• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.3
• /
• pp.186-189
• /
• 2003

The role of excess Pb about the crystallization behavior and electrical properties in b(Zr$\sub$0.52/Ti$\sub$0.48/)O3(PZT) thin films has not been precisely defined. In this work, the effect of excess Pb content on the ferroelectric properties of these films was investigated. To analyze the effect, PZT films containing various amounts of excess Pb were Prepared. PZT thin films were deposited on the Pt/Ti bottom electrode by rf magnetron sputtering method and then they were crystallized by rapid thermal annealing (RTA). The experiment showed that all PZT films indicated perovskite polycrystalline structure with preferred orientation (111) and no pyrochlore phase was observed. As higher excess Pb was included, the films showed that value of leakage current shift from 2.03${\times}$10$\^$-6/ to 6.63 ${\times}$ 10$\^$-8/A/cm$^2$ at 100kV/cm, and value of remanent polarization shift from 8.587 ${\mu}$C /cm$^2$ to 4.256 ${\mu}$C/ cm$^2$. Electrical properties of PZT thin film affected by Pb excess content of target were explained to be caused of defect among space charges and defect grain boundaries.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.11a
• /
• pp.41-43
• /
• 1999

Among the feffoelectric thin films that have been widely investigated for ferroelectric random access memory (FRAM) applications, SrBi$_2$Ta$_2$$O_{9}$ thin film is appropriate to memory capacitor materials for its excellent fatigue endurance. However, very few studies on etch properties of SBT thin film have been reported although dry etching is an area that demands a great deal of attention in the very large scale integrations. In this study, the a SrBi$_2$Ta$_2$$O_{9}$ thin films were etched by using magnetically enhanced inductively coupled Ar/CHF$_3$ plasma. Etch properties, such as etch rate, selectivity, and etched profile, were measured according to gas mixing ratio of CHF$_3$(Ar$_{7}$+CHF$_3$) and the other process conditions were fixed at RF power of 600 W, dc bias voltage of 150 V, chamber pressure of 10 mTorr. Maximum etch rate of SBT thin films was 1750 A77in, under CHF$_3$(Ar+CHF$_3$) of 0.1. The selectivities of SBT to Pt and PR were 1.35 and 0.94 respectively. The chemical reaction of etched surface were investigated by X-ray photoelectron spectroscopy (XPS) analysis. The Sr and Ta atoms of SBT film react with fluorine and then Sr-F and Ta-F were removed by the physical sputtering of Ar ion. The surface of etched SBT film with CHF$_3$(Ar+CHF$_3$) of 0.1 was analyzed by secondary ion mass spectrometer (SIMS). Scanning electron microscopy (SEM) was used for examination of etched profile of SBT film under CHF$_3$(Ar+CHF$_3$) of 0.1 was about 85˚.85˚.˚.

• Journal of the Korean Institute of Illuminating and Electrical Installation Engineers
• /
• v.17 no.3
• /
• pp.56-63
• /
• 2003

A silent type ozone generator using water surface has been studied and improved its ozone generation characteristics by installing dielectric heads in the just under the surface of the wale- At this time, different permittivitis of dielectric beads were used to change the discharge condition of water surface. The current-voltage characteristics and characteristics of ozone generation quantity of the test system were investigated and discharge photos of glass beads were observed The height of Taylor cone may be the cause of the discharge bridge to decrease the ozone generation on the discharge spacing. In this study, the hight of Taylor cone could be controlled greatly by installing dielectric beads just under the water surface. Therefore a higher ozone generation also could be obtained. As the permittivity of dielectric material increased. discharge starting voltage was advanced and maximum 110 ppmy of ozone was generated by using the ferroelectric ball.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1997.11a
• /
• pp.364-368
• /
• 1997

We have investigated Pt and RuO$_2$as a bottom electrode for a device application of PZT thin film. The bottom electrodes were prepared by using an RF magnetron sputtering method. We studied some of the property influencing factors such as substrate temperature, gas flow rate, and RF power. An oxygen partial pressure from 0 to 50% was investigated. The results show that only Ru metal was grown without supp1ying any O$_2$gas. Both Ru and RuO$_2$phases were formed for O$_2$partial pressure between 10∼40%. A Pure RuO$_2$ phase was obtained with O$_2$partial pressure of 50%. A substrate temperature from room temperature to 400$^{\circ}C$ was investigated with XRD for the film crystallinity examination. The substrate temperature influenced the surface morphology and the resistivity of Pt and RuO$_2$as well as the film crystal structure. From the various considerations, we recommend the substrate temperature of 300$^{\circ}C$ for the bottom electrode growth. Because PZT film growth on top of bottom electrode requires a temperature process higher than 500$^{\circ}C$, bottom electrode properties were investigated as a function of post anneal temperature. As post anneal temperature was increased, the resistivity of Pt and RuO$_2$was decreased. However, almost no change was observed in resistivity for an anneal temperature higher than 700$^{\circ}C$. From the studies on resistivity and surface morphology, we recommend a post anneal temperature less than 600$^{\circ}C$.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.104-107
• /
• 2001

The fabricated La-modified lead titanate (PLT) thin flirt without poling treatment was investigated for modulation frequency dependence of pyroelectric properties by the dynamic method. $Pb_{1-x}La_{x}Ti_{1-x/4}O_3$PLT (x=0.1) thin film having 10 mol% La content was deposited on a Pt/$TiO_{x}$/$SiO_2$/Si substrate by sol-gel method. The PLT(10) thin film exhibits a relatively excellent dielectric property. The pyroelectric coefficient (p) of the PLT(10) thin film is 6.6 x $10^{-9}$C/$\textrm{cm}^2$.K without frequency dependence. The figure of merits for the voltage responsivity and specific detectivity are 1.03${\times}$$10^{-11}$/C.cm/J and 1.46 x $10^{-9}$C.cm/J, respectively. The PLT(10) thin film has voltage responsivity ($R_{V}$) of 5.15 V/W at 8 Hz. Noise equivalent power (NEP) and specific detectivity (D＊) of the PLT(10) thin film are 9.93 x $10^{-8}$W/Hz$^{1/2}$ and 1.81 x $10^{6}$ cmHz$^{1/2}$/W at the same frequency of 100 Hz, respectively. The results means that PLT thin film having 10 mol % La content is suitable for the sensing materials of pyroelectric IR sensors.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.11a
• /
• pp.543-546
• /
• 2000

Ferroeleclric 0.05PZN-xPZT(90/10)-(0.95-x)PZT(10/90) (x=0.65, 0.85) specimens were fabricated by the mixed-oxide method and cold-pressing method using sol-gel derived PZT(90/10) and PZT(10/90) powders. All specimens show a uniform ferroelectric grain without the presence of the pyrocholre phase. Average grain size increased with an increase in sintering temperature, the value for the x=0.65 specimen sintered at 125$0^{\circ}C$ was 14.4$\mu$m. The dielectric constant and dielectric loss of the x=0.65 specimen sintered at 125$0^{\circ}C$ were 1247, 2.06%, respectively. All specimens showed fairly good temperature and frequency stability of dielectric constant with the range from -2$0^{\circ}C$ to 6$0^{\circ}C$ and 100Hz to 10MHz. The coercive field and the remanent polarization of x = 0.65 specimen sintered at 125$0^{\circ}C$ were 8.5 kV/cm and 13 $\mu$C/cm$^2$, respectively. The pyroelectric coefficient of the x=0.65 specimen sintered at 125$0^{\circ}C$ was 5.64$\times$10$^{-8}$ C/cm$^2$K, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05c
• /
• pp.116-119
• /
• 2003

Self-patterning of thin films using photosensitive sol solution has advantages such as simple manufacturing process compared to photoresist/dry etching process. In this study, ferroelectric $Sr_{0.9}Bi_{2.1}Ta_2O_9$(SBT) and $La_{0.5}Sr_{0.5}CoO_3$(LSCO)thin films have been prepared by spin coating method using photosensitive sol solution. $Sr(OC_2H5)_2$, $Bi(TMHD)_3$ and $Ta(OC_2H)_5)_5$ were used as starting materials for SBT solution and $La(OCH_2CH_2OCH_3)_3$, $Sr(OC_2H_5)_2$, $CO(OCH_2CH_2OCH_3)_2$ were used for LSCO solution. Solubility difference by UV irradiation on LSCO thin film allows to obtain a fine patterning due to M-O-M bond formation. The lowest resistivity($4{\times}10^{-3}{\Omega}cm$) of LSCO thin films was obtained by annealing at $740^{\circ}C$.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.7
• /
• pp.575-580
• /
• 2007

A 16 Mb 1T1C FeRAM device was integrated with BLT capacitors. But a lot of cells were failed randomly during the measuring the bit-line signal distribution of each cell. The reason was revealed that the grain size and orientation of the BLT thin film were severely non-uniform. And the grain size and orientation were severely affected by the process conditions of post heat treatment, especially nucleation step. The optimized annealing temperature at the nucleation step was $560^{\circ}C$. The microstructure of the BLT thin film was also varied by the annealing time at the step. The longer process time showed the finer grain size. Therefore, the uniformity of the grain size and orientation could be improved by changing the process conditions of the nucleation step. The FeRAM device without random bit-fail cell was successfully fabricated with the optimized BLT capacitor and the sensing margin in bit-line signal distribution of it was about 340 mV.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.346-347
• /
• 2006

기계적 품질계수(Qm)를 향상시키기 위해 $Y_2O_3$와 $MnO_2$를 첨가함에 따른 $SrBi_2Nb_2O_9$ 세라믹스의 강유전 특성을 알아보았다. 합성분말의 입도를 분석 한 결과 $SrBi_2Nb_2O_9$의 경우 781.27nm였고, $Y_2O_3$와 $MnO_2$를 첨가한 경우 각 각 830.4nm와 981.1nm로 particle size는 증가하였고, 소결 후 소결밀도는 차이가 거의 없었으며, grain size는 $SrBi_2Nb_2O_9$과 $Y_2O_3$를 첨가했을 경우 $1{\mu}m$이하이며 반면, $MnO_2$를 첨가하였을 때 결정립이 성장하여 $3{\sim}4{\mu}m$로 나타났다. 또한, 모두가 $450^{\circ}C$ 이상의 상전이온도를 갖았다.

• Proceedings of the Korean Magnestics Society Conference
• /
• 2011.06a
• /
• pp.7-8
• /
• 2011

Basically, the lattice mismatch between film and substrate can make those BiFeO3(BFO) films distorted with strain structure. BFO phase can be stabilized on LaAlO3(LAO) represents the example of a multiferroic with giant axial ratio. Its crystal structure is not strictly tetragonal, but tetragonal with a slight monoclinic distortion and related to the rotation of the oxygen octahedra. In this study, we show that phases with a tetragonal-like epitaxial BFO films can indeed be ferroelectric and also can be stabilized via epitaxial growth onto LAO. Recent reports on epitaxial BFO films show that the crystal structure changes from nearly rhombohedral ("R-like") to nearly tetragonal("T-like") at strains exceeding approximately -4.5%, with the "T-like" structure being characterized by a highly enhanced c/a ratio. While both the "R-like" and the "T-like" phases are monoclinic, our detailed x-ray diffraction results reveal asymmetry change from MA and MC type, respectively. By applying additional strain or by modifying the unit cell volume of the film by substituting Ba for Bi, the monoclinic distortion in the "T-like" MC phase is reduced, i.e. the system approaches a true tetragonal symmetry. There are two different M-H loops for $Bi_{1-x}Ba_xFeO_{3-{\delta}}$(BBFO) and BFO films on SrTiO3(STO) & LAO substrates. Along with the ferroelectric characterization, these magnetic data indicate that the BFO phase stabilized on LAO represents the first example of a multiferroic with giant axial ratio. However, there is a significant difference between this phase and other predicted ferroelectrics with a giant axial ratio: its crystal structure is not strictly tetragonal, but tetragonal with a slight monoclinic distortion. Therefore, in going from bulk to highly-strained films, a phase sequence of rhombohedral(R)-to-monoclinic ["R-like" MA-to-monoclinic, "T-like" MC-to-tetragonal (T)] is observed. This sequence is otherwise seen only near morphotropic phase boundaries in lead-based solid-solution perovskites (i.e. near a compositionally induced phase instability), where it can be controlled by electric field, temperature, or composition. Our results show that this evolution can occur in a lead-free, stoichiometric material and can be induced by stress alone. Those major results are summarized as follows ; 1) Ba-doping increases the unit cell volume, 2) BBFO on LAO can be fully strained up to x=0.08 as a strain limit (Fig. 1), 3) P(E) & M(H) properties can be tuned by the variation of composition, strain, and film thickness.