• Journal of the Korea Concrete Institute
• /
• v.16 no.5 s.83
• /
• pp.725-731
• /
• 2004

A field test program was conducted for the newly placed concrete pavement of US Interstate Highway 10 between March 26th and 28th, 2003. The test section was located between Van Horn and Sierra Blanca in Hudspeth County approximately 130 km east of El Paso, Texas. The main objective of the test was collecting moisture-related data to validate the models of effective curing thickness, evaporation rate, and moisture-based maturity. Effect of moisture loss on drying shrinkage strain was studied using additional test instrumentation.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2006.11a
• /
• pp.785-788
• /
• 2006

This paper investigates the temperature history of slab mock-up specimens with various surface curing sheets, in order to determine a favorable surface curing method in hot weather condition. Test showed that insulating double bubble sheets+aluminum foil simultaneously on the upper section of a specimen prevented an increase of sudden temperature and a decrease of vaporization when placed during the hot weather condition. It also secured the high strength in early age. Therefore it is found that using the double bubble sheets+aluminum foil on concrete surface declined the plastic and drying shrinkage and inclined the early strength, thus improving the concrete quality.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2006.11a
• /
• pp.87-90
• /
• 2006

This study investigates the temperature history of slab mock-up specimens for hot weather concreting applying various surface insulating methods, in order to improve concrete quality at hot weather condition. Test showed that the use of insulating blanket or a bubble sheet on upper section of slab prevented from abrupt increase of temperature and vaporization of moisture during early curing at hot weather circumstance. In addition, it secured higher strength at early age. Therefore it is concluded that concrete construction insulating with the bubble sheet will reduce the plastic and drying shrinkage as well as improve strength at early age, thus securing concrete duality.

• Journal of Institute of Control, Robotics and Systems
• /
• v.15 no.9
• /
• pp.877-880
• /
• 2009

A curing process in post-printing section of R2R process is required for an electrical property of the printed pattern when devices such as RFID, Solar cell are printed. PEN as well as heat-stabilized PET which is used as a plastic substrate would be deformed at high temperature due to change of its elastic modulus. And crack in the printed pattern, which is on the plastic substrate is occurred due to the deformation of the substrate. The occurrence of crack causes electrical resistance to increase and the quality of the device to deteriorate. In case of RFID antenna, the range of reading distance is shortened as the electrical resistance of the antenna is increased. Therefore, the deformation of the plastic substrate, which causes the occurrence of crack, should be minimized by setting up low operating tension in R2R process. In low tension, slippage between a moving substrate and a roller would be generated when the operating speed is increased. And scratch would be occurred when slippage is generated due to an air entrainment, which is related to the thickness of the air film. The thickness of the air film is increased when operating speed is increased as shown by simulation based on mathematical model. The occurrence of scratch in conductive pattern printed by roll to roll process is a critical damage because it causes degradation or failure of electrical property of it.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2006.11a
• /
• pp.5-8
• /
• 2006

This study investigates the field application, Songdo the # 1st WORLD, on zero-crack construction of the fundamental mass concrete using double bubble sheets and applying low heat mixture. Experimental results of hydration heat analysis showed that crack modulus of concrete incorporating 20% of blast furnace slag cement was 1.0 in 120 hours, representing 50% probability of crack occurrence, thus requiring additional measures. As for a curing method, a specimen insulating two layers of vinyl chloride+double bubble sheets exhibited only $16.5^{\circ}C$ difference between upper and lower sections, and it also showed favorable workability as well as competitive economic side. Therefore it was determined to use it for curing method in this field. For the curing results of practical field, using 2 layers of vinyl chloride+double bubble sheets and applying low heat mixture on the fundamental mass concrete in 3A residential building exhibited less than only $15^{\circ}C$ difference between surface and center section of that in 5 days elapse and less than $20^{\circ}C$ in 9 days. This means that the crack by hydration heat was prevented, and other fields structures also resisted the plastic shrinkage by insulating the vinyl, sinking crack by second temping, even drying shrinkage by the mixture of low unit water. Therefore the crack on the placement has not been found so far, since the construction was started before 6 month.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2008.11a
• /
• pp.509-512
• /
• 2008

The lining concrete of water tunnel is a much capability to occur crack due to drying shrinkage and vibrator compaction etc. Because of crack of concrete induce structural problem and decrease durability of concrete, it is need to reduce crack of concrete. In this an Analytical study to analyze the effect of curing of concrete and compaction on the lining concrete. As the results, it was found that control of construction condition into curing of concrete and compaction improve on construction efficiency of the lining concrete.