• Journal of the Korea Concrete Institute
• /
• v.12 no.4
• /
• pp.23-30
• /
• 2000

The purpose of this paper is to study on the shear strength of high strength concrete beams with steel fibrous. In general, the shear strength of reinforced concrete beams is affected by the compressive strengths of concrete( c), the shear span-depth ratio(a/d), the longitudinal steel ratio($\rho$ $\omega$), and shear reinforcement. An experimental investigation of the shear strength of high strength concrete beams with steel fibrous was conducted. In each series the shear span-depth ratio(a/d) was held constant at 1.5, 2.8, or 3.6, while concrete strengths were varied from 320 to 520, to 800kgf/$\textrm{cm}^2$. To verify the proposed equations the experimental results were compared with those from other researches such as equation of ACI code 318-95 or equation of Zsutty. To deduce equation for shear strength from experimental data carried out MINITAP program. According to the experimental results, the addition of steel fibrous has increased the deflection and strain at failure load, improving the brittleness of the high strength concrete.

• Magazine of the Korean Society of Agricultural Engineers
• /
• v.34 no.2
• /
• pp.49-59
• /
• 1992

In our researches we made mix-design, with the mixing ratio and pre-cracked ratio of steel fibrous different from each other, building the steel fibrous concrete beam which had pre-cracks. To obtain the fracture characteristics of steel fibrous reinforced concrete, series of experiment were conducted on pre-cracked beam subjected to 3-point bending. Thus, we carried out experiments on the destructive characteristics of its pre-crack and post-crack and the result is as follows. 1. The compressive strength of steel fibrous concrete beam increased more slightly than plane beam, and the tensile strength increased 37%, 59%, 94% and 121% respectively when the amount of fibrous was 0.5%, 0.1% 1.5%, and 1.75% respectively. 2. As the amount of steel fibrous mixing increased ant the steel fibrous inhibited the crack growth, the crack condition of steel fibrous concrete beam was retarded irregularly, and this increased fracture load. 3. The defiance of destruction was reduced in the ratio of 1.35 times and 1.22 times respectively when the length of pre-crack was each 2cm and 4cm in comparison with the case of being without the length, and was similar to that of plane beam when the amount of steel fibrous mixing was below 1.0%, and increased linearly when it as above 1.0%. 4. The experimental formula seeking fracture energy was follows and thus we found that the value of fracture energy depended upon tensile strength and the size of speciment. $G_f=K\;{\cdot}\;f_f^'{\cdot}$da/Ec 5. We observed that in the load-strain curve of steel fibrous concrete beam the progress of the crack became slow, compared with plane beam because the crack condition became long to the extent of about 10 times. Concrete was faultiest brittleness fracture through the study, it was known ductile.

• Computers and Concrete
• /
• v.9 no.3
• /
• pp.227-244
• /
• 2012

A theoretical model for shear strength evaluation of fibrous concrete beams reinforced with stirrups is proposed. The formulation is founded on the theory of plasticity and the stress field concepts, generalizing a known plastic model for calculating the bearing capacity of reinforced concrete beams, to the case of fibrous concrete. The beneficial effect of steel fibres is estimated taking into account the residual tensile strength of fibrous concrete, by modifying an analytical constitutive law which presents a plastic plateau as a post-peak branch. Around fifty results of experimental tests carried out on steel fibrous concrete beams available in the literature were collected, and a comparison of shear strength estimation provided by other semi-empirical models is performed, proving that the numerical values obtained with the proposed model are in very good agreement with the experimental results.

• Advances in concrete construction
• /
• v.4 no.1
• /
• pp.37-47
• /
• 2016

The objective of the present work is to evaluate the influence of two different methods of improving the ductility of Reinforced Concrete Frames and their influence on the full range behavior of the frames with M40 grade of concrete. For this purpose one fourth scale reinforced concrete square frames are experimentally tested subjected to static cyclic loading for three cases and monotonic loading for one case. The parameters are varied as method introducing ductility to the frame viz. (i) by using conventional concrete (ii) adding 1% of steel fibres by volume of concrete at hinging zones (iii) using self-compacting concrete with fibres at hinging zones. The energy absorption by ductile and non-ductile frames has been compared. The behavior of frames tested under cyclic loading have revealed that there is a positive trend in improvement of ductility of frames when fibrous concrete is used along with self-compacting concrete.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.11a
• /
• pp.491-496
• /
• 2001

In recent years, the research and development about the new material proceed rapidly and actively in the building industry. As building structures become bigger, higher and more specialized, so does the demand for material with higher strength. In the future, we will need to research repair and rehabilitation to make high strength concrete mixed steel fibrous building safe. The carbon fiber reinforced plastic bonding method is widely used in reinforcing the existing concrete structure among the various methods. The repair of initiate loaded reinforced high-strength concrete beams mixed steel fibrous with epoxy bonded Carbon Fiber Sheets(CFS) was investigated experimentally. The CFS thickness and length were varied to assess the peel failure at the curtailment of CFS, The behaviour of the repaired beams was represented by load-longitudinal steel strain relation and failure modes were discussed. The test results indicate that CFS is very effective for strengthening the demand beams and controlling deflections of reinforced high strength concrete beams mixed steel fibrous happen diagonal crack, the increase in the number of CFS layers over two layers didn't effect the increase in the strength of beams.

• Journal of the Korea Concrete Institute
• /
• v.11 no.6
• /
• pp.35-46
• /
• 1999

The steel fiber reinforced concrete may affect substantially to the tension stiffening at post cracking behavior. Even if several tension stiffening models exist, they are for plain and normal strength concrete. Thus, the development of tension stiffening models for steel fibrous high strength RC members are necessary at this time when steel fiber reinforced and high strength concretes are common in use. This paper presents tension stiffening effects from experimental results on direct tension members with the main variables such as concrete strength, concrete cover depth, steel fiber quantity and aspect ratio. The comparison of existing models against experimental results indicated that linear reduced model closely estimated the test results at normal strength level but overestimated at high strength level. Discontinuity stress reduced model underestimated at both strength levels. These existing models were not valid enough in applying at steel fibrous high strength concrete because they couldn't consider the concrete strength nor section area. Thus, new tension stiffening models for high strength and steel fiber reinforced concrete were proposed from the analysis of experimental results, considering concrete strength, rebar diameter, concrete cover depth, and steel fiber reinforcement.

• Advances in concrete construction
• /
• v.9 no.2
• /
• pp.195-205
• /
• 2020

In this study, effect of recycled aggregates and polypropylene fibers on the response of conventionally reinforced concrete element subjected to tensile loading in terms of tension stiffening and strain development was experimentally investigated. For this purpose, concrete prisms of 100 × 100 mm cross section and 500 mm length having one central deformed steel re-bar were cast using fibrous and non-fibrous Recycled Aggregate Concrete (RAC) with varying percentages of recycled aggregates (0%, 25%, 50%, 75% and 100%) and tested under uniaxial tensile load. For all fibrous RAC mixes, polypropylene fibers were used at constant dosage of 3.15 kg/㎥. Effect of recycled aggregates and fibers on the compressive strength of concrete was also explored in this study. Through studying tensile load versus global axial deformation of composite and strain development in concrete and steel, it was found that replacement of natural aggregates with recycled aggregates in concrete negatively affected the cracking load, tension stiffening and strain development, and this negative effect was observed to be increased with increasing contents of recycled aggregates in concrete. The results of this study showed that it was possible to minimize the negative effect of recycled aggregates in concrete by the addition of polypropylene fibers. Reinforced concrete element constructed using concrete containing 50% recycled aggregates and polypropylene fibers exhibited cracking behavior, tension stiffening and strain development response almost similar to that of concrete element constructed using natural aggregate concrete without fiber.

• Proceedings of the Computational Structural Engineering Institute Conference
• /
• 2001.10a
• /
• pp.375-382
• /
• 2001

This study is attempted to predict experimentally the fatigue crack propagation behavior of two-span beams with steel fibrous for various steel fibrous contents. The static tests and the fatigue tests were performed on a series of SFRC(steel fibrous reinforced concrete) to investigate the fatigue behavior of SFRC varying with the steel fibrous contents. Through this test, the diagonal cracking loads, ultimate loads, deflections, strains of concrete and steels. Fatigue crack length were measured by the eye-observation. As a result of test, A model for S-N relationship, and propagation life of fatigue crack of SFRC was proposed. The crack growth and failure of SFRC beams were studied.

• Computers and Concrete
• /
• v.17 no.3
• /
• pp.323-336
• /
• 2016

Although the self-compacting concrete (SCC) offers several practical and economic benefits and quality improvement in concrete constructions, in comparison with conventionally vibrated concretes confronts with autogenously chemical and drying shrinkage which causes the formation of different cracks and creates different problems in concrete structures. Using different fibers in the mix design and implementation of fibrous concrete, the problem can be solved by connecting cracks and micro cracks together and postponing the propagation of them. In this study an experimental investigation using response surface methodology (RSM) based on full factorial design has been undertaken in order to model and evaluate the polypropylene fiber effect on the fibrous self-compacting concrete and curing time, fiber percentage and fiber amount have been considered as input variables. Compressive strength has been measured and calculated as the output response to achieve a mathematical relationship between input variables. To evaluate the proposed model analysis of variance at a confidence level of 95% has been applied and finally optimum compressive strength predicted. After analyzing the data, it was found that the presented mathematical model is in very good agreement with experimental results. The overall results of the experiments confirm the validity of the proposed model and this model can be used to predict the compressive strength of fibrous self-compacting concrete.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2000.10a
• /
• pp.601-608
• /
• 2000

Steel fiber and Polymer are used widely for the reinforcement material of RC structures because of its excellence of durability, serviceability as well as mechanical properties. Polymer-Steel fibrous high strength concrete beam's input ratio are 1.0%. The shear span-to-depth ratio are 1.5, 2.8 and 3.6, compressive strength of specimens 320kg/㎠, 436kgf/㎠ and 520kgf/㎠ in 28 days. The static test was carried out to measure the ultimate load, the initial load of flexural crack and of diagonal crack, from which crack patte군 and fracture modes are earned. Also, stress-strain, load-strain and load-deflection are examined during the test cracks(shear crack, flexural crack, and diagonal tension crack), when the load values are sketched according to the growth of crack. Result are as follows; (1) The failure modes of the specimens increase in rigidity and durability in accordance with the increase of mixing steel fiber and polymer. (2) The load of initial crack was the same as the theory of shear-crack strength (3) Polymer-Steel fibrous high strength concrete beams have increased the deflection and strain at failure load, improving the brittleness of the high strength concrete. (4) In this result of study, an additional study need to make a need formular because the study is different from ACI formular and Zsutty formular.