• Restorative Dentistry and Endodontics
• /
• 제20권2호
• /
• pp.463-486
• /
• 1995

The effect of moistening and air-drying of acid-conditioned dentin before priming on the formation of resin-dentin hybrid zone was investigated, Freshly extracted human molars were used and divided at random into 5 groups, Groups 1 - 3 consisted of specimens conditioned with 10 % phosphoric acid for 20 seconds; Group 1 served as a control in which the conditioned dentin was simply blot-dried with a damp facial tissue; Group 2 was air dried for 30 seconds ; Group 3 was air dried for 30 seconds and immediately remoistened for 10 seconds with air-water syringe. and then the specimen was blot-dried with a damp facial tissue. Groups 4-5 were not acid conditioned ; In group 4, the smear layer on the dentin was blot dried before primer placement; Group 5 was air dried only for 30 seconds, The acetone-based primer and bonding agent of All Bond 2 (Bisco. Inc., USA) and composite resin (Z-100, 3M Dental products, USA) were applied for acid conditioned dentin and non-conditioned dentin. The morphologic ultrastructure of resin-dentin hybrid zone was examined by the use of SEM and TEM. and the existence of inorganic material and analysis of Ca/P weight-percent ratio in the resin-dentin hybrid zone were revealed by the EDAX, The results were as follows : 1. In the moistened specimens from acid-conditioned groups, the resin penetrated about 3-$4{\mu}m$ into dentin and the denatured collagen smear layer was not present at the surface. The resin tag was formed to a thickeness of 3-$4{\mu}m$ at the upper part of dentinal tubule and compactively connected to each other by means of many lateral branching. 2. In the air-dried specimens from acid-conditioned groups, the resin penetrated about 2.0-$2.5\;{\mu}m$ into dentin and an upper thin black layer to a thickness of 30-35nm was identified between adhesive resin and demineralized collagen layer. The resin tag to have a diameter of $2.5{\mu}m$ was formed at the upper part of dentinal tubule. However the funnel shape of the tag was not notable compared to the moistened specimens. 3. In the remoistened specimens from acid conditioned groups, the resin penetrated about 2.0-$2.5{\mu}m$ into dentin and an upper black layer was not present. The resin tag at the upper part of dentinal tubule was formed less than $2{\mu}m$ and was weakly connected to each other by means of few lateral branching. 4. In the non-conditioned groups, the smear layer was formed to a thickness of $0.5{\mu}m$ at dentin surface. However, the resin-dentin hybrid zone was not identified by TEM. The evidence of resin penetration into intertubular and intratubular dentin did not show. 5. All the acid-conditioned groups showed that the detected calcium and phosphorus weight percent ratios at the $2{\mu}m$ upper portion from the resin-dentin interface into the resin were much higher than that at the $2{\mu}m$ lower portion from the resin-dentin interface to dentin. (P<0.01).

• 보건행정학회지
• /
• 제17권3호
• /
• pp.1-25
• /
• 2007

Relative value scales introduced in 2001 remarkably improved health insurance fee schedule, but current relative value scales have many problems. In the beginning the government intended to introduce 'resource based relative value scales(RBRVSs)' like USA, but political adjustment of RBRVS studied in 19.17 weakened the relationship between relative value scale and resource consumption. So unbalance of health insurance fees are existing till now. Also relative value was not divided to physician work and practice expense, and malpractice fee was not divided separately. To correct the unbalance of current relative value scales, the refinement project of health insurance relative value scales started in 2003. The project team divided relative value scales into three components, which are physician work, practice expense, malpractice fee. Physician work was studied by professional organizations like Korean medical association. To develop the practice expense relative value, project team organized clinical practice expert panels(CPEPs) composed of physicians, nurses, and medical technicians. CPEPs constructed direct expense data like labor costs, material costs, equipment costs about each medical procedures. The practice expense relative values of medical procedures were developed by the allocation of the institution level direct & indirect costs according to CPEPs direct costs. Institution level direct & indirect costs were collected in 21 hospitals, 98 medical clinics, 53 dental clinics, 78 oriental clinics, and 46 pharmacies. The malpractice fee relative values were developed through the survey of malpractice related costs of hospitals, clinics, pharmacies. Putting together three components of relative values in one scale, the final relative values were made. The final relative values were calculated under budget neutrality by medical departments, that is, total relative value score of a department was same before and after the revision. but malpractice fee relative value scores were added to total scores of relative values. So total score of a department was increased by the malpractice fee relative value score of that department This project failed in making 'resource based' relative value scales in the true sense of the word, because the total relative value scores of medical departments were fixed. However the project team constructed the objective basis of relative value scale like physician's work, direct practice expense, malpractice fee. So step by step making process of the basis, the fixation of total scores by the departments will be resolved and the resource based relative value scale will be introduced in true sense.

• 한국식품과학회지
• /
• 제32권6호
• /
• pp.1358-1364
• /
• 2000

생산량이 풍부하고 가공성이 높지 않은 농산물인 무, 감자, 생강, 사과, 대추를 이용한 과채발효액을 제조하기 위하여, 박테리오신 생성 젖산균과 효모를 이용하여 발효를 순행하고, 발효액의 유기산 농도와 향기성분, 박테리오신의 생성 및 항균활성 등을 측정하여 저장성을 지닌 음료로서의 가능성을 검토하였다. 박테리오신 생성 젖산균인 Lc. lactis를 이용한 과채 젖산발효액의 pH는 4.07, 산도는 0.36%이며, lactic acid, citric acid, malic acid, succinic acid 등의 유기산을 함유하고 있으며, 박테리오신의 생성이 확인되었다. 발효중에 생성된 박테리오신의 항균역가는 냉장저장 중에도 매우 안정하였으며, Listeria monocytogenes와 Staphylococcus aureus, 그리고 충치 원인균인 Streptococcus mutans에 대한 저해효과가 있었다. 젖산발효액에 원료 혼합액에서 분리한 효모를 접종하여 후발효시킨 효모발효액에서는 일부 유기산의 소모로 인해 산도가 약간 감소하였으나, succinic acid의 함량은 1.5배정도 높아진 것으로 나타났다. 젖산발효액에서 검출된 ester의 종류는 불쾌하고 쓴맛을 내는 phthalate 종류가 많은 반면, 효모 접종구에서는 과일향을 내는 ester 종류가 많이 검출되었고, alcohol종류도 증가한 것으로 나타나 젖산발효액의 풍미개선에 기여한 것으로 판단된다.

• Restorative Dentistry and Endodontics
• /
• 제29권6호
• /
• pp.489-497
• /
• 2004

Objective: The purpose of this study was to investigate the viscoelastic properties related to handling characteristics of composite resins, Methods: A custom designed vertical oscillation rheometer (VOR) was used for rheological measurements of composites. The VOR consists of three parts: (1) a measuring unit, (2) a deformation induction unit and (3) a force detecting unit, Two medium viscous composites, Z100 and Z250 and two packable composites, P60 and SureFil were tested. The viscoelastic material function, including complex modulus $E^{*}$ and phase angle ${\delta}$, were measured. A dynamic oscillatory test was used to evaluate the storage modulus (E'), loss modulus (E") and loss tangent ($tan{\delta}$) of the composites as a function of frequency ($\omega$) from 0.1 to 20 Hz at $23^{\circ}C$. Results: The E' and E" increased with increasing frequency and showed differences in magnitude between brands. The $E^{*}s$ of composites at ${\omega}{\;}={\;}2{\;}Hz$, normalized to that of Z100, were 2.16 (Z250), 4,80 (P60) and 25.21 (SureFil). The magnitudes and patterns of the change of $tan{\delta}$ of composites with increasing frequency were significantly different between brands. The relationships between the complex modulus $E^{*}$, the phase angle ${\delta}$ and the frequency \omega were represented by frequency domain phasor form, $E^{*}{\;}(\omega){\;}={\;}E^{*}e^{i{\delta}}{\;}={\;}E^{*}{\angle}{\delta}$. Conclusions: The viscoelasticity of composites that influences handling characteristics is significant different between brands, The VOR is a relatively simple device for dynamic, mechanical analysis of high viscous dental composites. The locus of frequency domain phasor plots in a complex plane is a valuable method of representing the viscoelastic properties of composites.

• 한국콘텐츠학회논문지
• /
• 제19권4호
• /
• pp.359-367
• /
• 2019

본 연구는 치과용 수복재료의 연마유무에 따라 여러 가지 착색용액에서 색의 안정성을 보기 위해 유동성 레진, 하이브리드 레진, 컴포머, 레진강화형 글라스 아이오노머를 이용하여 평가하였다. 치과용 수복재료인 컴포짓트 레진을 테플론 몰드로 직경10 mm, 두께 2 mm 시편을 제작하였으며, 두 군으로 나누어 한 군은 연마지를 이용하여 20초간 연마하였고, 다른 한 군은 연마하지 않고 평가하였다. 실험 결과 기간과 재료별 착색시료 간에는 통계학적으로 유의한 차이가 있었다(p<0.05). 간장과 고추장에서는 레진 강화형 글라스 아이오노머 Fuji II LC와 하이브리드 레진 중 Prodigy에서 2일째 수용도 역치 이상의 색 변화가 나타났으며, 연마지를 사용한 군에서는 간장용액에서는 레진 강화형 글라스 아이오노머 Fuji II LC가 2일째에 색변화가 있었으며, 고추장용액에서는 유동성레진과 하이브리드 레진 중 Prodigy에서 7일째 색변화가 나타났다. 와인용액에서는 컴포머와 하이브리드 레진 중 Prodigy에서 2일째 색 변화가 나타났으며, 연마지를 사용한 군에서는 컴포머에서 2일째 수용도 역치 이상의 색 변화를 볼 수 있었다. 향후 레진 표면의 활택도에 따라 착색에 영향을 줄 수 있으므로 향후 다양한 연마방법을 통한 연구가 진행되어야 할 것으로 사료된다.

• 구강회복응용과학지
• /
• 제35권2호
• /
• pp.81-89
• /
• 2019

목적: 이 연구의 목적은 RMGIC에 레진 표면 코팅제를 적용하였을 때 용해도와 불소 유리량 간의 상관관계를 알아보는 것이다. 연구 재료 및 방법: 불소 유리량과 용해도 측정을 위해 표면 코팅제를 도포하지 않은 Fuji II $LC^{(R)}$, $Filtek^{TM}$ Z350XT와 G coat $plus^{TM}$를 도포한 Fuji II $LC^{(R)}$, $Permaseal^{(R)}$를 도포한 Fuji II $LC^{(R)}$를 준비하고 불소 유리량과 용해도를 측정하였다. 결과: 일간 불소 유리량은 표면 코팅제 간의 차이는 유의하지 않았다. 불소 누적 유리량은 56일에 RMGIC를 사용한 군에서 유의한 차이를 보였다(P < 0.05). 용해도 측정에서 표면 코팅제를 도포하지 않은 RMGIC가 다른 세 군에 비하여 7일 째에서만 유의한 차이를 보였다(P < 0.05). 결론: 표면 코팅제는 RMCIG에서 초기 용매에 의한 물성 저하를 막아 수복재 내부에 불소를 보존하며 추후 수복재의 불소의 방출과 저장에 대한 영향 또한 감소한다.

• 구강회복응용과학지
• /
• 제34권4호
• /
• pp.290-296
• /
• 2018

목적: 본 연구의 목적은 치아 스플린팅에 사용되는 레진계 재료들의 두께에 따른 중합 능력을 평가하는 것이다. 연구 재료 및 방법: 레진계 스플린팅 재료로 개발된 Light-Fix와 G-FIX, 수복용과 스플린트용으로 사용 가능한 고흐름성 복합레진인 G-aenial Universal Flo를 사용하여 직경 5 mm, 두께 2, 3, 4, 5 mm의 시편을 각각 10개씩(총 120개) 제작하였다. 비커스 경도 측정기를 이용하여 시편 상면과 하면의 미세경도값을 측정하였다. 각 두께에서 복합레진의 중합정도를 95% 유의수준에서 independent T-test를 이용하여 통계적으로 분석하였다. 결과: Light-Fix와 G-FIX는 두께에 상관없이 중합도의 차이를 보이지 않았다. G-aenial Universal Flo는 3 mm 두께부터 유의하게 낮은 중합도를 보였다. 결론: 스플린팅 전용 레진계 재료인 Light-Fix와 G-FIX는 5 mm 두께까지 적절한 광중합이 가능할 것으로 사료된다.

• 대한소아치과학회지
• /
• 제46권1호
• /
• pp.85-92
• /
• 2019

이 연구의 목적은 유치 줄기세포에 대해 다양한 Calcium silicate-based material (CSM)의 세포독성을 비교하고 평가하는 것이다. Retro $MTA^{(R)}$ (RM), $EZ-Seal^{TM}$ (EZ), ENDOCEM $Zr^{(R)}$ (EN)의 powder를 세포 배지를 이용하여 용출시키고 filtering 하였다. 유치 줄기세포가 다양한 농도의 용출액 하 배양되었다. MTS assay를 통해 CSM 용출액이 세포 증식에 미치는 영향을 분석하였고, Flow cytometry analysis를 통해 세포 표현형의 변화 여부를 관찰하였다. 10% 농도의 용출액에서 배양된 유치 줄기세포의 흡광도 값은 RM > EN > EZ 순이었다(p = 0.0439). 그러나 유치 줄기세포는 재료에 관계없이 간엽줄기세포의 표현형을 유지했다. 세 종류의 CSM이 줄기세포 marker를 변형시키진 않았지만, EZ가 RM과 EN보다 세포적합성이 낮음을 알 수 있었다.

• 구강회복응용과학지
• /
• 제37권4호
• /
• pp.232-243
• /
• 2021

목적: 다양한 3D 프린팅 의치상 레진과 여러 가지 의치 첨상 재료 간의 전단결합강도를 평가하여 기존의 열중합 의치상 레진과의 전단결합강도를 비교 평가하고자 하였다. 연구 재료 및 방법: 열중합레진(Vertex RS)과 3D프린팅 의치상 레진 두종(DENTCA Denture base II, NextDent^TM Base)을 사용하였다. 의치 첨상 재료로는 성분이 다른 총 4종(Tokuyama Rebase II fast, Kooliner, Denture Liner, Denture Liner, Lang Jet Denture Repair Kit)을 사용하여 12개의 군으로 분류하였다. ISO/TS 11405규격에 따라 접착을 시행하였다. 전단결합강도를 측정하였고, 이후 입체현미경과 주사전자현미경을 이용하여 접착 계면을 관찰하고 파절편의 분석을 통하여 파절 양상을 조사하였다. 결과: 3D 프린팅 의치상 레진 군에서 의치 첨상 재료와의 전단결합강도가 열중합레진 군에 비해 유의하게 낮은 전단결합강도 결과를 나타내었다(P < 0.05). Polymethyl methacrylate계열의 첨상재료의 경우, 의치상종류와 관계없이 높은 전단결합강도를 보였다. 파절 양상은 대부분의 군에서 접착성 파절이 나타났고 일부 군에서 응집성 파절과 혼합성 파절 양상이 나타났다. 결론: Polymethyl methacrylate를 주성분으로 하는 의치 첨상 재료가 실험에 사용된 모든 의치상 레진에서 다른 의치 첨상 재료와 비교하여 높은 전단 결합강도 값을 나타내었지만, 직접법으로 의치 첨상을 시행할 경우 단량체로 Isobutyl methacrylate 성분의 의치 첨상재료를 사용하는 것이 전단결합강도면에서 유리할 것으로 사료된다.

• 대한소아치과학회지
• /
• 제50권3호
• /
• pp.263-276
• /
• 2023

이 연구의 목적은 소아의 치근단 방사선 사진에서 인접면 우식증 객체 탐지 의 객체 탐지를 위해 YOLO (You Only Look Once)를 사용한 모델의 성능을 평가하는 것이다. M6 데이터베이스에서 학습자료군으로 2016개의 치근단 방사선 사진이 선택되었고 이 중 1143개는 한 명의 숙련된 치과의사가 주석 도구를 사용하여 인접면 우식증을 표시하였다. 표시한 주석을 데이터 세트로 변환한 후 단일 합성곱 신경망(CNN) 모델을 기반으로 하는 YOLO를 데이터 세트에 학습시켰다. 187개의 평가자료군에서 객체 탐지 모델 성능 평가를 위해 정확도, 재현율, 특이도, 정밀도, NPV, F1-score, PR 곡선 및 AP를 계산하였다. 결과로 정확도 0.95, 재현율 0.94, 특이도 0.97, 정밀도 0.82, NPV 0.96, F1-score 0.81, AP 0.83으로 인접면 우식증 탐지에 좋은 성능을 보였다. 이 모델은 치과의사에게 치근단 방사선 사진에서 인접면 우식증 병변을 객체 탐지하는 도구로 유용하게 사용될 수 있다.