• Journal of Korea Foundry Society
• /
• v.27 no.1
• /
• pp.24-30
• /
• 2007

The effects of C, Si and RE additions on the tendency of chill formation of ductile cast iron obtained from metal mold casting were investigated. In case of metal mold cast, the ductile cast iron with 2.5%Si had pearlitic matrix, and specimens with 2.9%Si had bull's eye type regardless of C contents. As-cast specimen with a large amount of fine graphites could be obtained by adding 0.2% RE. Normalizing process was necessary to remove carbide and form a large amount of spheroidal graphites for the as-cast specimens. Good mechanical properties could be obtained by heat-treatment of as-cast specimens with pearlitic matrix. Normalizing the specimens with RE caused the reduction in mechanical properties.

• Design & Manufacturing
• /
• v.15 no.1
• /
• pp.21-25
• /
• 2021

When the product is removed from the mold after molding during the sheet metal molding process, elastic recovery causes a springback phenomenon. Much research has been done to minimize this phenomenon. In this study, V-bending experiments were conducted using galvanized steel sheets, stainless steel, and aluminum sheet materials, using a total of nine types of thin sheet materials of 1.0t, 1.5t, and 2.0t, respectively. Molding analysis and experimental data were compared and analyzed. In the case of galvanized steel sheets, it was considered that the springback phenomenon occurs more frequently in molding analysis than in experiments. It was considered that the springback phenomenon occurs greatly in the experiment, not the interpretation of the molding of the stainless steel plate and the aluminum plate. It was considered that the springback occurrence tendency of the molding analysis and the experiment was the same, and the springback occurrence error rate of the molding analysis and the experimental result was about 4.0%.

• Design & Manufacturing
• /
• v.7 no.1
• /
• pp.23-27
• /
• 2013

Orchard sprayers, wide area dusters and multipurpose control cars are flagship products of Hansung T&I Ltd. Spray pumps are one of the essential parts for these products. But conventional belt pulleys for spray pumps are heavy and expensive, and they bring down the quality as well as productivity of the end-products. Therefore, this study focuses on mold design for aluminum die casting belt pulley and mold manufacture.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.18 no.11
• /
• pp.103-108
• /
• 2019

The cooling rate and the uniformity of mold temperature, in the injection molding process, possess great influences on the productivity and quality of replications. The conformal cooling channel, which is of a uniform spacing from the mold cavity by the metal additive manufacturing process, receives much attention recently. The purpose of this study is to develop a mold core with a curved conformal cooling channel for a pottery-shaped thick-wall cosmetic container through the hybrid method of direct metal tooling (DMT) process. In this study, we design a mold core that contains the curved cooling channel for the container. A method that divides the cavity is proposed and the DMT process is carried out to form the curved cooling channel. The test mold core, with the curved conformal cooling channel, has been fabricated by the proposed method to confirm the feasibility of the design concept. We show that no leakage is observed for the additive manufactured test mold core, and its physical properties demonstrate that it can be sufficiently used as the injection mold core.

• Journal of Korea Foundry Society
• /
• v.21 no.2
• /
• pp.85-92
• /
• 2001

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.26 no.4
• /
• pp.357-364
• /
• 2017

Metal casting is a process in which molten metal or liquid metal is poured into a mold made of sand, metal, or ceramic. The mold contains a cavity of the desired shape to form geometrically complex parts. The casting process is used to create complex shapes that are difficult to make using conventional manufacturing practices. For the optimal casting process design of sleeve parts, various analyses were performed in this study using commercial finite element analysis software. The simulation was focused on the behaviors of molten metal during the mold filling and solidification stages for the precision and sand casting products. This study developed high-life sleeve parts for the sink roll of continuous hot-dip galvanizing equipment by applying a wear-resistant alloy casting process.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.20 no.12
• /
• pp.8-15
• /
• 2021

Cold forging is a method in which molding is performed at room temperature. It has a high material recovery rate and dimensional precision and produces excellent surface quality, and it is mainly used for the production of bolted or housing products. The lifespan of cold forging molds is generally determined by the wear of the mold, plastic deformation of the mold, and fatigue strength. Cold forging molds are frequently damaged due to fatigue destruction rather than wear and plastic deformation in a high-temperature environment as it is molded at room temperature without preheating the raw material and mold. Based on the results analyzed through FEM, an effective mold structure design method was proposed by analyzing the changes in tensile and compressive stresses on molds according to the number of molds and reinforcement rings and comparing the product geometry and mold stress using three existing mold models.

• Design & Manufacturing
• /
• v.6 no.2
• /
• pp.12-16
• /
• 2012

In this study, an injection mold is made to produce polymer line post insulators. FRP (fiber reinforced plastics) is covered by silicone housing. In injection molding process, chances for offcenter are 60 percent. Given the structure of the product, offcenter occurs owing to the imbalances in positions of gates and improper -designs of cores and jigs. This study focuses on mold modifications and improvements.

• Transactions of Materials Processing
• /
• v.30 no.3
• /
• pp.149-156
• /
• 2021

Fine blanking is a high-precision process combining principles of metal stamping and cold forming. Unlike conventional metal stamping, fine blanking uses a special triple action such as V-ring force, counter force, shearing force. This study performed the effect of pocket-shaped compression molding on the mold life of the fine blanking using the 7.4mm thick SM45C material. In order to determine the lifespan of the punch and die in the fine blanking molds, a trial mold was manufactured and various punch materials were selected to perform the mold life test. A study on the life of a fine blanking mold by applying a thick plate material was experimentally performed through a mold test.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2002.02a
• /
• pp.180-186
• /
• 2002

The simulated die-casting process in which the traditional plaster casting process is combined with Rapid Prototyping technology is being used to produce Al, Mg, and Zn die-casting prototypes. Unlike in the die-casting process, molten metal in the conventional plaster casting process is fed via a gravity pour into a mold and the mold does not cool as quickly as a die-casting mold. The plaster castings have much larger and grosser grain structure as compared as the die-castings and the thin walls of the plaster mold cavity may not be completely fillet Because of lower mechanical properties induced by the large grain structure and incomplete Idling, the conventional plaster casting process is not suitable for the trial die-casting Process. In this work, an enhanced trial die-casting process has been developed in which molten metal in the plaster mold cavity is vibrated and pressurized simultaneously. Patterns for the casting are made by Rapid Prototyping technologies and then plaster molds, which have runner system, are made using these patterns. Imparted pressurized vibration to molten metal has made grain structure of castings much finer and improved fluidity of the molten metal enough to obtain complete filling at thin walls which can not be filled in the conventional plaster casting process.