• 한국재료학회지
• /
• 제27권2호
• /
• pp.100-106
• /
• 2017

Nanosized and aggregated $Y_2O_3:Eu$ Red phosphors were prepared by template method from metal salt impregnated into crystalline cellulose. The particle size and photoluminescent property of $Y_2O_3:Eu$ red phosphors were controlled by variation of the calcination temperature and time. Dispersed nanosol was also obtained from the aggregated $Y_2O_3:Eu$ Red phosphor under bead mill wet process. The dispersion property of the $Y_2O_3:Eu$ nanosol was optimized by controlling the bead size, bead content ratio and milling time. The median particle size ($D_{50}$) of $Y_2O_3:Eu$ nanosol was found to be around 100 nm, and to be below 90 nm after centrifuging. In spite of the low photoluminescent properties of $Y_2O_3:Eu$ nanosol, it was observed that the photoluminescent property recovered after re-calcination. The dispersion and photoluminescent properties of $Y_2O_3:Eu$ nanosol were investigated using a particle size analyzer, FE-SEM, and a fluorescence spectrometer.

• Journal of Electrochemical Science and Technology
• /
• 제8권3호
• /
• pp.215-221
• /
• 2017

The electroless plating process largely consists of substrate cleaning, seed formation (activator formation), and electroless plating. The most widely used activator in the seed formation step is Pd, and Sn ions are used to facilitate the formation of this Pd seed layer. This is problematic because the Sn ions interfere with the reduction of Cu ions during electroless plating; thus, the Sn ions must be removed by a hydrochloric acid cleaning process. This method is also expensive due to the use of Pd. In this study, Cu electroless plating was performed by forming a seed layer using a silver nanosol instead of Pd and Sn. The effects of the Ag nanosol concentration in the pretreatment solution and the pretreatment time on the thickness and surface morphology of the Cu layer were investigated. The degrees of adhesion to the substrate were similar for the electroless-plated Cu layers formed by conventional Pd activation and those formed by the Ag nanosol.

• 한국재료학회지
• /
• 제27권10호
• /
• pp.534-543
• /
• 2017

$Gd_2O_3:Eu^{3+}$ red phosphors were prepared by template method from crystalline cellulose impregnated by metal salt. The crystallite size and photoluminescence(PL) property of $Gd_2O_3:Eu^{3+}$ red phosphors were controlled by varying the calcination temperature and $Eu^{3+}$ mol ratio. The nano dispersion of $Gd_2O_3:Eu^{3+}$ was also conducted with a bead mill wet process. Dependent on the time of bead milling, $Gd_2O_3:Eu^{3+}$ nanosol of around 100 nm (median particle size : $D_{50}$) was produced. As the bead milling process proceeded, the luminescent efficiency decreased due to the low crystallinity of the $Gd_2O_3:Eu^{3+}$ nanoparticles. In spite of the low PL property of $Gd_2O_3:Eu^{3+}$ nanosol, it was observed that the photoluminescent property was recovered after re-calcination. In addition, in the dispersed nanosol treated at $85^{\circ}C$, a self assembly phenomenon between particles appeared, and the particles changed from spherical to rod-shaped. These results indicate that particle growth occurs due to mutual assembly of $Gd(OH)_3$ particles, which is the hydration of $Gd_2O_3$ particles, in aqueous solvent at $85^{\circ}C$.

• 한국세라믹학회:학술대회논문집
• /
• 한국세라믹학회 2003년도 추계총회 및 연구발표회 초록집
• /
• pp.85.2-85
• /
• 2003

• 한국재료학회지
• /
• 제26권12호
• /
• pp.733-740
• /
• 2016

$Al_2O_3$ nanosol dispersed under ethanol or N-Methyl-2-pyrrolidone(NMP) was studied and optimized with various dispersion factors and by utilizing the silane modification method. The two kinds of $Al_2O_3$ powders used were prepared by thermal decomposition method from aluminum ammonium sulfate$(AlNH_4(SO_4)_2)$ while controlling the calcination temperature. $Al_2O_3$ sol was prepared under ethanol solvent by using a batch-type bead mill. The dispersion properties of the $Al_2O_3$ sol have a close relationship to the dispersion factors such as the pH, the amount of acid additive(nitric acid, acetic acid), the milling time, and the size and combination of zirconia beads. Especially, $Al_2O_3$ sol added 4 wt% acetic acid was found to maintain the dispersion stability while its solid concentration increased to 15 wt%, this stability maintenance was the result of the electrostatic and steric repulsion of acetic acid molecules adsorbed on the surface of the $Al_2O_3$ particles. In order to observe the dispersion property of $Al_2O_3$ sol under NMP solvent, $Al_2O_3$ sol dispersed under ethanol solvent was modified and solvent-exchanged with N-Phenyl-(3-aminopropyl)trimethoxy silane(APTMS) through a binary solvent system. Characterization of the $Al_2O_3$ powder and the nanosol was observed by XRD, SEM, ICP, FT-IR, TGA, Particles size analysis, etc.

• 한국염색가공학회지
• /
• 제25권2호
• /
• pp.126-133
• /
• 2013

Although para-aramid fibers poss higher mechanical properties, they show very low resistance to sunlight exposure. This paper studied on the effect of nano-sol coated $TiO_2$ to improve the photo-stability of p-aramid fibers. Titanium dioxides were prepared by sol-gel method from titanium iso-propoxide at different R ratio ($H_2O$/titanium iso-propoxide). All samples were characterized by XRD, TEM and UV-vis spectrometer. The mechanical properties of p-aramid fabrics by $TiO_2$ nano-sol coating before and after sunlight irradiation were measured with tensile tester. XRD pattern of titanium dioxide particles was observed by mixing phase together with rutile and anatase type. The results showed, after sunlight irradiation, the decreased mechanical properties of the fiber. Furthermore, the sunlight irradiation obviously deteriorated the surface and defected areas of the fiber severely by photo-induced chain scission and end group oxidation in air.

• Korean Chemical Engineering Research
• /
• 제61권3호
• /
• pp.439-445
• /
• 2023

본 연구에서는 질산은을 PVA로 환원시켜 은 나노입자를 합성하였으며, 얻어진 은 나노입자에 Carboxymethyl cellulose (CMC)를 첨가시켜 제조된 용액을 PET 기재 위에 코팅함에 의해 항균 특성과 김서림 방지 기능을 갖는 코팅 도막을 제조하였다. 코팅 도막을 80 ℃의 수증기와 접촉 시 코팅되지 않은 PET 기재는 김서림 발생으로 인한 빛의 산란이 발생해 흐려진 결과를 보인 반면에 CMC가 첨가된 은 나노졸로 코팅된 도막은 수증기와의 접촉에도 불구하고 투명한 상태를 유지하여 김서림 방지 기능이 우수하였다. 또한 코팅 도막의 항균성을 그램 양성균인 포도상구균과 그람 음성균인 대장균에 대해 필름 밀착법으로 측정하였다. 코팅되지 않은 PET 기재에서는 많은 포도상구균과 대장균의 집락이 관찰된 반면에 은 나노졸로 코팅된 도막은 포도상구균과 대장균의 성장이 크게 억제되어 항균 효과가 우수하였다.

• 한국세라믹학회지
• /
• 제46권1호
• /
• pp.41-46
• /
• 2009

The rheological properties of highly concentrated Ag nano sol depending on particle size were studied. The Ag nano sol was prepared by reducing the Ag ion in aqueous solution. The size of Ag nano particle was controlled by two steps of nucleation and growth, and the thickness of adsorption layer was varied by molecular weight of polyelectrolytes. The polyelectrolytes acted as not only ionic complex agent in ionic state and but also dispersant after formation of Ag nano sol. The effective volume was controlled by combination of varying the molecular weight of polyelectrolytes and the size Ag nano sol. The particle size and the viscosity of nano sol were characterized by particle size analyzer, HR-TEM and cone & plate viscometer. It was found that the 10 nm and 40 nm-sized Ag nano sols were prepared by controlling the nucleation and growth steps, respectively. Finally, we could prepare highly concentrated Ag nano sol over 50 wt%.

• 공업화학
• /
• 제30권6호
• /
• pp.694-697
• /
• 2019

최근에 이산화티탄 분말을 나노입자로 제조하거나 결정성을 향상하기 위해 1차원 구조인 nanowire, nanotube, 3차원 구조인 mesoporous 구형으로 생산하여 차단율과 반사율을 통한 광 전극 소재로의 활용과 피부 광 노화 방지에 더욱 효율적으로 적용할 수 있는 연구가 진행되고 있다. 본 연구에서는 n-alcohol을 용매로 사용하여 높은 결정성을 갖는 이산화티탄 나노 졸을 합성하였다. 합성된 이산화티탄 나노 졸은 FE-SEM과 XRD을 통해 결정성을 확인하였고, 자외선 차단율을 확인하기 위해서 UV-Vis로 투과율을 확인했다. 또한. 용매에 따른 결정성을 확인하기 위하여 부탄올, 프로판올, 에탄올을 이용하여 각각을 제조하였고, 용매에 따른 차이를 비교하였다. 입자크기는 200~250 nm로 합성되었으며 광학적 투과율은 UVB, UVA 범위에서 높은 차단율을 보이고, 550 nm 파장에서 높은 투과율을 보여 태양전지의 광전 변환 효율 향상과 소량 사용으로도 제품의 자외선 차단 효율을 높일 수 있을 것으로 기대된다.

• 한국분말재료학회지
• /
• 제24권6호
• /
• pp.457-463
• /
• 2017

Nanosized $Gd_2O_3:Eu^{3+}$ red phosphor is prepared using a template method from metal salt impregnated into a crystalline cellulose and is dispersed using a bead mill wet process. The driving force of the surface coating between $Gd_2O_3:Eu^{3+}$ and mica is induced by the Coulomb force. The red phosphor nanosol is effectively coated on mica flakes by the electrostatic interaction between positively charged $Gd_2O_3:Eu^{3+}$ and negatively charged mica above pH 6. To prepare $Gd_2O_3:Eu^{3+}$-coated mica ($Gd_2O_3:Eu/mica$), the coating conditions are optimized, including the stirring temperature, pH, calcination temperature, and coating amount (wt%) of $Gd_2O_3:Eu^{3+}$. In spite of the low luminescence of the $Gd_2O_3:Eu/mica$, the luminescent property is recovered after calcination above $600^{\circ}C$ and is enhanced by increasing the $Gd_2O_3:Eu^{3+}$ coating amount. The $Gd_2O_3:Eu/mica$ is characterized using X-ray diffraction, field emission scanning electron microscopy, zeta potential measurements, and fluorescence spectrometer analysis.