• Journal of Hydrogen and New Energy
• /
• v.24 no.1
• /
• pp.61-69
• /
• 2013

Polymer exchange membrane (PEM) fuel cells have multifunctional properties, and bipolar plates are one of the key components in these fuel cells. Generally, a bipolar plate has a gas flow path for hydrogen and oxygen liberated at the anode and cathode, respectively. In this study, the influence of iodine applied to a bipolar plate was investigated. Accordingly, we compared bipolar plates with and without iodine coating, and the performances of these plates were evaluated under operating conditions of $75^{\circ}C$ and 100% relative humidity. The membrane and platinum-carbon layer were affected by the iodine-coated bipolar plate. Bipolar plates coated with iodine and a membrane-electrode assembly (MEA) were investigated by electron probe microanalyzer (EPMA) and energy-dispersive x-ray spectroscopy (EDS) analysis. Polarization curves showed that the performance of a coated bipolar plate is approximately 19% higher than that of a plate without coating. Moreover, electrochemical impedance spectroscopy (EIS) analysis revealed that charge transfer resistance and membrane resistance decreased with the influence of the iodine charge transfer complex for fuel cells on the performance.

• Journal of Ocean Engineering and Technology
• /
• v.11 no.3
• /
• pp.56-68
• /
• 1997

This work was intended to study the effect of a partial pressure ratio and a total pressure of reactive gases on the properties of TiC$_{x}$N$_{1-x}$ . coated layer. In this regard, various TiC$_{x}$N$_{1-x}$ coatings were synthesized with C2112 and N2 Mixture gas of different compositions by Arc Ion Plating process which has been highlighted for an industrial purpose. It was revealed from colors and X-ray diffraction patterns that the concentration of carbon of a TiC$_{x}$N$_{1-x}$ coating increases with a partial pressure ratio (PC$_{2}$H$_{2}$/PN$_{2}$) as well as a total pressure Of $C_{2}$H$_{2}$ and N$_{2}$ mixture gas. Accordingly, the hardness of TiC$_{x}$N$_{1-x}$ coated layer increased but the adhesion to the substrate of SKH 51 was degraded. On the other hand, the deposition rate was independent of a partial pressure ratio and a total pressure of mixture gas. It was found that a uniform gas distribution is critical for an industrial application since the composition of a coating depends strongly on the location of a substrate inside of the furnace. As a result of milling tests with different TiC$_{x}$N$_{1-x}$ coated end mills, the one which has a low carbon concentration was better than others studied in this work.d in this work.

• Proceedings of the Korean Institute of Information and Commucation Sciences Conference
• /
• v.9 no.2
• /
• pp.865-868
• /
• 2005

We fabricated the $Pb_{0.72}La_{0.28}TiO_3 (PLT(28))$ thin film successfully by using the sol-gel method and characterized it to evaluate its potential for being utilized as the capacitor dielectrics of ULSI DRAMs. In our sol-gel process, the acetates were used as the starting materials. Through the TGA-DTA analysis, we established the excellent fabrication conditions of the sol-gel method for the PLT(28) thin film. We obtained the dense and crack-free PLT(28) thin film of 100% perovskite phase by drying at 350$^{\circ}C$ after each coating and final annealing at 650$^{\circ}C$. Electrical properties of PLT(28) thin film were measured through formation on the Pt/Ti/SiO$_2$/Si substrate and its dielectric constant and leakage current density were measured as 936 and 1.1${\mu}$A/cm$^2$, respectively

• Journal of Surface Science and Engineering
• /
• v.43 no.3
• /
• pp.132-141
• /
• 2010

NiTi alloy has been used for orthodontic wire due to good mechanical properties, such as elastic strength and frictional resistance, combined with a high resistance to corrosion. Recently, these wire were coated by polymer and ceramic materials for aesthetics. The purpose of this study was to investigate surface characteristics of polymer coated NiTi alloy wire for orthodontics using various instruments. Wires (round type and rectangular type) were used, respectively, for experiment. Polymer coating was carried out for wire. Specimen was investigated with field emission scanning electron microscopy(FE-SEM), energy dispersive x-ray spectroscopy(EDS) and atomic force microscopy(AFM). The phase transformation of non-coated NiTi wire from martensite to austenite occurred at the range of $14{\sim}15^{\circ}C$, in the case of coated wire, it occurred at the range of $16{\sim}18^{\circ}C$. Polymer coating on NiTi wire surface decreased the surface defects such as scratch which was formed at severe machined surface. From the AFM results, the average surface roughness of non-coated and coated NiTi wire was 13.1 nm, and 224.5 nm, respectively. From convetional surface roughness test, the average surface roughness of non-coated and coated NiTi wire was $0.046{\mu}m$, and $0.718{\mu}m$, respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.27 no.8
• /
• pp.516-521
• /
• 2014

An excellent hydrophobic surface has a high contact angle over 147 degree and the contact angle hysteresis below $5^0$ was produced by using roughness combined with hydrophobic PTFE coatings, which were also confirmed to exhibit an extreme adhesion to glass substrate. To form the rough surface, the glass was etched by Ar-plasma. A very thin PTFE film was coated on the plasma etched glass surface. Roughness factors before or after PTFE coating on the plasma etched glass surface, based on Wensel's model were calculated, which agrees well with the dependence of the contact angle on the roughness factor is predicted by Wensel's model. The PTFE films deposited on glass by using a conventional rf-magnetron sputtering. The glass substrates were etched Ar-plasma prior to the deposition of PTFE. Their hydrophobicities are investigated for application as a anti-fouling coating layer on the screen of displays. It is found that the hydrophobicity of PTFE films mainly depends on the sputtering conditions, such as rf-power, Ar gas content introduced during deposition. These conditions are closely related to the deposition rate or thickness of PTFE film. Thus, it is also found that the deposition rate or the film thickness affects sensitively the geometrical morphology formed on surface of the rf-sputtered PTFE films. In particular, 1,950-nm-thick PTFE films deposited for 30 minute by rf-power 50 watt under Ar gas content of 20 sccm shows a very excellent optical transmittance and a good anti-fouling property and a good durability.

• Journal of Powder Materials
• /
• v.17 no.6
• /
• pp.456-463
• /
• 2010

This paper describes the results of the application of Cr-Diamond-like carbon (DLC) films for efficiency improvement through surface modification of spur gear parts in the hydraulic gear pump. Cr-DLC films were successfully deposited on SCM 415 substrates by a hybrid coating process using linear ion source (LIS) and magnetron sputtering method. The characteristics of the films were systematically investigated using FE-SEM, nano-indentation, sliding tester and AFM instrument. The microstructure of Cr-DLC films turned into the dense and fine grains with relatively preferred orientation. The thickness formed in our Cr buffer layer and DLC coating layer were obtained the 487 nm and $1.14\;{\mu}m$. The average friction coefficient of Cr-DLC films considerably decreased to 0.15 for 0.50 of uncoated SCM415 material. The hardness and surface roughness of Cr-DLC films were measured 20 GPa and 10.76 nm, respectively. And then, efficiency tests were performed on the hydraulic gear pump to investigate the efficiency performance of the Cr-DLC coated spur gear. The experimental results show that the volumetric and mechanical efficiency of hydraulic gear pump using the Cr-DLC spur gear were improved up to 2~5% and better efficiency improvement could be attributed to its excellent microstructure, higher hardness, and lower friction coefficient. This conclusion proves the feasibility in the efficiency improvement of hydraulic gear pump for industrial applications.

• Journal of Conservation Science
• /
• v.31 no.1
• /
• pp.13-20
• /
• 2015

Surface of the wooden cultural heritage has been protected from moisture by natural oils (such as perilla oil and tung oil), which accelerated degradation. But we can find seldom the research on the processes and performances of oil coatings. In this study, the water resistant performances by wood direction were compared to 3 types of natural oil and 2 types of oil stain, and the effect of additional indoor conditioning and temperature of oil were appraised in longitudinal direction. The natural oils block moisture about 79.2% comparing to the control in longitudinal direction. Especially the tung oil showed the outstanding water resistance about 90.5%. The water resistant performances decreased about 8.8% by additional indoor conditioning for 2 years. Heated oil improved the water resistance about average 5.0%.(Max. 9.6% with linseed oil).

• Journal of Surface Science and Engineering
• /
• v.38 no.3
• /
• pp.100-105
• /
• 2005

Cr-Si-C-N coatings were deposited on steel substrate (SKD 11) by a hybrid system of arc ion plating (AIP) and sputtering techniques. From XRD, XPS, and HRTEM analyses, it was found that Cr-Si-C-N had a fine composite microstructure comprising nano-sized crystallites of Cr(C, N) well distributed in the amorphous phase of $Si_3N_4/SiC$ mixture. Microhardness of Cr(C, N) coatings and Cr-Si-N coatings were reported about $\~22 GPa$ and $\~35 GPa$, respectively. As the Si was incorporated into Cr(C, N) coatings, The Cr-Si-C-N coatings having a Si content of $9.2 at.\%$ showed the maximum hardness value. As increased beyond Si content of $9.2 at.\%$, the interaction between nanocrystallites and amorphous phase was gone, the hardness was reduced as dependent on amorphous phase of $Si_3N_4/SiC$. In addition, the average coefficient of Cr-Si-C-N coatings largely decreased compared with Cr(C, N) coatings.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.511-511
• /
• 2007

Low-emissivity (low-e) coatings with visible transparency have attracted increased interest m reducing heat radiation loss through window panes from ecological and sustainable aspects. $TiO_2$-silver transparent thin films for low-e have good properties for UV and IR blocking as well as photocatalyst compared to that with commercial UV blocking films such as fluorine doped oxide (FTO), antimony doped tin oxide (ATO), etc. In this study, transparent $TiO_2$-silver thin films were prepared by successive ink-jet printing of commercial nano silver and $TiO_2$ sol. The $TiO_2$ sol, as ink for ink-jet printing, were synthesized by hydrothermal process in the autoclave externally pressurized with $N_2$ gas of 200 bar at $120^{\circ}C$ for 10 hrs. The synthesized $TiO_2$ sols were all formed with brookite phase and their particle size was several to 30 nm. At first nano sized silver sol was coated on glass substrate, after that $TiO_2$ sol was coated by ink-jet printing. With increasing coating thickness of $TiO_2$-silver multilayer by repeated ink-jet coating, the absorbance of UV region (under 400nm) and IR region (over 700nm) also increase reasonably, compared to that with commercial UV blocking films.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.33 no.6
• /
• pp.465-470
• /
• 2020

Heterolayered K(Ta,Nb)O₃/Pb(Zr,Ti)O₃ thin films on Pt/Ti/SiO₂/Si substrates were prepared by a sol-gel process and spin-coating method. The structural and electrical properties were measured to investigate the possibility of application as an electrocaloric effect device. All specimens exhibited dense and uniform cross-sectional structures without pores, and the average thickness of the specimen coated six times was approximately 394 nm. Curie temperatures were observed at 5℃ or less in type-I and 10℃ in type-II specimens, respectively. Type-II specimens coated 6 times showed a relative dielectric constant of 758 and remanent polarization of 9.71 μC/㎠ at room temperature. The maximum electrocaloric effect occurred between 20 and 25℃, slightly higher than their Curie temperature, and the electrocaloric property (ΔT) of the type-II specimens coated 6 times was approximately 1.2℃ at room temperature.