• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1988.05a
• /
• pp.10-12
• /
• 1988

High Tc Y-Ba-Cu-O Superconductors were fabricated by sintering, sintering + HIP and Hot Pressing. Specimens were sintered at $940^{\circ}C$ and $960^{\circ}C$. In case that sintered specimens were treated by HIP, the relative density was increased 5-6% in comparison with sintered ones. X-ray analysis of each specimens represented orthorhombic phase and Tc measurements showed a sharp drop in the temperature range $95-88^{\circ}K$. The relative density of hot pressed samples was lower than 80%.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1198-1199
• /
• 2006

Type I clathrate $Ba_8Al_{16}Si_{30}$ was produced by arc melting and hot pressing and thermoelectric properties were investigated. Negative Seebeck coefficient at all temperatures measured, which means that the majority carriers are electrons. Electrical conductivity decreased by increasing temperature and thermal conductivity was 0.012 W/cmK at room temperature and dimensionless thermoelectric figure of merit (ZT) was 0.01 at 873K.

• Journal of the Korean Ceramic Society
• /
• v.37 no.7
• /
• pp.645-650
• /
• 2000

Effects of the chemical composition and sintering atmosphere on the formation of reaction phases and physical properties of reactive hot-pressed TiB2-AlN-BN composites were investigated. At N2 atmosphere, TiN was formed by the reaction between Ti and N2, which inhibited the densification and results in inferior mechanical-and electrical properties of the composites. However, at Ar atmosphere, enhanced densification and physical properties of composites were obtained due to that the TiN formation reaction was excluded. Densification of the composites was also hindered by BN, therefore, inferior mechanical-and electrical properties of composites were obtained with amount of BN in the starting materials. At Ar atmosphere, TiB2-AlN-BN composites having 318 MPa of flexural strength, 3.5 MPa.m1/2 of fracture toughness and 276$\mu$Ω.cm of electrical resistivity were fabricated from mole ratio 1:2:1.6 of Ti-Al-BN mixtures.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 1996.04b
• /
• pp.20-24
• /
• 1996

Three kinds of the sialon ceramics with and without TiN additions were hot pressed. Hardness and fracture toughness were measured with prepared specimens to study the effect of additives on the mechanical properties. A gas blast type erosion tester was employed to examine erosion behavior of the specimens up to 600 $^{\circ}$C. Erosion tests showed an increase of erosion rate up to 400 $^{\circ}$C and a gradual decrease of erosion rate 500 $^{\circ}$C for all kinds of sialon. The results also showed that erosion rates of the sialons were controlled better by microstructure factors than by mechanical properties such as fracture toughness.

• Tribology and Lubricants
• /
• v.13 no.3
• /
• pp.42-47
• /
• 1997

Three kinds of the sialon ceramics with and without TiN additions were prepared by hot pressing to investigate the effect of microstructure on erosion behaviors. Hardness and fracture toughness were measured with prepared specimens to study the effect of additives on the mechanical properties. A gas blast type erosion tester was employed to examine erosion behavior of the specimens up to $600^{\circ}C$. Erosion tests showed an increase of erosion rate up to 40$0^{\circ}C$ and a gradual decrease of erosion rate up to 50$0^{\circ}C$ for all kinds of sialon. The results also showed that erosion rates of the sialons were controlled better by microstructural factors than by mechanical properties including fracture toughness and hardness.

• Journal of the Korean Magnetics Society
• /
• v.5 no.5
• /
• pp.421-426
• /
• 1995

The magnetic properties of the hot-pressed magnets made from the Fe-Nd-B alloys, mechanically ground and subsequently blended with binary additives such as Al-Cu and Ag-Zn before hot pressing, were investigated. The coercivities of the magnets increased as the concentration of Al-Cu increased up to 1 wt.% or up to 3 wt.% in the case of Ag-Zn. At higher concentrations the coercivities decreased markedly. The maximum gain in coercivity by the addition was about 20 %. typical values of $_{i}H_{c}$ and $B_{r}$ of a hotpressed magnet containing 1 wt.% Al-Cu were 18 kOe and 7 kG, respectively. It was found that Cu, Ag, and Zn, which diffused into the magnet during hot pressing, were mostly concentrated on the Nd-rich grain boundary phase whereas Al was present not only in the grain boundary region but also in the matrix grains.

• Journal of the Korean Wood Science and Technology
• /
• v.46 no.4
• /
• pp.355-361
• /
• 2018

In this study, the dimensional stability and mechanical properties of bamboo fiber-based composites (BFBCs) were studied at two pressing manufacturing processes, i.e., hot- and cold- pressing, and were compared with three density parameters (1.0, 1.1, and $1.2kg/m^3$). Width swelling ratio (WSR), thickness swelling ratio (TSR), and water absorption ratio (WAR) were calculated for water immersions of 4 and 28 h. WSR, TSR, and WAR for specimens immersed for 28 h were higher than those for 4 h treatment, which shows that the immersion time has a significant influence on the dimensional stabilities of BFBCs. Moreover, the positive linear relations between density and dimensional were observed at both the pressing ways, indicating that the WSR, TSR, and WAR decreased with an increase in the density of BFBCs. The compressive strength, shear strength, modulus of rupture (MOR), and modulus of elasticity (MOE) were determined. The compressive strength, MOR, and MOE of hot-pressed specimens were significantly higher than those for the cold-pressed specimens, which are also directly proportional to density. Moreover, the samples with the highest density of $1.2kg/m^3$ performed high values on mechanical properties in both the manufacturing methods.

• Korean Journal of Materials Research
• /
• v.7 no.1
• /
• pp.40-49
• /
• 1997

$Bi_{2}(Te_{0.9}Se_{0.1})_{3}$ thermoelectric matcrials havc 11et:n fahricxted hy mechanical alloying and hot pressing methods. Microstructure and thermoelectric properties of the hot 11resseii $Bi_{2}(Te_{0.9}Se_{0.1})_{3}$ have been investigated Lvith variations of hot pressing temperature and dopmt atltiition Formation of $Bi_{2}(Te_{0.9}Se_{0.1})_{3}$ alloy powders was completed by mechanical alloying of the as-mixed Ri. Te, arid Sc grmules of ~3.6mm size for 3 hours at ball-to-material weight ratio of 5 : 1. Figure of merit of $Bi_{2}(Te_{0.9}Se_{0.1})_{3}$ was markedly incrcwieti hy hot pressing at temperatures above $450^{\circ}C$, and value of $1.9{\times}10^{-3}/K$ was obtained for the specimen hot pressed at $550^{\circ}C$. With addition of 0.015 wt% Ri as acceptor dopant, figure of merit ol $Bi_{2}(Te_{0.9}Se_{0.1})_{3}$ hot pressed $550^{\circ}C$$2.1{\times}10^{-3}/K$.

• Korean Journal of Fisheries and Aquatic Sciences
• /
• v.4 no.1
• /
• pp.22-30
• /
• 1971

Sea mussel Mytilus edulis, world-widely distributed, is a sort of popular food in Korea. The demands of high quality and mass production are not being satisfied since it is usually sun dried. A rapid dehydration and the treatment of food additives to improve the quality of the product seems to be required. In this paper, the effect of antioxidants and EDTA treatment was studied when sea mussel was pressed and hot-air dehydrated for 10 hours at 45 to $52^{\circ}C$ under the air flow rate of 3 meter per second. The results are as follows: 1) Cooked and pressed sea mussel was dehydrated mere rapidly than cooked without pressing. 2) The rehydration rate of pressed and dehydrated sea mussel was higher than that of the unpressed. 3) Among six samples, BHA treated material showed the best color preservation during dehydration and storage. The treatment of Teonox-II was also effective following BHA. 4) The effects of antioxidants used during dehydration and storage were in order of BHA, Tenox-II and NDGA treatment, while EDTA was ineffective. 5) No significant difference in rehydration rate was found between those treated with antioxidants or EDTA and the untreated. 6) The amount of soluble protein was higher in the samples treated with antioxidants than in EDTA treated or untreated samples. 7) The results suggest that the treatment of BHA and pressing process produce improved product in quality which gives higher amount of soluble protein and better rehydration, color preservation and preventive effect of rancidity.

• Korean Journal of Food Science and Technology
• /
• v.10 no.4
• /
• pp.404-408
• /
• 1978

This experiment was carried out to study the characteristics and composition of the oil extracted from elder berry seeds. The results obtained were summarized as follows. 1. The elder berry fruits are composed of $1.56%{\sim}2.50%$ crude lipid, $2.50{\sim}6.10%$ crude protein, $0.7{\sim}1.3%$ crude ash, 0.73% pectin and the fresh whole fruits bore $6{\sim}7%$ of its seeds on weight basis. 2. The hot pressed oil had similar flavor and taste to sesame oil, and cold, pressed one, to olive oil. Its iodine value ranged $95{\sim}110$, and its oil extraction rate from seed $26.18{\sim}26.55%$. 3. The elder berry seed oil contained a high level of essential fatty acids, and the oil seed cakes, $12.65{\sim}18.65%$ of crude protein. These may be utilized as concentrated fodder for livestock.