• Polymer(Korea)
• /
• v.36 no.3
• /
• pp.275-280
• /
• 2012

Poly(amic acid)s were successfully synthesized from 1,4-bis(4-aminophenoxy)benzene (1,4-APB) or 2,2-bis[4-(4-aminophenoxy)phenyl]hexafluoropropane (HFBAPP) with pyromellitic dianhydride (PMDA), 3,3'-4,4'-benzopenonetetracarboxylic dianhydride (BPDA) and $p$-phenylenediamine ($p$-PDA) and then they were effectively converted into polyimide films by thermal imidization. The chemical structure and thermo-mechanical properties of polyimide films were examined using Fourier transform infrared spectroscopy (FTIR), thermo-gravimetric analyzer (TGA), thermo-mechanical analyzer, dynamic mechanical analyzer (DMA) and universal tensile machine (UTM). The moisture absorption, thermal and mechanical properties of polyimide films decreased with increasing the amount of 1,4-APB and HFBAPP. The polyimide films using HFBAPP showed lower properties than that of 1,4-APB at the same ratio, but it displayed better thermal properties and lower moisture absorption at the similar coefficient of thermal expansion (CTE) with a copper. On the basis of our finding, it is concluded that 4-component polyimide films could be utilized for base films for flexible copper clad laminates (FCCL) of flexible printed circuit boards.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2018.06a
• /
• pp.124-124
• /
• 2018

Polydopamine은 수중 접착력, 친환경 접착제, nanoparticle absorption 등 다양한 특성으로 많이 연구되고 있는 소재이다. 본 연구에서는 dopamine을 이용하여 수중 금속을 흡착시키는 thin film을 제작하였다. 종래의 Polydopamine coating 방법으로 wet coating 이 사용되고 있다. 하지만 wet 방식의 경우 시간이 오래 걸릴 뿐만 아니라 in-line, roll to roll 방식을 적용하는 것이 어렵기 때문에 생산적이지 않다. 이에 본 연구에서는 Atmospheric Pressure Plasma(APP)를 이용 하여 Polydopamine-like film을 coating 하였다. APP의 경우 vacuum system, solution tank가 필요 없고 in-line, roll to roll 방식을 적용 할 수 있기 때문에 더 경제적이고 생산적인 공정이다. 또한 기존의 Plasma polymerization 방법은 Plasma energy가 높기 때문에 source의 분자구조가 바뀌거나 atom 단위로 분해된다. source의 분자구조가 바뀌는 "Atomic polymerization", Neiswender-Rosskamp Mechanism이 적용되면 wet 방식 coating한 film과는 다른 특성을 갖게 된다. 하지만 APP polymerization은 Plasma energy가 vacuum plasma 보다 매우 낮기 때문에 stile polymerization mechanism을 구현 하는데 적합 하다. stile polymerization mechanism은 Plasma 내부에서 polymer source를 분해 성장 시켜서 Polymer film 얻는 것이 아닌 source의 분자구조가 깨지지 않으면서 polymer growing 시키는 방법이다. dopamine source의 분자구조를 최대한 유지하려고 하는 이유는 metal absorption과 같은 특성이 dopamine chemical structure에 영향을 받기 때문이다. 많은 논문들에서 dopamine의 catechol group이 metal absorption, adhesion force에 영향을 주는 주요 인자라고 주장하고 있기 때문이다. 그래서 본 논문에서는 Dopamine source의 형태를 보존하면서 Polymerization 하는 방법으로 APP process를 사용 하여 낮은 전압에서 Polydopamine-like film을 제작 하였다. APP system 의 Plasma 방전부 에 Dopamine source를 유입하기 위하여 본 논문에서는 Piezo Spray 방식을 사용 하였다. Dopamine을 evaporator 하는 것이 어렵고 chemical composition이 유사한 monomer를 사용해서 Plasma Polymerization으로 Dopamine 분자 구조를 재현하는 것도 어렵다. 그래서 본 연구에서는 Dopamine을 water에 immerse 하고 Dopamine solution을 mist 상태로 만들어서 Plasma discharge area에 유입하였다. 이러한 방법으로 만들어진 film은 Polydopamine film은 아니지만 Polydopamine film과 유사한 Chemical composition, chemical structure, metal absorption을 갖는 것을 FT-IR, SEM, XPS을 이용 하여 확인 하였다. Dopamine source의 보존에 대하여 명확하게 확인하기 위하여 FT-IR을 측정 하였다. 전압에 따른 Benzene ring, hydroxyl group의 비율을 확인 하였다. 낮은 전압으로 coating 된 Polydopamine-like film 일수록 hydroxyl group peak($3400{\sim}3000cm^{-1}$)과 비교하여 Benzene ring peak($1600{\sim}1580cm^{-1}$ and $1510{\sim}500cm^{-1}$)이 흡수를 더 많이 하는 것을 확인 할 수 있다. 이것은 Benzene ring이 파괴되지 않고 보존되는 것을 보여준다. Dopamine에서 Benzene ring은 absorption main factor인 catechol에 있는 chemical structure이다. 즉 Benzene ring peak이 높을수록 Catechol이 잘 보존 되었다는 의미 이다. Catechol의 보존은 absorption main factor가 보존 된다는 의미 이다. 이러한 Polydopamine-like film으로 As, Cr, Mg, Cu 200ppm solution에 대한 filtration 능력을 확인 하였다. As, Cr, Cu, Mg 의 제거율이 각각 약25%, 35%, 45%, 65%인 것을 확인 하였다. 이 수치는 시중에 판매되는 제품들과 비교했을 때 300%~500% 향상된 수치 이다.

• Clean Technology
• /
• v.15 no.3
• /
• pp.172-179
• /
• 2009

The thermoplastic polyurethane waste (TPU-S) with good tensile properties, hardness, NBS abrasion resistance, specific gravity and low wet coefficient of kinetic friction was melt-blended with ethylene propylene diene monomer rubber (EPDM) with high wet slip resistance and low mechanical properties to form EPDM/TPU-S blend films, and their composition-property relationship was investigated to find the optimum composition for shoe outsole material. The properties except the wet slip resistance increased with increasing TPU-S contents in the blend. All the properties except elongation at break, specific gravity and the wet coefficient of kinetic friction in the range of $0{\sim}65\;wt%$ of TPU-S did not attain the values predicted by the simple additive rule. The optimum weight ratio of EPDM/TPU-S for the application to the typical shoe outsole material was found to be 30/70.

• Journal of Korean Ophthalmic Optics Society
• /
• v.17 no.2
• /
• pp.135-141
• /
• 2012

Purpose: Polymerization of HEMA(2-hydroxyethyl methacrylate) which can be used in the soft contact lens has been performed by using electron beam(EB) irradiation, and examined the best condition for the polymerization. Comparing the physical properties of the contact lenses to the one fabricated by thermal polymerization method, we check the use possibility of the EB irradiation to the fabrication of the soft contact lens. Methods: We investigated the degree of polymerization of the HEMA according to the composition of the monomer, the additive ratio and the dose of electron beam (0~120 kGy). The degree of polymerization was measured depending on the EB dose to research the best synthetic condition under the EB irradiation. The physical properties of the contact lens such as water content(%), oxygen transmissibility(Dk/t) and optical transmittance were analysed by using the FT-IR results with comparing the two different polymerization method (thermal and electron beam polymerization) with same additive ratio. Results: When the dose of electron beam was above 100 kGy, the degree of polymerization of HEMA was above 99% with regardless using cross-linker and initiator. The water content of the lens fabricated by EB method showed 10% higher than the one by the thermal method which was 40%. The lens fabricated by EB method also showed higher oxygen transmissibility(Dk/t) as same with the water content, and showed twice higher value in the lens fabricated by pure HEMA. According to the FT-IR results, hydrophilic property of the lens fabricated by EB method was increased due to increasing the intermolecular hydrogen bonding. It showed above 90% optical transmittance in the visible range of wavelength on the contact lenses fabricated by the both of two different polymerization method. Conclusions: The polymerization of HEMA without cross-linker and initiator was successful above 100 kGy of EB irradiation. Moreover the lens fabricated from the polymer synthesized by pure HEMA with 100 kGy of EB showed the highest water content and oxygen transmissibility. Therefore EB irradiation is another possible method to synthesize the polymer which can be used for the soft contact lens.

• Journal of Adhesion and Interface
• /
• v.11 no.4
• /
• pp.155-161
• /
• 2010

A series of ethylene vinyl acetate (EVA) based hot melt adhesives containing different types and compositions of tackifier resins were prepared to investigate their rheological behavior and T-peel adhesion strength on polyurethane (PU) elastomeric sheets. C5 aliphatic hydrocarbon resin (C5 resin), C9 aromatic hydrocarbon resin (C9 resin), hydrogenated dicyclopentadiene resin ($H_2$-DCPD resin), and dicyclopentadiene and acrylic monomer copolymer resin (DCPD-acrylic resin) were used as the tackifiers for the hot melt adhesives. To determine the polarity of the tackifiers, their oxygen contents were analyzed, and the DCPDacrylic resin was found to contain an oxygen content higher than the other tackifiers. Only the DCPD-acrylic resin showed complete miscibility with EVA and the homogeneous phase of the hot melt adhesive blends at all compositions. The T-peel adhesion strength between the hot melt adhesives and polyurethane elastomeric sheets was mainly affected by the polarity of the tackifier resins in the hot melt adhesives, rather than by the storage moduli, G', of the hot melt adhesives themselves.

• Applied Chemistry for Engineering
• /
• v.8 no.4
• /
• pp.575-581
• /
• 1997

UDs were synthesized from two different polyols(PTMG, PBEAG), ionic chain extender(DMPA), EDA with $H_{12}-MDI$. PU/PMMA hybrids were prepared with free radical polymerization of MMA monomer in MMA-swelled PUD. PUD particle size and film properties were investigated ionic content and polyol type. Mechanical and thermal properties of PU/PMMA hybrid film were studied in terms of PU's ionic content and the venation of PU/PMMA compositions. As DMPA content increased from 2wt% to 10wt% in PUD, particle size of PUD decreased. PUD's particle size with ester type polyol was found to be smaller then ether type polyol used. Phase separation between hard segment(HS) and soft segment(SS) with ionic contents in PU was shown by the thermal, mechanical property measurement. Although the composition of MMA was changed from 0 to 40 wt% in PU/PMMA hybrid, the particle size of the hybrid did not increase. Using the ester type polyol, tensile strength of hybrid was found to increase by 2wt% - 6wt% DPMA content, but as higher content the strength of hybrid decreased. Moreover with the ether type polyol, tensile strength of hybrid was observed to increase by 2wt% - 4wt% DMPA content, while decreasing at higher content. PU and PMMA polymer molecule being mixed in molecular level was confirmed from the pattern of $T_g$ in DSC thermogram.

• Clean Technology
• /
• v.20 no.3
• /
• pp.226-231
• /
• 2014

This study presents a micromolding for the synthesis of Janus particles with reconfigurable shape by pH stimuli. First, we use acrylic acid (AA) as pH responsive monomer in the hydrophilic part and trimethylolpropane triacylate (TMPTA) in the hydrophobic part, respectively. The change of acidity in solvent induces the swelling of hydrophilic part in the Janus particles. The pH-responsive Janus particles show different swelling ratio of hydrophilic part in according to composition of acrylic acid in diverse range (0-70% v/v) and pH (3-11). As the concentration of acrylic acid in the hydrophilic part and environmental pH increase, the hydrophilic part in the Janus particles is proportionally swelled. Second, we fabricate novel type of Janus particles with two different hydrophilicities. As a proof of concept, we have applied acrylic acid (AA) and 2-(dimethylamino)ethyl methacrylate (DAEMA) into each part because the monomers provide reverse responsive activity. As expected, these Janus particles show different shape anisotropies with reconfigurable property in accordance with the polarity of each part at same acidity of environmental solvent. We envision that the stimuli responsive Janus particles have a wide application from fundamental science to diagnostic apparatus.

• Journal of the Society of Cosmetic Scientists of Korea
• /
• v.37 no.1
• /
• pp.1-21
• /
• 2011

This review describes several kinds of emulsification methods for nanoemulsions and the application of nanoemulsions. Nanoemulsion droplet sizes fall typically in the range of 20 ~200 nm and show narrow size distributions. Although most of the publications on either oil-in-water (O/W) or water-in-oil (W/O) nanoemulsions have reported their formation by dispersion or high-energy emulsification methods, an increased interest is observed in the study of nano-emulsion formation by condensation or low-energy emulsification methods based on the phase transitions that take place during the emulsification process. Phase behaviour studies have shown that the size of the droplets is governed by the surfactant phase structure (bicontinuous microemulsion or lamellar) at the inversion point induced by either temperature or composition. Studies on nanoemulsion formation by the phase inversion temperature (PIT) method have shown a relation between minimum droplet size and complete solubilization of the oil in a microemulsion bicontinuous phase independently of whether the initial phase equilibrium is single or multiphase. Due to their small droplet size nanoemulsions possess stability against sedimentation or creaming with Ostwald ripening forming the main mechanism of nanoemulsion breakdown. An application of nanoemulsions is the preparation of nanoparticles using a polymerizable monomer as the disperse phase where nanoemulsion droplets act as nanoreactors, cosmetics and controlled drug delivery. In this review, we mainly focus on the cosmetics.

• Restorative Dentistry and Endodontics
• /
• v.27 no.1
• /
• pp.77-86
• /
• 2002

Current composites are made with dimethacrylate monomers and silane-treated silica microfillers, either alone or with silane treated glass fillers The main reasons for clinical failure of dental composites are secondary caries, wear and fracture. Most of practitioner want to get a composite which is more tougher under occlusal stress, less polymerization contraction, and better handling properties in application clinically. The aim of this study was to investigate the influence of resin matrix with various flows on the physical proper-ties such as fracture toughness and degree of conversion of the experimental resins. It was hypothesized that flexible or tough resin composites can be designed by judicious choice of monomer composition Various flow resin matrices containing Bis-GMA, UDMA, and TEG-DMA were made by altering the pro-portion of the monomers. After the unfilled resins were light-cured for different light intensity, the fracture toughness(K$_{1c}$) was measured according to ASTM standard using the single edge notched geometry, and degree of conversion(DC) was measured by FTIR. And experimental composites were formulated with variations in the proportion of silanated quartz and strontium glass fillers as 60, 75, and 77wt%. Also, the physical properties of composites with various filer contents were evaluated as same manner. All resulting data were compared by ANOVA/Tukeys test at 0.05 level. The results were as follows; 1. The degree of conversion of high flow resin containing less Bis-GMA was higher than that of low flow unfilled resin 2. While the degree of conversion of unfilled resin was increased according to light intensity for polymerization, there was no significant increase with moderate and high light intensity. Also, the fracture toughness was not increased by high light intensity. 3. The fracture toughness was high in the low flow unfilled resin containing higher contents of Bis-GMA. 4. There was a significant increase for fracture toughness and a tendency for degree of conversion to be reduced when the content of fillers was increased. 5. In the experimental composites, the flow of resin matrix did not affected on the fracture toughness, even, which was decreased as increase of viscosity. These results showed that the physical properties of a dental composite could be attributed to the flow of resin matrix with relative content of monomers. Specific combination of resin monomers should be designed to fulfil the needs of specific indication for use.

• Macromolecular Research
• /
• v.11 no.4
• /
• pp.207-223
• /
• 2003

For last five years, we are developing the novel local drug delivery devices using biodegradable polymers, especially polylactide (PLA) and poly(D,L-lactide-co-glycolide) (PLGA) due to its relatively good biocompatibility, easily controlled biodegradability, good processability and only FDA approved synthetic degradable polymers. The relationship between various kinds of drug [water soluble small molecule drugs: gentamicin sulfate (GS), fentanyl citrate (FC), BCNU, azidothymidine (AZT), pamidronate (ADP), $1,25(OH)_2$ vitamin $D_3$, water insoluble small molecule drugs: fentanyl, ipriflavone (IP) and nifedipine, and water soluble large peptide molecule drug: nerve growth factor (NGF), and Japanese encephalitis virus (JEV)], different types of geometrical devices [microspheres (MSs), microcapsule, nanoparticle, wafers, pellet, beads, multiple-layered beads, implants, fiber, scaffolds, and films], and pharmacological activity are proposed and discussed for the application of pharmaceutics and tissue engineering. Also, local drug delivery devices proposed in this work are introduced in view of preparation method, drug release behavior, biocompatibility, pharmacological effect, and animal studies. In conclusion, we can control the drug release profiles varying with the preparation, formulation and geometrical parameters. Moreover, any types of drug were successfully applicable to achieve linear sustained release from short period ($1{\sim}3$ days) to long period (over 2 months). It is very important to design a suitable formulation for the wanting period of bioactive molecules loaded in biodegradable polymers for the local delivery of drug. The drug release is affected by many factors such as hydrophilicity of drug, electric charge of drug, drug loading amount, polymer molecular weight, the monomer composition, the size of implants, the applied fabrication techniques, and so on. It is well known that the commercialization of new drug needs a lot of cost of money (average: over 10 million US dollar per one drug) and time (average: above 9 years) whereas the development of DDS and high effective generic drug might be need relatively low investment with a short time period. Also, one core technology of DDS can be applicable to many drugs for the market needs. From these reasons, the DDS research on potent generic drugs might be suitable for less risk and high return.