• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1997.11a
• /
• pp.120-123
• /
• 1997

In this paper, we deal with the effect on magnetic properties when Nd is added to Sr ferrite bonded magnet. First, we choose SrO$_{n}$.Fe$_2$O$_3$(n=5.9), which is nonstoichiomatric composition, as specimen ferrite. Then, we add 5wt% polyvinyl alcohol and calcinate at 12$25^{\circ}C$ under $N_2$ environment for carbon coating on chemical compound specimen. After that we obtain 1.2${\mu}{\textrm}{m}$ single domain powder through grinding process for 18 hours. The single domain Sr ferrite Powder is well mixed with silage coupling and calcium stearate of 1wt% Then, it is kneaded by using polyamide12 as a binder and is pelleted. After adding Nd-Fe-B powder to the pelleted specimen, we injection-mould it under magnetic field by using anisotropic mould. Especially, when we add l3wt% Nd-Fe-B powder to the polyamide12, we obtain excellent magnetic propertiecs which are $_{B}$H$_{C}$=2.65KOe, Br=3.16KG and (BH)$_{max}$=2.61MGOeOeOeOeOe

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2001.11a
• /
• pp.56-56
• /
• 2001

Ni-W alloy deposit is one of the best alternatives to hard chromium plating because of its good mechanical properties (high hardness, high strength, and good wear resistance). Ni-W alloy is deposited from weakly acidic or alkaline electrolytic bath with nickel sulfate, sodium tungstate or APT, and some kinds of organic hydroxy-acid complex and ammonia salts. W content of the deposit can be changed from 0 to 5Owt% and the coating with high W content is more attracted. But, meanwhile, the deposited layers are always found high internal stress, which cause them to become brittle and to bond insufficiently with the substrate. On the second hand, as the W content is incresed, the current efficiency reduced, which results in large quantities of hydrogen evolution and then produces bubbles on surface and pitting appearance In this paper, the influence of some additives on Ni-W alloy electroplating was investigated by means of compositional analysis and SEM. The initial results showed that 2-butyne-1,4-diol was the best brightener for Ni-W plating process. It could brighten and level deposit, but decreased the cathodic current efficiency. Its optimum concentration range is from O.lgjL to 0.5gjL. Besides, three kinds of additives including 2-butyne-1,4-diol were examined with Dagguchi method.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2011.05a
• /
• pp.153-153
• /
• 2011

Ni $TiO_2$ nano composite coatings were fabricated by using pulse current electrodeposition technique at 100 Hz pulse frequency with a constant 50% pulse duty cycles and reference was taken with respect to the direct current electrodeposition. The properties of the composite coatings were investigated by using SEM, XRD, Wear test and Vicker's microhardness test. XRD patterns of pulse deposited composite coatings were found to be changed from preferred (100) orientation to the random mixed orientations. The results demonstrated that the Vickers microhardness of composite coatings under pulse condition was significantly improved than that of pure nickel coating as well as direct current electrodeposited Ni-$TiO_2$ composite coatings. Wear tracks have shown the less plastic deformation at pulse condition with reduced coefficient of friction. Nickel matrix grain size was also found to be lower in pulse plated composite coatings as compared to direct current electrodeposited composite coatings.

• Journal of Surface Science and Engineering
• /
• v.53 no.5
• /
• pp.201-206
• /
• 2020

A SiOxCy(-H) thin film was synthesized by atmospheric pressure dielectric barrier discharge(APDBD), and a SiO₂-like layer was formed on the surface of the film by oxidation treatment using oxygen plasma. Hexamethylcyclotrisiloxane was used as a precursor for the SiOxCy(-H) synthesis, and He gas was used for stabilizing APDBD. Oxygen permeability was evaluated by forming an oxidized SiOxCy(-H) thin film on a PET film. When the single-layer oxidized SiOxCy(-H) film was coated on the PET, the oxygen gas permeability decreased by 46% compared with bare PET. In case of three-layer oxidized SiOxCy(-H) film, the oxygen gas permeability decreased by 73%. The oxygen permeability was affected by the thickness of the SiO₂-like layer formed by oxidation treatment rather than the thickness of the SiOxCy(-H) film. The excellent corrosion resistance was demonstrated by coating an oxidized SiOxCy(-H) thin film on the silver-coated aluminum PCB for light emitting diode (LED).

• Proceedings of the KIEE Conference
• /
• 2005.07c
• /
• pp.1881-1883
• /
• 2005

In this study, PZT thin films were fabricated using sol-gel Processing onto $Si/SiO_2/Ti/Pt$ substrates. PZT sol with different Zr/Ti ratio(20/80, 30/70, 40/60, 52/48) were prepared, respectively. The films were fabricated by using the spin-coating method on substrates. The films were heat treated at $450^{\circ}C$, $650^{\circ}C$ by rapid thermal annealing(RTA). The preferred orientation of the PZT thin films were observed by X-ray diffraction(XRD), and Scanning electron microscopy(SEM). All of the resulting PZT thin films were crystallized with perovskite phase. The fine crystallinity of the films were fabricated. Also, we found that the ferroelectric properties from the dielectric constant of the PZT thin films were over 600 degrees, P-E hysteresis constant. And the leakage current densities of films were lower than $10^{-8}\;A/cm^2$. It is concluded that the PZT thin films by sol-gel process to be convinced of application for ferroelectric memory device.

• Proceedings of the KIEE Conference
• /
• 2003.07c
• /
• pp.1562-1564
• /
• 2003

In this study, PZT thin films were fabricated using sol-gel processing onto Si/$SiO_2$/Ti/Pt substrates. PZT sol with different Zr/Ti ratio(20/80, 30/70, 40/60, 52/48) were prepared, respectively. The films were fabricated by using the spin-coating method on substrates. The films were heat treated at $450^{\circ}C,\;650^{\circ}C$ by rapid thermal annealing(RTA). The preferred orientation of the PZT thin films were observed by X-ray diffraction(XRD), and Scanning electron microscopy(SEM). All of the resulting PZT thin films were crystallized with perovskite phase. The fine crystallinity of the films were fabricated. Also, we found that the ferroelectric properties from the dielectric constant of the PZT thin films were over 600 degrees, P-E hysteresis constant. And the leakage current densities of films were lower than $10^{-8}A/cm^2$. It is concluded that the PZT thin films by sol-gel process to be convinced of application for ferroelectric memory device.

• Proceedings of the KIEE Conference
• /
• 2003.07c
• /
• pp.1580-1582
• /
• 2003

Transformation of molecular film occurs only usually in air-water interface, 2 dimensions domain's growth and crash are achieved. Organic thin film that consist of growth of domain can understand correct special quality of accumulation film supplying information about fine structure and properties of matter of device observing information and so on that is surface forward player and optic enemy using AFM one of SPM application by nano electronics. In this paper Langmuir (L) that is one of basis technology to manufacture of organic matter device using Biology material PBDG that is kind of polypeptide that have Biology adaptedness. Detected of accumulation condition in observing Surface Pressure change by stimulus reaction of Langmuir (L) and Spin-Coating film. Therefore AFM by this confirm and compared.

• Journal of the Korea Furniture Society
• /
• v.23 no.4
• /
• pp.407-414
• /
• 2012

In order to develop the end use of cylindrical laminated veneer lumber (LVL) such as wooden crafts, the light resistance properties of natural dye-colored and finished cylindrical LVL was investigated. The study results were as follows; The cross section of LVL showed the higher light resistance than its tangential section, and the light resistance also increased with surface coated. On the other hand, LVL specimen were colored by 9 natural dyes of amur cork-tree etc., and the natural and apparent hue harmonized with wood was found after coating and light resistance test. Particularly, The dyes extracted from amur cork-tree, persimon and sappan wood showed orange color, reddish brown and red color respectively, giving an accenting effect to original wood color.

• Journal of Korea Foundry Society
• /
• v.22 no.3
• /
• pp.114-120
• /
• 2002

A new titanium based alloy, Ti-10Ta-10Nb, has designed to examine the improved mechanical properties and biocompatibility. A specimen of titanium alloy was melted in a consumable vacuum arc furnace and homogenized at $1050^{\circ}C$ for 24 h. The effect of hot rolling on microstructure was estimated after rolling at $400^{\circ}C$ and $800^{\circ}C$ respectively. Surface of melted alloy by consumable vacuum arc melting was consisted of rough surface and it was changed to sound surface by coating of $ZrO_2$ slurry on copper mold surface. The hardness of Ti-10Ta-10Nb alloy increased with the amount of${\alpha}+{\beta}$ phase. Ti-10Ta-10Nb alloy showed $Widmanst{\"{a}}ten$ structure by hot rolling at $800^{\circ}C$ and in the rolling ${\beta}-region$ was negligible effects on microstructure refining.

• Restorative Dentistry and Endodontics
• /
• v.42 no.1
• /
• pp.39-47
• /
• 2017

Objectives: Although the coating of surface sealants to dental composite resin may potentially reduce bacterial adhesion, there seems to be little information regarding this issue. This preliminary in vitro study investigated the adhesion of Streptococcus mutans (S. mutans) on the dental composite resins coated with three commercial surface sealants. Materials and Methods: Composite resin (Filtek Z250) discs (8 mm in diameter, 1 mm in thickness) were fabricated in a mold covered with a Mylar strip (control). In group PoGo, the surfaces were polished with PoGo. In groups PS, OG, and FP, the surfaces polished with PoGo were coated with the corresponding surface sealants (PermaSeal, PS; OptiGuard, OG; Fortify Plus, FP). The surfaces of the materials and S. mutans cells were characterized by various methods. S. mutans adhesion to the surfaces was quantitatively evaluated using flow cytometry (n = 9). Results: Group OG achieved the lowest water contact angle among all groups tested (p < 0.001). The cell surface of S. mutans tested showed hydrophobic characteristics. Group PoGo exhibited the greatest bacterial adhesion among all groups tested (p < 0.001). The sealant-coated groups showed statistically similar (groups PS and FP, p > 0.05) or significantly lower (group OG, p < 0.001) bacterial adhesion when compared with the control group. Conclusions: The application of the surface sealants significantly reduced S. mutans adhesion to the composite resin polished with the PoGo.