• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2002년도 Proceedings of the International Welding/Joining Conference-Korea
• /
• pp.688-693
• /
• 2002

Adhesive bonding is becoming one of the popular joining techniques in metal industries, since it has some advantages over other techniques such as welding and diffusion bonding, e.g., any dissimilar metals are easily adhesive-bonded together. In this study, the experiments were carried out in order to provide the statistical data with strength evaluation methods: tension, shear and four-point bending tests for thermoplastic epoxy resin based adhesive-bonded metal joints. We should certificate on the probability of the adhesive strength that has the tendency of brittle fracture, the adhesive bonding strength between metals with thermoplastic adhesive has the best probability at four-point bending test. The strength testing method that has higher probability is four-point bending test, shear test and tensile test in order.

• 한국가구학회지
• /
• 제11권1호
• /
• pp.25-29
• /
• 2000

This study was carried out to analyze the ultrasonic properties of sound board which was glued with various adhesives and to evaluate which adhesive is the best for the acoustic radiation of the musical instrument. The results are as follows: 1. Animal glue is the best adhesive for the sound board with respect to the acoustic radiation ratio of the musical instruments. Epoxy resin and polyvinyl acetate resin are the next group, urea formaldehyde resin and Hot melt are the third group, polychloroprene(CR) resin is the lowest. 2. Epoxy resin, animal glue and Titebond(PVA) give the highest shear strength and the highest wood failure relatively Hot melt and polychloroprene(CR) resin do not meet the standard because of low wood failure.

• 폴리머
• /
• 제34권1호
• /
• pp.52-57
• /
• 2010

고 신뢰도와 높은 물성을 갖는 이방성 전도성접착제(anisotropic conductive adhesive, ACA)용 레진 개발을 위하여, 환원특성을 갖는 카르복실산을 포함한 bisphenol F계열의 에폭시 레진에 저융점 솔더입자(low melting point alloys, LMPA)를 분산시켜 제조하였다. LMPA의 융점에서의 에폭시 레진의 경화특성 및 온도에 따른 유변학 특성을 동적 시차 주사 열량계(differential scanning calorimeter, DSC)와 레오미터(rheometer)로 측정하여 최적화된 ACA 접합 공정을 설계하였다. 접합 공정시 LMPA 표면에 생성되는 산화막을 제거하여 높은 전기전도도와 안정적인 전기적 특성을 얻을 수 있도록 세가지 종류의 카르복실산을 환원제로 사용하여 각각의 젖음(wetting) 특성을 확인하였다. 부틸 카르복실산은 $28^{\circ}$의 낮은 젖음각을 나타내었으나, 경화반응 중 다량의 기포가 발생하는 문제가 있었다. 그러나, 이관능성 카르복실산(1,3-bis(2-carboxypropyl)tetramethyl disaoxane(2-CTMS)) 및 1,3-bis(3-carboxypropyl)tetramethyl disiloxane(3-CTMS))의 경우, 기포의 발생 없이 각각 $18^{\circ}$와 $20.3^{\circ}$의 매우 우수한 젖음 특성을 보였다.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2019년도 추계 학술논문 발표대회
• /
• pp.62-63
• /
• 2019

Currently, polymer-based tile cement (Thin-bed method) and epoxy adhesive (Thick-bed method) are mainly used as tile adhesive for polishing and porcelain. In the case of epoxy adhesive, there is a low economic efficiency, there is a problem that the work efficiency is reduced by mixing the resin and the hardener. In particular, the epoxy contains a bisphenol A and amine component, there is a risk of workable disease when a worker is exposed to odor and harmful gases generated in the epoxy adhesive for a long time. Against this background, it is necessary to analyze the hazards of using epoxy adhesives indoors, and develop cementitious high performance tile adhesive products with significantly lower hazards than epoxy adhesives.

• 한국콘크리트학회:학술대회논문집
• /
• 한국콘크리트학회 1998년도 가을 학술발표회 논문집(I)
• /
• pp.145-150
• /
• 1998

This study deals with the effect on performance of epoxy resign mortar mixed special cement for surface control and maintenance of aging concrete construction. The test of main property of epoxy resign in this study are the evaluation on the adhesive strength between substrate and epoxy resign mortar under the environment of wet or concrete substrate surface. We gained the test results of good adhesive strength over 15 kgf/$\textrm{cm}^2$ under the wet and dry condition of concrete surface.

• 접착 및 계면
• /
• 제7권4호
• /
• pp.39-44
• /
• 2006

A new kind of silicone-epoxy composite is reported in this research. The silicone-epoxy resin was synthesized by the hydrosilylation of tetramethycyclotetrasiloxane and 4-vinyl-1-cyclohexene 1,2-epoxy with a high reaction yield. It was found that the obtained silicone-epoxy resin shows a high reactive activity to the aluminum complex-silanol catalyst. The resin could be cured under the catalysis of $(Al(acac)_3/Ph_2Si(OH)_2$ at a concentration below 0.1 wt% to give a hard cured resin showing excellent optical clarity, UV resistance and thermal stability. It was also found that the Si-H groups facilitated the curing reaction and the silicone-epoxy resin bearing Si-H group could be cured effectively even if $Ph_2Si(OH)_2h$ was absent. Moreover, the UV resistance and thermal stability were improved significantly by the introduction of Si-H groups. This is possibly due to the reductive property of Si-H groups which can annihilate radical and peroxide effectively. This kind of silicone-containing epoxy composite might have very promising applications as optical resin, optical adhesive and encapsulation materials for electronic devices.

• 접착 및 계면
• /
• 제21권2호
• /
• pp.65-70
• /
• 2020

각각의 다른 복합재료를 연결하는 데 주로 에폭시 접착제가 사용되고 있다. 에폭시 접착제 대표적인 열경화성 수지로서 에폭시와 경화제의 경화 반응을 통해 선형구조에서 3차원의 망상 구조로 변하게 되어 접착을 한다. 경화제의 종류에 따라 비율 및 경화 조건 등이 변하며, 이러한 조건에 따라 물성이 달라진다. 접착공정이 대형화 됨에 따라 접착제를 바르고 즉시 접착하지 못하기 때문에, 대기시간동안 습도 및 온도 등 외부환경에 영향을 받아 접착제의 접착력 저하로 이어지게 된다. 본 논문에서는 유리섬유강화 복합재료에 에폭시 접착제를 사용하여 접착하였고, 단일 랩 전단 시험을 통하여 가사시간에 따른 에폭시 접착제의 접착강도를 평가하였다. 가사시간에 따른 접착력 변화를 확인하기 위하여, 복합재료에 에폭시 접착제를 바르고 상온에서 각 시간에 따라 대기한 후 접착하였다. 단일 랩 전단 강도를 통하여 일정시간 이상 가사시간을 오래 둘 수록 접착강도가 감소한다는 것을 확인하였다. 습도조건에 따른 접착력 변화를 확인하기 위하여, 경화습도 조건을 항온항습기로 조절하여 경화 시켰고, 습도조건에 따른 접착 강도를 단일 랩 전단 시험을 통해 접착력을 평가하였다. 적은 양의 수분은 에폭시 접착제의 경화 반응을 가속시켜 접착 강도를 증가시켰으나, 일정 이상의 과도한 수분은 오히려 접착강도를 감소시킴을 확인하였다.

• 보존과학회지
• /
• 제27권1호
• /
• pp.115-121
• /
• 2011

석조 문화재의 복원을 위하여 우레탄 복원제를 제조하였다. 제조된 우레탄 복원제는 그간 석조 문화재 복원용 재료로 주로 사용해 왔던 에폭시계 복원제 정도의 강한 접착 강도와 인장 강도를 나타내고 있으며, 충진성, 수축성, 도색성 등의 물성 역시 에폭시계 복원제와 유사하게 제조되었다. 특히, 이 우레탄 복원제는 그간 가장 큰 문제점으로 대두되었던 에폭시계 복원제의 황변 현상과 비가역성 문제를 해결함으로서, 석조문화재의 복원의 항구성과 지속적인 안정성을 부여할 수 있을 것으로 보인다. 또 본 복원제를 메움제와 접착제로 직접 적용하여 사용하였으며, 이를 재 용해하여 복원에 사용된 우레탄을 제거할 수 있어 본 복원제의 가역성을 나타내었다. 이 복원제는 작업 환경에 따라 복원자가 가사 시간을 조정할 수 있도록 제조되어 사용의 편리성 또한 증진시켰다. 또 이 복원제는 강한 접착력과 인장 강도를 가지고 있어 석조문화재 이외의 도자기나 금속 문화재 등의 다양한 문화재의 메움제나 접착제로 사용이 가능할 것으로도 사료된다.

• Elastomers and Composites
• /
• 제26권3호
• /
• pp.193-201
• /
• 1991

Epoxy resin and CTBN(carboxyl terminated butadiene acrylonitrile) rubber were reacted at $150^{\circ}C$. Epoxy mixtures containing reactant in a ratio $0{\sim}75%(wt%)$ of total liquid component were with dicyandiamide(DICY) at $130{\sim}200^{\circ}C$. Cure, thermal and adhesive properties were investigated in relation to rubber content, cure temperature, hardner content and promoter content. $CTBN{\times}13$ showed better properties in miscibility, curing time and adhesive strength. 2PZ-CNS was more excellent in Tg, and melamine was in adhesive strength. Adhesive strength represented best at rubber content $12{\times}15%$.

• 접착 및 계면
• /
• 제16권1호
• /
• pp.22-28
• /
• 2015

본 연구에서는 수분산 폴리우레탄의 내가수분해성 및 접착력을 향상시키기 위하여 polyester polyol, epoxy resin, 4,4-dicyclohexylmethane diisocyanate ($H_{12}MDI$), dimethylol propionic acid (DMPA)를 사용하여 epoxy를 함유한 수분산 폴리우레탄을 합성하였다. 또한 합성된 수분산 폴리우레탄의 물성은 DSC, UTM, adhesion test 등을 통해 평가하였다. 합성된 수분산 폴리우레탄의 Tg는 $-50^{\circ}C$ 부근에서 나타났으며, epoxy resin의 함량이 증가함에 따라 Tg도 상승하는 결과를 나타내었다. Epoxy resin의 함량이 증가함에 따라 인장강도는 증가하였고, 신율은 감소하였다. 또한 접착력 및 내가수분해 접착력은 polyol : epoxy = 99 : 1에서 최고값을 나타내었다.