• Journal of the Korean Ceramic Society
• /
• v.38 no.12
• /
• pp.1104-1109
• /
• 2001

Samples with the nominal composition, B $i_{1.84}$P $b_{0.34}$S $r_{1.91}$C $a_{2.03}$C $u_{3.06}$ $O_{10+}$$\delta$/ high $T_{c}$ superconductors containing As as an additive were fabricated by a solid-state reaction method. Samples with Ag of 10wt%, 30 wt% and 50 wt% each were sintered at 86$0^{\circ}C$~875$^{\circ}C$ for 24 hours. The structural characteristics, critical temperature and grain size with respect to Ag contents were analyzed by XRD(X-ray Diffraction) and SEM(Scanning Electron Microscope), respectively. As Ag contents increased, XRD peaks of g in Bi-2223 phase superconductors intensified and the proportion of the phase transition from Bi-2223 to Bi-2212 was increased.increased.

• Progress in Superconductivity
• /
• v.7 no.1
• /
• pp.22-27
• /
• 2005

We have studied the standardization of critical temperature measurements by using an ac susceptometer. Wire forms of NbTi, $Nb_{3}Sn$, and Bi-2223 superconductors were prepared to measure the temperature dependences of the magnetization. In order to study the optimum ac magnetic field and frequency, various amplitudes from 2 Oe to 10 Oe with frequencies from 11.3 Hz to 1033 Hz were applied to three specimens. Analytical comparison of the magnetic curves with the resistive curves was accomplished to investigate validity of using the new method.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.52 no.6
• /
• pp.241-248
• /
• 2003

$Bi_{1.84}Pb_{0.34}Sr_{1.91}Ca_{2.03}Cu_{3.06}O_{10+\delta}$ high $T_{c}$ superconductors containing Ag as an additive were fabricated by a solid-state reaction method. The superconducting properties, such as the structural characteristics, the critical temperatures, the grain size and the image of mapping on the surface were investigated. Samples with Ag and Au of 50 wt% each were sintered at various temperature(820~$850^{\circ}C$). The structural characteristics, the microstructure of surface and the critical temperature with respect to the each samples were analyzed by XRD and SEM, EDS and four-prove methode respectively. The critical temperature showed the result which the Ag additive samples are higher than Au additive samples. The microstructure of the surface showed the tendency which the Ag additive samples become more minuteness than Au additive samples.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.280-281
• /
• 2005

We have studied the superconducting properties and flux pinning enhancement of $(Y_{0.5}Nd_{0.25}Sm_{0.25})_{1.8}Ba_{2.4}Cu_{3.4}O_y$ [(YNS)-1.8] composite oxides by melt growth process in air. A sample prepared by this method showed well-textured microstructure, and $(Y_{0.5}Nd_{0.25}Sm_{0.25})_2BaCuO_5$ [(YNS)211] nonsuperconducting particles were uniformly dispersed in large (YNS)123 superconducting matrix. The sample showed a sharp superconducting transition at 91 K. The magnetization measurements of the (YSN)-1.8 sample exhibited the enhanced flux pinning, compared with $YBa_2Cu_3O_y$ (Y-123) sample without Sm and Nd.

• Progress in Superconductivity and Cryogenics
• /
• v.5 no.3
• /
• pp.6-10
• /
• 2003

Silver nano-powder was added to Ma $B_2$ to make (Ag)$_{(x)wt.%}$(Mg $B_2$)$_{(l00-x)wt.%}$ (A $g_{x}$-Mg $B_2$) (10 $\leq$ x $\leq$ 50) composite superconductors to investigate the effect of the Ag nano-powder on the vortex pinning. Pellets made out of the mixed powder were put inside stainless steel tubes, which were sintered at 85$0^{\circ}C$ in Ar atmosphere. No impurity phase was identified for as-rolled samples. However, both the Mg $B_2$ and the A $g_{x}$-Mg $B_2$ composite pellets, when sintered, contain small amount of Mg $B_4$ and MgAg impurity phases. From the magnetization study, it was found that the flux pinning was improved in the high magnetic field region (> 3 T) only when 10w/o Ag was added to Mg $B_2$. The "two step" structures in ZFC M(T) curve gradually increased as the amount of Ag added increased. Pinning centers can be created by adding a suitable amount of Ag nano-powder which is not too large to increase the decoupling between the Mg $B_2$ grains.crease the decoupling between the Mg $B_2$ grains.

• Progress in Superconductivity
• /
• v.12 no.2
• /
• pp.82-87
• /
• 2011

We studied the trapped field properties of bulk Y-Ba-Cu-O superconductors by applying 3 T of the permanent or $Nb_3Ti$ superconducting magnet. The 28 mm circular type of YBCO bulk superconductor was prepared and then hole at the center of bulk, parallel to the c-axis, was mechanically drilled. Typical size of hole in YBCO bulk was 10 mm in diameter. In order to examine the trapped field variation in terms of different impregnated materials, a hole in YBCO bulk was filled with resin and indium respectively. The trapped field decay due to flux flow was determined in terms of time. Our preliminary result indicates the trapped field value measured on the YBCO without hole after 30 minute by applying 3 T, was 6,500 G, which is much higher than that, 4,500 G, measured on YBCO with hole. Also, we confirmed that the tendency of a trapped field decrement with time was almost the same regardless of the impregnated materials in YBCO.

• Korean Journal of Materials Research
• /
• v.4 no.1
• /
• pp.37-43
• /
• 1994

Y-Ra-Cu-0 oxide superconductors were fabricated by the sinter-forging method to make the critical current density improve through controlling of microstructure and crystal texture. The grain alignment of oxide superconductor was formed by the sinter-forging process and it's c-axis orientation was parallel to the press direction.The orientation factor of texture increased with sinking temperature and pressure, and also grain alignment was improved by the addition of Ag. As for the sinterforged Y-Ba-Cu-O/Ag sample, the $T_c$(on-set) was not almost varied with the sinter-forging temperature, but $T_c\;^{zero}$ decreased more or less at high sinter-forging temperatures. In addition, it was observed that added-Ag was mainly distributed along the grain boundar~es in the (123) matrix, resulting in the densification of microstructure. From these results, i t was thought that the improvement of $J_c$ over 2000A/$\textrm{cm}^2$ was attributed to the texture, densification of microstructure, and (123) grain growth due to the Ag addition.