Examination on Fatigue Limit and Crack Growth Characteristic of SBHS700 Base Metal

  • Ono, Yuki (Department of Civil Engineering, Gifu University) ;
  • Kinoshita, Koji (Department of Civil Engineering, Gifu University)
  • Received : 2017.12.20
  • Accepted : 2018.04.03
  • Published : 2018.11.30
⟨ Previous Next ⟩

Abstract

The object of this study is to clarify fatigue limit and fatigue crack growth characteristic of SBHS700 base metal which is 780 MPa class steel. This study carried out the fatigue tests of SBHS700 base metal containing different defect size, and the fatigue limit was compared with that of the conventional steel. Test results indicate that the fatigue limit increased with decrease initial defect size, and can be precisely evaluated by using ${\sqrt{area}}$ parameter model. This paper also presents that crack growth characteristic was almost the same as that of the conventional steel from the observation of striations by using Scanning electron microscope and length of beach marks.

Keywords

References

  1. Anami, K., Miki, C., Yamamoto, H., & Higuchi, Y. (2000). Fatigue strength of welded joint made of high strength steel and fatigue strength improvement. Journal of JSCE, 675/I-55, 251-260 (in Japanese).
  2. Gunther, H.-P. (Ed.). (2005). Use and application of high-performance steels for steel structures. In IABSE - AIPC - IVBH, structural engineering documents (Vol. 8).
  3. Hanji, T., & Anami, K. (2017). Influence of static strength of steels on fatigue strength improvement of welded joints by toe treatment. Journal of Structural Engineering, 63A, 646-658 (in Japanese).
  4. Hanji, T., Kazuo, T., Shuichi, O., & Danshita, Y. (2014). Fatigue strength of welded joints using steels for bridge high performance structures (SBHS). Steel Structural Engineering, 60A, 587-595 (in Japanese).
  5. Ishida, S., Tokumasu, M., Nakasa, K., & Ishihara, H. (1990). Evaluation of actual fatigue stress by using striation spacing and hardness. The Society of Materials Science, Japan, 39, 63-69 (in Japanese). https://doi.org/10.2472/jsms.39.63
  6. Japanese Society of Steel Construction. (2012). Fatigue design recommendations for steel structures. Gihodo (in Japanese).
  7. Kakiuchi, Y., Tanaka, M., Akiyama, E., & Kondou, T. (1983). An Interpretation of the Scatter in fatigue striation spacing for an aluminum alloy and a mild steel. Mechanical Engineers, 42, 3669-3678 (in Japanese).
  8. Konishi, T., Takahashi, K., & Miki, C. (2007). Application of high strength steel on steel bridge and its effects on weight reduction. Journal of JSCE, 654/I-52, 91-103 (in Japanese).
  9. Matsunaga, H., Murakami, Y., Kubota, M., & Lee, J. (2003). Fatigue strength of Ti-6Al-4 V alloys containing small artificial defects. Materials Science Research International, 9(4), 263-269.
  10. Miki, C., & Tai, M. (2013). Fatigue strength improvement of out-ofplane welded joints of steel girder under variable amplitude loading. Welding in the World, 57, 823-840. https://doi.org/10.1007/s40194-013-0076-9
  11. Mori, T., Shimanuki, H., & Tanaka, M. (2010). Influence of steel static strength on fatigue strength of web-gusset welded joints with UIT. Journal of the Japan Welding Society, 70(2), 210-220 (in Japanese).
  12. Murakami, Y. (1989). Effects of small defects and nonmetallic inclusions on the fatigue strength of metals. JSME International Journal, Series I, 32(2), 167-180.
  13. Murakami, Y. (1993). Metal fatigue: Effects of small defects and nonmetallic inclusions. Tokyo: YOKENDO Ltd (in Japanese).
  14. Murakami, Y., Machida, H., Susumu, M., & Takagi, T. (2017). A new quality control method based on statistics of extremes for preventing recalls for mass production products. The Japan Society of Mechanical Engineering, 83(853), 1-16 (in Japanese).
  15. Newman, J.C., Raju, I.S. (1984). Stress-intensity factor for cracks in three-dimensional finite bodies subjected to tension and bending loads. Nasa Technical Memorandum, TM-85793, 1-39.
  16. Ono, Y., & Kinoshita, K. (2017). Fatigue strength and crack growth characteristic of SBHS700 base metal. Proceedings of Constructional Steel, 25(93), 648-652 (in Japanese).
  17. Shimanuki, H. (2016). Factors affecting fatigue life extension by ultrasonic impact treatment in welded joints. Journal of Japan Welding Society, 85(2), 198-206 (in Japanese). https://doi.org/10.2207/jjws.85.198
  18. The Society of Materials Science Japan. (2000). Fractography: Fracture surface and fracture information analysis. Tokyo: Maruzen (in Japanese).

Cited by

  1. Fatigue failure analysis of ceramic tools in intermittent cutting harden steel based on experiments and finite element method vol.234, pp.4, 2018, https://doi.org/10.1177/0954405419883042