• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1999년도 학회창립 10주년 기념 1999년도 가을 학술발표회 논문집
• /
• pp.693-696
• /
• 1999

Reinforced concrete is, in general, known as high durability construction material under normal environments due to strong alkalinity of cement. It is , however, well known that moderate or minor cracks in reinforced concrete should be most serious causes to deteriorate the durability of RC structures. Furthermore, chloride contents penetrating through unexpected cracks in reinforced concrete bridges get to weaken corrosion resistance of reinforcement steel in concrete and than to accelerate the deterioration of concrete durability. The objective of this experimental research is 1) to evaluate the effect of various corrosion protection system for reinforced concrete specimens with moderate or minor cracks which are exposed to cyclic wet and dry seawater, and then 2) to develop effective corrosion protection system for reinforced concrete bridges under the exposure of various detrimental environments such as seawater, deicing and etc.

• Structural Engineering and Mechanics
• /
• 제75권4호
• /
• pp.455-464
• /
• 2020

Reinforcement corrosion is one of the major problems in the durability of reinforced concrete structures exposed to aggressive environments. Deterioration caused by reinforcement corrosion reduces the durability and the safety margin of concrete structures, causing excessive costs in managing these structures safely. This paper aims to investigate the effects of reinforcement corrosion on the load bearing capacity deterioration of the corroded reinforced concrete structures. A new analytical method is proposed to predict the crack growth of cover concrete and evaluate the residual strength of concrete structures with corroded reinforcement failing in bond. The structural performance indicators, such as concrete crack growth and flexural strength deterioration rate, are assumed to be a stochastic process for lifetime distribution modelling of structural performance deterioration over time during the life cycle. The Weibull life evolution model is employed for analysing lifetime reliability and estimating remaining useful life of the corroded concrete structures. The results for the worked example show that the proposed approach can provide a reliable method for lifetime performance assessment of the corroded reinforced concrete structures.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2006년도 춘계 학술발표회 논문집(II)
• /
• pp.597-600
• /
• 2006

In Marine Land underground reinforced concrete structures, such as electric box power structure, water and chloride ion penetrated into concrete through the cracks of concrete and its permeable property, cause the corrosion of reinforcing steel bar, which accelerates the expansive cracks and deterioration of concrete. The purpose of this paper is to evaluate on deterioration of durability concrete through instrumental analysis such as schmidt hammer and carbonation, chloride content. Under the reclaimed marine land, the main cause of deterioration of concrete structures is the steel corrosion due to the penetration of chlorides and the deterioration of outer concrete itself by chemical attack.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2006년도 춘계 학술발표회 논문집(II)
• /
• pp.457-460
• /
• 2006

There are many kind of materials decorating outward of building such as paint, tile, brick, wood, stone and so on. But it has been pointed out some problems because of the industrial pollutions and wastes. Color concrete is a method of expressing out surface of exposed concrete. Generally, color concrete is manufactured by adding pigment to concrete. In this paper we used cement paste as a preparation step to apply to concrete. Pigment was added to white cement for easy observance of color difference. And color change was measured by color reader. Finally, we can predict color difference according to amount of pigment. Also, we investigate the color concrete technology for Art type using developed color concrete.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2003년도 가을 학술발표회 논문집
• /
• pp.281-284
• /
• 2003

When concrete structures are exposed under marine condition for a long time, the steel in concrete is corroded due to the ingression of chlorides in the sea water. Because the damages of corrosion resulting from the chloride ion are very serious, many research have been performed. In this study, it was experimentally investigated that the mechanical and diffusion characteristics of concrete substituted with ordinary portland cement, silica fume and blast furnace slag to investigate the chloride ingress characteristics with concrete quality. Chloride diffusion coefficients in concrete shows increasing tendency as w/c ratio increase. Also test results indicate that blend of admixture become lower chloride diffusion coefficients in concrete as compared with normal concrete.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2003년도 가을 학술발표회 논문집
• /
• pp.527-532
• /
• 2003

When fresh concrete is exposed to sufficiently low temperature, the free water in the concrete is cooled below its freezing point and transforms into ice, which causes decrease in compressive strength of concrete. Of the many influencing factors on the loss of compressive strength, the age of concrete at the beginning of freezing, water-cement ratio, and cement-type are significantly important. The objective of this study is to examine how the these factors affect the compressive strength of concrete frozen at early ages. The results from the tests showed that as age at the beginning of freezing is delayed and water-cement ratio is low, the loss of compressive strength decreases. In addition, concrete made with high-early-strength cement is less susceptible to frost damage than concrete made with ordinary portland cement.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 2008년도 추계 학술발표회 제20권2호
• /
• pp.213-216
• /
• 2008

강관의 내부에 콘크리트를 충전한 구조인 콘크리트 충전 강관 구조(Concrete Filled Steel Tubular Structure, CFT 구조)는 강재와 콘크리트의 단점을 상호 보완하고 장점을 극대화 할 수 있다는 이점이 있다. 이와 같은 CFT 거더의 장점을 살리면서 CFT 거더보다 더 뛰어난 경제적, 구조적 효율성을 얻기 위해 기존의 CFT 구조에 아치 형식과 프리스트레스를 도입한 신형식 거더인 CFTA(Concrete-Filled and Tied Tubular Arch) 거더에 대한 연구가 현재 진행 중이다. CFTA 거더의 가장 큰 특징은 아치형상과 외부로 노출되어 있는 텐던인데 현재 연구과정에서 지적되고 있는 문제점 중의 하나는 외부로 노출된 텐던의 안전성에 관한 문제이다. 따라서 본 논문에서는 외부로 노출되어 있는 텐던에 대한 안전성 평가를 수행하였다. 또한, collision numerical simulation을 사용하여 동적 충돌에 대한 해석도 수행하였다. 모델의 해석을 위해 유한요소 해석 결과의 신뢰성이 높고, 타 연구에서도 많이 사용되고 있는 ABAQUS 6.5-1을 이용하였다.

• 한국화재소방학회논문지
• /
• 제18권3호
• /
• pp.51-56
• /
• 2004

철근콘크리트구조물에 화재가 발생하게 되면 콘크리트내의 시멘트 수화물과 골재의 상반된 거동으로 조직이 연화되며 열응력 등으로 균열이 발생하여 부분적 혹은 전체구조시스템에 심각한 영향을 끼칠 수 있는 손상이 발생하여, 철근 콘크리트 구조물의 내구성을 현저히 저하시키게 된다. 콘크리트의 화재피해 상황은 콘크리트에 사용된 혼화재료 및 골재 등 사용재료의 영향을 받게 되며 설계기준 강도에 따라 그 피해 상황 역시 다르게 나타나기 때문에 화재피해를 입은 콘크리트 구조물의 열화 진단은 화재에 의한 열화 메커니즘을 바탕으로 이루어져야 하며, 이를 위해서는 고온에 노출된 콘크리트의 공학적 특성에 관한 기초자료가 반드시 필요하다. 그러므로 본 연구에서는 설계기준 강도 및 사용재료에 따라 콘크리트를 제조 하여 고온환경에 노출시켜 폭열상태, 초음파속도, 압축강도 등을 측정하여 화재로 열화된 콘크리트 구조물의 재사용 여부 및 피해 등급 결정을 위한 정밀 진단과 보수ㆍ보강공법의 선정을 위한 기초 자료로 제시하고자 한다.

• 콘크리트학회논문집
• /
• 제15권4호
• /
• pp.606-614
• /
• 2003

본 연구는 서울시에 위치한 콘크리트 교량 바닥판의 제빙화학제로 인한 열화속도를 추정하기 위하여 제빙화학제 사용현황을 조사하고 실구조물 조사에 의한 표면 염소이온량 누적정도와 염소이온 확산계수의 확률 분포적 특성을 고려하여 국내 환경에 적합한 내구수명 예측을 수행하였다. 연구결과, 무작위성을 나타내는 표면 염소이온량과 염소이온 확산계수는 각각 규모매개변수 0.192, 29.828, 형상매개변수 7.899, 1.983을 갖는 gamma 분포가 형성되었다. 표면 염소이온량은 평균 1.5kg/㎥이며 약70%의 확률수준에서 1∼2kg/㎥까지 농축되었다. 본 연구결과를 종합하여 볼 때 콘크리트 교량 바닥판의 설계내구수명이 20년 이상이 되려면 필요한 피복두께는 최소 26mm 이상으로 시공되어야 하며 고내구성 콘크리트로 타설하여 염소이온 확산계수를 감소시키는 것이 유효할 것으로 판단된다.

• Computers and Concrete
• /
• 제19권5호
• /
• pp.545-553
• /
• 2017

In the authors' previous study, an axial force-flexural moment (P-M) interaction curve model was proposed to evaluate fire-resisting performances of reinforced concrete (RC) column members. The proposed method appeared to properly consider the axial and flexural strength degradations including the secondary moment effects in RC columns due to fire damage. However, the detailed P-M interaction curve model proposed in the authors' previous study requires somewhat complex computational procedures and iterative calculations, which makes it difficult to be used for practical design in its current form. Thus, the aim of this study was to develop a simplified P-M interaction curve model of RC columns exposed to fire considering the effects of fire damage on the material performances and magnitudes of secondary moments. The simplified P-M interaction model proposed in this study was verified using 66 column fire test results collected from literature, and the verification results showed that the proposed simplified method can provide an adequate analysis accuracy of the failure loads and fire-resisting times of the RC column specimens.