by rf magnetron sputtering method using $Sr_{0.7}Bi_{2.3}Nb_2O_9$ ceramic target. SBN thin films deposited were annealed at 600~800[$^{\circ}C$] by furnace in oxygen atmosphere during 40min. The polarization characteristics have been investigated to confirm the possibility of the SBN thin films for the application to destructive read out ferroelectric random access memory. The maximum remanent polarization and the coercive voltage are 0.6[${\mu}C/cm^2$], 1.2[V] respectively at annealing temperature of 800[$^{\circ}C$]. The leakage current density was the $2.57{\times}10^{-6}[A/cm^2]$ at an applied voltage of 5[V] at annealing temperature of 650[$^{\circ}C$]. Also, the fatigue characteristics of SBN thin films did not change up to $10^8$ switching cycles.

• Journal of Electrical Engineering and Technology
• /
• 제2권4호
• /
• pp.525-531
• /
• 2007

Ni(75 wt.%)-Cr(20 wt.%)-Al(3 wt.%)-Mn(4 wt.%)-Si(1 wt.%) alloy thin films were prepared using the DC magnetron sputtering process by varying the sputtering conditions such as power, pressure, substrate temperature, and post-deposition annealing temperature in order to fabricate a precision thin film resistor. For all the thin film resistors, sheet resistance, temperature coefficient of resistance (TCR), and crystallinity were analyzed and the effects of sputtering conditions on their properties were also investigated. The oxygen content and TCR of Ni-Cr-Al-Mn-Si resistors were decreased by increasing the sputtering pressure. Their sheet resistance, TCR, and crystallinity were enhanced by elevating the substrate temperature. In addition, the annealing of the resistor thin films in air at a temperature higher than $300^{\circ}C$ lead to a remarkable rise in their sheet resistance and TCR. This may be attributed to the improved formation of NiO layer on the surface of the resistor thin film at an elevated temperature.

• 센서학회지
• /
• 제14권5호
• /
• pp.362-367
• /
• 2005

ZnO films were deposited on MgO substrates (ZnO/MgO) by ultrasonic spray pyrolysis. Substrate temperature varied from $250^{\circ}C$ to $350^{\circ}C$. The crystallographic properties and surface morphologies of the ZnO/MgO films were studied by X-ray diffraction and scanning electron microscopy. The properties of photoluminescence (PL) for the films were investigated by dependence of PL spectra on the substrate temperature and the annealing temperature. The ZnO/MgO films prepared at $350^{\circ}C$ showed the strongest Ultraviolet light emission peak at 18 K and 300 K among the films in this study. The annealing process increases the visible light emission, which is due to the increased oxygen vacancies.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 하계학술대회 논문집
• /
• pp.547-549
• /
• 2001

The dielectric constants and dielectric losses of ZrTiO$_4$thin films deposited by DC magnetron reactive sputtering were investigated. The paraelectric properties were measured in the 100kHz range. As the deposition temperature increased (up to 67$0^{\circ}C$), the dielectric losses (tan$\delta$) decreased (down to 0.017$\pm$0.007), while the dielectric constants ($\varepsilon$) were in the range of 35$\pm$7. Post annealing at 80$0^{\circ}C$ in oxygen for 2h reduced tan$\delta$ down to 0.005$\pm$0.001, higher than those of well-sintered bulk ZrTiO$_4$.

• 한국재료학회지
• /
• 제9권4호
• /
• pp.368-372
• /
• 1999

The suggested electrode structure of MOCVD-Pt/sputtered-Ru/polysilicon has an excellent adhesion with increasing annealing temperatures and shows a stable electrode structure up to $600^{\circ}C$. However, the ruthenium used for barrier layer increased the roughness of platinum bottom electrodes because ruthenium diffused through the Pt bottom electrode and reacted with oxygen during the annealing above $700^{\circ}C$. The surface roughness increased the resistivity of Pt bottom electrodes. The resistivity of samples annealed at $600^{\circ}C$ was about $13\mu$Ω.cm. The electrode structure was possible to apply for ferroelectric thin film integration of semiconductor memory devices.