• Korean Journal of Materials Research
• /
• v.27 no.3
• /
• pp.172-178
• /
• 2017

The aim of this study is to consider the effect hydrogen on dezincification behavior of Cu-Zn alloys. The investigations include microstructural observations with scanning electron microscope and chemical composition analysis with energy dispersive spectrometer. The dezincification layer was found to occur in high pressure hydrogen atmosphere, not in air atmosphere. In addition, the layers penetrated into the inner side along the grain boundaries in the case of hydrogen condition. The shape of the dezincification layers was porous because of Zn dissolution from the ${\alpha}$ or ${\beta}$ phase. In the case of stress corrosion cracks formed in the Cu-Zn microstructure, the dezincification phenomenon with porous voids was also accompanied by grain boundary cracking.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.39 no.4
• /
• pp.291-297
• /
• 2003

Al-brass is usually used as the tube material of vessel's heat exchanger for seawater cooling system because it has high thermal conductivity and good mechanical properties and high corrosion resistance due to cuprous oxide (Cu20) layer against seawater. However, Al-brass tubes of heat exchanger for vessel at the actual environment is reported that local corrosion such as stress corrosion cracking occurred by synergism effect between mechanical factor and corrosion environment In this paper, the effect of corrosion environment on the stress corrosion cracking of Al-brass in various NH4OH of 3.5% NaCl solution, under flow by constant displacement tester. Based on the test results, the behavior of polarization, stress corrosion crack propagation and dezincification phenomenon of Al-brass are investigated. The main results are as follows：(1) Increasing range of potential from open circuit potential to repassivation gets lower, as the contain rate of NH4OH gets higher. (2) As contain rate of NH4OH gets higher, SCC of Al-brass is become activation but the protection film(Cu20) of Al-brass is created in 3.5% NaCl solution. (3) According as content of NH4OH increases in 3.5% NaCl solution, the dezincifiction area is spread. It is concluded that dezincification occurred by localized preferential anodic dissolution at stress focusing region.

• Corrosion Science and Technology
• /
• v.2 no.3
• /
• pp.135-140
• /
• 2003

The effect of temperature on stress corrosion cracking o f Al-brass used in vessel heat exchanger tube was studied in 3.5% NaCI + 0.1% $NH_4OH$ solution. The SCC test using a CDT(constant displacement test) and the specimens using a SEN(single edge notched) specimens. For setting the environment similar to working environment of a heat exchanger, the specimens was immersed in solution and solution flow onto the specimens were performed. The results are as follows : The latent time of stress corrosion crack occurrence gets shorter, as the temperature gets higher. Dezincification phase showed around the crack occupy wider range, as the temperature gets higher. Zn composition falls under 4% at the dezincifiction area.

• Journal of Ocean Engineering and Technology
• /
• v.18 no.1
• /
• pp.69-74
• /
• 2004

In general, the protection method of Shell and Tube Type heat exchanger for a vessel has been applied as a sacrificial anode, which is attached at the inner side of the shell. However, this is an insufficient protection method for tube. Therefore, a more suitable method, such as the impressed current cathodic protection for tube protection, is required. Al-brass is the raw material of tubes for heat exchanger of a vessel where seawater is used for cooling the water. It has a high level of heat conductivity, excellent mechanical properties, and a high level of corrosion resistance, due to a cuprous oxide (Cu$_2$O) layer against th seawater. However, in actuality, it has been reported that Al-brass tubes for heat exchanger of a vessel can produce local corrosion, such as stress corrosion cracking (SCC). This paper studied the effect of impressed potential on the stress corrosion cracking of Al-brass for impressed current cathodic protection in 3.5% NaCl +0.1% NH$_4$OH solution, under flow by a constant displacement tester. Based on the test results, the latent time of SCC, stress corrosion crack propagation, and the dezincification phase of Al-brass are investigated.

• Journal of the Korean Institute of Gas
• /
• v.7 no.2 s.19
• /
• pp.22-32
• /
• 2003

Al-brass material is generally used at the state of plastic deformation, for example; bending, extension of bell mouth at shell and tube type heat exchanger. And SCC(stress corrosion cracking) of Al-brass material will be affected by residual stress as plastic deformation. SCC results from synergism between mechanical factor and corrosion environment. Mechanical factor is stress that directly relates with stress intensity factor at the crack tip. This paper was studied on the effect of stress on SCC of Al-brass tube under in $3.5\%$ NaCl. + $0.1\%\;NH_4OH$ solution by constant displacement tester. Increasing of acidified water flow into sea and speeds up corrosion rate of Al-brass which is used as a tube material of vessel heat exchanger by polluted coast seawater. The experimental results are as follow The latent time of SCC occurrence gets longer as the initial stress intensity factor($K_{Ii}$) gets lower The main crack was propagated as the initial stress intensity factor($K_{Ii}$) gets higher, and secondary cracks occurred by electro-chemical factor a(ter stage of released stress. Dezincification phase showed around the crack, and the range of dezincification gets wider as the initial stress intensity factor($K_{Ii}$) gets higher.

• Journal of Conservation Science
• /
• v.33 no.3
• /
• pp.167-179
• /
• 2017

In this study, Sangpyeontongbo excavated at Bigyeongdo, Seosan, were investigated to determine the components of the corrosion products that were formed while they were buried underwater in an anaerobic environment. The causes of corrosion product formation were also determined. Microstructure observation, element mapping, principle component analysis for each year, and the detection of corrosion products were carried out. Results indicate that the concretions of corrosion products on the surface are needle-, hexahedral-, and octahedral-shaped; Pb, Cu, and S were among the elements detected. The Cu-S layer was clearly verified using element mapping. An analysis of major elements for each layer showed that Cu, S, and Pb were present and that most Zn was eliminated. The corrosion products detected were $PbCO_3$ (concretion) and $Cu_{1.96}S$ (metal). Accordingly, the anaerobic corrosion properties of Sangpyeongtongbo are summarized as follows: dezincification, copper sulfide, and lead compound.

• Journal of the Korean Institute of Gas
• /
• v.8 no.1 s.22
• /
• pp.1-6
• /
• 2004

In general, inlet temperature of cooling sea water for steam turbine condenser is about $25^{\circ}C$ and outlet temperature is about $60^{\circ}C$. For oil cooler, outlet temperature is about $40^{\circ}C$. Therefore corrosion heavily depends on the temperature of the coolant of a heat exchanger system. It is necessary to set the temperature of the cooling water to have maximum heat transfer efficiency. This paper was studied on the effect of temperature on SCC of Al-brass which is used as a tube material of vessel heat exchanger in $3.5\%$ NaCl + $0.1\%\;NH_4OH$ solution under flow by constant displacement tester. Based on the test results, the behavior of polarization characteristic, stress corrosion crack popagation and dezincification characteristic of Al-brass was investigated.

• Journal of the Korean Society of Safety
• /
• v.19 no.2
• /
• pp.1-5
• /
• 2004

Al-brass is the raw material of mnufacturing tubes for heat exchanger of vessel where seawater is used to coolant because it has high level of heat coductivity and excellent mechanical properties and high level of corrosion resistance due to cuprous oxide($Cu_2O$) layer against seawater. However, damage of Al-brass tubes for heat exchanger of vessel is reported that local corrosion such as stress corrosion cracking occurred by synergism effect between mechanical factor and corrosion environment. In this study, to investigate on the effect of stress on the polarization characteristics of Al-brass. At the stress of 0% and 95% yield strength by constant displacement tester, in 3.5% NaCl + 0.1% $NH_4OH$ solution, the polarization tests were carried out. And thus open circuit potential, corrosion current density, anodic polarization, cyclic polarization and dezincification behavior of Al-brass are investigated.

• Resources Recycling
• /
• v.7 no.2
• /
• pp.23-30
• /
• 1998

Aiming to rccycle the valuable mrnpunenl such as iron oxiiles and carbon from blast turnace sludge, [he physlco-chemical property and classification charactei~stics by hydrocyclone wcie invcstigxted. Carbon in sludge wils analysed to bo cxated mostly in coarse particles of sludge as a form of graphite whereas zinc lnortly in fine particles as zinc sulfides. On thc contrxy, iron oxides wne proved to be in the form of hematite, magnetile without any segregations according to particlc sizes of sludge. From the results of classiIication test using hydmcyclane of 75 mm dm, the recovcry and dczincificatian rate of low zinc sludge wcrc in the range of 67.9-73.6%, and 72.7-86 8%, respectively.

• Corrosion Science and Technology
• /
• v.15 no.6
• /
• pp.311-313
• /
• 2016

The anodic dissolution behavior of copper and brass in an electrolyte solution of 0.5M NaCl containing 0.5 mM $NaHCO_3$ was investigated by electrochemical impedance spectroscopy. The Nyquist plots of the copper impedance described a small loop in the high-frequency range and a large locus in the low-frequency range. Additionally, the features of the impedance spectrum of the brass were similar to those of the copper. This indicates that the copper-enriched layer formed on the brass surface due to the selective dissolution of the zinc from the surface. In addition, the rest potential and the anodic polarization curve for each sample were measured in order to discuss the selective dissolution of the zinc from the brass surface.