• Asian-Australasian Journal of Animal Sciences
• /
• v.25 no.2
• /
• pp.291-298
• /
• 2012

While attempting to develop low salt, low fat and high fibre chicken nuggets, the effect of partial (40%) common salt substitution and incorporation of chickpea hull flour (CHF) at three different levels viz., 5, 7.5 and 10% (Treatments) in pre-standardized low fat chicken nuggets (Control) were observed. Common salt replacement with salt substitute blend led to a significant decrease in pH, emulsion stability, moisture, ash, hardness, cohesiveness, gumminess and chewiness values while incorporation of CHF in low salt, low fat products resulted in decreased emulsion stability, cooking yield, moisture, protein, ash, color values, however dietary fibre and textural properties were increased (p<0.01). Lipid profile revealed a decrease in total cholesterol and glycolipid contents with the incorporation of CHF (p<0.01). All the sensory attributes except appearance and flavor, remained unaffected with salt replacement, while addition of CHF resulted in lower sensory scores (p<0.01). Among low salt, low fat chicken nuggets with CHF, incorporation CHF at 5% level was found optimum having sensory ratings close to very good. Thus most acceptable low salt, low fat and high fibre chicken nuggets could be developed by a salt replacement blend and addition of 5% CHF.

• Journal of the Korean Chemical Society
• /
• v.57 no.4
• /
• pp.439-446
• /
• 2013

Chitosan (CS) and hydroxypropylmethyl cellulose (HPMC) blend microspheres were prepared by water-in-oil emulsion technique and were loaded with an anti-cancer drug 5-fluorouracil (5-FU). CS-HPMC microspheres were characterized by Fourier transform infrared spectroscopy to confirm the cross-linking reaction. Scanning electron microscopy (SEM) was also used to assess the surface morphology of particles prepared. The quantity of release of 5-FU from the microspheres have been studied in terms of blend composition and amount of cross-linking agent. Differential scanning calorimetry and X-ray diffraction techniques indicated a uniform distribution of 5-FU particles in microspheres, whereas SEM suggested the spherical structure of the microspheres with slight rough surface. The in vitro drug release indicated that the particle size and release kinetics depend upon blend composition, amount of cross-linking agent used and amount of 5-FU present in the microspheres.

• Elastomers and Composites
• /
• v.54 no.2
• /
• pp.97-104
• /
• 2019

Emulsion styrene-butadiene rubber silica wet masterbatch (ESBR silica WMB) technology was studied to develop highly filled and highly dispersed silica compounds, involving the preparation of a composite by co-coagulating the modified silica and the rubber latex in a liquid phase. Previous studies have shown that when manufacturing ESBR silica WMB/Butadiene silica dry masterbatch (BR silica DMB) blend compounds, preparing BR silica dry masterbatch and mixing it with ESBR silica WMB gave excellent results. However, WMB still has the problem of lower crosslink density due to residual surfactants. Therefore, in this study, tetrabenzylthiuram disulfide (TBzTD) was added instead of diphenyl guanidine (DPG) in the ESBR silica WMB/BR silica DMB blend compounds and sulfur/CBS contents were increased to evaluate their cure characteristics, crosslink densities, mechanical properties, and dynamic viscoelastic properties. TBzTD was found to be more effective in increasing the crosslink density and to produce superior properties compared to DPG. In addition, with increasing sulfur/CBS contents, mechanical properties and rolling resistance were enhanced due to high crosslink density, but the abrasion resistance was not significantly changed because of the toughness.

• Polymer(Korea)
• /
• v.36 no.6
• /
• pp.727-732
• /
• 2012

Baroplastic poly(butyl acrylate) (PBA)/polystyrene (PS) blends were prepared by mixing PBA and PS emulsions synthesized by cationic and anionic surfactant, respectively. Interestingly, the heterocoagulation of nanoparticles have found to be affected strongly by emulsion concentration but the blends have been prepared with almost same compositions regardless of the amount of reactants. Utilizing this method, PBA/PS/Si hybrid nano-blends were prepared successfully via electrostatic attraction forces between PBA, PS and silica nanoparticles. The hybrid nano-blend having 2 or 5 wt% of silica was then processed to a semi-transparent film at $25^{\circ}C$ under 13.8 MPa for 10 min, which showed 3.0 MPa of tensile strength and 25 MPa of elastic modulus. Therefore, the heterocoagulation technique can be used for preparing baroplastics with uniform compositions of polymer and silica nanoparticles.

• Polymer(Korea)
• /
• v.35 no.6
• /
• pp.543-547
• /
• 2011

A study has been done to enhance the mechanical properties and processability of electrically conductive polyaniline(PANI) without the polymer's structural alternation. Functionalized acid doped PANI (PANI-DBSA) was prepared by an emulsion polymerization, and dodecylbenzenesulfonic acid (DBSA) played both roles of surfactant and dopant. Also, PANI-DBSA was solution cast blended with high impact polystyrene (HIPS) to produce PANI-DBSA/HIPS blend film. The structure and electrical properties of the conducting polymer blends were observed through UV-vis and FTIR/ATR spectroscopy. A study of the blend was carried by focusing on observation of mechanical and electrical properties based on dispersibility and changes in polymer morphology. The conductivity of the blends was increased by increasing the content of PANI-DBSA, and the sudden increase of conductivity to $3.5{\times}10^{-4}$ S/cm was observed even under a low content of 9 wt%. There was a strong association of continuous network formation with percolation and conductivity in the conducting polymer blends.

• Biotechnology and Bioprocess Engineering:BBE
• /
• v.6 no.6
• /
• pp.426-432
• /
• 2001

Perstractive fermentation is a good way to increase the productivity of bioreactors. Us-ing Propionibacteria as the model system, the feasibility of using supported emulsion liquid mem-brane(SELM) fro perstractive fermentation is assessed in this study. Five industrial solvents were considered as the solvent for perparing the SELM. The more polar a solvent, is the higher the par-tition coefficeint However, toxicity of a solvent also increases with its polarity. CO-1055(indus-trial decanol/octanol blend)has the highest partition coefficient toward propionic acid among the solvents that has no molecular toxicity toward Propionibacteria, A preliminary extraction study was conducted using tetradecane as solvent in a hydrophobic hollow fiber contactor. The results confirmed that SELM eliminates the equilibrium limitation of conventional liquid-liquid extrac-tion and allows the use of a non-toxic solvent with low partition coefficient.

• Elastomers and Composites
• /
• v.33 no.5
• /
• pp.324-334
• /
• 1998

SBR, polyurethane, acryl and epoxy latex were seperately mixed with ethylene-vinylacetate emulsion(EVA) in the range of $0{\sim}50%$ (wt.% ). For the mixtures, the various physical properties were examined. The viscosity of mixtures was mainly influenced by compatability with EVA emulsion, was decreased within 20% (wt.% ) of latex content, and showed the similar values over 20% (wt.% ) of latex content. The workable time of cement mixtures was mainly depended on the reactivity with cement. The formation of film could be only within $30{\sim}40$ minutes from mixing cement. The tack-free time of mixtures was influenced by the sorts of resin and the quantity of cement. The slow order of tack-free time was epoxy mixtures>SBR mixtures>urethane mixtures>acryl mixtures. The pencil hardness of mixtures was $4B{\sim}2H$, represented higher value in cement mixtures than in emulsion state.

• Elastomers and Composites
• /
• v.33 no.4
• /
• pp.231-237
• /
• 1998

In order to investigate the physical properties of rubber blend compound, this experiment was carried out on the cure rate, loss tangent, reinforcement and abrasion properties of S-SBR (solution styrene-butadiene rubber) blends containing silane coupled silica and E-SBR (emulsion styrene-butadiene rubber) blends containing carbon black as a model compound. E-SBR blend showed the highest total bound rubber(TBR), while S-SBR blends showed constant TBR level regardless of rubber type. Rapid cure rate was achieved when the styrene and vinyl content of rubber microstructure decreased and TBR content of rubber compounds increased. The modulus as the index of rubber reinforcement showed the linear relation with TBR content. The large amount of PICO loss was observed when the styrene and vinyl content of rubber microstructure increased, while the small amount of PICO loss was observed when the ratio of bu-tadiene increased in the S-SBR blends with silane copuled silica. The high loss tangent at $0^{\circ}C$, the low loss tangent at $60^{\circ}C$, and the large difference of loss tangent were shown in the S-SBR blends with high styrene content compared to E-SBR blend.

• The Korean Journal of Rheology
• /
• v.9 no.4
• /
• pp.151-162
• /
• 1997

다층 구조를 갖는 고무/아크릴 충격보강제가 poly(methyl methacrylate) (PMMA)/ 충격보강제 블렌드의 몰폴로지와 유변학적 성질에 미치는 영향을 고찰하였다. TEM으로 측 정한 블렌드 내의 충격보강제 몰폴로지는 그 함량에 관계없이 균일한 크기의 구형을 이루는 것으로 나타났으며 파괴 단면의 SEM 측정으로부터 충격보강제와 매트릭스 수지와의 강한 결합력을 확인할수있었다. 블렌드의 유변물성 측정 실험에서는 충격보강제 함량이 복합 점 도에 크게 영향을 준 반면, capillary rheometer로부터 얻은 정상상태 점도에는 별 영향을 주지않음이 확인되었다. 특히 동적응력 실험의 고진동 주파수 영역에서는 일정 충격보강제 함량이상 일 때 충격보강제 자체의 점도와 근사해졌으며 이와같은 현상을 충격보강제의 shell 분자 상호간 또는 매트릭스 분자와의 엉킴에서 비롯되는 물리적인 상호 작용측면에서 설명해보았다. 또한 실험 결과를 Palierne[16]의 비상용성 블렌드계의 이멀젼 모델과 비교한 결과 상당한 차이를 확인할수 있었으며 이러한 차이는 위에서 언급한 shell 분자 상호간 또 는 매트릭스 분자와의 엉킴에 기인한다고 추정된다.

• Polymer(Korea)
• /
• v.37 no.6
• /
• pp.764-769
• /
• 2013

Starch was grafted by poly(methyl methacrylate) through the emulsion polymerization method. Modified starch/(acrylonitrile-butadiene rubber) (NBR) compounds were prepared by a latex blend method. The morphology, thermal properties and mechanical properties of the modified starch/carbon black/NBR composites were investigated with the change of starch concentration. The mechanical properties of the composites were improved by the addition of modified starch. But, when the concentration of modified starch was higher than 40 phr, the mechanical properties were deteriorated due to the poor dispersion of modified starch. At the same ratio of starch to carbon black, the composite showed a synergistic reinforcing effect by the good dispersion and high cross-linking density. In addition, the tensile strength, storage modulus, hardness, swelling and other properties were the best.