• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.05a
• /
• pp.509-512
• /
• 1999

Ferroelectric Sr$_2$(Nb, Ta)$_2$O$_{7}$(SNTO), La$_2$Ti$_2$O$_{7}$(LTO) thin films were prepared by sol-gel processes. SNTO, LTO thin films were spin-coated on Pt/TiO$_2$/SiO$_2$/Si(100). Pt/Ti/SiO$_2$/Si(100). PT/ZrO$_2$/SiO$_2$/Si(100) substrates. After multiple coating, dried thin films were heat-treated for decomposition of residual organics and crystallization. Dielectric and other relevant electrical properties were measured and the results showed a little possibility in ferroelectric gate random access memory devices.ces.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.9
• /
• pp.762-767
• /
• 2001

We report the white light emission from the multilayer organic electroluminescent(EL) device using exciplex emission. The exciplex at 500nm originated between poly(N-vinylcarvazole)(PVK) and 2,5-bis(5'-tert-butyl-2-benzoxazoly)thiophene(BBOT) and exciplex of 50nm originated from N,N'-diphenyl-N,N'-(3-methyphenyl)-1,1'-biphenyl-4,4'-diamine(TPD) and BBOT were observed. Also, the energy transfer from PVK to BBOT and poly(3-hexylthiophene)(P3HT) in mixed emitting materials was occurred. The electroluminescence(EL) spectra of organic EL device which have a device structure of ITO/CuPc(5nm)/emitting layer(100nm)/BBOT(30nm)/LiF(1.4nm)/Al(200nm) were slightly changed as a function of the applied voltage. The luminance fo 12.3 ${\mu}$W/$\textrm{cm}^2$ was achieved at 20V and EL spectrum measured at 20V corresponds to Commission Internationale de L\`Eclairage(CIE) coordinates of x=0.29 and y=0.353.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1998.06a
• /
• pp.121-124
• /
• 1998

Generally the structure of powder electroluminescent devices (PELDs) on ITO-film was makeup of the ZnS:Cu phosphor layer and BaTiO$_3$ insulating layer. The active layer, which consists of a suitably doped ZnS powder mixed in a dielectric, is sandwiched between two electrodes; one of which are ITO film and the other is aluminum. In this paper, three kinds of powder eleotroluminescent devices (PELDs) : WK-A(ITO/BaTiO$_3$/ZnS:Cu/Silver paste). WK-B(ITO/BaTiO$_3$+ZnS:Cu/Silver paste) and WK-C(ITO/BaTiO$_3$/ZnS:Cu/BaTiO$_3$/Silver paste), fabricated by spin coating method, were investigated. To evaluate the luminescence properties of three kinds of PELDs, EL emission spectroscopy, transferred charge density and time response of EL emission intensity under square wave voltage driving were measured.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1999.05a
• /
• pp.681-684
• /
• 1999

N-methyl phenazinium 7, 7, 8, 8-tetra-cyanoquinonedimethane (TCNQ) complex salt was synthesized and bar-coated on PET film using various binders. Optical microscope and SEM reveals that TCNQ complex salt crystals were grown on the surface of binders and the shape was different with binders. The surface resistivity was 1$^{5}$ $\Omega$/$\square$ when binders has compatibility with TCNQ complex salt.

• Corrosion Science and Technology
• /
• v.10 no.2
• /
• pp.47-51
• /
• 2011

Main issues in the automotive industry are the reduction of vehicle body weight for energy savings and improvement of crashworthiness for passenger safety. In order to address both these issues, there has recently been increasing application of galvannealed advance high strength steel (GA AHSS) sheets for automobiles. However, GA AHSS sheets have some surface defects such as coating bare spots due to the addition of solid-solution strengthening elements, which result in the deterioration of the galvannealing reaction. In this study, the effects of galvannealed manufacturing conditions on surface and mechanical properties, resistance spot weldability on a laboratory scale, and GA 980 MPa steel sheets produced by commercial continuous galvannealing line (CGL) were investigated.

• Applied Science and Convergence Technology
• /
• v.23 no.5
• /
• pp.301-307
• /
• 2014

We have fabricated $SnO_2$/Zn core-shell nanowires by employing a sputtering technique with a Zn target. Scanning electron microscopy indicated that the surface of the nanowires became rougher by the coating. X-ray diffraction of the coated nanowires exhibited the hexagonal Zn diffraction peaks. TEM image of coated structures showed that shell layer was mainly comprised of hexagonal Zn phase. EDX spectra suggested that the shell layer consisted of Zn elements. The photoluminescence spectrum of the coated nanowires in conjunction with Gaussian fitting analysis revealed that the emission was disconvoluted with three Gaussian functions, which are centered at 2.1 eV in the yellow region, 2.4 eV in the green region, and 3.3 eV in the ultraviolet region. We speculated the possible mechanisms of these emission peaks.

• Korean Journal of Materials Research
• /
• v.25 no.10
• /
• pp.509-515
• /
• 2015

MAO ceramic coatings were prepared on AZ61 magnesium alloy for various processing times ranging from 5 to 60 min, in an electrolyte solution based on silicate-fluoride. The mechanical, electrochemical and, microstructural properties and the phase compositions of the coating layers were investigated. In this work, unlike previous studies, coatings with high amounts of the $Mag_2SiO_4$ phase were formed which contained small amounts of MgO and $MgF_2$ at a processing condition of 30 min. A microstructural analysis revealed that the porosity of the coatings was reduced considerably with an increase in the processing time, together with a change in the pore geometry from an irregular to a spherical shape. Potentiodynamic polarization and mechanical testing results showed that the coatings acquired after a processing time of 30 min were superior to all of the others.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2017.11a
• /
• pp.126-127
• /
• 2017

This study investigates the effect of improving the heat resistance performance when carbon fiber is mixed in the polyurea coating material. A tensile strength test method was carried out with the carbon fiber mixed polyurea specimens at an interval of 7, 14, and 21 days after heat treatment at 140±2℃. The test results showed that there was a significant decrease in the tensile strength performance. While the elongation and tensile performance decreased greatly, it was confirmed nevertheless the overall performance was maintained. This study proposes that mixing carbon fiber to the polyurea resin can effectively secure long-term heat resistance, thereby solving the problem of deterioration of physical properties caused by exposure to ultraviolet rays.

• Electrical & Electronic Materials
• /
• v.1 no.1
• /
• pp.26-34
• /
• 1988

Sintered CdS/CdTe solar cells have been farbricated by coating a (Cd+Te) slurry on sintered CdS films followed by the sintering at 625.deg.C for one hour with various heating rates. When cadmium and tellurinm powders are used instead of CdTe powder to form CdS/CdTe junction, CdTe is formed in the temperature range of 290.deg.C-400.deg.C. The microstructure of the CdTe films depends strongly on the heating rate of the sintering due to the low melting temperature and the high vapor pressure of the elemental Cd and Te. An optimum heating rate obtain CdTe films with uniform and dense microstructure which, in turn, improves the efficiency of the sintered CdS/CdTe solar cells. All-polycrystalline CdS/CdTe solar cells with an efficiency of 9.57% under 50mW/cm$^{2}$ tungsten light have been farbricated by using a heating rate of 14.deg.C/min.

• Electrical & Electronic Materials
• /
• v.10 no.6
• /
• pp.570-575
• /
• 1997

In this days, the thinner film of dielectric materials is required while its capacitance is required to be still large at the VLSI process. Most of such VLSI have MOS structures. For the research on this requirement, MOS capacitors were fabricated on the silicon wafer in four different thickness groups by RF sputtering method. SiO of the SiO/TiN film is used as the insulating layer and TiN is chosen as the barrier against the diffusion of Al which is the terminal connected by ohmic contact because TiN has the advantageous properties such as good thermal stability and very low diffusion rate in spite of its relatively low specific resistance. In this study their electrical and optical characteristics are investigated to find refractive index, absorption coefficient and Permittivity.