• 도시과학
• /
• 제7권1호
• /
• pp.39-43
• /
• 2018

This study investigates microstructural characteristics of alkali-activated cements incorporating slag and fly ash. Samples were prepared with four fly ash:slag ratios, i.e., 100:0, 90:10, 70:30 and 50:50, and they were synthesized by using an alkali activator. Microstructural characteristics of the alkali-activated cements were determined by XRD, TGA, SEM, N2 gas adsorption/desorption methods, and compressive strength test. The results showed that properties of alkali-activated fly ash/slag were significantly affected by slag contents. Alkali-activated fly ash/slag with slag content of 30-50% showed higher compressive strength than ordinary Portland cement paste. An increase in slag content resulted in a denser microstructure, which composed of amorphous gel, therefore contributed to strength development of the material.

• 한국분말재료학회지
• /
• 제1권2호
• /
• pp.174-180
• /
• 1994

Electrical contact property of the W-20wt%Cu contact materials manufactured by liquid phase sintering of nanocomposite W-Cu powders was investigated and discussed in terms of microstructural development during performance test. Nanocomposite powders were prepared by hydrogen reduction of ball milled W-Cu oxide mixture. They underwent complete densification and microstructural homogenization during liquid phase sintering. As a consequence, the W-Cu contacts produced from nanocomposite powders showed superior contact property of lower arc erosion and stable contact resistance. This might be mostly due to the fact that the arc erosion by evaporation of Cu liquid droplets and surface cracking remarkably became weakened. It is concluded that the improvement of anti-arc erosion of the composite specimen is basically attributed to microstructural homogeneity.

• 한국재료학회지
• /
• 제32권2호
• /
• pp.72-79
• /
• 2022

A cold roll-bonding process using AA1050, AA5052 and AA6061 alloy sheets is performed without lubrication. The roll-bonded specimen is a multi-layer complex aluminum alloy sheet in which the AA1050, AA5052 and AA6061 sheets are alternately stacked. The microstructural evolution with the increase of annealing temperature for the roll-bonded aluminum sheet is investigated in detail. The roll-bonded aluminum sheet shows a typical deformation structure in which the grains are elongated in the rolling direction over all regions. However, microstructural evolution of the annealed specimen is different depending on the type of material, resulting in a heterogeneous microstructure in the thickness direction of the layered aluminum sheet. Complete recrystallization occurs at 250 ℃ in the AA5052 region, which is lower by 100K than that of the AA1050 region. Variation of the misorientation angle distribution and texture development with increase of annealing temperature also differ depending on the type of material. Differences of microstructural evolution between aluminum alloys with increase of annealing temperature can be mainly explained in terms of amounts of impurities and initial grain size.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.948-949
• /
• 2006

An infiltration technique using W-Cu composite powder has been developed to enhance microstructural uniformity of W-Cu pseudo-alloy. W-Cu composite powder, manufactured by reduction from $WO_3$ and CuO powder mixtures, were blended with W powder and then cold iso-statically pressed into a cylindrical bar under 150 MPa. The pressed samples were pre-sintered at $1300^{\circ}C$ for 1 hour under hydrogen to make a skeleton structure. This skeleton structure was more homogeneous than that formed by using W and Cu powder mixtures. The skeleton structures were infiltrated with Cu under hydrogen atmosphere. The infiltrated W-Cu pseudo-alloy showed homogeneous microstructure without Cu rich region

• 한국재료학회지
• /
• 제22권1호
• /
• pp.16-23
• /
• 2012

Research into the development of high strength (1 GPa) and superior formability, such as total elongation (10%), and stretch-flangeability (50%) in hot-rolled steel was conducted with a thermomechanically controlled hot-rolling process. To improve the overall mechanical properties simultaneously, low-carbon steel using precipitation hardening of Ti-Nb-V multimicroalloying elements was employed. And, ideal microstructural characteristics for the realization of balanced mechanical properties were determined using SEM, EBSD, and TEM analyses. The developed steel, 0.06C-2.0Mn-0.5Cr-0.2(Ti + Nb + V), consisted of ferrite as the matrix phase and second phase of granular bainite with fine carbides (20-50 nm) in both phases. The significant factor of the microstructural characteristics that affect stretch-flangeability was found to be the microstructural homogeneity. The microstructural homogeneity, manifest in such characteristics as low localization of plastic strain and internally stored energy, was identified by grain average misorientation method, analyzed by electron backscattered diffraction (EBSD) and hardness deviation between the phases. In summar, a hot-rolled steel having a composition 0.06C-2.0Mn-0.5Cr-0.2(Ti + Nb + V) demonstrated a tensile strength of 998 MPa, a total elongation of 19%, and a hole expansion ratio of 65%. The most important factors to satisfy the mechanical property were the presence of fine carbides and the microstructural homogeneity, which provided low hardness deviation between the phases.

• 열처리공학회지
• /
• 제31권3호
• /
• pp.91-96
• /
• 2018

Microstructural development of ferritic 11Cr-3.45W heat-resistance steel for ultra-supercritical power plant during creep and thermal aging was investigated using electron microscopy. The test samples were isothermally aged at $700^{\circ}C$ for up to 4000 hours and subjected to creep loading at $700^{\circ}C$ for predetermined periods of lifetime to prepare the damaged materials. In this structural material, a various secondary phases are the primary influence on mechanical properties of ferritic heat-resistance steel. The typical precipitates of $M_{23}C_6$, MX and $M_2X$ secondary phases had been analyzed through qualitative and quantitative manner. Coarsening of precipitates and increase of lath width were observed during creep and thermal aging. This phenomenon was remarkable for creep process compared with isothermal aging process.

• 한국분말재료학회지
• /
• 제5권2호
• /
• pp.133-138
• /
• 1998

The effect of $\beta$-$Si_3N_4$ seeding on microstructural development of silicon nitride based materials has been investigated. In particular, to observe more distinctly the abnormal grain growth in pressureless sintering, fine $\alpha$-$Si_3N_4$(mean particle size: 0.26 ${\mu}m$) powder classified by sedimentation method was used. It was possible to prepare silicon nitride with abnormally grown grains under low nitrogen pressure of 1 atm thanks to the heterogeneous nucleation on $Si_3N_4$ seed particles. The size and morphology of silicon nitride grains were strongly influenced by the presence of $\beta$-$Si_3N_4$ seed and overall chemical composition. For specimens with initially low $\beta$-content, the large grains grew without a significant impingement by other large grains. On the contrary, for specimens with initially high $\beta$-content, steric hindrance was effective. The resulting microstructure was less inhomogeneous and characterized by unimodal grain size distribution.

• 한국세라믹학회지
• /
• 제21권3호
• /
• pp.253-258
• /
• 1984

This paper deals with the reaction-bonded silicon nitride I terms of its microstructural development during nitrida-tion. Silicon powder compacts were reacted with nitrogen at 1185$^{\circ}C$ and 13$65^{\circ}C$ according to the nitriding schedule. Microstructures of nitrided specimens were examined by means of optical and scanning electron microscope to discuss the nitridation or microstructural development at initial and intermediat stage of nitridation. Reaction products were also analysed by X-ray diffraction method at each stage of nitridation. The results indicate that ho-mogeneous and uniform microstructure with find porosity can be obtained only under the reaction condition. such as slow and relatively constant reaction rate with time.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.722-723
• /
• 2006

A new method has been developed to fabricate microcomponents by a combination of photolithography and sintering of metallic powder mixtures, without the need for compression and the addition of Mg. This involves (1) the fabrication of a micromould, (2) mould filling of the powder/binder mixture, (3) debinding and (3) sintering. The starting powdered materials consisted of a mixture of aluminium powder(average size of 2.5 um) and alloying elemental powder of Cu and Sn(less than 70nm), at appropriate proportions to achieve nominal compositions of Al-6wt%Cu, Al-6wt%Cu-3wt%Sn. This paper presents detailed investigation of debinding behaviour and microstructural development.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.282-283
• /
• 2006

Densification behavior of nano-agglomerate powder during pressureless sintering of Fe-Ni nanopowder was investigated in terms of diffusion kinetics and microstructural development. To understand the role of agglomerate boundary for sintering process, densification kinetics of Fe-Ni nano-agglomerate powder with different agglomerate size was investigated. It was found that activation energy for densification was lower in the small-sized agglomerate powder. The increase in the volume fraction of inter-agglomerate boundary acting as high diffusion path might be responsible for the enhanced diffusion process.