• Analytical Science and Technology
• /
• v.6 no.2
• /
• pp.207-215
• /
• 1993

$Si_3N_4$ powders were mixed with sintering additives($3Y_2O_3{\cdot}5Al_2O_3$, YAG) by coprecipitation method. Mixing homogeneity, sintered and mechanical properties of coprecipitation-mixed powder compacts were compared with those of mechanically-mixed ones. SIMS-analysis for composition on the surface and in the matrix of prepared powder mixtures showed that the added YAG exists mainly on the $Si_3N_4$ powder surfaces in a form of coating. From this result it could be concluded that coprecipitation method is superior to mechanical mixing in the mixing homogeneity. This mixing homogeneity can accompany an improvement in sintered density, microstructure and consequently the mechanical properties of sintered bodys.

• Textile Coloration and Finishing
• /
• v.11 no.4
• /
• pp.1-7
• /
• 1999

Urethane-acrylate propelymers for secondary coating of optical fiber and high - performance material were prepared from the 4,4'-diphenylmethane diisocyanate(MDI), poly(tetramethylene oxide)glycol(PTMG, Mw 650 or 1000), 1,6-hexanediol(HD), 2-hydroxyethyl acrylate(HEA), and dibutyltin dilaurate as a catalyst. UV-Curable polyurethane acrylates were formulated from the urethane-acrylate prepolymers, three types of reactive diluents(DTs) having mono-, di-, and trifunctional-phenoxyethyl acrylate(PEA), hexanediol diacrylate(HDDA), and trimethylolpropane triacrylate(TMPTA), and 1-hydtoxycyclohexyl phenyl ketone(Irgacure 184) as a photoinitiator. The UV-cured films of polyurethane acrylates were obtained by curing using a medium-pressure mercury lamp(U W/cm, $\lambda_{max}=365\;nm)$. In this work, the effects of molecular weights of polyol and diol with low molecular weight into polymer chain on mechanical and dynamic mechanical properties of UV-cured polyurethane acrylates were studied. The structure and properties of the films obtained from the UV photopolymerization of urethane-acrylate prepolymer were investigated by FT-IR spectroscopy, dynamic mechanical measurement, tensile testing, and X-ray diffractometry.

• Journal of Adhesion and Interface
• /
• v.18 no.4
• /
• pp.159-165
• /
• 2017

In this study, we synthesized UV-curable urethane acrylates with different contents of BA, reactive diluent and characterized their physical properties such as thermal, mechanical properties, adhesive strength and flexibility resistance. From a result of DSC, Tg of polyol and acrylate resin were separated as the BA content increased more than 40%. Also, tensile strength, elongation and adhesive strength decreased with increasing the BA content. The UV-curable urethane acrylate with 40% BA has shown good flexibility resistance compared to other resin due to poor hardness and Tm of acrylate resin.

• Journal of Surface Science and Engineering
• /
• v.40 no.6
• /
• pp.279-282
• /
• 2007

Cr-Mo-Si-C-N coatings were deposited on steel and Si wafer by a hybrid system of AIP and sputtering techniques using Cr, Mo and Si target in $Ar/N_2/CH_4$ gaseous mixture. Instrumental analyses of XRD and XPS revealed that the Cr-Mo-Si-C-N coatings must be a composite consisting of fine(Cr, Mo and Si)(C and N) crystallites and amorphous $Si_3N_4$ and SiC. The hardness value of Cr-Mo-Si-C-N coatings significantly increased from 41 GPa of Cr-Mo-C-N coatings to about 53 GPa with Si content of 9.3 at.% due to the refinement of (Cr, Mo and Si)(C and N) crystallites and the composite microstructure characteristics. A systematic investigation of the microstructures and mechanical properties of Cr-Mo-Si-C-N coatings prepared with various Si contents is reported in this paper.

• Journal of the Korean Ceramic Society
• /
• v.37 no.3
• /
• pp.233-239
• /
• 2000

Sr0.9Bi2+xTa2O9(x=0, 0.1, 0.2, 0.3) thin films on IrO2/SiO2/Si or Pt/Ti/SiO2/Si substrate were prepared by spin coating method using SBT stock solutions synthesized by MOD process. SBT thin films on IrO2 transformed to layered perovskite phase at $700^{\circ}C$, but showed low breakdown voltage due to their porous microstructure. The smaple of Sr0.9Bi2+xTa2O9 composition showed the best dielectric and electrical properties. When the sample of the same composition was annealed at 80$0^{\circ}C$, the dielectric and electric properties were improved due to the grian growth and dense surface. the remanent polarization values(2Pr) at $\pm$3 V for IrO2 and Pt electrodes were 10.5, 7.15$\mu$C/$\textrm{cm}^2$, respectively. The SBT thin film with IrO2 electrode showed the lower coercive field. The leakage current density and breakdown voltage of SBT thin films on IrO2 were higher than those on Pt.

• Transactions on Electrical and Electronic Materials
• /
• v.7 no.3
• /
• pp.129-133
• /
• 2006

Ferroelectric PZT heterolayered thick films were fabricated by the alkoxide-based sol-gel method. PZT(20/80) and PZT(80/20) paste were made and alternately screen-printed on the alumina substrates. The coating and drying procedure was repeated 4 times to form the heterolayered thick films. The thickness of the PZT heterolayered thick films was approximately $60{\mu}m$. All PZT thick films showed the typical XRD patterns of a polycrystalline rhombohedral structure. And in the PZT thick films sintered at $1100^{\circ}C$, the pyrochlore phase was observed due to the evaporation of PbO. The relative dielectric constant and the dielectric loss of the PZT thick films sintered at $1050^{\circ}C$ were 445.2 and 1.90 % at 1 kHz, respectively. The remanent polarization and coercive field of the PZT thick films sintered at $1050^{\circ}C$ were $14.15{\mu}C/cm^2$ and 19.13 kV/cm, respectively.

• Electrical & Electronic Materials
• /
• v.8 no.5
• /
• pp.606-610
• /
• 1995

In this study, Pb(Z $r_{0.52}$ $Ti_{0.48}$) $O_{3}$ ceramic thin films were fabricated from an alkoxide-based by Sol-Gel method. Pb(Z $r_{0.52}$ $Ti_{0.48}$) $O_{3}$ stock solution was made and spin-coated on the Pt/ $SiO_{2}$/Si substrate at 4000[rpm] for 30[sec.]. Coated specimens were chied at 400[.deg. C] for 10[min]. The coating process was repeated 6 times and then heat-treated at 500-800[.deg. C] and 1 hour. The final thickness of the thin films were about 4800[.angs.]. The ferroelectric perovskite phases precipitated under the sintering of 700[.deg. C] for 1 hour. Pb(Z $r_{0.52}$ $Ti_{0.48}$) $O_{3}$ thin films sintered at 700[.deg. C] for 1 hour showed good dielectric and ferroelectric properties.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2003.05c
• /
• pp.200-203
• /
• 2003

Ferroelectric europium-substitution $Bi_4Ti_3O_{12}$ thin films were fabricated by spin-coating onto a Pt/Ti/$SiO_2$/Si substrate. The $Bi_{3.25}Eu_{0.75}Ti_3O_{12}$ (BET) films have polycrystalline structure annealed at 700 C. We investigated that the influence of $Bi_4Ti_3O_{12}$ thin films by substituting for Bi ions with Bi ions using X-ray diffraction (XRD), scanning electron microscopy (SEM), and X-ray photoelectron spectroscopy (XPS). From the XPS measurement, it was suggested that the stability of the metal-oxygen octahedral should be related to substitute for Bi ions with Eu ions at annealed $800^{\circ}C$. The BET thin films showed a large remanent polarization (2Pr) of $60.99C/cm^2$ at an applied voltage of 10 V. The BET thin films exhibited no significant degradation of switching charge at least up to $5{\times}10^9$ switching cycles at a frequency of 50 kHz.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.9
• /
• pp.808-811
• /
• 2008

Optical and mechanical properties of diamond-like carbon (DLC) films synthesized by RF plasma enhanced chemical vapor deposition were investigated as a function the C/H ratio in gas mixture. The C/H ratio was varied from 6 to 10 %, adjusting the amount of $CH_4$ and $H_2$ as the source gas. The optical and mechanical properties of DLC films were characterized by UV spectrometer, Ellipsometer and Nano-indenter. The change of the C/H ratio during synthesis of DLC films had many effects on the growth rate, transmittance, refractive index and hardness. The growth rate of the films increased exponentially with the increase in C/H ratio. The hardness of the films showed the tendency to improve with increasing C/H ratio, whereas the transmittance decreased. The refractive index was varied from 2.03 to 2.17, and these refractive indexes close to 2.0 indicates that it can be applied to Si-based solar cell.

• Journal of Sensor Science and Technology
• /
• v.22 no.5
• /
• pp.315-320
• /
• 2013

In this paper, the properties of strain sensors made of spin-capable multi-walled carbon nanotubes (MWCNTs) were characterized and their sensing mechanisms analyzed. The key contribution of this paper is a new fabrication technique that introduces a simpler transfer method compared to spin-coating or dispersion CNT. Resistance of the MWCNT sheet strain sensor increased linearly with higher strain. To investigate the effect of CNT concentration on sensitivity, two strain sensors with different layer numbers of MWCNT sheets (one and three layers) were fabricated. According to the results, the sensor with a three-layer sheet showed higher sensitivity than that with one layer. In addition, experiments were conducted to examine the effects of environmental factors, temperature, and gas on sensor sensitivity. An increase in temperature resulted in a reduction in sensor sensitivity. It was also observed that ambient gas influenced the properties of the MWCNT sheet due to charge transfer. Experimental results showed that there was a linear change in resistance in response to strain, and the resistance of the sensor fully recovered to its unstressed state and exhibited stable electromechanical properties.