• Journal of the Korea institute for structural maintenance and inspection
• /
• v.18 no.4
• /
• pp.22-32
• /
• 2014

Durability is one of the most important and attractive subjects in concrete research field because not only durability of concrete is reduced by various degradation factors but also its reduction adversely influences the structural performance and service life of concrete structure. For this reason, a considerable amount of papers associated with concrete durability have been published and those researches were mainly focused on the changes of intrinsic properties of concrete due to chemicophysical degradations. However, the relationship between durability of concrete and structural behavior of concrete member has not been well established yet. In this study, calcium leaching degradation, a cause of concrete strength reduction, was dealt with. The experiments of compressive and flexural behavior of degraded concrete member were performed to evaluate the characteristics of structural behavior according to degradation level. Finally, the results from the experiments were compared with those obtained from nonlinear FEM analysis. The results from this study clearly showed that leaching degradation leads to decrease in compressive strength and compressive behavior evolves from brittle to ductile failure pattern during the degradation process. Load capacity and flexible rigidity of the degraded RC member decreased when the degradation level increased, in compressive zone. Additionally, it was found that the values from nonlinear FEM analysis, CDP model in ABAQUS, coincided well with the experimental results.

• Journal of the Korea Concrete Institute
• /
• v.17 no.6 s.90
• /
• pp.923-930
• /
• 2005

This paper was to evaluate the high strength lightweight self-compacting concrete(HLSCC) manufactured by Nan-Su, which main factor, Packing Factor(PF) for mixing design, has been modified and improved. We have examined HLSCC performance at its fresh condition as well as its mechanical properties at the hardened condition. The evaluation of HLSCC fluidity has been conducted per the standard of second class rating of JSCE, by three categories of flowability(slump-flow), segregation resistance ability(time required to reach 500mm of slump-flow and time required to flow through V-funnel) and filling ability(U-box test) of fresh concrete. The compressive strength of HLSSC at 28 days has come out to more than 30MPa in all mixes. The relationship between the compressive strength-splitting tensile strength and compressive strength-modulus of elasticity of HLSSC were similar those of typical lightweight concrete. Compressive strength and dry density of HLSCC at 28 days from the multiple regression analysis resulted as $f_c=-0.16LC-0.008LS+50.05(R=0.83)\;and\;f_d=-3.598LC-2.244LS+2,310(R=0.99)$, respectively.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.4 no.4
• /
• pp.363-370
• /
• 2016

Lightweight geopolymers are more readily produced and give higher fire resistant performance than foam cement concrete. Lowering the density of solid geopolymers can be achieved by inducing chemical reactions that entrain gases to foam the geopolymer structure. This paper reports on the effects of adding different concentrations of aluminum powder on the properties of cellular structured geopolymers. The apparent density of lightweight geopolymers has a range from 0.7 to $1.2g/m^3$ with 0.025, 0.05 and 0.10 wt% of a foaming agent concentration, which corresponds to about 37~60 % of the apparent density, $1.96g/cm^3$, of solid geopolymers. The compressive strength of cellular structured geopolymers decreased to 6~18 % of the compressive strength, 45 MPa of solid geopolymers. The microstructure of geopolymers gel was equivalent for both solid and cellular structured geopolymers. The workability of geopolymers with polyprophylene fibers needs to be improved as in fiber-reinforced cement concrete. The lightweight geopolymers could be used as indoor wall tile or board due to fire resistance and incombustibility of geopolymers.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.25 no.2
• /
• pp.1-7
• /
• 2021

The concrete deck slab at the continuous span support of the steel box girder bridge is a structure that is combined with the upper flange. It is a structure that can cause tension cracks in the deck slab at the support causing problems such as durability degradation in long span bridges. This is because the tensile stress in the longitudinal direction of the slab exceeds the design tensile strength due to the effects of dead load and live load when applying a long span. Accordingly, it is necessary to control tensile cracking by adding a reinforcing bar in the axial direction to the slab at the support and to introduce additional compressive stress. To solve this problem, a structural system of a steel box girder bridge was proposed that introduces compressive stress as PS steel wire tension in the tensile stress section of the upper slab in the continuous support. The resulting structural performance was compared and verified through the finite element analysis and the steel wire tension test of the actual specimen. By introducing compressive stress that can control the tensile stress and cracking of the slab generated in the negative moment through the tension of the PS steel wire, it is possible to improve structural safety and strengthen durability compared to the existing steel box girder bridge.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.11 no.3
• /
• pp.244-250
• /
• 2023

In this paper, mortar mixed with tapioca starch was manufactured to evaluate the effect of tapioca starch on mortar, through evaluating the quality characteristics of mortar, the impact of tapioca starch on improving the performance and basic quality of mortar was examined. Tapioca starch tended to decrease flow by increasing the viscosity of the dough consistency of fresh mortar, which tended to reduce flow, and decreased by about 10 % as the tapioca starch mixing ratio increased by 0.025 %. In addition, the effect of tapioca starch on the compressive strength of mortar was at the same level regardless of the tapioca starch mixture at 28 days of age. However, at an early age of 3 days, the speed of compressive strength development was accelerated by mix ing tapioca starch. In addition, the effect of tapioca starch on the compressive strength of mortar was at the same level regardless of the tapioca starch mixture at 28 days of age. However, at an early age of 3 days, the speed of compressive strength development was accelerated by mixing tapioca starch. The speed of strength development improved by about 20 % when mixing 0.050 % tapioca starch. The adhesion strength improved by about 60 % when mixing 0.050 % tapioca starch, and the final shrinkage in length change decreased by 5 %.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.27 no.5
• /
• pp.23-29
• /
• 2023

The goal of this study is to evaluate the bursting characteristics and fire resistance performance of mixed cement concrete containing fibers at very high temperatures. For this purpose, FA-based, Slag-based, and each mix according to the amount of fiber mixed were heated to room temperature, 150℃, 300℃, 600℃, and 900℃, and then the burst shape, compressive strength, and elastic modulus were measured and evaluated. As a result of the experiment, it was found that relatively more surface damage occurred in FA-based specimens when heated at ultra-high temperatures than in slag-based specimens, and there was a difference between the mix without fibers and the mix with fibers when heated at ultra-high temperatures, that is, at 900℃. In the mix without fibers, a decrease in strength of more than 5% occurred. In addition, the elastic modulus also showed the same phenomenon as the compressive strength, and in particular, the decrease in elastic modulus was found to be greater than the amount of decrease in compressive strength. Meanwhile, estimation equations for compressive strength and elastic modulus according to heating temperature were statistically proposed.

• Journal of the Korea Institute of Building Construction
• /
• v.17 no.4
• /
• pp.341-348
• /
• 2017

The performance degradation of concrete pavement by winter deicer is very serious in Korea, and its maintenance and rehabilitation brings a high expense. Therefore, a suitable method for rehabilitation of such concrete pavement and repair material of proper performance are required. In this study, the properties of compressive strength, ability to resist chloride ion penetration, and properties of dry shrinkage of magnesium phosphate ceramics were assessed to evaluate its applicability as a repair material for concrete pavement in Korea. As a result, the mortar flow showed a normal level of 190 mm, but the viscosity was high and the self-flow ability was poor. The setting time was 12 minutes, leading very rapid-hardening, and thus a prompt work was required. The compressive strength of mortar was 38.4MPa in 2 hours, 73.8MPa in 24 hours, and 111.0MPa in 28 days, showing a significant level. As a result of the test to chloride ion penetration resistance, mortar showed 143 Coulombs, and concrete showed 172.6 Coulombs, which fell under very low level. The drying shrinkage of MPC concrete in 40 days was below $60{\times}10-6$, and comparing with normal cement concrete, it showed the level below 1/10 of other concrete to secure an excellent volume stability. As above, magnesium phosphate ceramics has excellent strength performance, chloride ion penetration resistance, and volume stability, and this in the future shall be used in construction under the consideration of working time or workability, requiring further improvement for such performance.

• Journal of the Korea Institute of Building Construction
• /
• v.14 no.6
• /
• pp.639-645
• /
• 2014

For the construction materials, concrete, as the most widely used material, is focused on its improvement of performance. Although concrete has many advantages of easiness of handling, economical benefits, and high compressive strength, low tensile strength, brittleness and drying shrinkage are reported as the drawbacks of concrete. Hence, to solve these drawbacks of concrete, many research has conducted especially using fiber-reinforced concrete technology. Especially, HPFRCC which has high volume of fiber reinforcement was suggested as a solution of these drawbacks of normal concrete with increased ductility while it has the possibility of workability loss with fiber clumping which can cause low performance of concrete. Therefore, in this paper, optimized fiber combination with either or both metal and organic fibers is suggested to provide better performance of HPFRCC in tensile strength and ductility. As the results of experiment, better workability was achieved with 1 % of single fiber rather than multiple fibers combinations, espeically, short steel fiber showed the best workability result. Furthermore, in the case of organic fibers which showed higher air content than steel fibers, higher compressive strength was achieved while lower tensile and flexural strength were shown.

• Journal of the Korea Concrete Institute
• /
• v.19 no.4
• /
• pp.393-399
• /
• 2007

Concrete bridge decks are directly exposed to the severe environmental conditions such as rain water and deicing chemicals resulting in the freeze-thaw action and the rebar corrosion during their service lift. These deteriorations of bridge decks shorten the service lift and consequently they are the major concerns of the maintenance. The high performance concrete (HPC) deck is proposed as the alternative to minimize the deterioration problems. To develop more durable concrete deck, the performance characteristic tests of HPC mixtures were carried out. In this study, 4 different concrete mixtures were used varying the mineral admixtures as the cement replacement; ordinary portland cement (OPC), 20% fly ash (FA),20% fly ash with 4% silica fume (FS), and 40% ground granulated blast-furnace slag (BS). The design compressive strengths of HPC specimens were 27 MPa and 35 MPa, respectively. The results showed that the compressive strength of concrete did not much affect the durability of concrete. HPC with fly ash and silica lune (FS) were turned out to have the good durability and crack resistance.

• Journal of the Korea Institute of Building Construction
• /
• v.17 no.5
• /
• pp.445-451
• /
• 2017

Because of the supply-demand problem of aggregate, recently, the construction sites using 100% crushed sand are increasing and the use of low quality aggregate such as farmland sand is increasing too. When the low quality aggregate is used, the various quality defect of concrete such as the strength reduction, the increase of shrinkage and bleeding can be occurred. Therefore, in this study, the performance improvement PC admixture was developed to minimize the quality defect of plain concrete of basement parking area, when the low quality aggregate was used at the plain concrete of basement parking area. The slump loss to elapsed time test, the compressive strength test, the bleeding test and the drying shrinkage test were carried out.