Fabrication possibility of low-shrinkage alumina without oxidation and wetting agent was presented on the basis of observation about oxidation behavior, microstructure and physical characteristics of such reaction agents free Al2O3-Al system. The composition less than Al 10w/o where Al can act as a sintering agent for Al2O3 was excluded. Under the condition of present experiments oxidation of Al2O3-Al system was dependent not on holding time but mainly on oxidation temperature. In thes case of Al powder not comminuted effectively during powder mixing of Al2O3-Al, columnar structure which would act as a hindrance to the densification during sintering developed more during oxidation with higher Al contents, and which made the fabrication of low-shrinkage Al2O3 ceramics impossible. If Al powder was comminuted effectively due to co-mixed Al2O3 characteristics, densification was improved because of no columnar structure and made the fabrication of sintered body with -2.7% dimensional change and 81% relative density possible. As a result, it is possible to fabricate dense low-shrinkage Al2O3 ceramics without oxidation and wetting agent under conditions such as smaller particle size of Al, Al contents below 50v/o, higher green density of Al2O3-Al compact and the use of Al2O3 powder used for high-density ceramics.

• Corrosion Science and Technology
• /
• 제2권1호
• /
• pp.53-57
• /
• 2003

The MarM247 based superalloy (8wt.%Cr- 9wt.%Co- 3wt.%Ta- 1.5wt.%Hf- 5.6%wt.Al- 9.5wt.%W- Bal. Ni) specimens were diffusion aluminized by for types of pack cementation methods, and their coating structure and their high temperature oxidation resistance were investigated. The coated specimens treated at 973K in high aluminum concentration pack had a coating layer containing large hafunium rich precipitates, which were originally included in substrate alloy. After the high temperature oxidation test in air containing 30 vol.% $H_2O$ at 1273K ~ 323K, the deep localized corrosion which reached to the substrate were observed along with these hafnium rich precipitates. On the other hand, the coated specimens treated at 1323K using low aluminum concentration pack showed the coating layer without the large hafunium rich precipitates, and after the high temperature oxidation test at 1273K for 1800 ksec, it did not show the deep localized corrosion. The nickel electroplating before the aluminizing forms thick hafnium free area, and its high temperature oxidation resistance were comparable to platinum modified aluminizing coatings at 1273K.

• 한국공작기계학회:학술대회논문집
• /
• 한국공작기계학회 1999년도 추계학술대회 논문집 - 한국공작기계학회
• /
• pp.179-184
• /
• 1999

When the steel containing Si is oxidated in hi temperature, Re2O3, Red scale is made on the metal side as the spike phase, and this scale invasion into matrix. Therefore, it affects the feature, after rolling. It is reported that the role of Si is FeO/Fe2SiO4 eutectic compound, but Si can not affect pure iron independently. There must be Ni, then the spike phase can exist. Prominence and depression made by Ni that is necessity at the process to work iron. Therefore, in this study after the change of the amount of Ni in pure iron and steel and oxidation, the structure of the oxide and the surface, and the distribution of the elements were considered. In conclusion, at 100$0^{\circ}C$, 110$0^{\circ}C$, 120$0^{\circ}C$ the curves of oxidation weight are all S curves. Especially, in the beginning of oxidation as the amount of Ni increase, the amount of oxidation also increase. Practical steel has less oxidation than pure steel added Ni. There is much FeO in Fe-Ni alloy, compare to practical steel which has much Fe3O4. Especially, we could know considerable Ni was concentrated on the metal side in Fe-Ni alloy, practical steel. and the surface of the scale.

• 한국재료학회지
• /
• 제11권4호
• /
• pp.324-328
• /
• 2001

아크이온 플레이팅 장치를 이용하여 STD61강 기판 위에 이온질화 전처리를 행하거나 하지 않은 후, CrN 박막을 증착하고, 대기중 $700~900^{\circ}C$의 온도에서 40시간동안 이들에 대한 산화거동을 연구하였다. 산화거동은 열중량분석기, X선회절기, EDS, SEM을 이용하여 조사하였다. 증착된 CrN박막은 CrN과 $Cr_2$N의 두 상으로 구성되어 있었다. CrN박막은 보호적 $Cr_2$O$_3$층을 형성하여 기판을 산화로부터 보호하였다. 이온질화처리는 CrN박막의 내산화성에 영향을 주지 않았다.

• 한국표면공학회지
• /
• 제51권2호
• /
• pp.104-109
• /
• 2018

Fe-2 wt.%Ni alloys were fabricated by metal powder injection molding, and their oxidation behavior at $600-700^{\circ}C$ for 30 h in air was studied in order to find the effect of the small addition of Ni in the iron matrix on the high-temperature oxidation. Oxide scales that formed after oxidation consisted primarily of $Fe_2O_3$, where microscopic voids were scattered. Nickel was segregated initially at the scale/matrix interface, and later at the lower part of the $Fe_2O_3$ scale. At $600^{\circ}C$, Fe-2wt.%Ni alloys oxidized parabolically initially, and linearly after 15 h. At $650-700^{\circ}C$, they oxidized linearly from the initial period. Although Fe-2wt.%Ni alloys oxidized slower than pure iron, their oxidation rates were relatively fast.

• 한국분말재료학회지
• /
• 제14권5호
• /
• pp.303-308
• /
• 2007

The oxidation of $Fe_{73}Si_{16}B_7Nb_3Cu_1$ nanocrystalline powder has been conducted to investigate its influence on the electromagnetic wave absorption characteristics of the soft magnetic material. Oxidation occurred primarily on the surface of nanocrystals. Oxidation reduced the real part of complex permeability due to the reduction of the relative volume of the powder, which otherwise contributes to the permeability. Oxidation reduced the absorption efficiency of the sheet at frequencies over 1GHz, indicating that the relative contribution of skin depth increments to the absorption was not significant. The pulverization and milling process lowered the optimum crystallization temperature of the material by $40{\sim}50^{\circ}C$ because of the internal energy accumulated during the fragmentation and powder thinning processes.