Cellulose grafted with acrylic acid(AAc) was prepared by radiation grafting technique. The effects of reaction temperature. reaction time, monomer concentration, and the crosslinkers on the AAc grafting reaction on cellulose were examined. The amount of AAc grafted on the cellulose reached maximum at the concentration of 0.75vol% difunctional crosslinker and 1.0vol% trifunctional crosslinker, respectively. In the presence of acid, the amount of AAc grafted on the cellulose was decreased when reaction solution contains difunctional crosslinker, while that was increased when reaction solution contains trifunctional crosslinker. In the grafting reaction of cellulose with AAc and TMETA, mixture containing ferrous sulfate and acid enhanced further AAc grafting yield than mixture containing ferrous sulfate only.

• Elastomers and Composites
• /
• v.26 no.2
• /
• pp.109-114
• /
• 1991

The graft copolymerization of chloroprene rubber with methyl methacrylate in toluene solution has been carried out varying the concentration of monomer, initiator, CR, reaction time, and reaction temperature, etc.. It is observed that the grafting reaction follows conventional kinetic behavior under the present experimental conditions. Identification of grafting on to chloroprene rubber was obtained through characterization of the graft copolymer by infrared spectrometer.

• Polymer(Korea)
• /
• v.26 no.3
• /
• pp.287-292
• /
• 2002

Graft copolymerization of styrene and glycidyl methacrylate (GMA) to the peroxidized polypropylene (PP) fabric with E-beam in $O_2$ atmosphere was carried out in vapor phase with benzoyl peroxide (BPO) as an initiator. The degree of grafting of copolymers was increased with the increase of the reaction temperature and the highest degree of grafting was obtained at $70^{\circ}C$ with styrene, and at $80^{\circ}C$ with GMA. The highest degree of grafting of styrene grafted PP according to reaction time was higher than that of GMA grafted PP. In vapor phase graft polymerization, the degree of grafting of copolymers according to water composition in monomer mixture was effected by the boiling temperature of monomers.

• Journal of Radiation Industry
• /
• v.8 no.1
• /
• pp.53-57
• /
• 2014

The kenaf is quickly developing as a renewable resource. Kenaf can be grown under a wide range of weather conditions. Modification of kenaf fiber by graft polymerization provides a significant route to alter the chemical properties, including surface hydrophilicity or hydrophobicity. In this study, kenaf fiber surfaces were grafted with acrylic acid as a hydrophilic group using electron beam irradiation. The grafting rate increased with an increase in grafting time. The FT-IR results confirmed that acrylic acid was successfully grafted onto the kenaf fibers. The wettability of the kenaf fiber was increased, accompanied by acylic acid grafting on the fiber surface. According to the permeability test result, it was found that acrylic acid grafted kenaf fiber reinforced cement composite was more reduced than non-grafted kenaf fiber reinforced cement composite.

• Polymer(Korea)
• /
• v.38 no.1
• /
• pp.49-53
• /
• 2014

A novel monomeric UV-absorber was prepared by the reaction of 2,4-dihydroxybenzophenone with N-4-chlorocarbonylphenylmaleimide in the presence of triethylamine. This reactive maleimide was grafted onto polypropylene (PP) by the thermal melt-processing in a mini-max-moulder. IR spectroscopic method was used for the quantitative determination of the extent of grafting of monomeric maleimide. To find the optimal reaction conditions, the dependence of reaction temperature and time and the concentration of monomeric UV-absorber was investigated on the grafting yields. The photooxidative effect of the grafted PP was evaluated in the weatherometer comparing to the PP mixed with UV-absorbers using the carbonyl index of IR spectrum. The grafted PP showed an excellent anti-photooxidative effect.

• Proceedings of the Korean Society for Agricultural Machinery Conference
• /
• 2000.11c
• /
• pp.632-638
• /
• 2000

This paper represents the characteristics of evapotranspiration rate (EVTR) and graft-taking of watermelon grafted seedlings in a graft-taking enhancement system using fluorescent lamps as artificial lighting source. Four air temperature levels of 23, 25, 27 and 29C, three humidity levels of 85, 90 and 95%R.H. and two photosynthetic photon flux (PPF) levels of 30 and 50 ${\mu}$mol m$\^$-2/ S$\^$-1/ were provided to investigate the effects of air temperature, relative humidity and light intensity on EVTR and graft-taking of grafted seedlings. EVTR of grafted seedlings increased with increasing air temperature and the passage of time after grafting. Also EVTR increased with decreasing relative humidity. As relative humidity decreased and air temperature increased, vapor pressure deficit increased and thus EVTR increased. It is required to maintain a low level vapor pressure deficit for suppressing EVTR of grafted seedlings during first 1-2 days after grafting. Therefore, less EVTR at initial stage after grafting would be adequate for smooth joining of the scion and rootstock.

• Elastomers and Composites
• /
• v.28 no.3
• /
• pp.191-197
• /
• 1993

The graft copolymerization of methyl methacrylate(MMA) onto natural rubber latex(NRL) initiated by t-butyl hydroperoxide(t-BHPO) was investigated in aquous medium. The grafting percentage, grafting efficiency and total conversion were observed in various reaction conditions such as monomer, initiator and emulsifier concentration, reaction temperature, reaction time and agitation speed. The optimum conditions for the graft copolymerization onto natural rubber latex were as follows ; At given monomer concentration of $3{\times}10^{-2}mole/l$, the maximum grafting percentage was appeared in the case of grading in initiator concentration of $4{\times}10^{-2}mo1e/l$ and emulsifier concentration of 0.2wt.% at $40^{\circ}C$ for 5hrs.

• Macromolecular Research
• /
• v.11 no.5
• /
• pp.347-351
• /
• 2003

The hydrophobic ligand-containing hollow polypropylene (PP) membranes were synthesized by the mutual radiation induced graft copolymerization with glycidylmethacrylate (GMA) onto hollow PP membrane followed by the subsequent functionalization with L-phenylalanine. FT-IR, elemental analysis and UV spectroscopy were utilized to characterize copolymer composition, and degree of grafting, functionalization conversion and ${\gamma}$-globulins adsorption. The degree of grafting on the PP surface increased with the reaction time and total dose of E-beam. In the subsquent functionalization, the amount of L-phenylalanine increased with the increase in the degree of grafting and the degree of conversion was about 30%. The ${\gamma}$-globulins adsorption experiments showed that adsorption capacity had a maximum value at pH 8. The ${\gamma}$-globulins adsorption capacity in the basic pH region was higher than in the acidic pH region.

• Journal of Sericultural and Entomological Science
• /
• v.20 no.2
• /
• pp.40-44
• /
• 1978

Cerium (IV) ion-initiated graft copolymerizations of acrylonitrile to raw silk were investigated in an effort to carry out sericine-fixation. The change in ceric ammonium nitrate concentration exhibited a maximum in percentage of grafting at 0.003M. Also observed was that the change in nitric acid content in reaction media gave a maximum in percentage of grafting at 0.1M. Percentage of grafting was increased generally with increase in acrylonitrile concentration, reaction time and reaction temperature. Raw silk sericin grafted with acrylonitrile was not de gummed by boiling off test and optimum graft percentage was considered at 20%.

• Journal of the Korean Association of Oral and Maxillofacial Surgeons
• /
• v.45 no.4
• /
• pp.220-224
• /
• 2019

Maxillary sinus grafting is a dependable procedure that has been in use for a long time. However, clinical complications often arise. To prevent complications of maxillary sinus grafting, it is necessary to know the contra-indications, both for general implantation and for maxillary bone grafting. In addition, presence of various complications requires careful consideration of treatment method; therefore, dentists should be familiar with the treatment protocols. Complications can be divided into postoperative, immediate postoperative, and delayed postoperative complications. Particularly for the outpatient, it is necessary to quickly distinguish between treatable cases and cases for which transfer is required. The purpose of this review is to discuss the contra-indications, complications, and treatment options for complications of maxillary sinus graft.