• Advances in concrete construction
• /
• v.9 no.6
• /
• pp.529-535
• /
• 2020

The current study investigated experimentally the effectiveness of Carbon Fiber Reinforced Polymer (CFRP) in confining concrete cylinders after being subjected to high temperature. Parameters examined were: (a) the exposing temperatures (20, 100, 200, 400 600 and 700℃) and (b) the number of CFRP layers (1 and 3 layers). A uniaxial compressive testing was carried out on 36 concrete cylinders with dimensions of 150 mm×300 mm. The results obtained show that the compressive strength reduced with the increased of temperature compared to that measured at 20℃. In particular, the reduction in the compressive strength was more observed when the temperature exceeded 400℃. Further, the concrete cylinders confined with one and three layers of CFRP significantly increased the compressive strength compared to the counterpart unconfined specimen tested at the same temperature. Also, the average percentages of the increase in the compressive strength were approximately 112% and 158% when applying 1 and 3 layers of CFRP, respectively, compared to the counterpart unstrengthened specimen tested at the same temperature.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2020.11a
• /
• pp.98-99
• /
• 2020

This study is aim to assess mechanical properties which is highly related to structural safe and durability of 100MPa high strength concrete mixed with amorphous metallic fiber. All specimens were heated with low velocity heating rate(1℃/min.), residual compressive strength and residual flexural strength was evaluated. The specimens were cooled down to room temperature after heating. As a result, in the case of 100MPa high-strength concrete, the residual compressive strength enhancing effect of amorphous metallic fiber has showed with the mix proportion of fiber. In addition, residual flexural strength showed more regular pattern before 300℃ then residual compressive strength, but simillar decreasing behavior was shown after 300℃ like residual compressive strength. Further study about fiber pull-out behavior and fiber mechanical, chemical property change due to temperature is needed.

• Journal of the Korea Institute of Building Construction
• /
• v.6 no.3 s.21
• /
• pp.99-105
• /
• 2006

In this paper, the estimation of compressive strength of concrete incorporating fly ash subjected to high temperature is discussed. Ordinary Portland cement and fly ash cement(30% of fly ash) were used, respectively. Water to binder ration ranging from 30% to 60% and curing temperature ranging from $20^{\circ}C{\sim}65^{\circ}C$ were also adopted for the experimental parameters. According to results, at the high temperature, FAC had higher strength development at early age than OPC concrete and it kept its high strength development at later age due to accelerated pozzolanic reaction subjected to high temperature. For strength estimation, Logistic model based on maturity equation and Carino model based on equivalent age were applied to verify the availability of estimation model. It shows that fair agreements between calculated values and measured values were obtained evaluating compressive strength with logistic curve. The application of logistic model at high temperature had remarkable deviations in the same maturity. Whereas, the application of Carino model showed good agreements between calculated values and measured ones regardless of type of cement and W/B. However, some correction factors should be considered to enhance the accuracy of strength estimation of concrete.

• Journal of Environmental Science International
• /
• v.16 no.3
• /
• pp.347-355
• /
• 2007

In this paper, estimation of the compressive strength of the concrete incorporating blast furnace slag subjected to high temperature was discussed. Ordinary Portland cement and blast furnace slag cement (BSC;30% of blast furnace slag) were used, respectively. Water to binder ratio ranging from 30% to 60% and curing temperature ranging from $20^{\circ}C{\sim}65^{\circ}C$ were also chosen for the experimental parameters, respectively. At the high temperature, BSC had higher strength development at early age than OPC concrete and it kept its high strength development at later age due to accelerated latent hydration reaction subjected to high temperature. For the strength estimation, the Logistic model based on maturity equation and the Carino model based on equivalent age were applied to verify the availability of estimation model. It was found that fair agreements between calculated values and measured values were obtained evaluating compressive strength with logistic curve. The application of logistic model at high temperature had remarkable deviations in the same maturity. Whereas, the application of Carino model showed good agreements between calculated values and measured ones regardless of type of cement and W/B. However, some correction factors should be considered to enhance the accuracy of strength estimation of concrete.

• Tunnel and Underground Space
• /
• v.2 no.2
• /
• pp.224-236
• /
• 1992

It is very important to determine the thermo-mechanical characteristics of the rock mass surrounding the repository of radioctive waste and the LPG storage cavern. In this study, Hwasoon-Shist. Dado-Tuff adn Chunan-Tonalite were the selected rock types. Temperature dependence of the mechanical properteis such as uniaxial compressive strength, tensile strength, Young's modulus was investigated by measuring the behaviour of these properties due to the variation of temperature. Also, the characteristics of strength and deformation of these rocks were examined through high-temperature triaxial compression tests with varing temperatures and confining pressures. Important results obtained are as follows: In high temperature tests, the uniaxial compressive strength and Yong's modulus of Tonalite showed a sligth increase at a temperature up to 300$^{\circ}C$ and a sharp decrease beyond 300$^{\circ}C$, and the tensile strength showed a linear decrease with increasing heating-temperature. In high-temperature triaxial compression test, both the failure stress and Young's modulus of Tonalite increased with the increase of confining pressure at constant heating-temperature, and the failure stress decreased at 100$^{\circ}C$ but increased at 200$^{\circ}C$ under a constant confining pressure. In low temperature tests, the uniaxial compressive and tensile strengths and Young's modulus of these rocks increased as the cooling-temperature is reduced. Also, the uniaxial compressive and tensile strengths of wet rock specimens are less than those of dry rock specimens.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2015.11a
• /
• pp.139-140
• /
• 2015

The purpose of this study was to evaluate existing compressive strength equation with concrete exposed to high temperature by ultrasonic pulse velocity. As the result, original compressive strength equation is proper only for compressive strength of normal concrete. Therefore, an accumulation of experimental database of concrete exposed to high temperature is necessary for proposal of new compressive strength equation.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2019.05a
• /
• pp.103-104
• /
• 2019

The aim of the research is assessing the possibility of recovering the compressive strength of the mortar mixture replaced excessively high volume of blast furnace slag accidently. As a result of the experiment, in the case of compressive strength, painting sodium oxide showed higher compressive strength recovery effect than painting calcium oxide. As a curing temperature, 20℃ showed advanced result rather than 65℃. From the wet curing, the reaction was confirmed, deeper penetration depth was checked at 20℃ than 60℃ temperature. Therefore for the concrete mixture with excessively high volume of blast furnace slag, it is considered that painting sodium hydroxide and curing 20℃ can recover the compressive strength effectively.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.11 no.4
• /
• pp.117-124
• /
• 2003

The lightness of components required in automobile and machinery industry is requiring high strength of components. In particular, manufacturing process and new materials development for solving the fatigue fracture problem attendant upon high strength of suspension of automobile are actively advanced. In this paper, the effect of compressive residual stress of spring steel(JISG SUP-9) by shot-peening on fatigue crack growth characteristics in high temperatures($100^{\circ}C$, $150^{\circ}C$, $180^{\circ}C$) was investigated with considering fracture mechanics. So, we can obtain followings. (1)Compressive residual stress decreases in high temperature, that is, with increasing temperature. (2)The effect of compressive residual stress on fatigue crack growth behavior in high temperature increases below $\Delta$K=17~19MPa (3)It was investigated by SEM that the constraint of compressive residual stress for plastic zone of fatigue crack tip was decreased in high temperature as compared with room temperature.

• Structural Engineering and Mechanics
• /
• v.65 no.3
• /
• pp.343-348
• /
• 2018

This paper reports mechanical behavior of recycled fine aggregate concretes after high temperatures. It is found that compressive strength of recycled fine aggregate concretes decline significantly as the temperature rises. The elastic modulus of recycled fine aggregate concretes decreases with the increase in temperature, and the decrease is much quicker than the decrease in compressive strength. The split tensile strength of recycled fine aggregate concrete decrease as the temperature rises. Through the regression analysis, the relationship of the mechanical behavior with temperature are proposed, including the compressive behavior, elastic modulus and split tensile strength, which are fitting the test data.

• Journal of the Korea Institute of Building Construction
• /
• v.7 no.1 s.23
• /
• pp.71-77
• /
• 2007

This paper is to investigate the effect of the curing temperature on strength development of concrete incorporating cement kiln dust(CKD) and blast furnace slag (BS) quantitatively. Estimation of the compressive strength of the concrete was conducted using the equivalent age equation and the rate constant model proposed by Carino. Correction of Carino model was studied to secure the accuracy of strength development estimation by introducing correction factors regarding rate constant and age. An increasing curing temperature results in an increase in strength at early age, but with the elapse of age, strength development at high curing temperature decreases compared with that at low curing temperature. Especially, the use of BS has a remarkable strength development at early age and even at later age, high strength is maintained due to accelerated pozzolanic activity resulting from high temperature. Whereas, at low curing temperature, the use of BS leads to a decrease in compressive strength. Accordingly, much attention should be paid to prevent strength loss at low temperature. Based on the strength development estimation using equivalent age equation, good agreements between measured strength and calculated strength are obtained.