• Fire Science and Engineering
• /
• v.25 no.6
• /
• pp.146-155
• /
• 2011

In the study, test was carried out to compare the flame retardant performance for the specimen of MDF wood to which field flame retardant treatment (post processing flame retardant) is applied, which is coated with flame retardant film of 5 companies, locally distributed, and MDF wood (nontreated, flame retardant film non-coated) to which aqueous or oil-based fire-retardant paint is applied. As a result of combustion test of MDF wood which was coated with flame retardant film of 5 companies, 2 products showed suitable values in 4 criteria, but other 3 products showed 10~40 % disqualification rate. In regard of characteristics of fire-retardant paint, oil-based fire-retardant paint is better than aqueous fire-retardant paint in flame retardant performance criteria, but MDF wood to which oilbase fire-retardant paint was applied was shown to have higher toxicity index grade than MDF wood to which aqueous fire-retardant paint was applied relatively.

• Journal of the Korean Society of Safety
• /
• v.32 no.3
• /
• pp.28-33
• /
• 2017

In this study, the composite material of expandable graphite was made to the material development for improving such as a composite material of the sandwich panels or material properties of a fire door and was tested by the ISO 1182, ISO 5660-1(Cone calorimeter Method). For the test, the composite material of expandable graphite, what the expandable graphite ratio was increased by respectively 0g~30g, was classified A1,A2, A3, A4, and made to the test specimens. Through cone calorimeter test, peak heat release rate(HRR) and total heat release(THR), expanded thickness and expansion rate of each composite material of expandable graphite, and fire prone crack and mass loss rate after burning was measured. Thus, the effect of the addition of the expandable graphite and whether is suitable for reference as a fire retardant, was analyzed. Consequently the correlation of THR and fire retardant performance rate was confirmed.

• Journal of the Korea Safety Management & Science
• /
• v.14 no.2
• /
• pp.65-70
• /
• 2012

This study was performed to test the combustive properties of the pipe insulation materials which are mainly used in the industries and buildings. Fire characteristic test of pipe insulation film according to the KS F ISO 5660-1 was performed. The experimental materials commonly used in the pipe insulation were used four kinds of films. Two kinds of 4 types of products that have the flame retardant performance and the other two types of them have no flame retardant performance. They were selected for fire characteristic test. The result of finding 25kW/$m^2$ radiation from the ignition was that flame retardant products were 140sec and the other one were 69sec in average of heat release rate(HRR). The result of flame retardant products in the 50kW/$m^2$ was 34sec and the other one were 15sec in average of HRR. However, the HRR of flame retardant products was much higher than the other one. Flame propagation test was conducted according to the KOFEIS 1001. The result of flame retardant products was that flame retardant products had a hold without fire spread after firing them. But the other one were completely fired after firing them. Therefore, I want to recommend that flame retardant products need to be used by the regulation to prevent or decrease a fire spread.

• Fire Science and Engineering
• /
• v.24 no.3
• /
• pp.72-77
• /
• 2010

Honeycomb core structure with its excellent stiffness and strength is being utilized in many fields such as interior building material. Because it is inexpensive and renewable, honeycomb paper production is economically and environmentally helpful. However, the paper needs to be fireproofed because it is vulnerable to fire. In this study, we have undergone the performance evaluation process of the honeycomb paper which is widely used as interior material of a fire door and packing material. Four kinds of honeycomb (a honeycomb made of flame-resistant paper; a honeycomb attached with conventional flame-resistant film made in the laboratory; honeycomb impregnated with flame retardant; a honeycomb attached with flame-resistant film after impregnating fire retardant) were used in the study to compare the fire retardant performance. As a result, the honeycomb with impregnated flame retardant showed the highest performance. The flame-resistant film was effective in delaying the igniting time but had a negative effect on the rate of heat and smoke production.

• Journal of the Korean Society of Combustion
• /
• v.22 no.4
• /
• pp.1-8
• /
• 2017

This study was conducted to evaluate the fire retardant performance of exfoliated graphite nanoplatelets (xGnP) applied for particleboard. This work measured heat release rate(HRR), total heat release(THR) and smoke production rate(SPR) of xGnP added particleboard, using cone calorimeter to assess its fire characteristics according to the KS F ISO 5660-1 standard code. Heat release rates of all specimens treated by xGnP were less than the $200kW/m^2$ for a total experiment period of five minutes. Heat release rates of the specimens coated with xGnP were lower than those of the specimens made by mixing wood particles with xGnP directly. Meanwhile, the total heat release rates of xGnP coated specimen maintained quite lower level than the uncoated so the xGnP coating were effective in improving the fire retardant performance of particleboard. However, the smoke emission peaking problem at the initial combustion period, which was caused by adding base coating materials, should be resolved for further satisfaction as a fire retardant materials.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2022.11a
• /
• pp.35-36
• /
• 2022

In order to supplement the flame-retardant performance of oil stain, which can prevent wooden buildings from contamination, (NH4)2HPO4, a phosphorus flame-retardant, was added to oil stain and applied for each type of plywood, and an experiment was conducted. The addition rate was set to 0-60%, but white powder appeared on the surface of plywood from 40% and thus it was impossible to experiment, so the maximum addition rate was selected as 30%. As a result of the experiment, acacia plywood had the best performance. As the rate of addition of the flame retardant increased, the remaining time and carbonization length of all plywood decreased, but the carbonization length of the MDF plywood was not met with the standards.

• Journal of the Korean Wood Science and Technology
• /
• v.32 no.6
• /
• pp.7-13
• /
• 2004

In this study, the Korean pine wood (Pinus densiflora Sieb. et Zucc) and Italian poplar wood (Populus euramericana Guinier) was treated with a mixture of monoammonium phosphate (MAP) and boric acid. Their usability as fire retardant and as decay-resistant construction and interior materials were evaluated by testing of chemicals, corrosion rate and absorption rate, weight loss and chemical contents. An experiment was performed to compare treated pine wood and Italian poplar wood. According to the results, Italian poplar wood had higher specific gravity and retention of chemicals than pine wood, and treated wood showed higher decay-resistance than untreated one. Weight loss was less in treated wood than untreated one because the degree of decay was lower in the former than the latter. Corrosion rate and absorption rate met the KS standard for wood preservative performance. The chemical contents analysis was carried out to determine the degree of decay and it was found that the preservative effect of chemical treatment was lower in Italian poplar wood than in pine wood.

• Fire Science and Engineering
• /
• v.26 no.2
• /
• pp.105-111
• /
• 2012

In this research, aluminum composite panels of the general materials and fire retardant materials as building claddings make researches about fire performance comparison analysis. Test methods of the small and medium cone calorimeter experiments and SBI (Single Burning Item) experiments was applied to the determination. As a result, in the experiments peak heat release rate cone calorimeter the general aluminum composite panel $1,293kW/m^2$ ($75kW/m^2$), flame-retardant aluminum composite panel $70kW/m^2$ ($75kW/m^2$) was measured. In the SBI experiments fire growth rate the general fire aluminum composite panel is approximately 743 W/s and the flame-retardant aluminum composite panel is approximately 97 W/s of the value were measured. Thus, a standards enactment are urgently required in this case it is used as building claddings of the aluminum composite panel by fire risk assessment.

• Carbon letters
• /
• v.28
• /
• pp.66-71
• /
• 2018

To improve the flame retardant performance of cellulose fibers, fluorine functional groups were introduced under various controlled fluorination conditions. The properties of the fluorinated cellulose fibers were analyzed by X-ray photoelectron spectroscopy and a thermogravimetric analysis. The fluorine functional group content in the fluorinated cellulose fibers increased with an increase in the fluorination temperature. However, the fluorination reaction increased the char yield and decreased the rate of degradation of the cellulose fibers by introducing donors, enabling the formation of a thick and compact char layer. Therefore, the flame retardant properties of cellulose fibers were improved following the fluorination treatment.

• Fire Science and Engineering
• /
• v.34 no.2
• /
• pp.7-13
• /
• 2020

In this study, water glass was applied as a coating material to a rigid polyurethane foam to improve the flame-retardant properties of the foam. The heat release rate of the cone calorimeter of the urethane foam, in which the inorganic water-glass coating layer was applied, decreased rapidly. The water glass coated on the polyurethane surface formed a glassy foam by foaming with water, which did not escape during the vitrification reaction when the foam or glass was heated. The glassy foam formed on the polyurethane foam became a fire-resistant insulation layer that inhibited the combustion of the polyurethane foam for more than 10 min. Water glass was found to improve the flame-retardant properties of the rigid polyurethane foam.