• Korean Journal of Materials Research
• /
• v.13 no.1
• /
• pp.18-23
• /
• 2003

Properties of Ag thick films fabricated by using low temperature curable silver pastes were investigated. Ag pastes were consisted of polymer resins and silver powders. Ag pastes were used for conductive or fixing materials between board and various electrical and electronic devices. Low temperature curable Ag pastes have some advantages over high temperature curable types. In cases of chip mounting, soldering properties were required for screen printed Ag thick films. In this study, four types of Ag pastes were fabricated with different compositions. Screen printed Ag thick films on alumina substrates were fabricated at various curing temperatures and times. Thickness, resistivity, adhesive strength and solderability of fabricated Ag thick films were characterized. Finally, Ag thick films produced using Ag pastes, sample A and B, cured at $150^{\circ}C$ for longer than 6 h and $180^{\circ}C$ for longer than 2 h, and $150^{\circ}C$ for longer than 1 h and $180^{\circ}C$ for 1 h, respectively, showed low resistivities of $10^{-4}$ $∼10^{-5}$ Ωcm and good adhesive strength of 1∼5 Mpa. Soldering properties of those Ag thick films with curing temperatures at solder of 62Sn/36Pb/3Ag were also investigated.

• Korean Journal of Materials Research
• /
• v.29 no.2
• /
• pp.73-78
• /
• 2019

Lead free $(Ba_{0.7}Ca_{0.3})TiO_3$ thick films with nano-sized grains are prepared using an aerosol deposition (AD) method at room temperature. The crystallinity of the AD thick films is enhanced by a post annealing process. Contrary to the sharp phase transition of bulk ceramics that has been reported, AD films show broad phase transition behaviors due to the nano-sized grains. The polarization-electric hysteresis loop of annealed AD film shows ferroelectric behaviors. With an increase in annealing temperature, the saturation polarization increases because of an increase in crystallinity. However, the remnant polarization and cohesive field are not affected by the annealing temperature. BCT AD thick films annealed at $700^{\circ}C/2h$ have an energy density of $1.84J/cm^3$ and a charge-discharge efficiency of 69.9 %, which is much higher than those of bulk ceramic with the same composition. The higher energy storage properties are likely due to the increase in the breakdown field from a large number of grain boundaries of nano-sized grains.

• Korean Journal of Materials Research
• /
• v.17 no.6
• /
• pp.323-330
• /
• 2007

We fabricated thermaly evaporated 10 nmNi/(poly)Si films to investigate the energy saving property of silicides formed by rapid thermal annealing (RTA) at the temperature of $300{\sim}1200^{\circ}C$ for 40 seconds. Moreover, we fabricated $10{\sim}50$ nm-thick ITO/Si films with a rf-sputter as reference films. A four-point tester was used to investigate the sheet resistance. A transmission electron microscope (TEM) and an X-ray diffractometer were used for the determination of cross sectional microstructure and phase changes. A UV-VISNIR and FT-IR (Fourier transform infrared rays spectroscopy) were employed for near-IR and middle-IR absorbance. Through TEM analysis, we confirmed $20{\sim}70nm-thick$ silicide layers formed on the single and polycrystalline silicon substrates. Nickel silicides and ITO films on the single silicon substrates showed almost similar absorbance in near-IR region, while nickel silicides on polycrystalline silicon substrate showed superior absorbance above 850 nm near-IR region to ITO films. Nickel silicide on polycrystalline substrate also showed better absorbance in middle IR region than ITO. Our result implies that nano-thick nickel silicides may have exellent absorbing capacity in near-IR and middle-IR region.

• Journal of the Korean institute of surface engineering
• /
• v.56 no.5
• /
• pp.335-340
• /
• 2023

Quinary component of 3㎛ thick Ti-Al-Si-Cu-N films were deposited onto WC-Co and Si wafer substrates by using an arc ion plating(AIP) system. In this study, the influence of copper(Cu) contents on the mechanical properties and microstructure of the films were investigated. The hardness of the films with 3.1 at.% Cu addition exhibited the hardness value of above 42 GPa due to the microstructural change as well as the solid-solution hardening. The instrumental analyses revealed that the deposited film with Cu content of 3.1 at.% was a nano-composites with nano-sized crystallites (5-7 nm in dia.) and a thin layer of amorphous Si₃N₄ phase.

• Journal of the Korean Ceramic Society
• /
• v.43 no.5 s.288
• /
• pp.265-269
• /
• 2006

We have deposited NiO films by RF sputtering on $Al_2O_3/SiO_2/Si$ and 100 nm-thick Gd doped $CeO_2$ covered $Al_2O_3/SiO_2/Si$ substrates at various $Ar/O_2$ ratios. The deposited films were reduced to form porous Ni thin fllms in 4% $H_2\;at\;400^{\circ}C$. For the films deposited in pure Ar, the reduction was retarded due to the thickness and the orientation of the NiO films. On the other hand, the films deposited in oxygen mixed ambient were reduced and formed porous Ni films after 20 min of reduction. We also investigated the possibility of using the films for the single chamber operation by studying the electrical property of the films in the fuel/air mixed environment. It is shown that the resistance of the Ni film increases quickly in the mixed gas environment and thus further improvements of Ni-base anodes are required for using them in the single chamber operation.

• Proceedings of the KSME Conference
• /
• 2008.11a
• /
• pp.30-34
• /
• 2008

The transfer assembly (or transfer printing) technique is a promising method for fabricating multi-scale structures on various substrates including semiconductors and polymers, and has been applied to fabrication of flexible devices with superior performance to conventional organic flexible devices. The mechanical behaviors of the structures fabricated by the transfer assembly is a very important information for design and reliability evaluation purpose, but the measurement of the behaviors is difficult since their critical-dimensions are very tiny. In this study, Au films with nano-scale thickness were fabricated on a silicon substrate and their mechanical properties were measured using micro-tensile test. The Au films on the silicon substrate were then transferred to a PDMS substrate using the transfer assembly technique. Self-assembled monolayer (SAM) with a thiol group was used to enhance the transfer of Au films, and the mechanical behaviors were characterized using wrinkle-based test. The test results from micro-tensile and wrinkle-based test are compared to each other, and their implication to the transfer assembly technique is discussed.

• Korean Journal of Materials Research
• /
• v.18 no.10
• /
• pp.515-520
• /
• 2008

We fabricated 10 nm-$TiO_2$ thin films for DSSC (dye sensitized solar cell) electrode application using ALD (atomic layer deposition) method at the low temperatures of $150^{\circ}\;and\;250^{\circ}$. We characterized the crosssectional microstructure, phase, chemical binding energy, and absorption of the $TiO_2$ using TEM, HRXRD, XPS, and UV-VIS-NIR, respectively. TEM analysis showed a 10 nm-thick flat and uniform $TiO_2$ thin film regardless of the deposition temperatures. Through XPS analysis, it was found that the stoichiometric $TiO_2$ phase was formed and confirmed by measuring main characteristic peaks of Ti $2p^1$, Ti $2p^3$, and O 1s indicating the binding energy status. Through UV-VIS-NIR analysis, ALD-$TiO_2$ thin films were found to have a band gap of 3.4 eV resulting in the absorption edges at 360 nm, while the conventional $TiO_2$ films had a band gap of 3.0 eV (rutile)${\sim}$3.2 eV (anatase) with the absorption edges at 380 nm and 410 nm. Our results implied that the newly proposed nano-thick $TiO_2$ film using an ALD process at $150^{\circ}$ had almost the same properties as thsose of film at $250^{\circ}$. Therefore, we confirmed that the ALD-processed $TiO_2$ thin film with nano-thickness formed at low temperatures might be suitable for the electrode process of flexible devices.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.22 no.4
• /
• pp.297-302
• /
• 2009

We have successfully fabricated the alumina thick films using inkjet printing processes without a high temperature sintering process. Alumina suspension as dielectric ink was formulated by combining nano-sized alumina powders with an anionic polymer dispersant in formamide/water as co-solvent. The thickness of the printed alumina thick film was measured at around 5 um by field emission scanning electron microscope. The calculated packing density of 68.5 % from the printed alumina thick film was much higher than the same films fabricated by conventional casting or dip coating processes. Q factor of the dielectrics thick film infiltrated with cyanate ester resin was evaluated by impedance analyzer.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.24 no.2
• /
• pp.126-130
• /
• 2011

In this study, off-axis magnetron sputtering was used for the crystallized ITO thin films at a low temperature of about $120^{\circ}C$ instead of the conventional RF sputtering because the off-axis sputtering can avoid the damage for the plasma as well as fabrication of thin films with a high quality. The ITO thin films grown on PET substrate at $120^{\circ}C$ were crystallized with a (222) preferred orientation. 58-nm thick ITO films showed a resistivity of about $2{\times}10-4{\Omega}{\cdot}cm$ and a transmittance of about 75% at a wavelength of 550 nm. The transmittance of the ITO thin films by an insertion of SiO2 thin films on ITO films was improved.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.338-338
• /
• 2007

Photo-conductive properties of CdS films deposited on glass substrates by a reactive sputtering in Ar atmosphere were characterized as a function of working pressure and the film thickness. The XRD measurements of CdS films revealed obvious (002) preferred orientation. In 300nm-thick of films, difference between dark and photo-resistance increases with increasing working pressure within the films. The films at 5 mTorr of working pressure show a dark resistance of approximately $1\;{\times}\;10^6\;{\Omega}/{\square}$ and a photo-resistance of $3\;{\times}\;10^4\;{\Omega}/{\square}$. The decrease dark- and photo-resistance of films as thickness decrease were $1.4\;{\times}\;10^6$ and $3\;{\times}\;10^4\;{\Omega}/{\square}$, respectively. CdS films deposited on glass substrates are considered tobe suitable for photo-conductivity materials in stealth radome applications.