• The Journal of Korean Academy of Prosthodontics
• /
• v.35 no.2
• /
• pp.277-295
• /
• 1997

After clinical adjustment of dental casting restoration, re-polishing procedure is recommanded because the smooth gold sureface is lost. But there is the possibility to get more loose contact than that intended by loss of gold alloy according to the kinds of polishing materials and polishing time. Therefore in this study I polished type II gold alloy with 390gm force, 20,000rpm speed, and 8 kinds of gold alloy polishing materials, fabricated by 4 companies and then measured the amount of loss of gold alloy with Surfcorder SEF-30D and observed alloy surfaces polished by 3 brown rubber points with SEM. The amount of loss of gold alloys polished with 8 kinds of polishing materials and the degree of smoothness of gold alloys according to polishing time and polishing materials were compared. The following results were obtained : 1. When the amount of loss of gold alloys polished with 3 kinds of brown rubber point was compared, Alphalex brown point had the most amount of alloy loss, followed in decreasing order by Shofu brown point and Eveflex brown point. There was statistically significant difference in the amount of alloy loss according to polishing materials. 2. When the amount of loss of gold alloys polished with 5 kinds of green rubber point was compared, Shofu green point had the most amount of alloy loss, followed in decreasing order by Alphaflex green point, Dedeco green clasp polisher, and Eveflex green point. There was statistically significant difference in the amount of alloy loss according to polishing materials except Alphaflex green point and Dedeco green clasp polisher. 3. When the amount of loss of gold alloys polished with all kinds of rubber point was compared, there was no significant difference in Eveflex brown point, Alphaflex green point, and Dedeco green clasp polisher. 4. When average amount of alloy loss per 1 revolution by polishing materials was compared, Alphalex brown point had the greatest value as $0.329{\mu}m$ and Shofu supergreen point had the lowest value as $0.022{\mu}m$. 5. When the degree of sureface smoothness of gold alloy polished with 3 kinds of brown rubber point was compared, In Alphalex brown point surface roughness was completely lost after 20 seconds polishing time, in Shofu brown point 30 seconds, in Eveflex brown point 40 seconds. But in every gold alloys fine scratch formed by rubber points was observed. Based on the results of this study, as rubber polishing materials used in polishing of dental casting restoration after clinical adjustment influenced on the tightness of occlusal or proximal contact, we should make dental casting restoration with minimum error through careful laboratory procedure and form very smooth surface of restoration with tripoli and rouge after use of silicone polishing materials.

• 대한치과보철학회:학술대회논문집
• /
• 2000.11a
• /
• pp.26-26
• /
• 2000

• Journal of Technologic Dentistry
• /
• v.26 no.1
• /
• pp.41-48
• /
• 2004

Ti-20%Zr(-5%Cr) alloys not containing harmful Al and V were newly designed in order to reveal their possibility for dental casting and melted in an arc melting and casting furnace under Ar atmosphere. The corrosion resistance was studied by anodic polarization test. From the observation of anodic polarization behavior, it was found that the corrosion resistance was markedly increased by the addition of Cr. The corrosion resistance of Ti-20%Zr-5%Cr alloy was superior to that in Ti-6%Al-4%V alloy but almost similar to that in CP Ti using in market place today.

• Journal of Technologic Dentistry
• /
• v.25 no.1
• /
• pp.81-87
• /
• 2003

Ti-20%Zr-X%Cr(X=0,5) based alloys not containing hamful Al and V were newly designed in order to reveal their possibility for dental casting alloys, and melted in argon-arc casting machine. The mechanical properties were evaluated by using universal testing machine. The tensile strength and %elongaton of the alloys markedly increased with Cr content. The Ti-20%Zr-5%Cr alloy showed a similar tendency with Ti-6%Al-4%V alloy in tensile strength, but surpassed in %elongation. From these results, it was concluded that new alloys for successful dental casting materials should be designed as Ti-Zr-Cr based alloys.

• Journal of Biomedical Engineering Research
• /
• v.17 no.2
• /
• pp.247-254
• /
• 1996

The relationship between the isothermal age-hardening behavior and the phase transformation in the commercial dental Au-Ag-Cu-Pd alloy was investigated Age-hardening was mostly attributed to the lattice distortions of the supersaturated w phase resulting from the transformation to the metastable phasel which were more distinct at lower aging temperature. The lattice distortions resulting from the transformation of the metastable phases to the equilibrium phases also made a contribution to the age-hardening.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.11a
• /
• pp.303-303
• /
• 2015

In order to investigate ion release and biocompatibility of Ti-6Al-4V dental alloy by electrochemical corrosion test and MTT assay, commercial Ti-6Al-4V alloy rod (99.99% Ti, USA, Co) were used in the study. The microstructure of the alloys was examined by optical microscopy (OM), Field emission scanning electron microscopy (FE-SEM), energy dispersive X-ray spectroscopy (EDS), X-ray diffraction (XRD), MTT assay, and corrosion test. From the polarization curves, very low current densities were obtained for Ti-6Al-4V alloys, indicating a formation of stable passive layer.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2015.05a
• /
• pp.107-107
• /
• 2015

In order to investigate electrochemical behavior and biocompatibility of Co-Cr dental alloy by electrochemical corrosion test and MTT assay, the xCo-25Cr-yW-zNi alloys were used in this study. Samples of Co-Cr-W-Ni alloys were manufactured using arc melting furnace. The microstructure of the alloys was examined by optical microscopy (OM), Field emission scanning electron microscopy (FE-SEM), energy dispersive X-ray spectroscopy (EDS), X-ray diffraction (XRD), MTT assay, and corrosion test. Corrosion resistance increased slightly as cobalt (Co) content increased. And bioactivity was concerned with nickel (Ni) and tungsten (W). Biocompatibility of Co-Cr alloy depended on Ni and W contents.

• The korean journal of orthodontics
• /
• v.43 no.3
• /
• pp.127-133
• /
• 2013

Objective: We aimed to investigate the effects of silanation time on the shear bond strength (SBS) of metal brackets on gold alloy in a silicoating procedure and compare the SBS of metal brackets on gold alloy and enamel. Methods: Type III gold alloy plates were sandblasted with 30-${\mu}m$ silicon dioxide. Excess particles were removed with gentle air after silica coating, and silane was applied. Maxillary central-incisor metal brackets were bonded to each conditioned alloy surface with a light curing resin adhesive for 1 s, 30 s, 60 s, or 120 s after applying silane. The brackets were also bonded to 36 upper central incisors with the same adhesive. All samples were cured for 40 s with a light emitting diode curing light. The SBS was tested after 1 h and after 24 h. The adhesive remnant index (ARI) of the samples was also compared. Results: The 60-s and 120-s silanation time groups showed a higher SBS than the other groups (p < 0.05). Samples tested after 24 h showed a significantly higher SBS than did the samples tested after 1 h (p < 0.05). The 1-s group showed higher ARI scores. The one-way analysis of variance and Student-Newman-Keuls test showed that the SBS values of the 60-s and 120-s silanation time groups were not significantly different from the SBS values of enamel. Conclusions: Adequate silanation time is required to produce sufficient bond strength during silicoating.

• The Journal of Korean Academy of Prosthodontics
• /
• v.38 no.2
• /
• pp.160-168
• /
• 2000

This study evaluated the effects of four adhesive metal primers on the shear bond strength of a heat curing denture base resin(Lucitone 199) to cobalt-chromium alloy(Biosil-f). The adhesive metal primers were Cesead Opaque Primer, Metal Primer, MR Bond, and Super-Bond liquid. The metal surface primed or nonprimed was filled with the heat-curing methyl methacrylate resin. The specimens were stored in water at $37^{\circ}C$ for 24 hours and the alternately immersed in water bath at $5^{\circ}C\;and\;55^{\circ}C$ for up to 2,000 thermal cycles. Shear bond strengths were measured using UTM at a crosshead speed of 0.5mm/min. Failure surface were examined under magnifying glasses. All the primers examined improved the shear bond strength between denture base resin and cobalt-chromium alloy compared with nonprimed specimens before thermal cycling. The bond strength of Cesead Opaque Primer was greatest. And after 2,000 thermal cycles, the bond strengths between resin and cobalt-chromium alloy were decreased but the difference between thermal cycling 0 and 2,000 at Cesead Opaque primer and Metal Primer were not significant. This study indicated that Cesead Opaque Primer & Metal Primer is effective primers to obtain higher bond strength between heat cured denture base resin and cobalt-chromium alloy.

• Journal of Technologic Dentistry
• /
• v.45 no.3
• /
• pp.67-73
• /
• 2023

Purpose: This in vitro study aimed to evaluate the clinical acceptability of precision of fit of the support thickness of Co-Cr alloy copings fabricated using selective laser melting (SLM). Methods: Thirty dental stone models of maxillary left molar abutments were manufactured, images were taken using a scanner, and a computer-aided design program was used to design the form of a conventional metal ceramic crown coping. Overall, 30 single copings were made from Co-Cr alloy using SLM and divided into three support radius groups (0.1, 0.25, and 0.35 mm) of 10 for each. Digitized data were superimposed with three-dimensional inspection software to quantitatively obtain the machinability of a ceramic crown coping, and visual differences were confirmed using a color map. The root mean square values of the ceramic crown coping group were statistically analyzed using one-way analysis of variance (α=0.05). Results: The precision of fit was superior with 0.25 mm compared with 0.1 mm and 0.35 mm, and the results exhibited significant differences (p<0.05). All specimens showed that various support thicknesses did not exceed the clinically permitted value of 120 ㎛, which mean that more than 0.1 mm and 0.35 mm of support radius for SLM was adequate. Conclusion: The support thickness of Co-Cr alloy restoration fabricated using SLM is shown to affect the adaptation.