• 한국기계가공학회지
• /
• 제9권1호
• /
• pp.25-34
• /
• 2010

Fretting damage reduces fatigue life of the material due to low amplitude cyclic sliding and changes in the contact surfaces of strongly connected machine and structures such as bolt, key, fixed rivet and connected shaft, which have relative slip of repeatedly very low frequency amplitude. In this study, the fretting fatigue behavior of 7050-T7451 aluminum alloys used mainly in aircraft and automobile industry were evaluated. The plain fatigue test and fretting fatigue test under cyclic bending load carried out commercial bending fatigue tester and specially devised equipments to cause fretting damage. From these experimental work, the following results obtained: (1) The plain fatigue limit for stress ratio R=-l was about 151MPa. (2) In case of fretting fatigue, fatigue limit for stress ratio R=-l about 72MPa, the fatigue limit for R=0 about 81MPa, and the fatigue limit for R=0.3 about 93MPa. (3) The fatigue limit reduction rates by the fretting damage were about 52%(R=-1), 46%(R=0) and 38%(R=0.3) respectively. (4) The fatigue limit reduction rate decreased with stress ratio increase. In fretting bending test, as stress ratio increased, occurrence of initial oblique crack by fretting decreased or phased out, so that fracture surfaces were formed by plain fatigue crack occurrence, and such tendency was notable as stress amplitude increased. (5) Tire tracks and rubbed scars were observed in the fracture surface and contacted surface.

• 산업기술연구
• /
• 제18권
• /
• pp.203-208
• /
• 1998

Fatigue tests were performed to examine the 4 parameter method for specimens prepared by various heat treatment which resulted in different mechanical properties. Obtained main results are as follows. (1) Samples treated by austempering did not show the expected improvement of fatigue limit although hardness and strength increased. This is attributed to the fact that defect sensitivities of materials increase as increasing of hardness and tensile strength, it is also shown that the graphites acting as stress concentration place become larger by austempering heat treatment than by normal annealing. (2) It is very reasonable to predict the fatigue limit of ductile irons with 4 parameter method based on ${\sigma}_{TS}$, $H_v$, ${\Delta}K_{th}$ and ${\sqrt{area}}_{max}$. (3) The half-austempering treatment appeared to be more useful than the full-austempering method to improve the fatigue limit in the spheroidal graphite cast iron with multi defective material.

• 국제강구조저널
• /
• 제18권4호
• /
• pp.1098-1106
• /
• 2018

The object of this study is to clarify fatigue limit and fatigue crack growth characteristic of SBHS700 base metal which is 780 MPa class steel. This study carried out the fatigue tests of SBHS700 base metal containing different defect size, and the fatigue limit was compared with that of the conventional steel. Test results indicate that the fatigue limit increased with decrease initial defect size, and can be precisely evaluated by using ${\sqrt{area}}$ parameter model. This paper also presents that crack growth characteristic was almost the same as that of the conventional steel from the observation of striations by using Scanning electron microscope and length of beach marks.

• Journal of Advanced Marine Engineering and Technology
• /
• 제32권6호
• /
• pp.834-840
• /
• 2008

We carried out fatigue testing with materials of aluminum alloyC7075-T6, 2024-T4) by rotary bending fatigue tester. We investigated fatigue limit, fatigue crack initiation, fatigue crack propagation behavior and possibility of fatigue life prediction to the different small circular hole defect. The summarized result are as follows; Fatigue limit of the smooth specimens were related tensile strength and yield strength. In case of more large applied stress and small circular hole crack defect, the fatigue crack was grown rapidly. The fatigue crack propagation behavior proceed at according to inclusion. Fatigue crack propagation ratio appeared instability and retardation phenomenon in the first half of fatigue life but appeared stability and replied in the latter half. On other hand, this experimental data of the materials are appeared fatigue life predictability.

• Steel and Composite Structures
• /
• 제46권6호
• /
• pp.745-757
• /
• 2023

In order to study the fatigue performance of the flat steel plate-lightweight aggregate concrete hollow composite bridge slab subjected to fatigue load, both static test on two specimens and fatigue test on six specimens were conducted. The effects of the arrangement of the steel pipes, the amplitude of the fatigue load and the upper limit as well as lower limit of fatigue load on failure performance were investigated. Besides, for specimens in fatigue test, strains of the concrete, residual deflection, bending stiffness, residual bearing capacity and dynamic response were analyzed. Test results showed that the specimens failed in the fracture of the bottom flat steel plate regardless of the arrangement of the steel pipes. Moreover, the fatigue loading cycles of composite slab were mainly controlled by the amplitude of the fatigue load, but the influences of upper limit and lower limit of fatigue load on fatigue life was slight. The fatigue life of the composite bridge slabs can be determined by the fatigue strength of bottom flat steel plate, which can be calculated by the method of allowable stress amplitude in steel structure design code.

• 대한기계학회논문집A
• /
• 제33권2호
• /
• pp.99-107
• /
• 2009

This study produced a design curve and fatigue limit for a variation in volume ratio and reduction ratio of TiNi/Al composites. In many cases, stress-life curve does not indicate fatigue limit, so it was presented by probabilistic-stress-life curve. Goodman diagram was used to analyze the fatigue strength of materials with a finite life determined by repeated load and the fatigue strength of endurance limit with an infinite life. The fatigue experiment was conducted using the scenk-type plane bending specimen in same shape. The result of the fatigue test, which had been conducted under consistent stress amplitude, was examined. (i) The optimal condition for TiNi/Al in accordance with hot pressing (ii) Impacts of fatigue limit caused by a variation in reduction ratio and volume ratio of TiNi/Al composites (iii) Probability distribution for fatigue limit of TiNi/Al2024 and TiNi/Al6061.

• 대한기계학회논문집A
• /
• 제33권10호
• /
• pp.1158-1162
• /
• 2009

Fatigue limit of the copper film coated by Sn was estimated using Goodman diagram and Gerber diagram. To obtain the high cycle fatigue life curve, S-N curve, of the film, the high cycle fatigue test was carried out by applying the constant amplitude load to the film specimen with three different stress ratio of 0.05, 0.3 and 0.5 and the frequency of 40 Hz at room temperature in air. The free-standing film specimen 15.26${\mu}m$ thick was fabricated by etching process. The fatigue limits and S-N curves at the respective stress ratios were determined from the experimental works. It was shown that the S-N curves were dependent on the stress ratio and the fatigue limit was increased with decreasing the stress ratio. The dependency of the fatigue behavior was presented in empirical relationship. Using these relationships, the fatigue limit was predicted.

• 한국산업융합학회 논문집
• /
• 제26권4_2호
• /
• pp.585-589
• /
• 2023

Unlike general carbon steel, stainless steel's mechanical properties change depending on the content of chromium and nickel. In this study, since stainless steel for high-temperature pressure container parts is used as shafts, the fatigue strength and fatigue limit of the materials were evaluated using a rotational bending fatigue test. Meanwhile, fatigue analysis was conducted under the same conditions as the specimen for structural analysis and fatigue analysis of stainless steel for high-temperature pressure container parts. Using the fatigue analysis results, we tried to derive the life of the material and the safety factor for each part. As a result of performing a fatigue test by processing a specimen for the fatigue test of A182 F6A stainless steel, the fatigue limit was 548 MPa. The ratio between the tensile strength and fatigue limit of the material was 0.545, representing 54.5% of the tensile strength.

• 대한기계학회논문집
• /
• 제8권2호
• /
• pp.141-144
• /
• 1984

본 연구에서는 완전 역 피로응력(completely reversed fatgue stress)를 받는 타원 노치에서 균열 발생과 전파에 대한 이론 임계 피로 한도를 응력 세기 계수 개념 을 도입하여 임의의 재질과 임으의 타원 노치 형상에 대해서 적용할 수 있도록 유도하 며 그 결과는 기존 이론보다 Frost의 실험치에 더 잘 일치함을 보이고자 한다.

• 한국산업융합학회 논문집
• /
• 제5권1호
• /
• pp.3-9
• /
• 2002

In the field of design of mechanical structure and expectation of life time, characteristic of fatigue limit comes out to he the most important problem. In this paper, in order to get fatigue limit, (I) investigate the aspects of economy, time and confidence comparing two methods: the method by fracture probability introducing statistical conception and the staircase method. And (II) examine the experience approaching fatigue limit and coaxing effect. The value of fatigue limit by staircase method in very effective in view of practical use, and coaxing comes out by the same material effect as restraining crack progress, not as strengthening the tip of crack alone.