• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.660-660
• /
• 2006

• 한국분말재료학회지
• /
• 제4권3호
• /
• pp.170-178
• /
• 1997

An investigation was performed to apply the M3/2 grade high speed steel for metal injection molding using both prealloyed and elementally blended powders. The injected samples were subjected to a debinding step in $H_2/N_2$ gas atmosphere at a ratio that affected the carbon content of the material. The carbon content ranged from 1.4wt.% to 1.43wt%. with increasing $H_2$ content up to 80% $H_2$ in $H_2/N_2$ atmosphere for the prealloyed powders. The carbon contents of the elementally blended powders exhibited 1.44wt.% and 1.62wt.% at 10% $H_2/N_2$ and 20% $H_2/N_2$ gas, respectively. This level decreased to 0.17wt.% upon increasing the $H_2$ content. The sintered density of both powders increased rapidly as the temperature reached the liquid phase forming temperature. After forming the liquid phase, the density rapidly increased to the optimum sintering temperature for the prealloyed powders, whereas the density of mixed elemental powders goes up slowly to the optimum sintering temperature. The optimum sintering temperature and density are 126$0^{\circ}C$ and 97.3% for the prealloyed powders and 128$0^{\circ}C$ and 96.9% for the elementally blended powders, respectively. The microstructure of the specimen at the optimum sintering temperature consisted of fine grains with primary carbides of MC and $M_6C$ type for the prealloyed powders. The elementally blended powders exhibited coarse grains with eutectic carbides of MC, $M_2C$ and $M_6C$ type.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 하계학술대회 논문집 Vol.4 No.2
• /
• pp.735-738
• /
• 2003

Downsizing electronics requires precision position control with an accuracy of sub-micron order, which demands development of ultra-fine displacive devices. Piezoelectric transducer is one of devices transferring electric field energy into mechanical energy and being capable for fine displacement control. The transducer has been widely used as fine Position control device Multilayer piezoelectric actuator, one of typical piezo-transducer, is fabricated by stacking alternatively ceramic and electrode layers several hundred times followed by cofiring process. Electrode material should be tolerable in the firing process maintaining at ceramic-sintering temperatures up to $1100{\sim}1300^{\circ}C$. Ag-Pd can be used as stable electrode material in heat treatment above $960^{\circ}C$. Besides, adding small quantity ceramic powder allow the actuator to be fabricated in a good shape by diminishing shrinkage difference between ceramic and electrode layers, resulting in avoidance of crack and delamination at and/or nearby interface between ceramic an electrode layers. This study presents synthesis of nano-oxide-added Ag/Pd powders and its feasibility to candidate material tolerable at high temperature. The powders were formed in a co-precipitation process of Ag and Pd in nano-oxide-dispersed solution where Ag and Pd precursors are melted in $HNO_3$ acid.

• Carbon letters
• /
• 제13권4호
• /
• pp.254-259
• /
• 2012

Nanoporous non-woven carbon fibers for a gas sensor were prepared from a pitch/polyacrylonitrile (PAN) mixed solution through an electrospinning process and their gas-sensing properties were investigated. In order to create nanoscale pores, magnesium oxide (MgO) powders were added as a pore-forming agent during the mixing of these carbon precursors. The prepared nanoporous carbon fibers derived from the MgO pore-forming agent were characterized by scanning electron microscopy (SEM), $N_2$-adsorption isotherms, and a gas-sensing analysis. The SEM images showed that the MgO powders affected the viscosity of the pitch/PAN solution, which led to the production of beaded fibers. The specific surface area of carbon fibers increased from 2.0 to $763.2m^2/g$ when using this method. The template method therefore improved the porous structure, which allows for more efficient gas adsorption. The sensing ability and the response time for the NO gas adsorption were improved by the increased surface area and micropore fraction. In conclusion, the carbon fibers with high micropore fractions created through the use of MgO as a pore-forming agent exhibited improved NO gas sensitivity.

• 한국세라믹학회지
• /
• 제25권1호
• /
• pp.54-58
• /
• 1988

In order to depress PbO vaporization during calcination and improve sinterability in low temperature, a method for preparing homogeous Lead-Zirconate-Titanate (PZT) powder from aqueous salt solution by precipitation is described. In this method, single phae PZT fine powders are formed at above 500$^{\circ}C$. PZT-ceramics using these powders have high sinterability, and good sintering characteristics relatively low temp. (-high apparent density, low porosity, low water adsorption etc.)

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.706-707
• /
• 2006

Premixes treated with a binder, such as in the FLOMET process, exhibit better flow, reduced dusting and segregation and improved productivity and part consistency compared to conventional premixes. The binder treatment is highly suitable for high performance P/M applications which often require premixes containing very fine alloying additives and excellent die filling characteristics. With this process, various binders and lubricants can be utilized in order to make premixes with unique properties. In this paper, the characteristics and performances of bonded premixes are reported.

• Korean Chemical Engineering Research
• /
• 제45권6호
• /
• pp.560-565
• /
• 2007

화학환원법을 이용하여 폐동분 수용액에 환원제인 hydrazine을 첨가하여 $0.11{\sim}0.64{\mu}m$ 크기의 Cu 미립자를 제조하였으며, 이 과정 중 hydrazine의 첨가량이 얻어진 분말의 물성에 미치는 영향을 살펴보았다. 또한 분말합성 과정 중 분산제인 polyvinyl alcohol(PVA) 또는 polyvinyl pyrrolidone(PVP) 첨가가 분말의 물성에 미치는 영향도 조사하였다. 1 M 농도의 폐동분 수용액에 hydrazine이 0.8 mol, 1.0 mol 첨가된 경우에는 Cu와 $Cu_2O$의 혼합물을 나타내어 순수한 Cu 분말을 생성하지 못했다. 반면 적당량의 hydrazine(1.2 mol)이 첨가된 경우에는 순수한 Cu 분말이 생성되었다. 또한 얻어진 Cu 분말의 평균크기는 hydrazine과 분산제의 첨가량이 증가함에 따라 감소하였다. 한편 분말의 응집을 억제하는 분산제로서 PVA의 사용이 PVP 보다 더욱 효과적이었다.

• 자원리싸이클링
• /
• 제3권1호
• /
• pp.9-16
• /
• 1994

Stellite 스크랩을 용융 NaOH로 분해하고 이로부터 Co가분말을 제조하였다. NaOH에 의한 Stellite 스크랩의 완전분해는 $750~800^{\circ}C$에서 Stellite에 대한 NaOH의 중량비 약 2로 1시간 이내에 이루어졌다. 함Co화합물은 X-선분석과 시차열중량분석에 의해 $Co_2O_3{\dot}H_2O$로 판명되었다. 함Co화합물은 HCl로 용해하여 $CoCl_2$용액으로 만들고, 그리고 용액의 pH를 조절하여 먼저 Fedldhs을 제거한 후, pH 약 13 또는 4에서 각각 2가 EH는 3가의 수산화코발트로 침전시켰다. 이 침전물들은 $400~500^{\circ}C$에서 수소로 환원하여 1.0~$1.5\mu\textrm{m}$크기의 고순도 Co로 제조되었다. Stellite스크랩으로부터 Co 회수율은 약 75~86 중량 %이었다.

• 한국재료학회지
• /
• 제31권2호
• /
• pp.61-67
• /
• 2021

Fabrication of a ferromagnetic composite powder for the magnesium and BaFe12O19 system by mechanical alloying (MA) is investigated at room temperature. Mixtures of Mg and BaFe12O19 powders with a weight ratio of Mg:BaFe12O19 = 4:1, 3:2, 2:3 and 1:4 are used. Optimal MA conditions to obtain a ferromagnetic composite with fine microstructure are investigated by X-ray diffraction, differential scanning calorimetry (DSC) and vibrating sample magnetometer (VSM) measurement. It is found that Mg-BaFe12O19 composite powders in which BaFe12O19 is dispersed in Mg matrix are successfully produced by MA of BaFe12O19 with Mg for 80 min. for all compositions. Magnetization of Mg-BaFe12O19 composite powders gradually increases with increasing the amounts of BaFe12O19, whereas coercive force of MA powders gradually decreases due to the refinement of BaFe12O19 powders with MA time for all compositions. However, it can be seen that the coercivity of Mg-BaFe12O19 MA composite powders with a weight ratio of Mg:BaFe12O19=4:1 and 3:2 for MA 80 min. are still high, with values of 1260 Oe and 1320 Oe compared to that of Mg:BaFe12O19=1:4. This clearly suggests that the refinement of BaFe12O19 powders during MA process for Mg:BaFe12O19=4:1 and 3:2 tends to be suppressed due to ductile Mg powders.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2012년도 추계 학술논문 발표대회
• /
• pp.61-62
• /
• 2012

This study is for analyzing possibility of utilizing as cement from waste concrete. The scrapped fine powder which contains a large amount of hydrate of cement can supercede lime stone, and greenhouse gas reductions are expected. However, Fine Aggregate powder efficient separation technology development is essential for that limestone substitution effect and reduce greenhouse gas emissions in order to facilitate through the recycling of the scrapped fine powders.