• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.357-360
• /
• 2000

Ferroelectric 0.05PZN-xPZT(90/10)-(0.95-x)PZT(10/90) (x=0.65, 0.85) specimens were fabricated by the mixed-oxide method and cold-pressing method using sol-gel derived PZT(90/10) and PZT(10/90) powders. All specimens show a uniform ferroelectric grain without the presence of the pyrocholre phase. Average grain size increased with an increase in sintering temperature, the value for the x=0.65 specimen sintered at 125$0^{\circ}C$ was 14.4${\mu}{\textrm}{m}$. The dielectric constant and dielectric loss of the x=0.65 specimen sintered at 125$0^{\circ}C$ were 1247, 2.05%, respectively. All specimens showed fairly good temperature and frequency stability of dielectric constant with the range from -2$0^{\circ}C$ to 6$0^{\circ}C$ and 100Hz to 10MHz. The coercive electric field and the remanent polarization of x = 0.65 specimen sintered at 125$0^{\circ}C$ were 8.5 kV/cm and 13 $\mu$C/cm$^2$, respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.12
• /
• pp.1108-1114
• /
• 1998

$BaTiO_3$ thin films preferred c-axis orientation for the potential application of ferroelectric memory devices were deposited on silicon substrates(100) by RF sputtering and annealed at 800 and 900[$^{\circ}C$] in air. The BT(100)/BT(110) peak ratio of the sputtered sample was decreased with post-annealing in air. According to increasing with annealing temperature and time, the peak ratio of BT(100)/BT(110) was decreased and the surface density of thin film was high. Dielectric characteristics of $BaTiO_3$ thin film was measured as a function of annealing temperature and frequency. The dielectric constants were increased with annealing and decreased with frequency by space charge polarization and dipole polarization below 600[kHz]. The remanent polarization and coercive field in P-E hysteresis loop of $BaTiO_3$thin film were increased with the annealing temperature in air. The remanent polarization and coercive filed annealed at 800[$^{\circ}C$] for 1hr were 1.2[$\mu$C/$cm^2$] and 200[kV/cm]

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.394-397
• /
• 2001

In this paper, in-situ deposited Ru/RuO$_2$ bottom electrodes have been investigated as new bottom electrodes for PZT thin film capacitor application. As a comparison, structural and electrical properties of PZT thin films on Pt/Ti and RuO$_2$ bottom electrodes are also investigated. The use of Ru/RuO$_2$ hybrid electrodes showed better electrical properties in compression with RuO$_2$ bottom electrode. With increasing Ru electrode thickness, the PZT thin films showed preferred orientation along the (110) direction and leakage current of PZT thin films were improved. The PZT thin films on Ru (100nm)/RuO$_2$ electrodes exhibited excellent ferroelectric properties such as remant polarization and coercive field of 7.2 C/$\textrm{cm}^2$ and 46.35 kV/cm, respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.5
• /
• pp.383-387
• /
• 2002

N-channel metal-ferroelectric-insulator-semiconductor field-effect-transistors (MFISFET's) by using $SrBi_2Ta_2O_9$/Silicon Nitride/Si (100) structure were fabricated. The fabricated devices exhibit comfortable memory windows, fast switching speeds, good fatigue resistances, and long retention times that are suitable for advanced ferroelectric memory applications. The estimated switching time and polarization ($2P_r$) of the fabricated FET measured at applied electric field of 376 kV/cm were less than 50 ns and about 1.5 uC/$\textrm{cm}^2$, respectively. The magnitude of on/off ratio indicating the stored information performance was maintained more than 3 orders until 3 days at room temperature. The $I_DV_G$ characteristics before and after being subjected to $10^11$ cycles of fatigue at a frequency of 1 MHz remained almost the same except a little distortion in off state.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05c
• /
• pp.190-193
• /
• 2003

Sm-doped lead zirconate titanate($Pb_{1.1}(Zr_{0.6}Ti_{0.4})O_3$; PZT) thin films on the Pt(111)/Ti/$SiO_2$/Si(100) substrates prepared by a sol-gel method. The effect on structural and electrical properties of PZT thin films measured according to the Sm content. Sm-doping altered significantly dielectric and ferroelectric properties. The remanent polarization and the coercive field decreased with the increasing Sm content. The dielectric constant and the dielectric loss of PZT thin films decreased with the increasing Sm content. At 100 kHz, the dielectric constant and the dielectric loss of. the 0.3 mol% of Sm-doped PZT thin film were 1200 and 0.12 respectively. The remanent polarization (2Pr) of the 0.3 mol% of Sm-doped PZT thin film was $52.13{\mu}C/cm^2$ and the coercive field was 94.01 kV/cm. The 0.3 mol% of Sm-doped PZT thin film showed an improved fatigue characteristic comparing to the undoped PZT thin film.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.302-302
• /
• 2007

The $SrRuO_3$/Si thin film electrodes are grown with (00l) preferred orientations on SrO buffered-Si (001) substrates by pulsed laser deposition. The optimum conditions of SrO buffer layers for $SrRuO_3$ preferred orientations are the deposition temperature of $700^{\circ}C$, deposition pressure of $1\;{\times}\;10^{-6}\;Torr$, and the thickness of 6 nm. The 100nm thick-$SrRuO_3$ bottom electrodes deposited above $650^{\circ}C$ on SrO buffered-Si (001) substrates have a rms roughness of approximately $5.0\;{\AA}$ and a resistivity of 1700 -cm, exhibiting a (00l) relationship. The 100nm thick-$Pb(Zr_{0.2}Ti_{0.8})O_3$ thin films deposited at $575^{\circ}C$ have a (00l) preferred orientation and exhibit $2P_r$ of $40\;C/cm^2$, $E_c$ of 100 kV/cm, and leakage current of about $1\;{\times}\;10^{-7}\;A/cm^2$ at 1V.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.202-203
• /
• 2007

Ferroelectric SBT($SrBi_2Ta_2O_9$) thin films were deposited on Pt/Ti/$SiO_2$/Si substrate using R.F. magnetron sputtering method. The ferroelectric and electric characteristics were investigated with various post-annealing of Pt at $200{\sim}600^{\circ}C$. Compared with SBT thin film which had not post-annealed, the electrical properties and crystallizations of the SBT thin films were relatively improved by the post-annealing of Pt bottom electrode. The crystallization were characterized by X-ray diffraction (XRD). The electrical properties characteristics were observed by HP 4192A and precision LC.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.71-74
• /
• 2000

Pt/Pb$TiO_3$/$SrTiO_3$/p-Si films were prepared by metallo-organic solution deposition(M0SD) method and investigated its structure and ferroelectric properties. Crystallinity of specimen as a funtions of post annealing temperature and the thickness of $SrTiO_3$(STO) buffer layer was studied using XRD and AFM. Based on C-V and P-E curve, $PbTiO_3$(PTO) capacitors showed good ferroelectric hysteresis arising from the polarization switching properties. When the thickness of ST0 buffer layer between PTO and Si substrate was 260 nrn and the post annealing temperature was $650^{\circ}C$, it was showed that production of the pyrochlore phase due to interdiffusion of Si into FTO was prevented. The dielectric constant of FTO thin films calculated from a maximum Cma in the accumulation region was 180 and the dielectric loss was 0.30 at 100 kHz frequency. The memory window in the C-V curve is 1.6V at a gate voltage of 5V.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.743-746
• /
• 2000

Metal-ferroelectric-insulator-semiconductor(MFIS) devices using Pt/$LiNbO_3$/Si structure were successfully fabricated. The dielectric constant of the AIN film calculated from the capacitance in the accumulation region in the capacitance-voltage(C-V) curve was about 8.2. The gate leakage current density of MIS devices using a aluminum electrode showed the least value of 1$\times$$1O^{-8}$A/$cm^2$ order at the electric field of 500kV/cm. The dielectric constant of $LiNbO_3$film on AIN/Si structure was about 23 derived from 1MHz capacitance-voltage (C-V) measurement and the resistivity of the film at the field of 500kV/cm was about 5.6$\times$ $1O^{13}$ $\Omega$.cm.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.11a
• /
• pp.25-28
• /
• 1999

Metal ferroelectric semiconductor Field Effect- Transistors(MFSFET) with various gate electrodes, that are aluminum, platinum and poly -Si, using LiNbO$_3$/Si(100) structures were fabricated and the properties of the FETs have been discussed. The drain current of the state of FET with Pt electrode was more than 3 orders of magnitude larger than the state current at the same gate voltage of 1.5 V, 7.rich means the memory operation of the MFSFET. A write voltage as low as about $\pm$4 V, which is applicable to low power integrated circuits, was used for polarization reversal. The retention properties of the FET using Al electrode were quite good up to about 10$^3$s and using Pt electrode remained almost the same value of its initial value over 2 days at room temperature.